CN106590336A - Water-based anticorrosive coating and manufacturing method thereof - Google Patents
Water-based anticorrosive coating and manufacturing method thereof Download PDFInfo
- Publication number
- CN106590336A CN106590336A CN201611130528.6A CN201611130528A CN106590336A CN 106590336 A CN106590336 A CN 106590336A CN 201611130528 A CN201611130528 A CN 201611130528A CN 106590336 A CN106590336 A CN 106590336A
- Authority
- CN
- China
- Prior art keywords
- water
- parts
- based anticorrosive
- anticorrosive paint
- added
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A color plate housing of a solar water tank is prone to abrasion due to being exposed in air. Although the most universal, most economical and most practical protection measure so far is coating protection, solvent based coatings are usually adopted at present, the coatings containing harmful gas that easily harms a human body, so as to result in the problem of environment pollution. Meanwhile, the characteristics of flammabilityand combustibility of the solvent bring unsafe hidden dangers. The invention relates to the field of coating manufacturing, in particular to a water-based anticorrosive coating and a manufacturing method thereof. The water-based anticorrosive coating comprises the following components in parts by weight: distilled water, mica iron oxide, aluminum tripolyphosphate, talcum powder, mica powder, hollow microspheres, silica fume, an epoxy resin emulsion, acrylic resin, a defoaming agent, a dispersing agent, a flatting agent and a curing agent. The water-based anticorrosive coating, which is not added with an organic solvent, can reduce harm to the human body and the environment, and is good in film-forming property, easy to use, high in adhesive force and good in anticorrosive performance.
Description
Technical field
The present invention relates to coating manufacture field, specifically a kind of water-based anticorrosive paint and preparation method thereof.
Background technology
The phenomenon that metal is damaged by chemistry or the electrochemical action of surrounding medium is referred to as metal erosion.At present too
It is positive can water tank be substantially exposed to outdoor, the work of the medium such as oxygen, water, the electrolyte ion of the color steel surface of shell around it
With under, there is burn into heavy corrosion or damage with accumulating over a long period, or even cause a serious accident and huge economic losses.People adopt
Many measure protection solar water container shells have been taken, but protective measure most universal, most economical, most practical so far is still applied
Material protection, anticorrosion with coat with its easy construction, it is economic and practical, fill not by device area, the constraint of shape and with certain
Decorations effect the features such as and be widely used.At present frequently be solvent based coating, although they have the works for suppressing corrosion
With, but because they contain the harmful gass that infringement is easily caused to human body, cause problem of environmental pollution, while solvent it is inflammable,
Explosive the characteristics of, brings unsafe hidden danger to environment.With increasingly enhancing of the people to environmental consciousness, water paint becomes
The important directions and study hotspot of paint development.In water-based anticorrosive paint, the anti-corrosion that water corrosion-resistant epoxy paint is projected because of it
Performance and become the research emphasis in water paint.
The content of the invention
In order to solve the above problems, the invention provides a kind of water-based anticorrosive paint and preparation method thereof, particular technique side
Case is as follows：
A kind of water-based anticorrosive paint includes following components by weight percent distilled water 50-55 parts, micaceous iron oxide 6-12 parts, aluminium triphosphate
5-15 parts, Pulvis Talci 5-10 parts, mica powder 3-10 parts, cenosphere 5-12 parts, wollastonite powder 5-15 parts, epoxy resin latex 30-
45 parts, acrylic resin 10-15 parts, defoamer 0.2-1.0 parts, dispersant 0.2-1.0 parts, levelling agent 0.2-1.0 parts, firming agent
0.2-1.5 parts.
Preferably, the defoamer is polydimethylsiloxane or polyether-silicone.
Preferably, the dispersant is modified siloxane or polymeric carboxylic.
Preferably, the levelling agent is polyester-modified polysiloxanes or polydimethylsiloxane.
Preferably, the firming agent is ethylenediamine or triethylene tetramine.
