CN1487160A - Antibiotic and humidty-regulating board for cultural data bank and producing method thereof - Google Patents
Antibiotic and humidty-regulating board for cultural data bank and producing method thereof Download PDFInfo
- Publication number
- CN1487160A CN1487160A CNA031029280A CN03102928A CN1487160A CN 1487160 A CN1487160 A CN 1487160A CN A031029280 A CNA031029280 A CN A031029280A CN 03102928 A CN03102928 A CN 03102928A CN 1487160 A CN1487160 A CN 1487160A
- Authority
- CN
- China
- Prior art keywords
- conditioning plate
- antibiotic
- cellulose
- make
- mentioned
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
An antibiotic moisture-control panel for storing up cultural assets is provided to control moisture and to have an antibiotic function. The antibiotic moisture-control panel(1) for storing up cultural assets is manufactured by joining a medium density fiberboard(11) and an insulation board(12) in the double layers using adhesives.
Description
Technical field
The present invention relates to decorate the function of adjusting humidity antibiotic conditioning plate, existing, again the antibiotic conditioning plate of cultural data save room of anti-mildew function and the manufacture method of this antibiotic conditioning plate arranged as the wall of the cultural data save room of preserving precious cultural data and ceiling.
Background technology
Usually, for cultural data save room, requirement can keep cultural data desired uniform temperature of keeping and humidity to be taken care of fully, for this reason, be to process log with the inside wall that is used to decorate cultural data save room traditionally with paulownia wood, China fir or dragon spruce etc. of moisture-absorption characteristics, but the characteristics of above-mentioned log itself can not be regulated the desired temperature of save room, so adopted the method for regulating temperature and humidity in the save room by the Constant Temperature and Humidity Chambers of mechanical device recently always.
Constant Temperature and Humidity Chambers makes air circulation and regulates the characteristic that air themperature is also regulated humidity contained in the air simultaneously in the power with machinery; on the other hand; for will make interior temperature and humidity keep constant humidistat to work continuously always; so the running expense of Constant Temperature and Humidity Chambers is very high; and; because Constant Temperature and Humidity Chambers is mechanical device, the maintenance cost that usually can break down is very high again, so also exist the quite high problem of maintenance expense when being used for cultural data save room.
The present invention is for solving above-mentioned variety of problems, its purpose is to provide a kind of antibiotic conditioning plate and manufacture method thereof, this antibiotic conditioning plate is the improvement that the inventor carries out for No. 22880 its previous Korea S invention special permission, the wall with humidity conditioning function decorate with and ceiling decorate with adding antibacterial material in the conditioning plate to strengthen the function of conditioning plate, can keep, regulate temperature constant in the save room, and can suppress mouldy.
Content of the present invention
For achieving the above object, antibiotic conditioning plate of the present invention is the antibiotic conditioning plate of a kind of cultural data save room, and it is that to adopt bonding agent that lignocellulosic is compressed into density be 380-470kg/m
3Softboard and lignocellulosic be compressed into 630-730kg/m
3And cutting has the middle matter fiberboard of many grooves to be bonded together and the dual bonding wall that forms air communication channel between above-mentioned softboard and middle matter fiberboard is decorated and used conditioning plate, be characterized in, contain in decorating with the softboard of conditioning plate and middle matter fiberboard by iodine and be and chlorine is the antibacterial material 600-800ppm that compound is formed constituting above-mentioned wall.
Antibiotic conditioning plate of the present invention is the antibiotic conditioning plate of a kind of cultural data save room, and it is that wooden series fiber element is compressed into 630-730kg/m
3And both sides cuttings have can mutual chimeric assembling the recess and the ceiling of protuberance decorate and use conditioning plate, be characterized in, in above-mentioned ceiling is decorated with conditioning plate, contain by iodine and be and chlorine is the antibacterial material 600-800ppm that compound is formed.
