CN1463611A - Process for production of biological degradable chewing gum - Google Patents
Process for production of biological degradable chewing gum Download PDFInfo
- Publication number
- CN1463611A CN1463611A CN 02115932 CN02115932A CN1463611A CN 1463611 A CN1463611 A CN 1463611A CN 02115932 CN02115932 CN 02115932 CN 02115932 A CN02115932 A CN 02115932A CN 1463611 A CN1463611 A CN 1463611A
- Authority
- CN
- China
- Prior art keywords
- zeins
- chewing gum
- crosslinking agent
- shitosan
- gram
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention features that yellow corn powder as corn processing leftover is used as main material, into which ethanol is added to produce alcohol soluble protein for producing gum. Alcohol soluble corn protein as gum is produced through adding 70-90 % concentration ethanol solution into yellow corn powder and immediate microwave treatment, and is modified with chitosan and crosslinking agent to form chitosan-alcohol soluble protein gum. The gum is mixed with sweetener, edible essence and color to produce biodegradable chewing gum with bacteriostasis function. The present invention opens one new way for producing environment-protecting chewing gum.
Description
Technical field
The invention belongs to the chewing gum production technical field, relevant with Food Chemistry.
Background technology
Maize yellow-powder also claims the corn glutelin, is a large amount of accessory substances during cornstarch is produced, and includes abundant zeins (about 60%), generally makes feed in the past and uses.The relevant existing report of zeins that from maize yellow-powder, extracts, as application number is that 00101222.3 Chinese invention patent application discloses a kind of method of extracting zeins, this method is made solvent with 60%-95% ethanol, 60-70 ℃ needs down to extract 90 minutes, and the zeins of extraction is mainly used on the packaging material.This method takes time and grows (90 minutes), energy consumption height.
Zeins is a kind of natural macromolecular material, and certain filming performance is arranged, if through special modification, can reach high resiliency, high strength, replaces the matrix of chewing gum.The matrix of the chewing gum of selling because of existing market is to be made into natural resin (as gutta-percha, ester gum etc.) and synthetic resin (as polyvinyl acetate, polyisobutene etc.), and they can not biodegradation at occurring in nature, thereby causes environmental pollution easily.As application number is that 891088555.5 Chinese invention patent application discloses a kind of chewing gum method for making that contains the intense sweetener particle of band modification alcohol soluble protein coating, zeins with the hydroxy propyl cellulose modification, because of its intensity and elasticity relatively poor, so can only be as the coating film of sweetener, play the delay release action, can not be as matrix.Chinese invention patent application (application number is 97198574.x) adopts plasticizer to make protein material plasticization and modifications such as zeins, wheat gluten protein, is used to make the matrix of chewing gum.The plasticizer of being used mainly contains glycerine, ethylene glycol etc.; Protein has zeins, wheat gluten and gelatin etc.Since plasticising can only change protein three, quaternary structure.Plasticizer and protein form hydrogen bond, thereby make the hydrogen bond rupture of protein, and the I and II structure of protein fails to change, so the intensity of protein changes not quite, the matrix of chewing gum is desirable not enough.
Summary of the invention
The objective of the invention is to be to overcome the deficiency that prior art exists, propose the better also production method of the environmentally friendly chewing gums of biodegradable chewing gum base of a kind of performance, to reach environmental protection requirement and to open up new chewing gum production approach.
The present invention is achieved through the following technical solutions:
A kind of production method of environmentally friendly chewing gums of biodegradable chewing gum base, with corn processing fent maize yellow-powder is raw material, add the alcohol extract alcohol soluble protein, it is characterized in that, in maize yellow-powder, add 70%-90% ethanol, carry out microwave treatment then immediately, obtain being used to produce chewing gum base raw material zeins, make shitosan-alcohol soluble protein chewing gum base through shitosan+crosslinking agent modification, in improved matrix, add sweetener, edibility essence and pigment and make chewing gum with biodegradation character and bacteria resistance function.
The processing step that extracts zeins comprises:
1) by weight/volume by maize yellow-powder and ethanol is 1: 8-1: 14 to raw material adding ethanol;
2) be that 2450MHz or 915MHz, power are 800-2000 watt microwave with the bloom frequency of step 1), handled 1-6 minute;
3) with step 2) mixture centrifugal, obtain supernatant;
4) supernatant of step 3) is saltoutd with 1% sodium chloride, the centrifugal sediment that obtains with described sediment oven dry, obtains zeins.
Described zeins method of modifying comprises: earlier the alcoholic solution with zeins mixes with the citric acid solution of shitosan, makes shitosan and zeins crosslinked with crosslinking agent then, makes it become the modified corn alcohol soluble protein.Wherein the usage ratio of zeins and shitosan is 2: 1-4: 1
Described crosslinking agent is a food grade products, being used for crosslinking agent of the present invention selects from tannic acid, polyhydric phenols, glutamic acid, L-Lysine mono Hydrochloride, glutaraldehyde, cinnamic acid a kind of or mixture wherein, wherein best crosslinking agent is glutaraldehyde or cinnamic acid, and the 1-4% that the addition of crosslinking agent is pressed the zeins consumption adds.
