CN1503871A - Composite panel for repairing reinforcing con'c body and method of using the same

Info

Publication number: CN1503871A
Application number: CNA018183441A
Authority: CN
Inventors: 朴相泰; 安相镐; 曺伯纯
Original assignee: Taichang Sms Corp; MAINTENANCE PROFESSIONAL CO
Current assignee: Taichang Sms Corp; MAINTENANCE PROFESSIONAL CO
Priority date: 2000-10-30
Filing date: 2001-10-30
Publication date: 2004-06-09
Anticipated expiration: 2021-10-30
Also published as: EP1346118A4; JP2004513268A; EP1346118A1; AU1280002A; CN1265069C; CA2427218A1; AU2002212800B2; WO2002036902A1

Abstract

Disclosed are a panel for repairing and reinforcing a concrete body, a multi-purpose anchor, an anchor for level adjustment and injection a method for repairing and reinforcing the concrete body using the same, which can connect adhesives and anchors at weak parts of the concrete body, which is neutralized, aged, deteriorated, cracked due to water leakage, or segregated, or at parts requiring the repair and reinforcement due to a change in use environment. The composite reinforced panel includes lightweight concrete, high strength concrete or a steel plate and reinforcing means, thereby being effectively prevented from bad environments causing a drop of reinforcing capacity, providing good heatproof and fireproof properties, and maximizing merits of materials used as the reinforcing means. The multi-purpose anchor has a bolt and an injection pipe, fixes the panel to the concrete body effectively, serves as a spacer maintaining a prescribed interval between the panel and the concrete body, and serves to inject filler and discharge the inside air to the outside, thereby improving construction efficiency. The anchor for level adjustment and injection has a male screw and a female screw at an end and an injection pipe of a straw type, thereby improving the construction efficiency when the concrete panel is installed.

Description

Be used to repair, strengthen the composite plate and the using method thereof of concrete body

Technical field

The present invention relates to a kind ofly to be used to repair, strengthen the plate of concrete body, multi-functional holdfast (anchor), be used to adjust height and the holdfast that injects and use these to repair and strengthen the method for concrete body.More specifically, the present invention relates to a kind of plate, multi-functional holdfast that is used to repair, strengthen concrete body, be used for the holdfast of Height Adjustment and injection and use these to repair and strengthen the method for concrete body, wherein said plate can be connected cementing agent and holdfast the vulnerable area (weak part) of described concrete body, described vulnerable area for neutrality, aging, that damage, since water leak produces the crack or separated portions, perhaps be connected because the environment for use change needs the part of reparation and reinforcement.

Background technology

People it is generally acknowledged that the concrete body of reinforcement is semi-permanent, but the concrete body of strengthening is because different former thereby aging and damages, outer owing to the dry change of peeling off, shrink and expand, design error, construction error, fatigue load, environment for use such as the burn into of neutralization, reinforcement steel, therefore described concrete body is along with the change of time and use annular need repair and strengthen.Therefore, people have researched and developed deterioration and reparation and the described concrete body of reinforcement that new material and new building method are used to suppress structure.

Recently, be used to repair and the conventional method of strengthening concrete body has: the carbon fibre thin plate adds strong method (carbon fiber sheet reinforcing method), glass fiber thin plate and adds strong method (glass fiber sheet reinforcing method), aramid fibre thin plate and add strong method (aramide fiber sheet reinforcing method), steel plate bonding and add strong method, be used to strengthen wherein to contain the method or the like of the synthetic resin board of reinforcing fibre and hot setting glue.In addition, the concrete body restorative procedure is paved (pitching) method and cross section restored method.

Described carbon fibre thin plate adds strong method, glass fiber thin plate and adds strong method and aramid fibre thin plate and add strong method and finish in the following manner: the concrete body that strengthen is carried out surfacing, apply prime paint from the teeth outwards, utilize the expoxy putty agent to make become level and of this surface with in fibre building board (carbon fibre thin plate, glass fiber thin plate or aramid fibre thin plate) dipping (impregnate) concrete body and make it pass through epoxy resin (being used for bonding and dipping) and described concrete body bonding.

Adopt fibre building board this to add strong method be light-duty, and have good operating characteristics, anticorrosive, high strength, high elastic coefficient, the tolerance of salinity and chemical resistance.But, adopt the strong method that adds of fibre building board to have several problems: a little less than its heat resistance and the fire line, to cause the loss of life and property thereby therefore when catching fire, can produce rapid decline of toxic gas and stiffening effect.And, adopting this main processing procedure that adds strong method of reinforcing fibre is the dipping of reinforcing fibre, but in fact, can not finish ideal because the condition official post of building site gets the impregnation process of reinforcing fibre, and the stiffening effect after finishing and actual conditions are by the constructor's of building site technical level decision.Also have, this method need be carried out repeatedly lamination process to guarantee suitable reinforcement intensity.

Described steel plate adhesive method is a kind of building method, its process is as described below, the concrete body that will strengthen carries out surfacing, after grappling (anchoring) operation and weld job, installs and the sealing steel plate, and injection ring epoxy resins and bond together with it.The advantage of described steel plate adhesive method is that material is bought easily and the assurance properties of materials can show.But, the weak point of this method is, because steel plate is very heavy, (usually adopting 4.5mm and thicker steel plate to guarantee needed intensity) transports and handle material and safety is managed relatively difficulty, and owing in welding or other operations, to use fire, therefore dangerous.Also have the load that this method causes strengthened concrete body owing to static load after strengthening increases too much, the corrosion of steel plate and the heat-resisting and low inferior shortcoming of the fire prevention thermal efficiency.

In synthetic resin board bonding with add strong method and steel plate bonding and adding in the strong method, fix plate by holdfast, and use filler to come formed gap between infill panel and the concrete body such as hot setting glue.For described filling process, other different materials also are installed except that holdfast, promptly, form injection hole to inject filler and to form steam vent when injecting filler, the air of inside is discharged sept (spacer) clocklike to be set at interval to form identical gap.Because the existence of sept, injection hole and steam vent must be arranged on the several sections of plate, therefore require a great deal of time, and may damage and make dirty plate and because in mounting structure with the air delivery ratio of anchor hole inside difficulty, do not make stiffening effect descend thereby described filler seals described gap fully.Also have because most of existing holdfast is made of metal, if strengthened wet concrete body As time goes on holdfast can get rusty, thereby cause its performance to descend and that outward appearance becomes is ugly.

Described pave with the process of cross section method of reducing as follows: the vulnerable area that excavates (dig) and removal concrete body, if strengthened steel plate is oxidized then carry out corrosion-resistant treatments, repair materials is injected crannied part to be contacted with air or water to prevent strengthened steel plate, smear described removal part thickly several times with the concrete of epoxy mortar (epoxy mortar), non-contraction and different polymer cement mortar (polymer cement mortar), and reduce described cross section.Kinds of materials and method have been developed as patching material and method, for example, cross section method of reducing of the different polymer cement mortar of polyurethane injecting method, the epoxy injection method that is used for humidification, little cement (micro-cement) injecting method, the cross section method of reducing that adopts the epoxy radicals mortar, employing such as acrylic high concentration mortar (acryl group high intensity mortar) or the like.But,,, restricted aspect the bond strength between the surface that conventional method is restored in existing concrete body and cross section owing to the cross section reduction work of the concrete body of removing is finished by float work though the material that is adopted is all fine.In addition, As time goes on, can produce again to peel off to enter and peel off and crannied surface, thereby make concrete body turn back to original situation (for example, the steel plate of reinforcement is corroded) again with crack and water and air.

Therefore, the inventor has developed a kind of plate, multi-functional holdfast that is used to repair and strengthen concrete body, has been used for the holdfast of Height Adjustment and injection and uses these methods of repairing and strengthening concrete body, is used to repair and strengthen the conventional method of described concrete body with improvement.

Summary of the invention

Therefore, the purpose of this invention is to provide and a kind of the reinforcing fibre thin plate is attached to compound stiffener in the steel plate and a kind of method that is used to repair and strengthens concrete body to ensure the safety of concrete body.

Another object of the present invention provides and a kind of the reinforcing fibre thin plate is compound to compound stiffener in the steel plate, thereby make every kind of properties of materials optimization as much as possible with the method that is used to repair and strengthen concrete body, improve the heat-resisting and fireproof performance of described compound stiffener and prevent non-plastic fracture by the defective of supplying material by the pliability that guarantees described compound stiffener.

An also purpose of the present invention provides the compound stiffener of a kind of light-duty precast concrete, and its light plate is connected the ability with the reinforcement concrete body with light-duty precast concrete plank.

An also purpose of the present invention provides the stiffening device that a kind of utilization is used to strengthen the light prefabricated concrete slab of concrete body ability.

An also purpose of the present invention provides a kind of device, it can different compound stiffeners improves because the situation of the relatively poor structure that conventional building site dipping causes by making in factory, and by being reduced in dipping and bonding aspect, be the principal element of architecture quality, provide consistent and safe stiffening effect the technician's of building site degree of dependence.

An also purpose of the present invention provides and can inject filler and not need the device of injection hole by holdfast.

An also purpose of the present invention provides and can form the device that sept clocklike need not be set at interval between plate and concrete body.

