CN1464013A - Environment friendly aquosity woodware nano paint - Google Patents
Environment friendly aquosity woodware nano paint Download PDFInfo
- Publication number
- CN1464013A CN1464013A CN 02122200 CN02122200A CN1464013A CN 1464013 A CN1464013 A CN 1464013A CN 02122200 CN02122200 CN 02122200 CN 02122200 A CN02122200 A CN 02122200A CN 1464013 A CN1464013 A CN 1464013A
- Authority
- CN
- China
- Prior art keywords
- amount
- agent
- water
- woodware
- add
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The environment protecting aqueous nano woodenware lacquer is prepared with special emulsion, water, nano slurry and water soluble fluoric resin as well as proper amount of HR crosslinking agent, K40 leveling agent, defoaming agent, mildew inhibitor, reinforcing agent and modifier, and the preparation includes mixing and grinding. The aqueous nano woodenware lacquer as one green product has no negative effect on human body and environment during its production and use.
Description
Affiliated technical field
The present invention relates to be used for the lacquer on brushing woodenware surface.
Background technology
As everyone knows, the lacquer that is used for brushing woodenware surface has a variety of, as varnish, paint, piano lacquer etc., these lacquers though to be coated with brushing effects each has something to recommend him, but all comprise harmful composition, as benzene, formaldehyde etc., in process of manufacture also because of these harmful HUMAN HEALTH being arranged and to the also harmful chemical substance of environment, caused serious environmental to pollute and destruction, so these those skilled in the art just constantly research and develop the lacquer with feature of environmental protection, in the hope of both guaranteeing that result of use does not reduce, simultaneously also favourable to environment and user.The present invention is exactly under the guidance of this research direction and the environment friendly aquosity woodware nano paint of developing.
Summary of the invention
The invention provides a kind of environment friendly aquosity woodware nano paint, it is to be mixed by following material to form, and contains by weight percentage:
Aqueous wooden ware special emulsion 40%
Water 20%
Many somaplasms of nanometer material 20%
The HR glue crosslinking agent is an amount of
K
40Flow agent is an amount of
Water-soluble fluorine resin 10%
Defoamer is an amount of
Mould inhibitor is an amount of
Strength agents is an amount of
Properties-correcting agent is an amount of
The said HR glue crosslinking agent of the above-mentioned batching of the present invention, K40 flow agent, water-soluble fluorine resin, defoamer, mould inhibitor, strength agents and properties-correcting agent are material commonly used in the paint vehicle industry, do not add special qualification at this.
Compound method is as follows:
In the special-purpose latax of aqueous wooden ware, add entry, add many somaplasms of nanometer material after stirring, react adding water-soluble fluorine resin after 30 minutes, add HR glue crosslinking agent, K more successively
40Behind flow agent, mould inhibitor, strength agents, properties-correcting agent and the defoamer, grinding can obtain.
The present invention utilizes and add many somaplasms of novel material nanometer material in wood lacquer, can be made into water-miscible paint, and manufacturing processed and use back all do not have any detrimentally affect to human body and environment, are environmental type woodenware paint vehicle.
Embodiment
Example 1
After adding 200kg water stirs in the special-purpose latax of the aqueous wooden ware of 400kg, add the reaction of many somaplasms of 200kg nanometer material after 30 minutes, add 100kg water-soluble fluorine resin, add 20kgHR glue crosslinking agent, 10kgK more successively
40Behind flow agent, 15kg defoamer, 15kg mould inhibitor, 20kg strength agents, the 20kg properties-correcting agent, grinding can obtain 1 ton of environment friendly aquosity woodware nano paint of the present invention.
Claims (1)
1, a kind of environment friendly aquosity woodware nano paint is characterized in that it contains by weight percentage:
Aqueous wooden ware special emulsion 40%
Water 20%
Many somaplasms of nanometer material 20%
The HR glue crosslinking agent is an amount of
K
40Flow agent is an amount of
Water-soluble fluorine resin 10%
Defoamer is an amount of
Mould inhibitor is an amount of
Strength agents is an amount of
Properties-correcting agent is an amount of
In the special-purpose latax of aqueous wooden ware, add entry, add many somaplasms of nanometer material after stirring, react adding water-soluble fluorine resin after 30 minutes, add HR glue crosslinking agent, K more successively
40Behind flow agent, mould inhibitor, strength agents, properties-correcting agent and the defoamer, grinding can obtain.