In addition, a kind of cultural data save room of the present invention comprises that with the manufacture method of antibiotic conditioning plate following manufacturing procedure constituted: pulverizing process, this operation are that the cutting material of conifer log material or section material (comprising cutting bits material) are broken into size about 3cm, 2cm and 0.5cm as raw meal; Fiber decomposition process, this operation are to make through the particle of pulverizing process to keep suitable moisture content and it is decomposed into cellulose under 160-190 ℃ HTHP; Working procedure of coating, this operation are to make the cellulose that obtains from the fiber decomposition process by blowpipe resin adhesive is coated to cellulose to get on; Drying process, this operation are to make the cellulose that scribbles resin adhesive in working procedure of coating be dried to the cellulose that moisture content is 8-13% by drier continuously; Mould is annotated operation, and this operation is cellulose dry in drying process to be disperseed and the thick lamination that forms the base plate shape in shaping dies in shaped pipe by air; Beat operation, this operation is to beat continuously repeatedly and the thickness of cellulose base plate is reduced annotate the cellulose that becomes thick lamination in the operation in the shaping dies at above-mentioned mould; Forming process, this operation are to make through mould to annotate the interim forming board of operation at 150-170 ℃ and 20-30kg/cm
2HTHP under hot pressing and make it to have wall decorate with in matter fiberboard and softboard and ceiling decoration plus-pressure is pressed into conditioning plate with the desired thickness of fiberboard; Refrigerating work procedure, this operation are the conditioning plate that is compressed into given thickness by forming process to be put into cooler the resin adhesive that is coated on the cellulose is cooled off fully harden; And cut out, grinding step, this operation is to remove scalping after the specification and polish cutting out through the conditioning plate of refrigerating work procedure to become; Be characterized in, make that to add by iodine system and chlorine in the resin adhesive of above-mentioned working procedure of coating be the antibacterial material formed of compound and be mixed into mixture and with its diffusing being applied on the cellulose, in the working procedure of coating of the mixture of this bonding agent and antibacterial material, make conditioning plate have antibacterial functions.
As mentioned above, according to the present invention, because each antibiotic conditioning plate of the wall of architectural culture data save room and ceiling is to be raw material with lignocellulosic, the mixture of resin adhesive and antibacterial material is coated on to compress on it to make forms, so with comparing temp regulating function and will get well with the log manufacturing, the full-time difference of humidity is little, and mild inhibition effect is arranged, in addition, owing to have the anti-mildew function, so have the wall of inhibition save room and the effect that the ceiling place produces mould, and, even the former crack that the generation of the air conditioner of save room stops for a long time yet having the identical effect of the maintenance of the temperature in the save room.
Brief description of drawings
Fig. 1 is that wall of the present invention is decorated the stereogram with antibiotic conditioning plate.
Fig. 2 is that wall of the present invention is decorated the construction state profile with antibiotic conditioning plate.
Fig. 3 is the sectional view along the A-A line direction of arrow among Fig. 2.
Fig. 4 is that ceiling of the present invention is decorated the stereogram with antibiotic conditioning plate.
Fig. 5 is that ceiling of the present invention is decorated the confined state sectional drawing with antibiotic conditioning plate.
Fig. 6 is that wall decoration usefulness of the present invention and ceiling are decorated the manufacturing procedure picture with antibiotic conditioning plate.
The specific embodiment
Followingly be described in detail one embodiment of the invention with reference to accompanying drawing.
Fig. 1 is that wall of the present invention is decorated the stereogram with antibiotic conditioning plate; Fig. 2 is that wall of the present invention is decorated the construction state profile with antibiotic conditioning plate; Fig. 3 is the sectional view along the A-A line direction of arrow among Fig. 2; Fig. 4 is that ceiling of the present invention is decorated the stereogram with antibiotic conditioning plate; Fig. 5 is that ceiling of the present invention is decorated the confined state sectional drawing with antibiotic conditioning plate; Fig. 6 is that wall decoration usefulness of the present invention and ceiling are decorated the manufacturing procedure picture with antibiotic conditioning plate.
Label 1 expression wall among the figure is decorated and use antibiotic conditioning plate, and it is that the usefulness bonding agent is dual is bonded by middle matter fiberboard 11 and softboard 12 that this wall is decorated with conditioning plate 1, and label 2 is represented the antibiotic conditioning plate of ceilings decoration.