An also purpose of the present invention provides the air that can discharge by holdfast between plate and the concrete body and without any need for the device of steam vent when injecting filler.

An also purpose of this aspect provides a kind of light-duty precast concrete plank 410, be used to improve the heat resistance and the fireproof performance on concrete body surface, wherein utilize adopt the strong method that adds of traditional carbon fibre building board, glass fiber thin plate or aramid fibre thin plate described concrete is strengthened and to be repaired.

Description of drawings

To be easier to understand objects and advantages of the present invention by description below in conjunction with accompanying drawing, wherein:

Fig. 1 is the sectional view of the detailed example of the expression composite plate that is used to strengthen concrete body according to the present invention;

Fig. 2 is the flow chart of manufacture method of the composite plate of presentation graphs 1;

Fig. 3 is the sectional view of another detailed example of the expression composite plate that is used to strengthen concrete body according to the present invention;

Fig. 4 is the flow chart of manufacture method of the composite plate of presentation graphs 3;

Fig. 5 is the schematic diagram of expression according to the manufacture process and the structure of light prefabricated concrete slab of the present invention;

Fig. 6 is the flow chart of expression according to the manufacture process of the compound stiffener of light prefabricated concrete of the present invention;

Fig. 7 is the schematic diagram of expression according to the manufacture process of light prefabricated concrete stiffener of the present invention;

Fig. 8 is that expression is according to the simple stereogram that is used for the compound stiffener of light prefabricated concrete of rehabilitating concrete body of the present invention;

Fig. 9 is the elevation and the sectional view of the holdfast of the expression height that is used to adjust plate and injection;

Figure 10 is the view of the state that is connected with clip of holdfast and the flow in pipes of the expression height that is used to adjust plate and injection;

Figure 11 is elevation and the partial cross section figure of expression according to insertion of the present invention and expanded bore;

Figure 12 is elevation and the partial cross section figure of expression according to bolt of the present invention and flow in pipes;

Figure 13 is the schematic diagram of the state of the expression bottom that utilizes the beam that the compound stiffener of light prefabricated concrete strengthens;

Figure 14 is the schematic diagram of the state of the bottom of an expression side of utilizing the beam that the compound stiffener of light prefabricated concrete strengthens and sidepiece;

Figure 15 represents that the holdfast that is used for the plate of rehabilitating concrete body and is used for Height Adjustment and injection comes the schematic diagram of the part of rehabilitating concrete road damage;

Figure 16 is the bonded flow chart that adds strong method of expression, and this method utilization is according to the composite plate reinforcement concrete body that is used to strengthen concrete body of the present invention; With

Figure 17 is the schematic diagram that expression is used for the state of the plate of rehabilitating concrete body and the part that multi-functional holdfast comes the damage of rehabilitating concrete road.

The specific embodiment

Describe the present invention below with reference to accompanying drawings and in conjunction with the preferred embodiments in detail.In institute's drawings attached, identical label is represented corresponding parts.

Fig. 1 is expression according to the flow chart of the manufacture method of the sectional view of the embodiment of the composite plate that is used to strengthen concrete body of the present invention and the composite plate that Fig. 2 is presentation graphs 1.In Fig. 1 and 2, the described composite plate that is used to strengthen concrete body comprises: the steel plate 510 of prescribed level; The tack coat 520 ' that floods that on the upper surface of steel plate 510, forms; Be arranged on the tack coat 520 ' infiltration that also can be flooded on the upper surface of steel plate 510 and the reinforcing fibre 530 that bonds; With on the upper surface that is ejected into steel plate 510 and impregnated and be bonded in the powder 540 that can flood on the tack coat 520 '.In addition, the step that comprises of the manufacture method of composite plate has: form the tack coat 520 ' that can flood on the surface according to the steel plate 510 of pre-sizing cutting; Reinforcing fibre 530 dipping and bonding are formed with thereon on the surface of steel plate 510 of the tack coat 520 ' that can flood; Powder 540 is sprayed, floods and is bonded on the surface of steel plate 510 and reinforcing fibre thin plate layer 530; With make the 520 ' sclerosis of the tack coat that floods that in second step, forms.

Shown in Fig. 1 b, make the sandwich-type composite plate with identical manufacture method, with reinforcing fibre dipping and be bonded on two surfaces of steel plate, spray then and bond powders.

The compound stiffener that is used to strengthen concrete body also comprises: the tack coat that forms on the soffit of the steel plate of composite plate (seeing Fig. 1 a and 1b); With the light prefabricated concrete slab 550 of prescribed level on the soffit that is bonded in steel plate by tack coat, thereby increase reinforcement ability and fireproof performance.Also can use and adopt the another kind of precast concrete plank (see figure 5) of general aggregate to replace described light prefabricated concrete slab 550.

When light-duty precast concrete plank 550 is cut into planar rectangular, being used to of Fig. 1 a and 1b, the composite plate of strengthening concrete body was cut into the size the same with described light prefabricated concrete slab being connected with described light prefabricated concrete slab, the size that perhaps cuts into greater than have a projection on described light prefabricated concrete slab and the one side in four limits, have two projections at opposite side, have on its excess-three limit except that on one side three projections or all will with limit that described light prefabricated concrete slab is connected on have four projections.Thereby composite plate adjacent in the composite plate by connection layout 1a and 1b strengthens stiffening effect.Also can adopt the precast concrete plank of general aggregate to replace described light prefabricated concrete slab 550 with another kind.

The described composite plate that is used to strengthen concrete body comprises: the reinforcing fibre of prescribed level; The tack coat that floods that on the upper surface of described reinforcing fibre, forms; Be arranged on the upper surface of described reinforcing fibre and by the described tack coat dipping that floods and the steel plate of bonding; With injected, flood and be bonded in powder on the upper surface of described steel plate.In addition, the described compound stiffener that is used to strengthen concrete body also comprises: the tack coat that forms on the soffit of the reinforcing fibre of the composite plate that is used to strengthen concrete body; With the light prefabricated concrete slab of the prescribed level that bonds on the soffit that is arranged on described reinforcing fibre and by described tack coat, thereby strengthen reinforcement ability and fireproof performance.In addition, when described light-duty pre-notes concrete slab cuts into planar rectangular, the described composite plate (reinforcing fibre that comprises prescribed level; The tack coat that floods that on the upper surface of described reinforcing fibre, forms; Be arranged on the upper surface of described reinforcing fibre and by the described tack coat dipping that floods and the steel plate of bonding; With injected, flood with the upper surface that is bonded in described steel plate on powder) be cut into the size the same being connected with described light prefabricated concrete slab with described light prefabricated concrete slab, the size that perhaps cuts into greater than have a projection on described light prefabricated concrete slab and the one side in four limits, have two projections the relative edge, have on its excess-three limit except that on one side three projections or all will with limit that described light prefabricated concrete slab is connected on have four projections.Thereby composite plate adjacent in the composite plate by connection layout 1a and 1b strengthens stiffening effect.Also can adopt the precast concrete plank of general aggregate to replace described light prefabricated concrete slab 550 with another kind.

The described composite plate that is used to strengthen concrete body comprises: the upper steel plate of prescribed level; The lower steel plate of prescribed level; The tack coat that floods that on the upper surface of described upper steel plate, forms; Be arranged on tack coat dipping that also can be flooded on the upper surface of described upper steel plate and the reinforcing fibre that bonds; The tack coat that on the upper surface of described reinforcing fibre, forms; The lower steel plate of the tack coat bonding that on the upper surface of described reinforcing fibre, is formed; The tack coat that on the surface of upper and lower steel plate, forms; With injected and be bonded in powder on the tack coat that forms on the surface of described upper and lower steel plate.In addition, the compound stiffener that is used to strengthen concrete body also comprises: the tack coat that forms on the soffit of described lower steel plate; With the light prefabricated concrete slab that is bonded in the prescribed level on the described lower steel plate by described tack coat, thereby improve reinforcement ability and fireproof performance.Also have, when described light-duty pre-notes concrete slab cut into planar rectangular, described composite plate (comprised upper steel plate; Lower steel plate; The tack coat that floods that on the upper surface of described upper steel plate, forms; Be arranged on tack coat dipping that also can be flooded on the upper surface of described upper steel plate and the reinforcing fibre that bonds; The tack coat that on the upper surface of described reinforcing fibre, forms; The lower steel plate of the tack coat bonding that on the upper surface of described reinforcing fibre, is formed; The tack coat that on the surface of upper and lower steel plate, forms; With injected and be bonded in powder on the tack coat that forms on the surface of described upper and lower steel plate) be cut into the size the same to be connected with described light prefabricated concrete slab with described light prefabricated concrete slab, the size that perhaps cuts into is greater than described light prefabricated concrete slab, and have a projection on the one side in four limits, have two projections the relative edge, have on its excess-three limit except that on one side three projections or all will with limit that described light prefabricated concrete slab is connected on have four projections.Thereby composite plate adjacent in the composite plate by connection layout 1a and 1b strengthens stiffening effect.Also can adopt the precast concrete plank of general aggregate to replace described light prefabricated concrete slab 550 with another kind.