A kind of method of the water-based anticorrosive paint prepared described in claim 1 is comprised the following steps：
（1）Distilled water is added in high-speed shearing emulsion machine, the dispersant and defoamer of the proportioning is added, starts dispersed with stirring,
Mixed liquor is obtained after stirring 5-15 minutes；
（2）Successively micaceous iron oxide, aluminium triphosphate, Pulvis Talci, mica powder, cenosphere, wollastonite powder are added by the proportioning,
Shearing is then sent through being ground to fineness in basket type sand mill and is not more than 30 after being uniformly dispersed, and obtains mixture；
（3）In step（2）The epoxy resin latex and step of the proportioning are added in the mixture of gained（1）Gained mixed liquor is stirred
5-25 minutes are mixed, mixed liquor is obtained；
（4）In step（3）The levelling agent of the proportioning is added in the mixed liquor of gained, solution PH is determined with acidometer after 20 minutes
Value, adds ammonia to adjust paint vehicle to 8 ~ 9, and mixed liquor is obtained after stirring；
（5）In step（4）The firming agent of the proportioning is added in gained mixed liquor, stirring is not stopped while adding until
It is even, the coating can be obtained after placing half an hour.
Preferably, the stirring is stirred with the speed of 40-60r/min.
Preferably, the step（2）The middle basket type sand mill speed of mainshaft be 3000-5000r/min, milling time be 45 ~
70min。
Beneficial effects of the present invention are：
1st, water-based anticorrosive paint of the invention does not add organic solvent, it is possible to reduce the harm to human body and environment；
2nd, water-based anticorrosive paint good film-forming property of the invention, use are simple；
3rd, the proportion optimizing of water-based anticorrosive paint of the present invention substantially increase water-based anticorrosive paint and color steel adhesive force,
Antiseptic property, hardness and chemical-resistance.
Specific embodiment
In order to be better understood from the present invention.With reference to specific embodiment, the present invention will be further described：
Embodiment one：
A kind of water-based anticorrosive paint includes 50 parts of following components by weight percent distilled water, 6 parts of micaceous iron oxide, 5 parts of aluminium triphosphate, cunning
5 parts of stone powder, 3 parts of mica powder, 5 parts of cenosphere, 5 parts of wollastonite powder, 30 parts of epoxy resin latex, 10 parts of acrylic resin, poly- two
0.2 part of methylsiloxane, 0.2 part of modified siloxane, 0.2 part of polyester-modified polysiloxanes, 0.2 part of ethylenediamine.
The preparation method of described water-based anticorrosive paint is comprised the following steps：
（1）Distilled water is added in high-speed shearing emulsion machine, the modified siloxane and polydimethylsiloxane of the proportioning is added, is opened
Begin, with the speed dispersed with stirring of 40r/min, after stirring 5-15 minutes mixed liquor to be obtained；
（2）Successively micaceous iron oxide, aluminium triphosphate, Pulvis Talci, mica powder, cenosphere, wollastonite powder are added by the proportioning,
Shearing is then sent through basket type sand mill with the speed of mainshaft as 3000r/min after being uniformly dispersed, and milling time is ground to fineness for 45min
No more than 50, obtain mixture；
（3）In step（2）The epoxy resin latex and step of the proportioning are added in the mixture of gained（1）Gained mixed liquor with
The speed stirring 5-25 minutes of 40r/min, obtain mixed liquor；
（4）In step（3）The levelling agent of the proportioning is added in the mixed liquor of gained, solution PH is determined with acidometer after 20 minutes
Value, adds ammonia to adjust paint vehicle to 8 ~ 9, and mixed liquor is obtained after stirring；
（5）In step（4）The firming agent of the proportioning is added in gained mixed liquor, is not stopped with 40r/min's while adding
Speed is stirred until uniformly, and the coating can be obtained after placing half an hour.
Embodiment two：
A kind of water-based anticorrosive paint include 55 parts of following components by weight percent distilled water, 12 parts of micaceous iron oxide, 15 parts of aluminium triphosphate,
10 parts of Pulvis Talci, 10 parts of mica powder, 12 parts of cenosphere, 15 parts of wollastonite powder, 45 parts of epoxy resin latex, acrylic resin 15
Part, 1 part of polyether-silicone, 1 part of polymeric carboxylic, 1 part of polydimethylsiloxane, 1.5 parts of triethylene tetramine.