Above-mentioned wall is decorated and decorated with antibiotic conditioning plate 2 with antibiotic conditioning plate 1 and ceiling is to be made of wooden series fiber element, therefore, humid occasion can absorb moisture in air, has the humidity regulation function thereby the moisture that absorbs can be released in the few occasion of moisture.
Characteristics of the present invention are, constitute above-mentioned wall and decorate that to contain respectively by iodine with antibiotic conditioning plate 2 with the middle matter fiberboard 11 of antibiotic conditioning plate 1 and softboard 12 and ceiling decoration be that a spot of chlorine of thing is the antibacterial material 600-800ppm that forms of compound and have the anti-mildew function.
The above-mentioned antibacterial material cording of being made up of the compound of iodine system and chlorine system has the material of powerful antibiotic and anti-mildew function.
Therefore, wall of the present invention decorate with and ceiling decorate with antibiotic conditioning plate 1,2 and just not only had the function of regulating the humidity in the save room but also the function of mould fungus inhibition and so on generation is arranged.
In addition, in the occasion of above-mentioned wall with antibiotic conditioning plate 1, middle matter fiberboard 11 parts are contained in save room interior location place, softboard 12 parts are contained in save room external position place, the back side of above-mentioned softboard 12 be bonding in the opposition side of matter fiberboard 11 all pasting the saturating wet plate 2 that is stained with aluminium sheet paper on the two sides of water-fast clamping plate.
The saturating wet plate 3 that sticks on softboard 12 back sides is as mentioned above made and can be prevented fully that moisture is dipped in the save room thoroughly from the outside.
Constitute above-mentioned wall decorate with the one side of the middle matter fiberboard 11 of antibiotic conditioning plate 1 promptly with stickup face that softboard 12 is pasted mutually on a plurality of cancellate air communication channel 11a that intersect in length and breadth of formation, this air communication channel can flow the air in the save room between middle matter fiberboard 11 and softboard 12, like this, because flowing through in the process of air communication channel 11a, air in save room contacts with middle matter fiberboard 11 and softboard 12, so in the high occasion of air themperature, matter and softboard absorb in the part quilt of moisture, perhaps, in the low occasion of air humidity, middle matter and softboard are emitted by the moisture that will before absorb, and above-mentioned middle matter and softboard just can be regulated the humidity of the air in the save room.
In addition, be formed on above-mentioned in air communication channel 11a on the matter fiberboard 11 make level and the plumbness that air can be flowed smoothly, and make at the two side portions air of the above-mentioned air communication channel 11a of formation and can lightheartedly come in and go out and form the certain spacing S of being separated by.
Secondly, above-mentioned ceiling is decorated with antibiotic conditioning plate 2 and is also made the state that contains the antibacterial material of being made up of the compound of iodine system and a spot of chlorine system and have the anti-mildew function with the middle matter and the softboard 11,12 of antibiotic conditioning plate 1 as above-mentioned wall decoration when making lignocellulosic.
In the occasion of above-mentioned ceiling decoration with antibiotic conditioning plate 2, be to be formed at both sides of the edge portion to be in the recess 21 of symmetrical shape and protuberance 22 tablings and to assemble construction, but decorate also to make at above-mentioned ceiling and have extremely narrow clearance D with the office, department of assembly of antibiotic conditioning plate 2, moisture also can absorb at above-mentioned clearance D place or emit smoothly, in addition, on ceiling is decorated with the upper side among the lateral surface figure of antibiotic conditioning plate 2, also can be sticked and to prevent the wet plate 3 thoroughly that soaks into of moisture.
It is to prevent soaking into of moisture by the saturating wet plate 3 that is pasted on its lateral surface that above-mentioned ceiling is decorated with antibiotic conditioning plate 2, in addition also owing to containing antibacterial material, so can also be improved the anti-fungi performance that mould fungus inhibition produces.
Secondly, above-mentioned wall is decorated and decorated with antibiotic conditioning plate 2 with antibiotic conditioning plate 1 and ceiling all is to be that the same manufacture method of raw material employing is made with wooden series fiber element, below sets forth its manufacture method by its manufacturing procedure respectively.