The described composite plate that is used to strengthen concrete body comprises: the steel plate of prescribed level; The tack coat that floods that on the upper surface of described steel plate, forms; Be arranged on tack coat dipping that also can be flooded on the upper surface of described steel plate and the upper strata reinforcing fibre that bonds; Injected, flood and be bonded in powder on the upper surface of described upper strata reinforcing fibre; The tack coat that floods that on the soffit of described steel plate, forms; Be arranged on tack coat dipping that also can be flooded on the soffit of described steel plate and the lower floor's reinforcing fibre that bonds; Injected, flood and be bonded in powder on the soffit of described lower floor reinforcing fibre.In addition, the described compound stiffener that is used to strengthen concrete body also comprises: the tack coat that forms on the soffit of described lower floor reinforcing fibre; With the light prefabricated concrete slab of also bonded layer bonding on the bottom that is arranged on described lower floor reinforcing fibre, thereby improve reinforcement ability and fireproof performance.Also have, when described light-duty pre-notes concrete slab cut into planar rectangular, described composite plate (comprised steel plate; The tack coat that floods that on the upper surface of described steel plate, forms; Be arranged on tack coat dipping that also can be flooded on the upper surface of described steel plate and the upper strata reinforcing fibre that bonds; Injected, flood and be bonded in powder on the upper surface of described upper strata reinforcing fibre; The tack coat that floods that on the soffit of described steel plate, forms; Be arranged on tack coat dipping that also can be flooded on the soffit of described steel plate and the lower floor's reinforcing fibre that bonds; Injected, flood and be bonded in powder on the soffit of described lower floor reinforcing fibre) be cut into the same size to be connected with described light prefabricated concrete slab with described light prefabricated concrete slab, the size that perhaps cuts into is greater than described light prefabricated concrete slab, and have a projection on the one side in four limits, have two projections on both sides relatively, removing have on its excess-three limit one side three projections or all will with limit that described light prefabricated concrete slab is connected on have four projections.Thereby the composite plate by Fig. 1 a and 1b is connected adjacent composite plate enhancing stiffening effect.Also can replace described light prefabricated concrete slab 550 with the another kind of precast concrete plank of general aggregate (generalaggregate) that adopts.

Steel plate 510 is one of them of steel plate, and it has good flexural strength and generally be used for steel plate and adds strong method, and can adjust thickness according to the density of the concrete body that will strengthen.That is, because utilize reinforcing fibre 530 to strengthen steel plates 510, so can use 1mm or less than the stratiform steel plate of 1mm with good tensile strength and coefficient of elasticity.Also have, if owing to the building method of composite plate (bonded or holdfast is fixed, injection and bonded) adopts that holdfast is fixed, injection and bondedly add strong method, then steel plate 510 can have a plurality of anchor hole 511.

The cementing agent that can flood by coating on the upper surface of steel plate forms the tack coat 520 ' that can flood.With regard to the described cementing agent that floods, it is suitable selecting the resin that is exclusively used in dipping and bonding for use, as the cementing agent that can flood, steel plate is had good adhesion strength to described resin and good intensity and described reinforcing fibre can easily be immersed in wherein such as the epoxy resin that is used to flood and bonds.The surface that the described tack coat that floods 520 is used to apply described steel plate 510 is with the corrosion that prevents steel plate 510 and improve acid-resisting.

Reinforcing fibre 530 is arranged on the tack coat 520 ' dipping that also can be flooded on the upper surface of steel plate 510 and bonds to strengthen steel plate 510.In the carbon fibre with high-tensile, better elastic coefficient and durability, glass fiber and aramid fibre, select at least one or a plurality of and they are combined into described reinforcing fibre.In addition, can also which floor reinforcing fibre 530 be divided into according to the needed intensity of concrete body that will strengthen.When described reinforcing fibre 530 is piled up for which floor, repeat to form the step of the tack coat 520 ' that can flood and the dipping and the described reinforcing fibre 530 that bonds and the workman will note removing bubble to realize perfect dipping.Steel plate 510 is used to strengthen bending resistance or shear resistance, and reinforcing fibre 530 is used to strengthen the pulling force of described steel plate to satisfy the requirement of high-tensile strength, thereby make the concrete body that must strengthen be strengthened fully causing non-plastic fracture owing to lack flexibility to support resistance to bending, shearing and pulling force and to prevent, this be existing employing reinforcing fibre add one of major defect of strong method.Therefore, can fully guarantee safety according to composite plate of the present invention.

Before the described tack coat that floods 520 ' sclerosis, powder 540 is sprayed, floods and is bonded on the surface of the tack coat 520 ' that can flood.Thereby therefore powder 540 helps to make described composite plate and concrete body to be combined into one by making the rough surface enhancing of composite plate and the adhesion strength of binding resin.

Fig. 3 is expression according to the flow chart of the manufacture method of the sectional view of another embodiment of the composite plate that is used to strengthen concrete body of the present invention and the composite plate that Fig. 4 is presentation graphs 3.In Fig. 3 and 4, adopt prefabricated concrete slab to strengthen the fire line of composite plate 560.Described composite plate comprises: the prefabricated concrete slab 550 of prescribed level; The tack coat 520 that on the upper surface of prefabricated concrete slab 550, forms; Be arranged on the upper surface of described precast concrete plank 550 and the steel plate 510 by tack coat 520 bondings; The tack coat 520 that on the upper surface of steel plate 510, forms; Powder 540 with also bonded layer 520 adhesion on the upper surface that is injected in steel plate 510.

The same among steel plate 510 and first embodiment, and tack coat 520 bonds together steel plate 510 and prefabricated concrete slab 550 mutually.Form steel plate 510 by being coated with the epoxy resin that is applied to bonding.Thereby prefabricated concrete slab 550 plays booster action by tack coat 520 and steel plate 510 bondings, and when finished composite plate 562 formation finished surface during as the plate that is used to strengthen concrete body.Because the pre-concrete slab of annotating 550 is make and surperficial cover caps that form steel plate 510 by the material the same with the concrete body that will strengthen, so it is still superior and have a good effect of finishing than the plate of being made up of steel plate and reinforcing fibre aspect fireproof performance.Because light and fireproof performance is the key factor of stiffener, therefore use light prefabricated concrete slab 550 better effects if.

Fig. 5 is manufacture process and the structural representation of expression by the precast concrete plank 110 of dipping light concrete layer 111, inorganic elements group fiber thin flaggy (igorganic element group fiber sheet layer) and water-soluble cement based (watersoluable cement group) or polymer base resin bed (polymer group resin layer) formation.

In that mixed cement, the light-duty aggregate of inorganic based porous (inorganic group porous lightweight aggregate) and water pour into this layer of concrete after making described light concrete layer 111 by utilizing electronic artificial mixer or mortar mixer.

Described inorganic porous light-duty aggregate and cement mixing are together as described aggregate and in light weight.According to the condition of panel, can change the mixed proportion of cement and inorganic porous light-duty aggregate.If inorganic porous light-duty aggregate is pearlite (perlite), cement can be adjusted described panel with respect to the blending ratio of inorganic porous light-duty aggregate in the scope of mixed proportion in the scope of the 5%-80% of weight and according to needed intensity of plate and heat resistance.Described plate generally has suitable fireproof performance and intensity in the scope of about 20% mixed proportion.

Described inorganic based (inorganic group) fiber thin flaggy 112 is that a kind of inorganic based fibre web of reinforcement (is by the inorganic based fiber is immersed in the thermosetting paragutta, and evenly disperse mode that quartz sand or blast furnace slag harden then to make), and be positioned at described light concrete layer 111.Inorganic based fiber thin flaggy 112 is used to strengthen the pulling force of described light concrete plate 110 and forms a layer or several layer.But in inorganic based fiber thin flaggy 112, if 110 of described plates include the inorganic based fibre building board, then the upper and lower of plate 110 occur peeling off and separate with inorganic based fiber thin flaggy 112.Therefore, if described reinforcement inorganic based fibre building board is set, then can prevent to peel off and separate.Described little cement (micro-cement) is used to strengthen described inorfil thin plate.But,, therefore flood the insulation effect of the fine powder of the light-duty aggregate of inorganic based porous with stiffener because little cement can reduce the insulation effect of described plate.When the little cement that floods in the light-duty aggregate of inorganic based porous and described inorganic based fibre building board were impregnated in the described cement board, water-soluble cement based, latex cement mortar (polymer cement) base or polymer base resin were substrate.

The plate of making by above-mentioned process 110 carries out spontaneous curing processing (naturalcure) and cure under pressure processing (forced cure) (steam cure is handled (steam cure)) successively, finishes the processing of described light prefabricated concrete slab 110 then.

Fig. 6 is the flow chart of the manufacture process of the another kind of light prefabricated concrete slab 410 of expression, and described plate has reinforced glass fibre web stacked between light concrete layer 411.

