CN101747007A - Baking-free brick made from renewable material of building waste - Google Patents
Baking-free brick made from renewable material of building waste Download PDFInfo
- Publication number
- CN101747007A CN101747007A CN200910163225A CN200910163225A CN101747007A CN 101747007 A CN101747007 A CN 101747007A CN 200910163225 A CN200910163225 A CN 200910163225A CN 200910163225 A CN200910163225 A CN 200910163225A CN 101747007 A CN101747007 A CN 101747007A
- Authority
- CN
- China
- Prior art keywords
- building waste
- waste
- baking
- building
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a baking-free brick prepared by renewable material of building waste, which belongs to technology field of building material baking-free brick. The mixture ratios of raw-material quality of the baking-free brick are as follows: building waste debris 75-85, phosphorite slag sand-like material 15-20, cement 10-15, quicklime 0.5 - 0.8, gelling agent 0.3 - 0.5, accelerant 0.2-0.4, sodium silicate 0.1-0.15, and water 10-15, wherein, the granularity of the building waste debris is not more than 15mm, the granularity of the phosphorite slag sand-like material is not more than 0.8 mm. The invention can integratedly utilize the building waste and the phosphogypsum waste which are difficult to deal with, and reduce the production cost, meanwhile, decrease the environment pollution.
Description
Technical field
The present invention relates to a kind of the non-burning brick of made from renewable material of building waste preparation that adopt, belong to the non-burning brick technical field of material of construction.
Background technology
Building waste and phosphorus ore waste residue all belong to and are difficult to the waste handling and utilize, and the treatment process that adopts usually is to concentrate landfill or concentrate and stack at present.But the process of urbanization development is swift and violent, the phosphorus chemical industry of China is also in development, urban architecture rubbish rubbish that is produced and phosphorus ore waste residue are along with accumulation year by year is more and more, concentrate landfill or concentrate the mode of stacking can't adopt, the result has caused a large amount of soils occupied, when raining to around cause very big environmental pollution, the while is also caused waste to making profits with resource.
Summary of the invention
Technical problem to be solved by this invention provides a kind of baking-free brick made from renewable material of building waste, can fully utilize reluctant building waste and phosphorus ore waste residue, reduces production costs, and reduces environmental pollution simultaneously again.
Solving the scheme that technical problem of the present invention adopts is:
Each non-burning brick raw material mass mixture ratio is, 75～85 parts of building waste particles, 15～20 parts in the sand-like material of phosphorus ore slag, 10～15 parts of cement, 0.5～0.8 part of unslaked lime, 0.3～0.5 part of jelling agent, 0.2～0.4 part of promotor, 0.1～0.15 part of water glass, 10～15 parts in water, and wherein the granularity of building waste particle is≤15mm, and the granularity of the sand-like material of phosphorus ore slag is≤0.8mm.
What building waste of the present invention adopted is that the dismounting waste of old building and the useless brick of new construction, disintegrating slag, the single of concrete waste residue plant or mixture; The sand-like material of described phosphorus ore slag adopts the Rock Phosphate (72Min BPL) raw material to smelt and extracts the slag waste of discharging behind the yellow phosphorus.
Also having added 0.15～0.25 part of villaumite in described each raw material mass mixture ratio is frostproofer, and suitable cold district uses in the winter time.
The invention has the beneficial effects as follows: made full use of reluctant waste, turned waste into wealth, saved the resource and the energy, eliminated environmental pollution, production cost is low, and maintenance rises but and shifts to an earlier date 1/3 day than routine is non-burning brick.No matter the non-burning brick reworked material of the present invention is used for producing holllow building block, still produces solid commentaries on classics, and quality all surpasses company standard.
Embodiment
Embodiment 1
Get the dismounting waste of old building, be crushed to 13～15mm; The Rock Phosphate (72Min BPL) raw material is produced the waste residue that discharges behind the yellow phosphorus be crushed to 0.4mm.Mix 75 parts of building waste particles, 20 parts in the sand-like material of phosphorus ore slag, 10 parts of cement, 0.5 part of unslaked lime, 0.3 part of jelling agent, 0.2 part of promotor, 0.1 part of water glass, 11 parts in water by following quality proportioning.Send in the holllow building block shaper, compression moulding, maintenance 12 days obtains the holllow building block finished product.
Embodiment 2
Get the mixture of useless brick, disintegrating slag and the concrete waste residue of new construction, be crushed to 8～10mm; The Rock Phosphate (72Min BPL) raw material is produced the waste residue that discharges behind the yellow phosphorus be crushed to 0.6mm.Mix 85 parts of building waste particles, 15 parts in the sand-like material of phosphorus ore slag, 15 parts of cement, 0.8 part of unslaked lime, 0.5 part of jelling agent, 0.4 part of promotor, 0.15 part of water glass, 15 parts in water by following quality proportioning.Send in the solid brick formation of lots machine, compression moulding, maintenance 12 days obtains unburned solid brick finished product.
Embodiment 3
Get the useless brick of dismounting of old building, be crushed to 7mm; The Rock Phosphate (72Min BPL) raw material is produced the waste residue that discharges behind the yellow phosphorus be crushed to 0.8mm.Mix by following quality proportioning, 80 parts of building waste particles, 17 parts in the sand-like material of phosphorus ore slag, 13 parts of cement, 0.7 part of unslaked lime, 0.4 part of jelling agent, 0.3 part of promotor, 0.13 part of water glass, 14 parts in water adds 0.2 part of sodium-chlor frostproofer in addition.Send in the solid brick formation of lots machine, compression moulding, maintenance 12 days obtains unburned solid brick finished product.
Claims (3)
1. baking-free brick made from renewable material of building waste, it is characterized in that: each non-burning brick raw material mass mixture ratio is 75～85 parts of building waste particles, 15～20 parts in the sand-like material of phosphorus ore slag, 10～15 parts of cement, 0.5～0.8 part of unslaked lime, 0.3～0.5 part of jelling agent, 0.2～0.4 part of promotor, 0.1～0.15 part of water glass, 10～15 parts in water, and wherein the granularity of building waste particle is≤15mm, the granularity of the sand-like material of phosphorus ore slag is≤0.8mm.
2. baking-free brick made from renewable material of building waste according to claim 1 is characterized in that: what building waste of the present invention adopted is that the dismounting waste of old building and the useless brick of new construction, disintegrating slag, the single of concrete waste residue plant or mixture; The sand-like material of described phosphorus ore slag adopts Rock Phosphate (72Min BPL) to smelt and extracts the slag waste of discharging behind the yellow phosphorus.
3. baking-free brick made from renewable material of building waste according to claim 1 is characterized in that: also having added 0.15～0.25 part of villaumite in described each raw material mass mixture ratio is frostproofer.