[comminution engineering]
This operation is to be the cutting material of log saw lumber or after the sawdust that the wood shavings of saw lumber planing operation or sawing produce is feared with pine, utilizes grinder that it is ground into the manufacturing procedure of particle for 3cm, 2cm, 0.5cm left and right sides all size.
[fiber decomposition process]
This operation is to add water and after making it to keep suitable moisture content, under 160-190 ℃ HTHP it to be decomposed into cellulosic manufacturing procedure through the particle material of above-mentioned pulverizing process.
[working procedure of coating of adhesive-applying and antibacterial material mixture]
This operation is to decompose the operation that the cellulose form drops into the mixture that coating in the blowpipe mixes mutually by resin adhesive (natural resin) and antibacterial material in the above-mentioned fiber decomposition process, and the mixture of above-mentioned resin adhesive and antibacterial material is the liquid condition distribution and comes and bond on the cellulose.
Antibacterial material above-mentioned and that resin adhesive mixes mutually is that iodine system and a spot of chlorine are compound, and it has powerful antibiotic, anti-mildew function.
[drying process]
This operation is that the cellulose that will pass through the working procedure of coating of above-mentioned bonding agent and antibacterial material mixture drops into the operation of carrying out drying in the drier, and at this moment, it is about 8-13% that cellulose is dried to moisture content.
[mould notes operation]
This operation is with air cellulose injection molding mould dry in the above-mentioned drying process to be formed the operation of base plate shape, and the cellulose that injects this shaping dies is laminated to the thickness of having set with the great state in space.
[hammering operation]
This operation is repeatedly to beat the cellulose that is the former lamination of base plate shape in shaping dies with annotating at above-mentioned mould in the operation with forcing press and operation that the stack height of injecting the cellulose base plate that is stacked in shaping dies is reduced.
[forming process]
This operation is will be densified to the cellulose base plate of above-mentioned hammering operation degree with 20-30kg/cm under 150-170 ℃ high temperature
2Pressure hot pressing and be compressed into the operation of conditioning plate institute required thickness, decide ornamental antibiotic conditioning plate of wall and ceiling to decorate according to the thickness of the plate of compression molding in this operation and density and use antibiotic conditioning plate.
That is to say that constituting the occasion of wall decoration with the middle matter fiberboard of antibiotic conditioning plate, being pressed into thickness is that 8-10mm, density are 630-730kg/cm
2About; And in the occasion of softboard, being pressed into thickness is that 14-16mm, density are 380-470kg/cm
3About; Ceiling is decorated and then is pressed into thickness with antibiotic conditioning plate is that 14-16mm, density are 630-670kg/cm
3About.
[refrigerating work procedure]
This operation is for making the cellulosic resin adhesive that is hot pressed into desired thickness and density and is coated on antibiotic conditioning plate respectively in above-mentioned forming process become the state of sclerosis fully, and it is dropped in cooler certain hour (about 30-40 minute) cooling and resin adhesive is hardened fully.
[cutting and grinding step]
This operation be after will cutting into certain specification through each antibiotic conditioning plate of above-mentioned this refrigerating work procedure, grind and remove the surface operation, in this occasion, because the surface of each the antibiotic conditioning plate by above-mentioned refrigerating work procedure is very weak because of harden the in advance adhesion of resin adhesive of cooling effect, so be removed with grinding operation, and smooth processing done on the surface of each antibiotic conditioning plate.
Working procedure is: by the made wall of aforesaid operation decorate middle matter fiberboard 11, softboard 12 and ceiling with antibiotic conditioning plate 1 decorate with antibiotic conditioning plate 2 put into different categories check and discriminating after, in custodial warehouse, preserve, and then deliver to the manufacturing scene of save room, again in the on-the-spot following process of carrying out of this making; But in the occasion of above-mentioned wall decoration with antibiotic conditioning plate 1, it then is coating acrylic resin bonding agent and after making it drying on the surface of middle matter fiberboard 11, paste special decorative pattern plank in the above again, again in above-mentioned the back side of matter fiberboard 11 place slot processing with form with many air communication channel 11a that the inner area and the air conditioning condition of save room are consistent after, paste with bonding agent on the inner face of softboard 12 in case will form the stickup face of above-mentioned many air communication channel 11a, just can be formed in the wall that forms many air communication channel 11a between the stickup face of matter fiberboard 11 and softboard 12 in this and decorate with antibiotic conditioning plate 1.