Process described light prefabricated concrete slab 410 in the following manner, fully mix light-duty aggregate and portland cement (Portland cement) according to suitable mixed proportion such as dirty coal (bony coal), the water that adds scheduled volume, at first pour into 1/3 of plate thickness by the well-mixed light concrete of mortar mixer, the glass fiber silk screen of reinforcement is set on the surface of the light concrete layer 411 that pours into for the first time, and pours into described light concrete for the second time immediately and be cured processing (spontaneous curing processing and steam cure are handled).At this moment, 412 dipping synthetic resin of the glass fiber silk screen by will being used for booster action and make quartz sand or blast furnace slag evenly disperses and the mode of sclerosis is made described reinforced glass fibre web.Described glass fiber silk screen 412 is netted, and the interval between should fiber of net is greater than general fibre building board, and strengthens the bending force and the pulling force of light concrete.Described quartz sand or blast furnace slag 430 are used to improve adhesion strength between the glass fiber silk screen 412 of reinforcement and the light concrete 411.Therefore, light prefabricated concrete slab 410 according to the present invention has fully-integrated element, so glass fiber silk screen 412 stably is fixed in the light concrete so that pulling force is maximum and improve the durability of plate.And, in order to make thicker plate, preferably wire gauze or stiffener are layered in the light concrete 411.Described light fire-proof precast plate 410 by compound described light prefabricated plate 410 and other materials (existing reinforcing fibre (carbon fibre, glass fiber, aramid fibre etc.) dipping plate, the prestressing force reinforcing fibre composite plate that adopts prestressing method to make) such as the reinforcing fibre that is used to flood that below will describe thus can be used to make compound stiffener with the demonstration fireproof performance.In addition, when needs improve the fire prevention efficient of concrete body, perhaps when adopting described light fire-proof precast plate 410 because stiffening effect weakens when needing to strengthen described concrete body gradually, wherein said concrete body is strengthened by the strong method that adds of adopting traditional carbon fibre building board, glass fiber thin plate or aramid fiber thin plate.Also have; described light prefabricated plate 410 is by providing the beautiful outward appearance can be as protection and the method for repairing described concrete body for concrete body, described concrete body is because the materials variances between concrete body and the fibre building board or because wearing out of concrete body causes outward appearance ugly.

A kind of method of utilizing light fire-proof precast plate 410 to repair and strengthen concrete body, this method cuts into suitable size (the same with the tile (tile) of routine big or big slightly) with described light fire-proof precast plate and with its compression be bonded on the surface of concrete body, wherein said surface is by utilizing the traditional carbon fiber, described concrete body is strengthened in the strong method that adds of glass fiber or aramid fibre thin plate, perhaps connects by synthetic resin based bonding or the latex cement mortar that is used to bond is bonded to the surface of the concrete body of serious aging.

To describe this method in detail below.

Remove fully attached to dust on the existing basal plane and impurity by jetting machine or deduster, and the workman will note not damaging the reinforcing fibre attached on the described basal plane, the workman checks the part defectiveness whether be bonded with existing reinforcing fibre then, such as bubble, bonding is not enough and peel off, and finishes the reinforcement operation.Scribble epoxy radicals or water and oil base (aqueous and oil group) if be bonded with the part surface of existing reinforcing fibre, then apply the very low epoxy radicals cementing agent of viscosity, and on the surface of coating, spray the powder of body such as quartz sand simultaneously so that rough surface.Scribble urethane ester group (urethane group) if be bonded with the surface of the part of existing reinforcing fibre, then apply the urethanes based binder.

Afterwards, the described plate that bonds, and from then on step begins, and adopts the adhesive method of synthetic resin based binder to begin different with the mode of finishing of the method that adopts latex cement mortar based binder.The adhesive method of described employing synthetic resin based binder is finished by bond described plate and filling joint (joint).Coated and be bonded on the surface of described concrete body for the full-bodied epoxy of grease form or urethanes based binder, wherein Tu Fu cementing agent is in sclerosis and on average being approximately at thickness on the surface of described light prefabricated plate of 3-5mm fully on this surface.Afterwards, within workman 30 minutes after adhesive board these plates are linked together and will be ejected into joint such as the aggregate of quartz sand so that rough surface is finished (pointed) joint work of appointment then.At this moment, can use epoxy resin to bond by mixing fines or thin light-duty aggregate.The material that is used to fill joint is synthetic resin or existing composite cement mortar, and the width of joint is approximately 5mm.If the width of joint surpasses 5mm, then the workman fills this joint twice and suppresses fully to prevent to produce the crack.

By on basal plane, smearing mortar, the described plate of bonding and filling joint and finish adhesive method described and employing latex cement mortar based binder.When smearing mortar on the surface of workman at concrete body, thereby the cementing agent that applies on the surface of described concrete body fully sclerosis make rough surface, the workman finishes and describedly smears work and note being no more than 10mm when the thickness of smearing surpasses 10mm.Finish described mortar and smear after the work, the surface of smearing is carried out the curing in a week and handle.The workman checked and repaired excitatory (excitation) and the crack on the surface of smearing mortar before the described plate of bonding.If external buildings, then workman's injection water and the described plate and the surface of concrete body are contacted fully to prevent the infiltration of rainwater or water on the surface of described plate increases adhesion stress and prevents the phenomenon of peeling off, solidifying and melting.An application area of the basal surface that mortar is smeared is less than 1.0m ²The described plate of bonding behind the adhesive mortar of evenly smearing about 3-6mm thickness.After the described adhesive mortar of evenly smearing about 3-4mm thickness once more, the tile that bonds immediately, and at this moment, the workman knocks tile with wooden mallet so that the mortar ledge (protrude) of joint surpasses 1/2 thickness of plate.The described plate that bonds is spent 3 hours afterwards, and the workman excavates described joint and finishes the joint work of smearing.Before smearing joint work, the workman on the basal plane of joint injection water to keep humidity.Preferably, the width of joint is approximately 5mm, if still the width of joint is greater than 5mm, then the workman fills described joint twice and suppresses fully to prevent the crack.

Fig. 7 represents the state that described reinforcing fibre thin plate 120 is connected with light prefabricated concrete slab 110 as the stiffening device of concrete body.In other words, described stiffening device comprises: reinforcing fibre thin plate 120 and powder bed.The described reinforcing fibre thin plate of dipping on the basis of lip-deep thermosetting resin that is coated in light prefabricated concrete slab 110 and thermosetting resin 123, and be cut to described light prefabricated concrete slab 110 the same sizes and with described light prefabricated concrete slab 110 and engage, engage the formation ledge greater than described light prefabricated concrete slab 110 and with described light prefabricated concrete slab 110 thereby perhaps be cut to.Spray described powder bed on the top of the reinforcing fibre thin plate layer of described dipping to increase adhesion stress to the concrete body that will strengthen.Described thermosetting resin 123 can be one of them of (converted) epoxy resin of epoxy resin or conversion.Described reinforcing fibre thin plate layer the upper surface of described light prefabricated concrete slab form and pile up at least one or more layers.That is, on the upper surface of described plate after the coating cementing agent that can flood, finish processing to described reinforcing fibre thin plate layer by the dipping and the described reinforcing fibre thin plate that bonds on the upper surface of one deck or the cementing agent that floods in which floor.By from carbon fibre, glass fiber and aramid fibre, select at least one or a plurality of and they be combined with each other and make described reinforcing fibre thin plate, wherein said carbon fibre, glass fiber and aramid fibre have high-tensile, better elastic coefficient and durability.In addition, for make described reinforcing fibre thin plate pile up at least one or more layers, the step and the workman that repeat to apply the described cementing agent that floods and dipping and the described reinforcing fibre thin plate of bonding will note removing bubble to obtain desirable dipping effect.

To be bonded on the described concrete body by the compound stiffener that light prefabricated concrete slab, reinforcing fibre thin plate layer and powder constitute by the adhesive method that adopts holdfast.For this reason, described compound stiffener has a plurality of anchor hole.If described reinforcing fibre thin plate layer is piled up for which floor, then cut described reinforcing fibre thin plate so that they have different extension length each other.Preferably, the extension length of the reinforcing fibre thin plate of described accumulation reduces from the bottom up gradually.Before described reinforcing fibre thin plate layer hardens fully with powderject and be bonded on the surface of described reinforcing fibre thin plate layer.Described powder makes the rough surface of compound stiffener, thereby the viscous force that is increased in the process of structure with binding resin helps described compound stiffener and described concrete body to become one.Described powder can be quartz sand or blast furnace slag.Which floor is if described reinforcing fibre thin plate layer is piled up, then described reinforcing fibre thin plate 120 must be piled up so that the pulling force maximum according to identical weaving direction (weaving direction).For the device that is used to add the reinforced concrete ability, can replace prime paint, thermosetting resin and reinforcing fibre thin plate to apply with the thermosetting resin mortar.To be bonded on the described concrete body by the compound stiffener that light prefabricated concrete slab, reinforcing fibre thin plate layer and powder constitute by the adhesive method that adopts holdfast.For this reason, described compound stiffener has a plurality of anchor hole.

Fig. 8 is schematic diagram and the stereogram that expression is used to repair the compound stiffener 310 of light prefabricated concrete of described concrete body, and described plate comprises light concrete layer 311 and is used to strengthen the stiffening device 312 of described light concrete layer 311.The compound stiffener 310 of described light prefabricated concrete different with the compound stiffener 110 of light prefabricated concrete of Fig. 5 on stiffening device 120.