The present invention is with chitin modified zeins, based on the amino generation cross-linking reaction in amino in the shell dimeric molecule and the zeins molecule (this moment, the I and II structure of protein changed), form bigger protein-chitosan molecule with network structure.This material has elasticity and intensity preferably, can substitute natural resin and synthetic resin matrix fully as matrix, adds auxiliary materials such as sweetener, essence again and makes chewing gum.With the chewing gum that the present invention makes, all form, but abandon all biological degraded in 30 days in environment by natural component.And the shitosan in this chewing gum has bacteria resistance function, can prevent and treat mouth disease, plays the effect of strong tooth.
The preparation method of chewing gum of the present invention is: take by weighing zeins 20 grams, with 160 milliliters of 70%-90% ethanol dissolvings, add 5-10 gram shitosan (elder generation dissolves with 1% citric acid), crosslinking agent 0.5 gram, under 50 ℃ of constant temperatures, reacted while stirring 1-6 minute, be heated to moisture 20% o'clock at 70 ℃-90 ℃, add 0.1 gram glyceryl stearate, 0.2 gram glycerine, 0.1 gram palm oil and an amount of auxiliary material, essence, in driving refining formula rubber mixing machine, mix, when moisture drops to 10%, pass through compression molding, section, arrangement, be packaged to be the antibacterial chewing gum of biodegradation.The technological process of production is seen Fig. 3
Description of drawings
Accompanying drawing 1 is existing preparation zeins process chart (correlation technique);
Accompanying drawing 2 is process charts of the present invention.
The specific embodiment
Embodiment 1:
Is mixing in 2000 milliliters the glass container with the ethanol of maize yellow-powder 100 gram and 800 milliliter 70% at volume, 6 minutes (microwave conditions: 915MHz of heating using microwave, 800W), centrifugal, get supernatant, add 800 milliliter of 1% sodium chloride and saltout, centrifugal after 10 minutes, taking precipitate is dried in 70 ℃ of hot blasts, and product is a zeins.
Embodiment 2:
Is mixing in 2000 milliliters the glass container with maize yellow-powder 100 gram and 800 milliliter of 80% ethanol at volume, 6 minutes (microwave conditions: 915MHz of heating using microwave, 800W), centrifugal, get supernatant, add 800 milliliter of 1% sodium chloride and saltout, centrifugal after 10 minutes, taking precipitate is dried in 70 ℃ of hot blasts, and product is a zeins.
Embodiment 3:
Is mixing in 2000 milliliters the glass container with maize yellow-powder 100 gram and 800 milliliter of 90% ethanol at volume, 6 minutes (microwave conditions: 915MHz of heating using microwave, 800W), centrifugal, get supernatant, add 800 milliliter of 1% sodium chloride and saltout, centrifugal after 10 minutes, taking precipitate is dried in 70 ℃ of hot blasts, and product is a zeins.
Embodiment 4:
Take by weighing zeins 20 grams, with 160 milliliter of 80% ethanol dissolving, add 10 gram shitosans (shitosan is dissolved with 1% citric acid in elder generation), crosslinking agent cinnamic acid 0.5 gram, under 50 ℃ of constant temperatures, reacted while stirring 5 minutes, be heated to moisture 20% o'clock at 70 ℃-90 ℃, add 0.1 gram glyceryl stearate, 0.2 gram glycerine, 0.1 gram palm oil and an amount of auxiliary material, essence, in driving refining formula rubber mixing machine, mix, when moisture drops to 10%, by compression molding, section, put, be packaged to be the antibacterial chewing gum of biodegradation in order.
Embodiment 5:
Take by weighing zeins 20 grams, with 160 milliliter of 80% ethanol dissolving, add 5 gram shitosans (shitosan is dissolved with 1% citric acid in elder generation), crosslinking agent cinnamic acid 0.5 gram, under 50 ℃ of constant temperatures, reacted while stirring 5 minutes, be heated to moisture 20% o'clock at 70 ℃-90 ℃, add 0.1 gram glyceryl stearate, 0.2 gram glycerine, 0.1 gram palm oil and an amount of auxiliary material, essence, in driving refining formula rubber mixing machine, mix, when moisture drops to 10%, by compression molding, section, put, be packaged to be the antibacterial chewing gum of biodegradation in order.
Embodiment 6:
Take by weighing zeins 20 grams, with 160 milliliter of 80% ethanol dissolving, add 7.5 gram shitosans (shitosan is dissolved with 1% citric acid in elder generation), crosslinking agent cinnamic acid 0.5 gram, under 50 ℃ of constant temperatures, reacted while stirring 5 minutes, be heated to moisture 20% o'clock at 70 ℃-90 ℃, add 0.1 gram glyceryl stearate, 0.2 gram glycerine, 0.1 gram palm oil and an amount of auxiliary material, essence, in driving refining formula rubber mixing machine, mix, when moisture drops to 10%, by compression molding, section, put, be packaged to be the antibacterial chewing gum of biodegradation in order.
