CN1519105A - 一种聚四氟乙烯微孔薄膜层压保暖材料的制备方法 - Google Patents

一种聚四氟乙烯微孔薄膜层压保暖材料的制备方法 Download PDF

Info

Publication number
CN1519105A
CN1519105A CNA031008143A CN03100814A CN1519105A CN 1519105 A CN1519105 A CN 1519105A CN A031008143 A CNA031008143 A CN A031008143A CN 03100814 A CN03100814 A CN 03100814A CN 1519105 A CN1519105 A CN 1519105A
Authority
CN
China
Prior art keywords
microporous membrane
insulating material
heat insulating
material formed
polytetrafluoroethylmicroporous microporous
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA031008143A
Other languages
English (en)
Inventor
张建春
郝新敏
郭玉海
王�锋
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Research Center of Soldier System, Institute of Military Equipment, General Logistics of People's Liberation Army of China
Shanghai New &. Special Textile Material Research Center Co., Ltd.
Zhejiang Sci Tech University ZSTU
Original Assignee
Shanghai New & Special Textile Material Research Center Co Ltd
Research Center Of Soldier System Institute Of Military Equipment General Logistics Of People's Liberation Army Of China
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai New & Special Textile Material Research Center Co Ltd, Research Center Of Soldier System Institute Of Military Equipment General Logistics Of People's Liberation Army Of China filed Critical Shanghai New & Special Textile Material Research Center Co Ltd
Priority to CNA031008143A priority Critical patent/CN1519105A/zh
Publication of CN1519105A publication Critical patent/CN1519105A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种聚四氟乙烯微孔薄膜层压保暖材料的制备方法，通过针刺、水刺加工处理，将羽绒、涤纶、腈纶、粘胶、羊毛类纤维加工成无纺布絮毡；使用粘合剂，将聚四氟乙烯微孔薄膜与絮毡粘合，或将聚四氟乙烯微孔薄膜与絮毡叠和，制备成层压保暖材料。该保暖材料的透湿量高达9120g/m224h，耐水压72KPa，1.2克罗值。该保暖材料可广泛用于运动服、风衣、夹克、防寒服、防寒大衣、防寒鞋靴等。本发明与已有技术相比，具有工艺简单、成本低，且经济效益和社会效益显著的优点。