At first, make the compound stiffener 310 of the light prefabricated concrete that comprises the stiffening device 312 that is connected with the side of light concrete layer 311 in the following manner, the epoxy resin and the hardener of high-strength mortar are mixed mutually, according to predetermined ratio this mixture is mixed with quartz sand aggregate, and this mixture is poured on the light concrete layer 311 that cure under pressure is handled.

The compound stiffener 310 of light prefabricated concrete with the light concrete layer 311 that wherein includes stiffening device 312 can be divided into light concrete upper strata and light concrete lower floor with described light concrete layer, and the boundary member between described stiffening device 312 formation light concrete upper stratas and the light concrete lower floor.And, can form two kinds of compound stiffeners 310 of light prefabricated concrete: a kind ofly form the template of prior perfusion and curing and be connected for described light concrete layer 311 with stiffening device 312; With another kind is to inject described stiffening device 312 before the sclerosis after 311 perfusion of light concrete layer, and then concrete perfusion is to connect stiffening device 312 and light concrete layer 311.If necessary, replace described light concrete layer 311 with general strong concrete.

As mentioned above, the compound stiffener 310 of light prefabricated concrete according to the present invention can be according to stiffening device 312 classification.From unidirectional (prepreg one-way) carbon fibre, the spy of pre-preg thin two-way braiding (extra thin two-way woven) carbon fibre, aramid fibre, glass fiber, wire lath, wire gauze and reinforcing bar, select one of them, and be connected by between the upper and lower layer 311 of described light concrete of epoxy resin and hardener dipping as stiffening device 312.To describe manufacture process in detail below.

According to the width and the degree of depth of the broken parts 383 of concrete body, make a framework and on the surface of this framework, adhere to one deck film special.With one of them of portland cement, back side rubber cement and coloured cement, the light-duty aggregate of the aggregate that adopts such as pearlite, Fei Laite (filite), kieselguhr, ALC (Autoclaved lightweight concrete) aggregate and ALC crushing engine, and water mixes, and the mixture that obtains is filled on the described framework and sclerosis tabular to form, thereby form the upper and lower layer 311 of light concrete.Epoxy resin that is mixed for flooding according to predetermined mixed proportion and hardener also are coated in mixture on the side of described light concrete lower floor.After coating epoxy resin, one of them of two-way braiding carbon fibre, aramid fibre and the glass fiber that unidirectional carbon fibre, the spy of pre-preg is thin is immersed in the epoxy resin.The bubble that removal produces in dipping process, and be coated with the epoxy resin that is applied to the top dipping once more.After being coated with the epoxy resin that is applied to top dipping, connecting the light concrete upper strata, thereby and form the compound stiffener 310 of described light prefabricated concrete.Perhaps, do not have at described light concrete layer 311 under the condition of sclerosis, form the compound stiffener 310 of described light prefabricated concrete by one of them of impregnated glass fiber silk screen, wire gauze and reinforcing bar, and pour into described light concrete upper strata immediately.In addition, by utilizing general coarse aggregate to replace the light-duty aggregate of light concrete layer can form and use general concrete slab.And, can make described light prefabricated composite plate or described precast concrete composite plate and make it bigger and utilize hand cutter to cut described light prefabricated composite plate or described precast concrete composite plate makes its shape corresponding with the part that will repair than the concrete body that will repair part.

Because the compound stiffener 310 of described light prefabricated concrete is light and be easy to structure, but owing to use light-duty aggregate, therefore the restriction of intensity aspect is arranged.If the compressive strength that the part that will repair of concrete body 380 need be stipulated then can be used the compound stiffener 314 of precast concrete.The compound stiffener 314 of described precast concrete is included in stiffening device 312 that form and that connect between upper and lower layer 315 of concrete and the upper and lower layer 315 of concrete.As mentioned above, form described layer of concrete 315, and from portland cement, back side rubber cement and coloured cement, select one of them as described cement by general aggregate, cement and water are mixed.The upper and lower layer 315 of described concrete can be connected with stiffening device 312 with the form of prior perfusion with the sclerosis plate.Perhaps, can form the upper and lower layer of described concrete 315 in the following manner: the described stiffening device 312 of dipping before concrete lower floor sclerosis after the perfusion, and concrete perfusion upper strata once more.Form stiffening device 312 in the following manner: select one of them in unidirectional carbon fibre, glass fiber and the aramid fibre of two-way or unidirectional braiding carbon fibre that the spy approaches, pre-preg with perfusion in advance and the precast concrete plank that is connected with the upper and lower layer of the template concrete of sclerosis, it is coated on the side of template concrete lower floor with epoxy resin with as the hardener of bottom immersion system, apply described epoxy resin and hardener once more as the top immersion system, and before described immersion system sclerosis, connect the concrete upper strata of template.If described plate stiffening device is glass fiber silk screen, wire or reinforcing bar, then before the concrete lower floor sclerosis of perfusion, glass fiber silk screen, wire or reinforcing bar be immersed in described concrete lower floor, then the concrete perfusion upper strata.Described plate stiffening device can form in the following manner: one of them of wire or reinforcing bar is set, mixes the synthetic resin and the hardener of high-strength mortar, mix quartz sand aggregate, and pour into resulting mixture and be connected with described concrete body.For provide with glass fiber silk screen, wire and reinforcing bar stronger be connected power, on the surface of glass fiber silk screen, wire or reinforcing bar, smear and flood little cement paste.For increasing the intensity of precast concrete plank, the sclerosis back is carried out cure under pressure to described plate and is handled after official hour.

Fig. 9 and 10 is expression is used to adjust the holdfast of the height of plate and injection according to the present invention elevation and sectional views.Described holdfast comprises body part 320, nut 323, the intermediate plate 330 that is used to transport and the pipeline 340 that is used to inject.Body part 320 has the part 325 of hollow and is shaped as cylindricality.Body part 320 is included in the external screw thread 321 that forms on the excircle, at the end of cavity 325 and its through hole 324 that intersects, and the internal thread 333 and the dihedral ledge 322 that on the other end of the inner periphery of cavity 325, form.The shape of described ledge 322 can be hexagon or octagon.External screw thread 321 that forms on the excircle of body part 320 and nut 323 engagements.Described nut is the rotating instrument that is connected with described ledge 322, and when body part 320 rotates, and the nut 323 that is fixed to plate 310 moves along the vertical direction of body part 320, thereby adjusts the height of plate 310.The intermediate plate 330 that is used to transport has cylindrical section 331, described cylindrical section 331 is formed with internal thread 333 on the circumference within it, and internal thread 333 meshes with the external screw thread 321 of body part 320, and described body part and nut 323 engagements are used to transport plate thereby form connecting rod (link).The shape of the pipeline 340 that is used to inject is generally shaft-like (straw) and it at one end is formed with external screw thread 341.The external screw thread 341 of pipeline 340 and the internal thread engagement that on the inner periphery of the ledge 322 of body part 320, forms.By pipeline 340, the cavity 325 of body part and through hole 324 are expelled to filler in the vaccum interval (empty space) of the rear surface of plate.When the injection of filler finishes, remove pipeline 340.

Figure 11 is plug-in unit (insert) 210 of the expression multi-functional holdfast that is used to connect plate and concrete body and the elevation and the partial cross section figure of expander tool 220.Plug-in unit 210 has a plurality of holes 212 that shape is generally the body part 211 of cylindricality and form in body part 211.The hole 212 that forms in the body part 211 of plug-in unit 210 is as the injection path of the filler of injecting by injection-tube (injection pipe) 240 with as the discharge path of discharging the gas between plate and the concrete body.Body part 211 has the internal thread 213 that connects with the bolt 230 that inserts prescribed depth from an end.Be formed with in the end of internal thread 213 beginning from the outstanding head (head part) 214 of body part 211 and as sept.The interval of regulation that the plate that head 214 permissions are connected with holdfast of the present invention keeps and concrete body is separated by.Because the interval between plate and the concrete body is by the thickness decision of head 214, so the thickness of head 214 is according to the interval variation between plate and the concrete body.Head 214 can have other difformities except that Figure 11.When beaing expander tool 220 with tup, the other end of plug-in unit 210 is divided into several sections to launch.

After plug-in unit 210 is inserted in the hole that concrete body forms, expander tool 220 is inserted in the plug-in units 210, thereby increased the diameter of plug-in unit and concrete body and plug-in unit 210 are linked together.For aforesaid operations is carried out smoothly, form cavity 221, its vertical section and described injection-tube 240 with trapezoidal column inserts wherein.

Figure 12 is expression the present invention's (multi-functional holdfast) bolt 230 and injection-tube 240 elevations and a sectional view.Bolt 230 comprises body part 231 and head 232.Bolt 230 has the vertical cavity 235 of body part 231 and head 232 that passes through to allow the insertion of injection-tube 240.Body part 231 have in its surface form and with the external screw thread 233 of internal thread 213 engagements of plug-in unit 210 and a plurality of as the injection path of filler and the hole 236 of internal gas discharge path.Vertically the cavity 235 by head 232 centers is formed with the internal thread 234 that meshes with injection-tube 240 on inner periphery.Can replace thread connection between head 232 and the injection-tube 240 with other coupling arrangements with same purpose.The diameter of the cavity 221 of expander tool 220 is the same with the diameter of the cavity 235 of bolt 230, therefore can make described expander tool and bolt elongate by attachment bolt 230 and plug-in unit 210.