The preparation method of described water-based anticorrosive paint is comprised the following steps：
（1）Distilled water is added in high-speed shearing emulsion machine, the polymeric carboxylic and polyether-silicone of the proportioning is added, is started
With the speed dispersed with stirring of 60r/min, after stirring 5-15 minutes mixed liquor is obtained；
（2）Successively micaceous iron oxide, aluminium triphosphate, Pulvis Talci, mica powder, cenosphere, wollastonite powder are added by the proportioning,
Shearing is then sent through basket type sand mill with the speed of mainshaft as 5000r/min after being uniformly dispersed, and milling time is ground to fineness for 70min
No more than 30, obtain mixture；
（3）In step（2）The epoxy resin latex and step of the proportioning are added in the mixture of gained（1）Gained mixed liquor with
The speed stirring 5-25 minutes of 60r/min, obtain mixed liquor；
（4）In step（3）The levelling agent of the proportioning is added in the mixed liquor of gained, solution PH is determined with acidometer after 20 minutes
Value, adds ammonia to adjust paint vehicle to 8 ~ 9, and mixed liquor is obtained after stirring；
（5）In step（4）The firming agent of the proportioning is added in gained mixed liquor, is not stopped with 60r/min's while adding
Speed is stirred until uniformly, and the coating can be obtained after placing half an hour.
The present invention is not limited to above-described specific embodiment, the foregoing is only the preferable case study on implementation of the present invention
, not to limit the present invention, all any modifications made within the spirit and principles in the present invention, equivalent and change
Enter, should be included within the scope of the present invention.
Claims (8)
1. a kind of water-based anticorrosive paint, it is characterised in that：The water-based anticorrosive paint includes following components by weight percent distilled water 50-55
Part, micaceous iron oxide 6-12 parts, aluminium triphosphate 5-15 parts, Pulvis Talci 5-10 parts, mica powder 3-10 parts, cenosphere 5-12
Part, wollastonite powder 5-15 parts, epoxy resin latex 30-45 parts, acrylic resin 10-15 parts, defoamer 0.2-1.0 parts, dispersant
0.2-1.0 parts, levelling agent 0.2-1.0 parts, firming agent 0.2-1.5 parts.
2. a kind of water-based anticorrosive paint according to claim 1, it is characterised in that：The defoamer is polydimethylsiloxanes
Alkane or polyether-silicone.
3. a kind of water-based anticorrosive paint according to claim 1, it is characterised in that：The dispersant be modified siloxane or
Polymeric carboxylic.
4. a kind of water-based anticorrosive paint according to claim 1, it is characterised in that：The levelling agent is the poly- silicon of polyester modification
Oxygen alkane or polydimethylsiloxane.
5. a kind of water-based anticorrosive paint according to claim 1, it is characterised in that：The firming agent is ethylenediamine or three second
Alkene tetramine.
6. a kind of method of the water-based anticorrosive paint prepared described in claim 1, it is characterised in that：Comprise the following steps：
（1）Distilled water is added in high-speed shearing emulsion machine, the dispersant and defoamer of the proportioning is added, starts dispersed with stirring,
Mixed liquor is obtained after stirring 5-15 minutes；
（2）Successively micaceous iron oxide, aluminium triphosphate, Pulvis Talci, mica powder, cenosphere, wollastonite powder are added by the proportioning,
Shearing is then sent through being ground to fineness in basket type sand mill and is not more than 50 after being uniformly dispersed, and obtains mixture；
（3）In step（2）The epoxy resin latex and step of the proportioning are added in the mixture of gained（1）Gained mixed liquor is stirred
5-25 minutes are mixed, mixed liquor is obtained；
（4）In step（3）The levelling agent of the proportioning is added in the mixed liquor of gained, solution PH is determined with acidometer after 20 minutes
Value, adds ammonia to adjust paint vehicle to 8 ~ 9, and mixed liquor is obtained after stirring；
（5）In step（4）The firming agent of the proportioning is added in gained mixed liquor, stirring is not stopped while adding until
It is even, the coating can be obtained after placing half an hour.
7. a kind of method of water-based anticorrosive paint prepared described in claim 1 according to claim 6, its feature exists
In：The stirring is stirred with the speed of 40-60r/min.
8. a kind of method of water-based anticorrosive paint prepared described in claim 1 according to claim 6, its feature exists
In：The step（2）The middle basket type sand mill speed of mainshaft is 3000-5000r/min, and milling time is 45 ~ 70min.