CN1486951A - Steel slag cement - Google Patents
Steel slag cement Download PDFInfo
- Publication number
- CN1486951A CN1486951A CNA031389422A CN03138942A CN1486951A CN 1486951 A CN1486951 A CN 1486951A CN A031389422 A CNA031389422 A CN A031389422A CN 03138942 A CN03138942 A CN 03138942A CN 1486951 A CN1486951 A CN 1486951A
- Authority
- CN
- China
- Prior art keywords
- cement
- slag
- steel slag
- clinker
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The steel slag cement is produced with limestone, clay, sandstone and steel slag and through mixing in certain proportion, milling and baking to produce cement clinker. The cement clinker is then mixed with water granulated slag, steel slag, additive, etc. in certain proportion, and the mixture is milled into cement. The present invention used steel slag in producing both clinker and cement, and this can save resource and protect ecological environment. The cement of the present invention has the advantages of low water quantity demanded, high late strength and good compatibility with lignin and naphthoic water reducing agent, and has also better performance of resisting sulfate erosion, resisting drying shrinkage and suppressing alkali aggregate expansion.
Description
Technical field
The present invention relates to a kind of material of construction, particularly relate to a kind of steel slag cement.
Background technology
All use sulfate slag and iron ore in the production technique of the composite Portland cement of stipulating among Portland blast of stipulating among the GB1344-1999 and the GB12958-1999, volume is 3～5%, they exist water requirement big, later strength is low, with xylogen and shortcoming such as based water reducer bad adaptability how, and its resisting erosion of sulfate, resist drying shrinks and it is all relatively poor to suppress the alkali expansion character of gathering materials.Not only there is above-mentioned shortcoming in they, but also have the shortage of resources problem, do not utilize industrial residue well, and the slag of iron and steel enterprise is handled by the way of burying on the other hand, both easily environment has been polluted, and need take a large amount of places again.
Summary of the invention
Purpose of the present invention is intended to overcome above-mentioned shortcoming, provides a kind of and can utilize industrial residue, protects environment, can improve the steel slag cement of complex cement performance again.
For reaching above-mentioned purpose, steel slag cement of the present invention is after earlier raw materials such as Wingdale, clay, sandstone, slag being proportioned, make cement clinker through grinding, calcining, the common grinding that then raw materials such as cement clinker and grain slag, slag, additive proportioned promptly forms cement, and the weight part proportioning that wherein prepares each raw material of cement clinker is:
Wingdale 675-735 part clay 100-160 part
Sandstone 85-95 part slag 75-85 part
The weight part proportioning of each raw material of preparation cement is:
Grog 375-425 part grain slag 375-425 part
Slag 160-180 part additive 25-35 part.
Above-mentioned steel slag cement is characterized in that: described additive is one or more in bassanite, alunite and the Sodium sulfate anhydrous.min(99).
Compared with prior art, the present invention has following advantage:
1, the present invention has all used slag when producing grog and cement, has improved the consumption of slag, has solved environmental pollution and shortage of resources problem, for industrial waste residue disposal has found an effective way, has very high social benefit and economic benefit.
2, the present invention is easy to prepare the higher grog of silica modulus with the raw material raw material of slag as calcination of cement clinker, can improve the later strength of grog, but also can utilize the crystal seed effect of slag, improves the burn-ability of cement clinker, reduces hear rate.In high-content slag cement, introduce an amount of slag, the activity of activated slag, make the blended material total amount reach 60～65%, the strength of cement grade can reach 42.5, compare with the composite Portland cement of stipulating among the Portland blast of stipulating among the GB1344-1999 and the GB12958-1999, it is little that the present invention has water requirement, the later strength height, with xylogen and advantage such as how based water reducer adaptability is good, and its resisting erosion of sulfate, resist drying shrinks and inhibition alkali gathers materials, and expansion character all is higher than above-mentioned two kinds of cement.
3, the present invention is not increasing cement manufacture plant, is not changing under the situation of cement industry condition, and grog output improves 36%, and clinker strength improves 10MPa, and energy consumption reduces by 25%, CO
2Quantity discharged reduces 12%.If the cement production enterprise widespread use in the whole nation, but every year 2000 ten thousand tons in digestibility and utilization slag.
Embodiment
Embodiment 1: the weight part proportioning that present embodiment prepares each raw material of cement clinker is: Wingdale 695kg, clay 135kg, sandstone 89kg, slag 81kg; The weight part proportioning of each raw material of preparation cement is: grog 425kg, grain slag 375kg, slag 170kg, bassanite 12kg, alunite 6kg, Sodium sulfate anhydrous.min(99) 12kg.
Embodiment 2: the weight part proportioning that present embodiment prepares each raw material of cement clinker is: Wingdale 700kg, clay 130kg, sandstone 90kg, slag 80kg; The weight part proportioning of each raw material of preparation cement is: grog 420kg, grain slag 380kg, slag 170kg, bassanite 18kg, Sodium sulfate anhydrous.min(99) 12kg.
Embodiment 3: the weight part proportioning that present embodiment prepares each raw material of cement clinker is: Wingdale 710kg, clay 120kg, sandstone 92kg, slag 78kg; The weight part proportioning of each raw material of preparation cement is: grog 400kg, grain slag 400kg, slag 170kg, bassanite 30kg.
The physicals of above-mentioned three embodiment grogs
| Sequence number | Stability | Mark thick water | Fineness | Time of coagulation (h: m) | Folding strength (Mpa) | Ultimate compression strength (Mpa) | |||
| ％ | ?％ | Initial set | Final set | ??3d | ??28d | ??3d | ??28d | ||
| ??1 | Qualified | 22.5 | ?5.0 | ?2∶10 | ?3∶00 | ??5.4 | ??9.3 | ??28.2 | ??61.8 |
| ??2 | Qualified | 22.5 | ?6.0 | ?1∶50 | ?2∶45 | ??5.6 | ??9.4 | ??24.3 | ??59.5 |
| ??3 | Qualified | 22.5 | ?5.0 | ?1∶55 | ?2∶30 | ??4.8 | ??9.5 | ??21.8 | ??63.3 |
The cement performance of above-mentioned three embodiment
| Sequence number | Stability | Mark thick water | Fineness | Time of coagulation (h: m) | Folding strength (Mpa) | Ultimate compression strength (Mpa) | |||
| ％ | ?％ | Initial set | Final set | ????3d | ????28d | ????3d | ??28d | ||
| ??1 | Qualified | 24.0 | ?4.8 | ?2∶30 | ?5∶06 | ????4.6 | ????8.8 | ????18.7 | ??54.3 |
| ??2 | Qualified | 25.3 | ?6.0 | ?1∶59 | ?5∶14 | ????3.6 | ????8.6 | ????17.0 | ??53.2 |
| ??3 | Qualified | 24.8 | ?5.6 | ?3∶17 | ?6∶42 | ????4.4 | ????9.1 | ????14.1 | ??47.0 |
Claims (2)
1, a kind of steel slag cement, it is characterized in that: it is after earlier raw materials such as Wingdale, clay, sandstone, slag being proportioned, make cement clinker through grinding, calcining, the common grinding that then raw materials such as cement clinker and grain slag, slag, additive proportioned promptly forms cement, and the weight part proportioning that wherein prepares each raw material of cement clinker is:
Wingdale 675-735 clay 100-160
Sandstone 85-95 slag 75-85
The weight part proportioning of each raw material of preparation cement is:
Grog 375-425 grain slag 375-425
Slag 160-180 additive 25-35.
2, steel slag cement according to claim 1 is characterized in that: described additive is one or more in bassanite, alunite and the Sodium sulfate anhydrous.min(99).