The injection-tube 240 that shape is generally shaft-like (straw) comprises head 241 and body part 243.The diameter of body part 243 can make body part 243 can be inserted in the cavity 221 of bolt 230 and the expander tool 220 and be formed with external screw thread 244 at an end of its excircle, connects or separates with head 241.The filler that injection-tube 240 receives from head 241.The neck that forms head 241 becomes interior concave relief, beats head 241 with hammer like this after the injection filler and head 241 can be removed.Head 241 is formed with external screw thread 242 and connects with the internal thread 234 of bolt 230 on the excircle of lower end, and is formed with internal thread connects with the external screw thread 244 of the body part 243 of injection-tube on inner periphery.

Multi-functional holdfast can be made by metal material or thermosetting resin.If holdfast is made by thermosetting resin, then holdfast is anticorrosive, thereby makes the appearance looks elegant of holdfast.

Be used for strengthening the plate 560 of concrete bending, shearing and stretching aspect by synthesizing steel plate and reinforcing fibre or steel plate, reinforcing fibre and precast concrete, 562 make the advantage optimization of every kind of material and remedy the shortcoming of these materials, thereby the pliability that guarantees plate is to prevent brittle fracture and stablely to strengthen described concrete body.

The compound stiffener of described light concrete; wherein stiffening device is connected with the light concrete plate strengthening concrete body and to improve the ability of concrete body, thereby it has improved the fireproof performance of on the surface of described light concrete plate dipping, bonding and synthetic stiffening device and the influence by the adverse circumstances protecting described stiffening device not to be subjected to effectively to change suddenly such as weather provides stable stiffening effect.

Can be fixed on the concrete body effectively according to plate of the present invention.This plate allows filler need not pass through injection orifice by the holdfast injection, described plate is formed with the interval of regulation between plate and concrete body, and the permission air is discharged by described holdfast and need not be passed through any steam vent when the filler between injection plate and the concrete body.Described holdfast is made by thermosetting resin, and therefore described holdfast is anticorrosive.

The compound stiffener of being made by continual manufacturing system in the factory of light concrete can guarantee dipping uniformly.The phenomenon that the structure quality that just simple assembling when the composite plate of making in the factory is constructed in the building site and eliminating in advance causes descends also reduces degree of dependence to the workman's in building site technical level, thereby obtains stiffening effect stable and that wish.

Described light prefabricated concrete slab 410 is by with reinforced glass fiber held stationary and be integrated in bending and the stretching durability that can improve plate in the described light concrete.In addition, the present invention be used to strengthen by connection the reinforcing fibre thin plate of ability of concrete body and light prefabricated concrete slab 410 can have to the good adhesive property of concrete body and on the surface of reinforcing fibre thin plate pulverized powder so that rough surface.

The compound stiffener of described light concrete; wherein stiffening device is connected with the light concrete plate with reinforcement concrete body and the ability of improving concrete body, thereby it improves on the surface of described light concrete plate the fireproof performance of the stiffening device that floods, bonds and synthesize and is not subjected to provide stable stiffening effect such as the influence of the unexpected adverse circumstances that change of weather by the described stiffening device of effective protection.

The schematic diagram of the lower end of the state of the lower end of Figure 13 and 14 beam that to be expression strengthened by the compound stiffener of light prefabricated concrete 100 and the beam strengthened by the compound stiffener 100 of light prefabricated concrete and the state of side.Described reinforcing fibre thin plate is used to strengthen the ability of concrete body as stiffening device.As shown in the figure, according to the shape and the be provided with condition (arranged condition) of the compound stiffener 100 of the described light prefabricated concrete of area change between the unit of plate 100 of the concrete body that will strengthen.For covering adjacent plate unit and reinforcing fibre thin plate 120 and continuous structure, cut described reinforcing fibre thin plate 120 and make its shape, thereby make the reinforcing fibre thin plate 120 outstanding length of stipulating greater than light prefabricated concrete slab 110 and bonding.Unit area according to reinforcing fibre thin plate 120 is regulated outstanding length by weight proportion.For example, if the weight of reinforcing fibre thin plate 120 is every 1m ²Be 200g, 300g and 400g, then reinforcing fibre thin plate 120 is given prominence to 20cm, 25cm and 30cm.The unit that connects the compound stiffener 100 of light prefabricated concrete in the following manner: one side one side of the outstanding from it plate 100 of reinforcing fibre thin plate 120 and reinforcing fibre thin plate 120 outstanding from it mutually in the face of and be connected.Therefore, when 100 cuttings of light prefabricated concrete slab be shaped as rectangle the time, one side, two relative edges of reinforcing fibre thin plate 120 from four limits of described light prefabricated concrete slab 110, its excess-three limit removing on one side or give prominence to from the four all limits of light-duty precast concrete plank 110.

Figure 15 represents to utilize the holdfast of the height that is used to adjust plate and injection plate to be set to the method on the road surface of spreading concrete 380 that comprises broken parts 383.In more detail, work and the part that is labeled with the pavement cutting machine cutting are shown in the table of joint indicating finished on the road surface of damaging of workman.The broken parts 383 on the road surface of spreading concrete is positioned at the inboard of line of cut 381, and it meets at right angles for the line of cut of straight line and another line of cut 381.Described cutting part damages because of the power of hydraulic pressure or electric hammer.The ratio of pouring into wherein in the basal surface 388 that damages is according to the rules mixed the synthetic resin of high adhesion stress and the epoxy mortar 361 of quartz sand.Finish the leveling work of basal surface when at this moment, the workman forms the pore of about 10mm between surface that is coated with epoxy mortar and plate.The nut 123 of described holdfast is secured in the anchor hole 313 that forms on the plate 310 by araldite, body part 320 and nut 323 engagements, and intermediate plate 330 and body part 320 engagements transport and fix described plate 310 then on the part of described damage.After removing intermediate plate 330, as mentioned above, the height that rotates body part 320 and adjustment plate makes it consistent with the rigid pavement.Because nut is fixed, therefore when body part 320 rotates, can adjust the height of described plate.Behind the adjustment end-of-job of plate, the slit between the plate and the road surface of spreading concrete is sealed, is provided for injecting hypobaric cylinder 352 and pipeline 340 is set on holdfast at the assigned position of hermetic unit.At first, the pore of the rear surface of the synthetic resin based filler infill panel by injection-tube 340 usefulness such as epoxy resin.For preventing to exist unfilled part, for the second time filler is expelled to by low pressure injection cylinder 352 in the pore of rear surface of plate.When injection during end-of-job, finish decompression part such as anchor hole 313 with epoxy mortar.

Figure 16 represents to utilize composite plate 560 to strengthen the flow chart of the method for concrete body.At this moment, use the bonded strong method that adds.That is, describedly add the basal surface 500 that strong method comprises the following steps: to prepare the concrete body that will strengthen; On the surface of the basal surface 500 of concrete body and composite plate 560, form tack coat 520; With composite plate 560 is bonded on the basal surface 500 of concrete body.

If the preparation of the basal surface of concrete body 500 finishes, then in the end of composite plate 560 or in composite plate 560 clocklike to form anchor hole at interval.When forming anchor hole, remove the interior dust of anchor hole and go up the tack coat that formation can be flooded on surface (being coated with the permeable cementing agent of epoxy).Permeable tack coat is used to remove the micronic dust of basal surface 500, strengthens vulnerable area to improve the adhesion stress of composite plate 560.After permeable tack coat of coating on the basal surface 500 hardened fully, applied thickness was about 3mm or thicker being used for and bonds the epoxy adhesive of composite plate 560 to form tack coat.Also form described tack coat and also fixed thereon on the surface of composite plate 560 with described basal surface bonding.When composite plate 560 was fixed on the described basal surface, the workman utilized crab-bolt (anchor bolt) that it is fastening, so this holdfast can prevent that described composite plate from breaking.

If the composite plate of prescribed level is set continuously, then, prolongs steel plate and make it longer, thereby form coupling part 515 than precast concrete plank in order to realize the perfection bonding of coupling part.At this moment, on the soffit of coupling part 515 pulverized powder 540 to improve the adhesion stress of coupling part.If necessary, on the coupling part, holdfast can be set.

If wherein synthetic have the thickness of the composite plate of steel plate and reinforcing fibre to combine greater than 3mm or with light prefabricated concrete slab, then use the described plate of method construct of injection and bonding synthetic resin.

Figure 17 represents to utilize compound stiffener 310 reparations of light prefabricated concrete to have the method for the concrete body of broken parts.The broken parts 383 of concrete body can be different piece.