Embodiment 7:
Take by weighing zeins 20 grams, with 160 milliliter of 80% ethanol dissolving, add 7.5 gram shitosans (shitosan is dissolved with 1% citric acid in elder generation), crosslinking agent glutaraldehyde 0.2 gram, under 50 ℃ of constant temperatures, reacted while stirring 5 minutes, be heated to moisture 20% o'clock at 70 ℃-90 ℃, add 0.1 gram glyceryl stearate, 0.2 gram glycerine, 0.1 gram palm oil and an amount of auxiliary material, essence, in driving refining formula rubber mixing machine, mix, when moisture drops to 10%, by compression molding, section, put, be packaged to be the antibacterial chewing gum of biodegradation in order.
Embodiment 8:
Take by weighing zeins 20 grams, with 160 milliliter of 80% ethanol dissolving, add 7.5 gram shitosans (shitosan is dissolved with 1% citric acid in elder generation), crosslinking agent glutaraldehyde 0.5 gram, under 50 ℃ of constant temperatures, reacted while stirring 5 minutes, be heated to moisture 20% o'clock at 70 ℃-90 ℃, add 0.1 gram glyceryl stearate, 0.2 gram glycerine, 0.1 gram palm oil and an amount of auxiliary material, essence, in driving refining formula rubber mixing machine, mix, when moisture drops to 10%, by compression molding, section, put, be packaged to be the antibacterial chewing gum of biodegradation in order.
Embodiment 9:
Take by weighing zeins 20 grams, with 160 milliliter of 80% ethanol dissolving, add 7.5 gram shitosans (shitosan is dissolved with 1% citric acid in elder generation), crosslinking agent glutaraldehyde 0.9 gram, under 50 ℃ of constant temperatures, reacted while stirring 5 minutes, be heated to moisture 20% o'clock at 70 ℃-90 ℃, add 0.1 gram glyceryl stearate, 0.2 gram glycerine, 0.1 gram palm oil and an amount of auxiliary material, essence, in driving refining formula rubber mixing machine, mix, when moisture drops to 10%, by compression molding, section, put, be packaged to be the antibacterial chewing gum of biodegradation in order.
Embodiment 7:
Take by weighing zeins 20 grams, with 160 milliliter of 80% ethanol dissolving, add 7.5 gram shitosans (shitosan is dissolved with 1% citric acid in elder generation), crosslinking agent glutaraldehyde 0.5 gram, under 50 ℃ of constant temperatures, reacted while stirring 5 minutes, be heated to moisture 20% o'clock at 70 ℃-90 ℃, add 0.1 gram glyceryl stearate, 0.2 gram glycerine, 0.1 gram palm oil and an amount of auxiliary material, essence, in driving refining formula rubber mixing machine, mix, when moisture drops to 10%, by compression molding, section, put, be packaged to be the antibacterial chewing gum of biodegradation in order.
Claims (7)
1, a kind of production method of biodegradable chewing gum, with corn processing fent maize yellow-powder is raw material, add the alcohol extract alcohol soluble protein and produce matrix with it, it is characterized in that, in maize yellow-powder, add 70%-90% ethanol, carry out microwave treatment then immediately, obtain being used to produce chewing gum base raw material zeins, make shitosan-alcohol soluble protein chewing gum base through shitosan+crosslinking agent modification, in improved matrix, add sweetener, edibility essence and pigment and make chewing gum with biodegradation character and bacteria resistance function.
2, the method for claim 1 is characterized in that, the processing step that extracts zeins comprises:
1) by weight/volume by maize yellow-powder and ethanol is 1: 8-1: 14 to raw material adding ethanol;
2) be that 2450MHz or 915MHz, power are 800-2000 watt microwave with the bloom frequency of step 1), handled 1-6 minute;
3) with step 2) mixture centrifugal, obtain supernatant;
4) supernatant of step 3) is saltoutd with 1% sodium chloride, the centrifugal sediment that obtains with described sediment oven dry, obtains zeins.
3, method as claimed in claim 1 or 2 is characterized in that, earlier the alcoholic solution with zeins mixes with the citric acid solution of shitosan, makes shitosan and zeins crosslinked with crosslinking agent then, makes it become the modified corn alcohol soluble protein.
4, method as claimed in claim 1 or 2 is characterized in that, the usage ratio of zeins and shitosan is 2: 1-4: 1
5, method as claimed in claim 1 or 2 is characterized in that described crosslinking agent is a food grade products, and described crosslinking agent is selected from tannic acid, polyhydric phenols, glutamic acid, L-Lysine mono Hydrochloride, glutaraldehyde, cinnamic acid a kind of or mixture wherein.
6, the method for claim 1 is characterized in that crosslinking agent adds by the 1-4% of zeins consumption.
7, method as claimed in claim 5 is characterized in that the crosslinking agent that adopts is glutaraldehyde or cinnamic acid.