CN1517319A - Application of fluidized bed gangue slag of fluidized bed furnace to instead conventional engineering fine aggregate to compose architeetural grout - Google Patents
Application of fluidized bed gangue slag of fluidized bed furnace to instead conventional engineering fine aggregate to compose architeetural grout Download PDFInfo
- Publication number
- CN1517319A CN1517319A CNA031171575A CN03117157A CN1517319A CN 1517319 A CN1517319 A CN 1517319A CN A031171575 A CNA031171575 A CN A031171575A CN 03117157 A CN03117157 A CN 03117157A CN 1517319 A CN1517319 A CN 1517319A
- Authority
- CN
- China
- Prior art keywords
- fluidized bed
- mortar
- furnace slag
- boiling furnace
- fine aggregate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
An application of the gangue slage from fluidized-bed furnace in preparing building mortar without traditional fine aggregate (natural sand and artificial sand) features that said slage, cement and lime are proportionally mixed.
Description
Affiliated technical field:
The present invention relates to material of construction, particularly a kind of fluidized bed coal spoil boiling furnace slag (ash) that utilizes replaces traditional engineering fine aggregate, comprises natural sand and manually is sand, the application of preparation building mortar aggregate in construction work.
Background technology:
Slag is the products of combustion of Industrial Boiler (as coal electrician industry), and boiling furnace slag then is the products of combustion of fluidizing furnace.Fluidizing furnace claims the bubbling bed again, belongs to first-generation fluid-bed combustion furnace.Boiling Combustion is a kind of combustion technology between the grate firing of solid combustion and pulverized coal friring, its combustion principle is: fuel crushing and classification particle by under the curtain air effect that under fire grate, is blown into-just so-called by air draught " fluidisation ", rolling up and down in the space of certain altitude above fire grate is similar to the motion of liquid boiling, and the fuel staging particle carries out perfect combustion just under a kind of so violent, rambling " boiling " state.Therefore, fluidizing furnace can use high ash, Gao Shui, low heat value, low-volatile etc. difficult to burn material inferior-as coal gangue, the thorax ash that boils is exactly a boiling furnace slag.The resulting boiling furnace slag of the coal gangue particle of boiling furnace combustion crushing and classification has low temperature (850 ℃～1000 ℃) and grills thoroughly innate advantage, thereby has certain activity and corrosion resistance preferably.
At present, the discharging of fluidized bed coal spoil boiling furnace slag (ash) has taken a large amount of soils, and environment there is serious pollution, simultaneously, masonry mortar be in the masonry project one of many uses, the material of construction that consumption is big, in all kinds of masonry structures, the masonry mortar role is exactly with the monolithic brick, stone or building block gluing constitute masonry integral body altogether, need a large amount of mortar and river sand etc. of using, soil erosion influence for river course etc. is serious, destroyed the eubiosis, and cost is also high, and fluidized bed coal spoil boiling furnace slag (ash) is to have certain intensity and construction workability, can guarantee that the intensity of whole masonry satisfies design, service requirements.
Summary of the invention:
The invention provides a kind of fluidized bed coal spoil boiling furnace slag (ash) that utilizes and replace traditional engineering fine aggregate, comprise natural sand and artificial sand, the technology of preparation building mortar in construction work, this technology has solved for a long time, the pollution problem that fluidized bed coal spoil boiling furnace slag (ash) brings to environment, and steady quality, cost is low, under the condition that satisfies the engineering discipline requirement, broken the forbidden zone of people's traditional concepts, for a new road has been opened up in the comprehensive utilization of industrial residue.
Concrete technical scheme of the present invention is as follows:
The invention is characterized in: it is 20%-100% that fluidized bed coal spoil boiling furnace slag (ash) preparation building mortar replaces the ratio of traditional engineering fine aggregate.
The accumulation unit weight of fluid coal spoil boiling furnace slag of the present invention (ash) is 800-1400 kilogram/cubic meter.
The size range of fluidized bed coal spoil boiling furnace slag of the present invention (ash) is the 0.045-8 millimeter.
Fluidized bed coal spoil boiling furnace slag of the present invention (ash) with the weight proportion of cement, lime putty is: 2.5-13: 1: 0.2-1.1.
The degree of sinking to of lime putty of the present invention (denseness) is 8-14 centimetre.
Cement of the present invention is ordinary Portland cement or silicate cement, comprise from label be 325 to label be 525.
Fluidized bed coal spoil boiling furnace slag of the present invention (ash) adds water and forces to stir with after cement, lime putty mix, and makes mortar, comprises masonry mortar, plastering mortar, waterproof mortar, jointing mortar, veneer mortar.
Fluidized bed coal spoil boiling furnace slag of the present invention (ash) can be selected the furnace bottom slag ash of climbing coal gangue power plant of coal (group) company 30,000 KW fluidizing furnaces for use.
The invention solves slag emission and environmental issue, waste residue fully utilized, have following innovation point:
(1) boiling furnace slag is batch, the typing " product " of coal gangue power plant burning classification coal gangue particle, source and physicochemical property are stable than traditional fine aggregates such as river sand, mountain sand, river sand, mountain sand etc. be can solve because of changed by many unfavorable factor such as the place of production, season, granular size and grating, silt content and organic impurity to cause the building mortar quality state unsettled technical barrier that fluctuates, thereby building mortar quality and construction quality guaranteed.