Description

一种聚四氟乙烯微孔薄膜层压保暖材料的制备方法
技术领域
本发明涉及一种聚四氟乙烯微孔薄膜层压保暖材料的制备方法，该方法是将聚四氟乙烯微孔薄膜与保暖絮片或无纺布叠和或粘合，加工成新型的具有防水、透湿、防风、轻便的保暖材料。
背景技术
目前的保暖絮片存在一个共同的缺点，即保暖量较低。若希望达到较高的克罗值，必须增加絮片的厚度，这就带来臃肿、笨重、不贴身等问题。用聚四氟乙烯微孔薄膜制成的防水透湿层压织物是集防水、透湿、防风等功能于一身的高科技产品。薄膜厚度为10～30微米，孔径0.1～0.3微米，每平方英寸上约有90亿个微孔，开孔率高达80％以上。聚四氟乙烯微孔薄膜具有优良的防风性能，防止空气形成对流，有效减小热量的散失。因此，需要提出一种聚四氟乙烯微孔薄膜层压保暖材料的制备方法。
发明内容
本发明的目的是提供一种聚四氟乙烯微孔薄膜层压保暖材料的制备方法，该方法是将聚四氟乙烯微孔薄膜与保暖絮片或无纺布叠和或粘合，加工成新型的具有防水、透湿、防风、轻便的保暖材料。
本发明的目的是这样实现的：一种聚四氟乙烯微孔薄膜层压保暖材料的制备方法，其步骤是：
a、通过针刺、水刺加工处理，将羽绒、涤纶、腈纶、粘胶、羊毛类纤维物品加工成无纺布絮毡；
b、使用粘合剂，将聚四氟乙烯微孔薄膜与絮毡粘合，或将聚四氟乙烯微孔薄膜与絮毡叠和，制备成层压保暖材料。
本发明与已有技术相比，具有透湿量和耐水压高、保暖量高、工艺简单、成本低，且经济效益和社会效益显著的优点。
具体实施方式
实施例一：
一种聚四氟乙烯微孔薄膜层压保暖材料的制备方法，其步骤如下：
a、通过针刺、水刺加工处理，将羽绒、涤纶、腈纶、粘胶、羊毛类纤维物品加工成无纺布絮毡；
b、使用粘合剂，将聚四氟乙烯微孔薄膜与絮毡粘合，或将聚四氟乙烯微孔薄膜与絮毡叠和，制备成层压保暖材料。
在本实施例中，所用粘合剂可以在如下的粘合剂中任选一种，所述的粘合剂为聚酰胺、有机硅、乙烯-醋酸乙酯、聚酯或聚氨酯。
本实施例所述的粘合方式为撒粉、粉点、浆点、双点、熔融胶点、裂纹薄膜、喷涂或刮涂方式中的一种。
本实施例所用的纤维物品可以在如下的纤维物品中任选一种，所述纤维物品是羽绒、涤纶、腈纶、粘胶或羊毛。
实验结果表明，通过本发明的方法可生产出具有防水、透湿、轻便等特点的聚四氟乙烯微孔薄膜层压保暖材料。例如，采用与羽绒絮毡粘合的保暖材料其透湿量高达9120g/m2 24h(按GB/T12704-91中干燥杯法测试)，耐水压72Kpa(按GB4744-84测试)，1.2克罗值(利用暖体假人测试，测试温度-9℃，湿度30％，风速3m/s，)。该保暖材料可广泛用于运动服、风衣、夹克、防寒服、防寒鞋靴等。
实施例二：
一种聚四氟乙烯微孔薄膜层压保暖材料的制备方法，其步骤如下：
a、通过喷雾，将抗静电剂和粘合剂的混合液体喷在洗净的羽绒上，密闭2小时。然后与羊毛、腈纶、涤纶、粘胶混合，开松后，梳理成网。最后经过针刺制成絮毡；
b、采用浆点施胶方式，将聚酰胺粘合剂转移到聚四氟乙烯微孔薄膜上，将聚四氟乙烯微孔薄膜与上述絮毡复合，于130℃烘干，制成具有防水、透湿、防风、轻便等特点的聚四氟乙烯微孔薄膜层压保暖材料，其性能见表1。
此外，还可以将聚四氟乙烯微孔薄膜与机织布粘合，再与絮毡叠和，制成具有防水、透湿、防风、轻便等特点的聚四氟乙烯微孔薄膜层压保暖材料。
表1  本发明制作的保暖材料的性能*
透湿量，g/m2·24h     9120
耐水压，Kpa     72
透气量，ml/m2·s     3427
克罗值(利用暖体假人测试，测试温度-9℃，湿度30％，风速3m/s，)     1.2
透湿量按GB/T12704-91中干燥杯法测试，耐水压按GB4744-84测试，透气量按GB5455-85测试。

Claims (4)

1、一种聚四氟乙烯微孔薄膜层压保暖材料的制备方法，其特征在于：
a、通过针刺、水刺加工处理，将羽绒、涤纶、腈纶、粘胶、羊毛类纤维物品加工成无纺布絮毡；
b、使用粘合剂，将聚四氟乙烯微孔薄膜与絮毡粘合，或将聚四氟乙烯微孔薄膜与絮毡叠和，制备成层压保暖材料。
2、根据权利要求1所述的聚四氟乙烯微孔薄膜层压保暖材料的制备方法，其特征在于：所述的粘合剂为聚酰胺、有机硅、乙烯-醋酸乙酯、聚酯或聚氨酯中的一种。
3、根据权利要求1所述的聚四氟乙烯微孔薄膜层压保暖材料的制备方法，其特征在于：所述的粘合方式为撒粉、粉点、浆点、双点、熔融胶点、裂纹薄膜、喷涂或刮涂中的一种。
4、根据权利要求1所述的聚四氟乙烯微孔薄膜层压保暖材料的制备方法，其特征在于：所述的纤维物品是羽绒、涤纶、腈纶、粘胶或羊毛中的一种。
CNA031008143A 2003-01-22 2003-01-22 一种聚四氟乙烯微孔薄膜层压保暖材料的制备方法 Pending CN1519105A (zh)