Decorate at the wall that as above makes and to paste with bonding agent with the place, the back side of antibiotic conditioning plate 1 and wall is decorated with antibiotic conditioning plate 1 with thoroughly after wet plate 3 being integral, the state of pasting special decorative pattern plank with the inner face place of the matter fiberboard 11 that is arranged in save room carries out the wall of save room and constructs.
In addition, decorate occasion, then be not pasted with not the construction of carrying out ceiling under the state of pasting special decorative pattern plank on the face of wet plate 3 thoroughly with antibiotic conditioning plate 2 at above-mentioned ceiling.
Claims (3)
1. antibiotic conditioning plate of cultural data save room is that to adopt bonding agent that wooden series fiber element is compressed into density be 380-470kg/m
3Softboard and wooden series fiber element to be compressed into density be 630-730kg/m
3And cutting has the middle matter fiberboard of many grooves to be bonded together, and the dual bonding wall decoration that between above-mentioned softboard and middle matter fiberboard, forms air communication channel conditioning plate, it is characterized in that, contain in decorating with the softboard of conditioning plate and middle matter fiberboard by iodine and be and chlorine is the antibacterial material 600-800ppm that compound is formed constituting described wall.
2. antibiotic conditioning plate of cultural data save room, chain timbers matter series fiber element is compressed into 630-670kg/m
3And both sides cuttings have can mutual chimeric assembling the recess and the ceiling of protuberance decorate and use conditioning plate, it is characterized in that, in described ceiling is decorated with conditioning plate, contain by iodine and be and chlorine is the antibacterial material 600-800ppm that compound is formed.
3. a cultural data save room is with the manufacture method of antibiotic conditioning plate, this method comprises that following manufacturing procedure constitutes: pulverizing process, this operation are that the cutting material of conifer log material or section material (comprising cutting bits material) are broken into size about 3cm, 2cm and 0.5cm as raw meal; Fiber decomposition process, this operation are to make through the particle of pulverizing process to keep suitable moisture content and it is decomposed into cellulose under 160-190 ℃ HTHP; Working procedure of coating, this operation are to make the cellulose that obtains from the fiber decomposition process by blowpipe resin adhesive is coated to cellulose to get on; Drying process, this operation are to make the cellulose that scribbles resin adhesive in working procedure of coating be dried to the cellulose that moisture content is 8-13% by drier continuously; Mould is annotated operation, and this operation is cellulose dry in drying process to be disperseed and the thick lamination that forms the base plate shape in shaping dies in shaped pipe by air; Beat operation, this operation is to beat continuously repeatedly and the thickness of cellulose base plate is reduced annotate the cellulose that becomes thick lamination in the operation in the shaping dies at above-mentioned mould; Forming process, this operation are to make through mould to annotate the interim forming board of operation at 150-170 ℃ and 20-30kg/cm
2HTHP under hot pressing and make it to have wall decorate with in matter fiberboard and softboard and ceiling decoration plus-pressure is pressed into conditioning plate with the desired thickness of fiberboard; Refrigerating work procedure, this operation are the conditioning plate that is compressed into given thickness by forming process to be put into cooler the resin adhesive that is coated on the cellulose is cooled off fully harden; And cut out, grinding step, this operation is to remove scalping after the specification and polish cutting out through the conditioning plate of refrigerating work procedure to become; It is characterized in that, make that to add by iodine system and chlorine in the resin adhesive of above-mentioned working procedure of coating be the antibacterial material formed of compound and be mixed into mixture and with its diffusing being applied on the cellulose, in the working procedure of coating of the mixture of this bonding agent and antibacterial material, make conditioning plate have antibacterial functions.