At first, if aging, material disengaging, neutralization reaction, deterioration, obstruction groove (lock pocket) and peel off to be leaked by water and cause that then the workman demarcates broken parts, formation is in decussate line of cut 381 and finishes cutting work.If the reinforcing bar that exposes to the open air 384 is corroded, then the workman is used for the sander that derusts and removes the rust of the part that is corroded, and applies corrosion inhibitor with brush then.When derust and after the application job of anticorrosive finishes the filler opening that the workman utilizes hammer punch and inject to form on broken parts.After punching work, remove the dust in the hole, the packer that seals and be fixed for injecting (packer) 363, and the workman utilizes high pressure injector to finish injection and filling work.When by packer 363 injection cofferdam (coffering levee), utilize hammer to beat described packer 363 with its dismounting, remove lip-deep dust and manually or utilize the steel trowel to smear (wet adhesion type) high strength cofferdam 371 of wet binding type.After 24 hours, the workman checked that whether water takes place leaks after the work of smearing, and utilized hammer drill to form multi-functional anchor hole 385 and utilized air pump to remove dust and impurity in the anchor hole 385.Multi-functional holdfast and a height that is used to strengthen the composite plate 310 of concrete body and adjust plate are installed to eliminate the surface offsets between plate and the existing concrete body.Come gap between sealing plate and the concrete body with the inorganic based encapsulant.Because described multi-functional holdfast is as steam vent, so only in the gap on the top of plate, form steam vent 342.Behind sealing material curing, up inject wet binding type plaster material 372 from the multi-functional holdfast of lower end.After injection is finished for the first time,, finish low pressure injection for the second time to realize perfect filling after 24 hours.After injection is finished for the second time,, process multi-functional anchor hole decompression part on every side, be formed with the part of steam vent 342 and the surface of making dirty after 24 hours.

Industrial applicability

Although invention has been described above with reference to specific embodiment, the present invention is not subjected to this The restriction of a little embodiment, its claimed scope should be as the criterion with claims. Art technology Personnel can revise or improve these embodiment in the situation that does not deviate from spiritual scope of the present invention.

Claims

1, a kind of composite plate that is used to strengthen concrete body comprises:

The steel plate of prescribed level;

The tack coat that floods that on the upper surface of described steel plate, forms;

Be arranged on the upper surface of described steel plate and by the described tack coat dipping that floods and the reinforcing fibre of bonding; With

Be injected on the upper surface of described steel plate and impregnated and be bonded in powder on the described tack coat that floods.

2, composite plate as claimed in claim 1 is characterized in that, also comprises:

The tack coat that on the soffit of described steel plate, forms; With

The precast concrete plank of the prescribed level that is bondd by described tack coat.

3, composite plate as claimed in claim 2 is characterized in that, described precast concrete plank is the light prefabricated concrete slab that adopts light-duty aggregate.

4, composite plate as claimed in claim 3, it is characterized in that, when described light prefabricated coagulate plate is cut into planar rectangular shape, the composite plate that is used to strengthen the concrete body of claim 1 is cut into big or small the same as to be connected with described light prefabricated concrete slab with described light prefabricated concrete slab, perhaps cut into greater than described light prefabricated concrete slab and at a side of the four side that is connected with described light prefabricated concrete slab and have a projection, have two projections two relative edges, have three projections at its excess-three side except that a side, perhaps on four side, have four projections.

5, composite plate as claimed in claim 1, it is characterized in that, described reinforcing fibre is one of them of carbon fibre, glass fiber and aramid fibre at least, or one of them formation by piling up carbon fibre, glass fiber and aramid fibre, or by in synthetic carbon fibre, glass fiber and the aramid fibre two or more form at least, or by pile up and synthetic carbon fibre, glass fiber and aramid fibre in two or more form at least.

6, a kind of composite plate that is used to strengthen concrete body comprises:

The reinforcing fibre of prescribed level;

The tack coat that floods that on the upper surface of described reinforcing fibre, forms;

Be arranged on the upper surface of described reinforcing fibre and by the steel plate of described tack coat bonding of flooding; With

Spray, flood and be bonded in powder on the upper surface of described steel plate.

7, composite plate as claimed in claim 6 is characterized in that, also comprises:

The tack coat that on the soffit of described reinforcing fibre, forms; With

The precast concrete plank of the prescribed level that is arranged on the soffit of described reinforcing fibre and is bondd by described tack coat.

8, composite plate as claimed in claim 7 is characterized in that, described precast concrete plank is the light prefabricated concrete slab that adopts light-duty aggregate.

9, composite plate as claimed in claim 8, it is characterized in that, when described light prefabricated concrete slab is cut into planar rectangular shape, the composite plate that is used to strengthen the concrete body of claim 6 is cut into the same size with described light prefabricated concrete slab to be connected with described light prefabricated concrete slab, perhaps cut into greater than described light prefabricated concrete slab and at a side of the four side that is connected with described light prefabricated concrete slab and have a projection, have two projections two relative edges, have three projections at its excess-three side except that a side, perhaps on four side, have four projections.

10, a kind of composite plate that is used to strengthen concrete body comprises:

The upper steel plate of prescribed level;

The lower steel plate of prescribed level;

The tack coat that floods that on the upper surface of described upper steel plate, forms;

Be arranged on the upper surface of described upper steel plate and by the described tack coat dipping that floods and the reinforcing fibre of bonding;

The tack coat that on the upper surface of described reinforcing fibre, forms;

The tack coat bonding that this lower steel plate is formed on the upper surface of described reinforcing fibre;

The tack coat that on the surface of described upper and lower steel plate, forms;

Spray and be bonded in powder on the tack coat that forms on the surface of described upper and lower steel plate.

11, composite plate as claimed in claim 10 is characterized in that, also comprises:

The tack coat that on the soffit of described lower steel plate, forms; With

Be bonded in the precast concrete plank of the prescribed level on the described lower steel plate by described tack coat.

12, composite plate as claimed in claim 11 is characterized in that, described precast concrete plank is the light prefabricated concrete slab that adopts light-duty aggregate.

13, composite plate as claimed in claim 12, it is characterized in that, when described light prefabricated concrete slab is cut into planar rectangular shape, the composite plate that is used to strengthen the concrete body of claim 10 cuts into the same size with described light prefabricated concrete slab to be connected with described light prefabricated concrete slab, perhaps cut into greater than described light prefabricated concrete slab and at a side of the four side that is connected with described light prefabricated concrete slab and have a projection, have two projections two relative edges, have three projections at its excess-three side except that a side, perhaps on four side, have four projections.

14, a kind of composite plate that is used to strengthen concrete body comprises:

The steel plate of prescribed level;

Be installed on the upper surface of described steel plate and by the described tack coat dipping that floods and the upper strata reinforcing fibre of bonding; With

Spray, flood and be bonded in powder on the upper surface of described upper strata reinforcing fibre;

The tack coat that floods that on the soffit of described steel plate, forms;

Be installed on the soffit of described steel plate and by the described tack coat dipping that floods and lower floor's reinforcing fibre of bonding; With

Spray, flood and be bonded in powder on the soffit of described lower floor reinforcing fibre.

15, composite plate as claimed in claim 14 is characterized in that, also comprises:

The tack coat that on the soffit of described lower floor reinforcing fibre, forms; With

Be installed in the bottom of described lower floor reinforcing fibre and the precast concrete plank that is bondd by described tack coat.

16, composite plate as claimed in claim 15 is characterized in that, described precast concrete plank is the light prefabricated concrete slab that adopts light-duty aggregate.

17, composite plate as claimed in claim 16, it is characterized in that, when described light prefabricated concrete slab is cut into planar rectangular shape, the composite plate that is used to strengthen the concrete body of claim 14 cuts into the same size with described light prefabricated concrete slab to be connected with described light prefabricated concrete slab, perhaps cut into greater than described light prefabricated concrete slab and at a side of the four side that is connected with described light prefabricated concrete slab and have a projection, have two projections two relative edges, have three projections at its excess-three side except that a side, perhaps on all sides, have four projections.

18, a kind of compound stiffener of light prefabricated concrete that is used for the reinforcement of concrete body, described composite plate comprises:

Light prefabricated concrete slab, it comprises: the light concrete layer, be arranged on the netted reinforced glass fibre web of described light concrete layer inside, with the water-soluble cement based, latex cement mortar base or the polymer base resin bed that are included in the described light concrete layer, carry out spontaneous curing processing and cure under pressure successively and handle forming described light prefabricated concrete slab, one of them and water and cement mixing by aggregate that pearlite, Fei Laite, kieselguhr, ALC aggregate and ALC crushing engine are adopted form described light prefabricated concrete slab; With

With described light prefabricated coagulate plate bonding and the concrete body stiffening device that is connected.

19, composite plate as claimed in claim 18 is characterized in that, described concrete body stiffening device comprises:

Be coated in the thermosetting resin on the described light prefabricated concrete slab; With

Inorganic based reinforcing fibre thin plate, it immerses described thermosetting resin, and be cut into size the same with described light prefabricated concrete slab and engage, perhaps be cut into greater than described light prefabricated concrete slab and by ledge and engage with described light prefabricated concrete slab.

20, composite plate as claimed in claim 19, it is characterized in that, from unidirectional braiding aramid fibre thin plate, the unidirectional braiding carbon fibre of pre-preg, select at least a or multiple in cross braiding carbon fibre and the glass fiber thin plate as described inorganic based reinforcing fibre thin plate, this inorganic based reinforcing fibre thin plate is piled at least one or more layers, if there is direction in the braided fiber of wherein described reinforcing fibre thin plate, then described inorganic based reinforcing fibre thin plate is piled up in identical direction and is engaged and irrelevant with its accumulation quantity and stacking sequence, and wherein as long as described reinforcing fibre thin plate is piled up, described inorganic based reinforcing fibre thin plate just is immersed in the described thermosetting resin and engages.

