CN1468928A - 混凝土伸缩缝密封硅橡胶 - Google Patents

混凝土伸缩缝密封硅橡胶 Download PDF

Info

Publication number
CN1468928A
CN1468928A CNA021334889A CN02133488A CN1468928A CN 1468928 A CN1468928 A CN 1468928A CN A021334889 A CNA021334889 A CN A021334889A CN 02133488 A CN02133488 A CN 02133488A CN 1468928 A CN1468928 A CN 1468928A
Authority
CN
China
Prior art keywords
silicone rubber
extension joint
sealing
weight portions
concrete extension
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA021334889A
Other languages
English (en)
Other versions
CN1182221C (zh
Inventor
兵 祝
祝兵
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CNB021334889A priority Critical patent/CN1182221C/zh
Publication of CN1468928A publication Critical patent/CN1468928A/zh
Application granted granted Critical
Publication of CN1182221C publication Critical patent/CN1182221C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明提供一种混凝土伸缩缝密封硅橡胶，其特征在于组分按重量份计算如下：107室温硫化硅橡胶100，纳米碳酸钙50～150，白炭黑2～10，交联固化剂3～20。该硅橡胶对桥梁、隧道和道路工程的混凝土构件具有良好的附着力，具有极佳的抗紫外线、耐老化性性能，在阳光、雨水、冰雪、极高或极低温度环境均能保持其弹性性能，且无污染，易于回收和再利用。主要用于桥梁、隧道、道路工程、高速公路、机场跑道等混凝土伸缩缝的密封，开裂混凝土结构的修补，以及桥梁缆索、吊杆等及金属表面的防腐处理。

Description

混凝土伸缩缝密封硅橡胶
技术领域
本发明涉及一种密封胶，特别是涉及一种混凝土伸缩缝密封硅橡胶。
背景技术
随着交通事业的发展，城市道路、高架桥梁及隧道工程等日益增多，混凝土伸缩缝的问题已引起工程界的重视，要求进一步提高混凝土伸缩缝材料的耐久性能、弹性性能、整体粘结性和强度。国内目前混凝土伸缩缝材料主要采用沥青和硫化橡胶，以及聚氨酯材料，这些材料的耐久性能、弹性性能、整体粘结性和强度均较差，且具有毒性，易造成环境污染，影响道路和桥梁、隧道等的使用寿命。
发明内容
本发明的目的在于提供一种在于克服上述缺点，提供一种弹性伸缩能力强，具有卓越的密封粘结性能，且耐候性优良的混凝土伸缩缝密封硅橡胶。
本发明混凝土伸缩缝密封硅橡胶组分按重量份计算如下：
107室温硫化硅橡胶            100
纳米碳酸钙                   50～150
白炭黑                       2～10
交联固化剂                   3～20其中，交联固化剂组分按重量份计算如下：
酮肟基硅烷                   100
酰胺基硅烷                   50～150
羟胺基硅烷                   50～150
有机锡催化剂                 5～10
硅烷偶联剂                    4～10
二甲基硅油                    10～30其中，酮肟基硅烷是甲基三丁酮肟基硅烷、苯基三丁酮肟基硅烷等；酰胺基硅烷是甲基乙烯基酰胺基硅烷等；羟胺基硅烷是二甲基羟胺基硅烷等；有机锡催化剂是二丁基二月桂酸锡等；硅烷偶联剂是KH550、KH560等。
本发明混凝土伸缩缝密封硅橡胶的优点在于，1)弹性伸缩能力强：在伸缩缝粘结时可拉伸160％或压缩50％，当放松时，它能恢复到原状的95％，甚至更好，伸长或压缩多次均能恢复原状。2)卓越的密封粘结性能：即对桥梁、隧道及道路工程的混凝土构件具有良好的附差力，在拉伸至160％或压缩至50％状态下，仍具有良好地粘结性能，拉伸粘结强度≥0.4Mpa。3)耐候性：具有极佳的抗紫外线、耐老化性能，在阳光、雨水、冰雪、极高或极低温度环境均能保持其弹性性能，其使用温度范围为-45℃～149℃。4)无污染，易于回收和再利用。主要用于桥梁、隧道、道路工程、高速公路、机场跑道等混凝土伸缩缝的密封，开裂混凝土结构的修补，以及桥梁缆索、吊杆等及金属表面的防腐处理。
具体实施方式
实施例1：
本发明混凝土伸缩缝密封硅橡胶组分按重量份计算如下：
107室温硫化硅橡胶             100
纳米碳酸钙                    80
白炭黑                        2
交联固化剂                    12
其中，交联固化剂组分按重量份计算如下：
甲基三丁酮肟基硅烷            100
甲基乙烯基酰胺基硅烷          100
二甲基羟胺基硅烷              50
二丁基二月桂酸锡              5
KH-550                        3
KH-560                        3
二甲基硅油                    15
先将上述交联固化剂组分加入真空反应釜中混合反应，制得交联固化剂。再将密封硅橡胶组分与交联固化剂在行星搅拌机内混合均匀，脱除反应中生成的部分低分子物质，得本发明密封硅橡胶。其性能指标如表1所示。
实施例2：
本发明混凝土伸缩缝密封硅橡胶组分按重量份计算如下：
107室温硫化硅橡胶             100
纳米碳酸钙                    120
白炭黑                        5
交联固化剂                    15
其中，交联固化剂组分按重量份计算如下：
苯基三丁酮肟基硅烷            100
甲基乙烯基酰胺基硅烷          120
二甲基羟胺基硅烷              80
二丁基二月桂酸锡              8
KH-550                        2
KH-560                        2
二甲基硅油                    20
先将上述交联固化剂组分加入真空反应釜中混合反应，制得交联固化剂。再将密封硅橡胶组分与交联固化剂在行星搅拌机内混合均匀，脱除反应中生成的部分低分子物质，得本发明密封硅橡胶，其性能指标如表1所示。
表1：
 性能     指标   实施例1     实施例2
 下垂度(mm)     ≤1   0     0
 挤出性(mL/min)     ≥80   93     90
 表于时间(min)     20～150   50     30
 硬度(HAS)     15～50   36     30
 恢复率(％)     ≥90   95     95
剥离强度(MPa)     ≥0.9     0.95     1.02
伸长率(％)     50～1000     500     300

Claims (2)

1、一种混凝土伸缩缝密封硅橡胶，其特征在于组分按重量份计算如下：
107室温硫化硅橡胶         100
纳米碳酸钙                50～150
白炭黑                    2～10
交联固化剂                3～20
2、如权利要求1所述的混凝土伸缩缝密封硅橡胶，其特征在于交联固化剂组分按重量份计算如下：
酮肟基硅烷               100
酰胺基硅烷               50～150
羟胺基硅烷               50～150
有机锡催化剂             5～10
硅烷偶联剂               4～10
二甲基硅油               10～30
CNB021334889A 2002-07-19 2002-07-19 混凝土伸缩缝密封硅橡胶 Expired - Fee Related CN1182221C (zh)