(2) boiling furnace slag has low temperature and grills thoroughly character, and slag granules has Siq, Al203 isoreactivity composition, surface reaction can take place improve granular boundary intensity, and performances such as mortar strength are had long-term favourable influence, improves the masonry project weather resistance.
(3) boiling furnace slag is built mortar by laying bricks or stones and is had lower Young's modulus, favourablely under the bigger condition of the temperature difference alleviates and limits the development of masonry crack, helps improving the building aseismicity performance simultaneously, and this point is particularly useful for Panxi Diqu.
(4) having alleviated working-yard examination allotment of labor does and the quality control difficulty.Because physicochemical property, steady sources have reduced the working-yard examination and joined workload, can reduce working-yard engineering quality control difficulty, boiling furnace slag is easier to be accepted by vast construction management personnel and user for the sand technology.Under the condition that satisfies the engineering discipline requirement, broken the forbidden zone of people's traditional concepts, for a new road has been opened up in the comprehensive utilization of industrial residue.
Embodiment:
Embodiment 1
It is 100% that fluidized bed coal spoil boiling furnace slag of the present invention (ash) preparation building mortar replaces the ratio of traditional engineering fine aggregate.It piles up unit weight is 1200 kilograms/cubic metre, and its size range is the 0.045-8 millimeter.
Fluidized bed coal spoil boiling furnace slag of the present invention (ash) with the weight proportion of cement, lime putty is: 6: 1: 0.8.
The degree of sinking to of lime putty of the present invention (denseness) is 10 centimetres.
Cement of the present invention is ordinary Portland cement, and label is 325.
Fluidized bed coal spoil boiling furnace slag of the present invention (ash) adds water and forces to stir with after cement, lime putty mix, and makes mortar, comprises masonry mortar, plastering mortar, waterproof mortar, jointing mortar, veneer mortar.
Embodiment 2
Fluidized bed coal spoil boiling furnace slag of the present invention (ash) can be selected the furnace bottom slag ash of climbing coal gangue power plant of coal (group) company 30,000 KW fluidizing furnaces for use.Its physicals is: apparent state is greyish white particle, and piling up unit weight is 990-1050 kilogram/cubic meter, and its chemical ingredients mainly includes silicon-dioxide, aluminium sesquioxide etc.
This fluidized bed coal spoil boiling furnace slag (ash) belongs to (II) district sand, and grating is better, and water-intake rate is big than river sand, and voidage is suitable with river sand medium sand.
The chemical main component of lime putty is a calcium hydroxide.
Embodiment 3
After choosing 235 kilograms of 2360 kilograms of fluidized bed coal spoil boiling furnace slags (ash) and 350 kilograms of cement, lime putties and mixing, add water and force to stir, make the masonry mortar that strength grade is M5.0.
Embodiment 4
After choosing 175 kilograms of 1190 kilograms of fluidized bed coal spoil boiling furnace slags (ash) and 350 kilograms of cement, lime putties and mixing, add water and force to stir, make the masonry mortar that strength grade is M5.0.
The present invention utilizes fluidized bed coal spoil boiling furnace slag (ash) to replace traditional engineering fine aggregate, comprise natural sand and artificial sand, the technology of preparation building mortar, this technology has solved for a long time, the pollution problem that fluidized bed coal spoil boiling furnace slag (ash) brings to environment, and steady quality, cost is low, under the condition that satisfies the engineering discipline requirement, broken the forbidden zone of people's traditional concepts, for a new road has been opened up in the comprehensive utilization of industrial residue.
Claims (7)
1, fluidized bed coal spoil boiling furnace slag replaces the application of traditional engineering fine aggregate preparation building mortar, it is characterized in that: it is 20%-100% that fluidized bed coal spoil boiling furnace slag (ash) preparation building mortar replaces the ratio of traditional engineering fine aggregate.
2, fluidized bed coal spoil boiling furnace slag according to claim 1 replaces the application of traditional engineering fine aggregate preparation building mortar, and it is characterized in that: the accumulation unit weight of described fluid coal spoil boiling furnace slag (ash) is 800-1400 kilogram/cubic meter.
3, fluidized bed coal spoil boiling furnace slag according to claim 1 replaces the application of traditional engineering fine aggregate preparation building mortar, and it is characterized in that: the size range of described fluidized bed coal spoil boiling furnace slag (ash) is the 0.045-8 millimeter.
4, fluidized bed coal spoil boiling furnace slag according to claim 1 replaces the application of traditional engineering fine aggregate preparation building mortar, it is characterized in that: described fluidized bed coal spoil boiling furnace slag (ash) with the weight proportion of cement, lime putty is: 2.5-13: 1: 0.2-1.1.
5, fluidized bed coal spoil boiling furnace slag according to claim 4 replaces the application of traditional engineering fine aggregate preparation building mortar, and it is characterized in that: the degree of sinking to of described lime putty (denseness) is 8-14 centimetre.
6, fluidized bed coal spoil boiling furnace slag according to claim 4 replaces the application of traditional engineering fine aggregate preparation building mortar, and it is characterized in that: described cement is ordinary Portland cement or silicate cement, comprise from label be 325 to label be 525.
7, replace traditional engineering fine aggregate to prepare the application of building mortar according to claim 1 or 4 described fluidized bed coal spoil boiling furnace slags, it is characterized in that: described fluidized bed coal spoil boiling furnace slag (ash) is with after cement, lime putty mix, adding water forces to stir, make mortar, comprise masonry mortar, plastering mortar, waterproof mortar, jointing mortar, veneer mortar.