21, composite plate as claimed in claim 20, it is characterized in that, when described light prefabricated concrete slab is cut into planar rectangular shape, described reinforcing fibre thin plate cuts into the same size with described light prefabricated concrete slab to be connected with described light prefabricated concrete slab, perhaps cut into greater than described light prefabricated concrete slab and at a side of the four side that is connected with described light prefabricated concrete slab and have a projection, have two projections two relative edges, have three projections at its excess-three side except that a side, perhaps on all sides, have four projections.

22, a kind of being used to improved the weather variation performance of concrete body and the light prefabricated concrete slab of fireproof performance, wherein utilizes and adopts the strong method that adds of reinforcing fibre thin plate to strengthen described concrete body, and described light prefabricated concrete slab comprises:

The light concrete layer, it forms by mixed cement, light-duty aggregate and water; With

The reinforced glass fibre web, it is piled up in described light prefabricated layer of concrete and integrated, and this reinforced glass fibre web is by immersing the glass fiber silk screen in the cementing agent that can flood and spraying and sclerosis quartz sand or blast furnace slag form.

23, a kind of method that is used to install light prefabricated plate, described method is used for by adopting the concrete body that strong method is strengthened extraly that adds of reinforcing fibre thin plate, thereby improve fireproof performance or be used to form the beautiful refacing of the concrete body that need redress because outward appearance is bad, described method comprises the following steps:

Removal impurity from described concrete body surface;

Whether the surface of checking described concrete body defectiveness and fill up this surface;

On the surface of the light prefabricated plate of the surface of described concrete body and claim 22 adhesive stripe-coating or mortar and will described light prefabricated plate and described concrete body bond; With

Between described light prefabricated plate, excavate joint and finish the joint work of fixed point.

24, a kind of compound stiffener of light prefabricated concrete that adds competent structure that is used for concrete body, described composite plate comprises:

The light prefabricated concrete slab of claim 22; With

Reinforcing fibre dipping plate or prestressing force reinforcing fibre composite plate, its bonding and being deposited on the upper surface of described light prefabricated concrete slab.

25, a kind of multi-functional holdfast, it comprises:

The plug-in unit of post shapes, described plug-in unit comprises body part and head, described body part is formed with a plurality of holes (212) on excircle, described body part at one end has internal thread, the other end is divided into several sections, the thickness that the described head that forms in the female end of formation is given prominence to and had regulation from described body part;

Insert in the described plug-in unit and have the expander tool of the cavity that vertically passes through therein, described expander tool size and shape can make the expanded in diameter of described plug-in unit;

Bolt, it has: body part; Head, its end from described body part extends, and the diameter of described head is greater than described body part; And cavity, it vertically passes through the center of described body part and head, described body part has the external screw thread that connects with internal thread and a plurality of hole of described plug-in unit, and described cavity is connected with the hole of described body part and is formed with internal thread on the inner periphery of head; With

Injection-tube with neck, head and body part of indent, described head is being formed with external screw thread and is connecting with the internal thread that forms on the inner periphery at described bolt head on the excircle, and form internal thread on the circumference within it, described body part is forming external screw thread and is connecting with the internal thread that forms on the inner periphery at described head on the excircle of one end, when described plug-in unit and described Bolt Connection, described injection-tube inserts the cavity of described bolt and the cavity of described expander tool.

26, a kind of compound stiffener of light prefabricated concrete that is used to repair and strengthen concrete body, described composite plate comprises:

By one of them of aggregate that pearlite, Fei Laite, kieselguhr, ALC aggregate and ALC crushing engine are adopted and the light concrete layer of water and cement mixing formation; With

The plate stiffening device that is connected with the surface of the light concrete layer of tabular prior perfusion and sclerosis.

27, a kind of compound stiffener of precast concrete that is used to repair and strengthen concrete body, described composite plate comprises:

Mix the concrete lower floor that forms by being used for concrete sand, aggregate, cement and water, it has the compressive strength the same or bigger with the concrete body that will strengthen;

Precast concrete plank, its generation type be for being arranged on one of them of reinforced glass fibre web, wire and reinforcing bar described concrete lower floor, and concrete spouting that at once will be the same with described concrete lower floor is to top; With

Be connected the concrete body stiffening device of the surface of described precast concrete plank.

28, a kind of compound stiffener of precast concrete that is used to repair and strengthen concrete body, described composite plate comprises:

Precast concrete plank, its generation type be for being arranged on one of them of reinforced glass fibre web, wire and reinforcing bar described concrete lower floor, and concrete spouting that at once will be the same with described concrete lower floor is to top;

Wherein one of them of reinforced glass fibre web, wire and reinforcing bar is provided with on the surface of described precast concrete plank, mixes the synthetic resin and the hardener of high-strength mortar, and the mixture that obtains mixes with quartz sand aggregate and pours into and bond.

29, a kind of precast concrete plank that is used to repair and strengthen concrete body, described precast concrete plank comprises:

Concrete lower floor with size the same with described concrete body or bigger compressive strength pours in advance and to carry out cure process tabular to form;

Utilize epoxy resin and hardener on the upper surface of concrete lower floor, to flood one of them of unidirectional carbon fibre, glass fiber and aramid fibre of special thin two-way or unidirectional carbon fibre, pre-preg; With

The concrete upper strata, it is used with described concrete lower floor's identical materials and with the mixed proportion identical with described concrete lower floor and forms, and utilize described epoxy resin and hardener with described concrete upper strata and described impregnation of fibers bonding, pour into described concrete upper strata in advance and make its sclerosis tabular to form.

30, a kind of compound stiffener of light prefabricated concrete that is used to repair and strengthen concrete body, described composite plate comprises:

The light concrete lower floor that one of them and water and cement mixing by aggregate that pearlite, Fei Laite, kieselguhr, ALC aggregate and ALC crushing engine are adopted forms;

Be bonded in the plate stiffening device on the upper surface of described light concrete lower floor; With

Be bonded in the light concrete upper strata on the upper surface of described plate stiffening device, it is used with light concrete lower floor identical materials with the mixed proportion identical with light concrete lower floor and forms.

31, composite plate as claimed in claim 30, it is characterized in that described plate stiffening device utilizes epoxy resin and hardener to inject and one of them of the unidirectional carbon fibre of bonding pre-preg, special thin unidirectional and two-way carbon fibre, aramid fiber and glass fiber between the tabular light concrete the upper and lower of perfusion in advance and sclerosis.

32, composite plate as claimed in claim 30, it is characterized in that, form described plate stiffening device in the following manner, one of them of glass fiber silk screen, wire and reinforcing bar is coated on the upper surface of described tabular light concrete lower floor, the epoxy resin and the hardener that mix quartz sand, high-strength mortar, mixture is poured on the upper surface of described light concrete lower floor with will described tabular light concrete upper strata and described light concrete lower floor bond.

33, a kind ofly be used to repair and the method for strengthening having because of the concrete body of the broken parts aging, that material separates, neutralization and damage cause, described method comprises the following steps:

The part of damaging is cut into rectangle;

Excavate and remove the concrete that is included in line of cut inside;

Form anchor hole;

With a kind of being arranged in the described anchor hole in the plate of the multi-functional holdfast of claim 25 and claim 26 to 32;

With inorganic based encapsulant or synthetic resin based encapsulant seal described plate and the concrete that breaks part between boundary member;

The part place forms a plurality of steam vents in the coboundary of described boundary member;

By multi-functional holdfast injection high strength synthetic resin and

Utilize inorganic material to repair the surface of described plate.

34, a kind of height of adjustable plate and holdfast of injection of being used for, described holdfast comprises:

The cylindrical body part, it has the conventional cavity that forms, described body part is formed with external screw thread on excircle, be formed with the through hole that intersects with described cavity at the one end, and the female other end of formation is formed with the dihedral ledge on the inner periphery at described cavity;

Nut with the engagement of the external screw thread of described body part;

Be the shaft-like injection-tube of routine, described injection-tube the one end be formed with external screw thread and with the engagement of the internal thread of described body part; With

Intermediate plate with column part and the annular section that is connected with described column part, described column part on inner periphery, be formed with internal thread and with the engagement of the external screw thread of described body part.

When 35, there is broken parts on a kind of road surface of laying when concrete, be used to repair and strengthen the method for concrete body, this method comprises the following steps:

Prepare prefabricated concrete slab, it has the anchor hole of a plurality of holdfasts that are used to install claim 34 and be provided with or be not provided with reinforcing bar on described plate;

The part of damaging is cut into rectangle;

Excavate and remove the concrete that is included in the line of cut inboard;

On the concrete surface of described excavation and removal, apply epoxy mortar;

The nut of the holdfast of claim 34 is fixed in the anchor hole of described precast concrete plank;

Screw the body part of the described holdfast that is fixed on nut in the described anchor hole and claim 34 and described precast concrete plank is arranged on the rigid pavement of excavation;

The body part that rotates holdfast is to regulate the height of described plate;

Utilize encapsulant to seal boundary member between described plate and the rigid pavement;

Utilize bar injection and filled synthetic resin cementing agent; With

Remove described bar and utilize the anchor hole that inorganic based is resin-sealed and repair described plate.