CN1460564A - 负压实型铸造用涂料 - Google Patents

负压实型铸造用涂料 Download PDF

Info

Publication number
CN1460564A
CN1460564A CN 03134231 CN03134231A CN1460564A CN 1460564 A CN1460564 A CN 1460564A CN 03134231 CN03134231 CN 03134231 CN 03134231 A CN03134231 A CN 03134231A CN 1460564 A CN1460564 A CN 1460564A
Authority
CN
China
Prior art keywords
coating
agent
acetone
order
key material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 03134231
Other languages
English (en)
Other versions
CN1209210C (zh
Inventor
王恩泽
邢建东
高义民
鲍崇高
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Xian Jiaotong University
Original Assignee
Xian Jiaotong University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Xian Jiaotong University filed Critical Xian Jiaotong University
Priority to CN 03134231 priority Critical patent/CN1209210C/zh
Publication of CN1460564A publication Critical patent/CN1460564A/zh
Application granted granted Critical
Publication of CN1209210C publication Critical patent/CN1209210C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明公开了一种负压实型铸造用涂料，包括：骨干材料、粘结剂、溶剂、湿润剂和发泡剂混合构成；其特征是，骨干材料为：320目锆英粉或320目铝矾土或320目石墨；粘结剂为：磷酸钠或水玻璃或聚乙烯醇缩甲醛及其结合；溶剂为：水或乙醇；湿润剂为：丙酮；发泡剂为：烷基磺酸钠；涂料重量配比为：骨干材料70％－80％，粘结剂4％－8％，湿润剂0.8％－1.2％，发泡剂：1.4％－2.0％，其余为溶剂。本发明的负压实型铸造用涂料具有与泡沫塑料湿润性好，附着力强，高温强度高及透气性好等特点，为负压实型铸造新工艺的成功使用奠定了基础。

Description

负压实型铸造用涂料
一、所属技术领域
本发明属于铸造使用的一种材料，涉及一种负压实型铸造用涂料。
二、背景技术
在普通的砂型铸造过程中，所使用的涂料有许多，通常涂料是刷在铸型的表面，以提高铸件的表面光洁度、减少粘砂夹砂等铸造缺陷，在这样的情况下，涂料是直接刷在粗燥的型砂表面，不存在涂料与铸型间附着力的问题；也不存在有大量的气体需要通过涂料排除去的问题；在涂料背后有坚实的铸型，也不要求涂料具有高的高温强度。而负压实型铸造是一种新的特种铸造工艺，其基本过程是在与所需工件形状相同的泡沫塑料上刷上涂料烘干后，埋在无任何粘结剂的松散干沙中，在负压状态下浇铸获得铸件的一种方法，在浇注前是没有空的型腔的，而是靠金属液的高温使泡末塑料汽化而形成型腔，汽化后会有大量的气体通过涂料排除，因此要求涂料要有非常好的透气性；此外常规涂料与泡沫塑料的湿润性较差，涂料厚度不易均匀，且与泡沫塑料的附着力差，涂料干后容易块状脱落，这是负压实型铸造对涂料另一特殊的要求；还有，负压实型铸造涂料背后是无任何粘结剂的干砂，若涂料高温强度太低，就会塌箱。因此，涂料是否具有透气性好、与泡沫塑料湿润性好、高温强度高的特点，就决定了该工件的成功与否。
三、发明内容
本发明的目的在于，提供一种负压实型铸造用涂料，发明的基本内容为：通过在涂料中加入湿润剂，提高涂料与泡沫塑料之间的附着力；通过在涂料中加入发泡剂，提高涂料的透气性；通过在涂料中加入无机高温粘结剂，以提高涂料的高温强度。
实现上述发明目的的技术解决方案是，该涂料包括：骨干材料、粘结剂、溶剂、湿润剂、发泡剂构成；
其骨干材料为：320目锆英粉或320目铝矾土或320目石墨；
粘结剂为：磷酸钠或水玻璃或聚乙烯醇缩甲醛及其结合；
溶剂为：水或乙醇；
湿润剂为：丙酮；
发泡剂为：烷基磺酸钠；
涂料重量配比为：骨干材料70％-80％，粘结剂4％-8％，湿润剂0.8％-1.2％，发泡剂：1.4％-2.0％，其余为溶剂。
本发明的负压实型铸造用涂料具有与泡沫塑料湿润性好，附着力强，高温强度高及透气性好等特点，为负压实型铸造新工艺的成功使用奠定了基础。
四、具体实施方式
以下结合发明人依照本发明的技术方案给出的实施例对本发明作进一步的详细说明。
实施例1：
骨干材料取320目锆英粉80％，粘接剂为水玻璃4％和聚乙烯醇缩甲醛3％，丙酮0.8％，烷基磺酸钠1.6％，其余为乙醇或水。
实施例2：
骨干材料取320目铝矾土76％，粘接剂为磷酸钠4％和聚乙烯醇缩甲醛3％，丙酮0.8％，烷基磺酸钠1.6％，其余为水。
实施例3：
骨干材料取320目石墨74％，粘接剂为水玻璃4％和聚乙烯醇缩甲醛3％，丙酮1.0％，烷基磺酸钠1.8％，其余为乙醇或水。
上述实施例可以进行多种组合，只要是在本发明的上述范围内，都可以制备出负压实型铸造用涂料。

Claims (4)

1.一种负压实型铸造用涂料，其特征在于：按以下配方制备：
骨干材料：320目锆英粉或320目铝矾土或320目石墨
粘结剂：磷酸钠或水玻璃或聚乙烯醇缩甲醛及其结合
湿润剂：丙酮
发泡剂：烷基磺酸钠
溶剂：水或乙醇
涂料重量配比为：骨干材料70％-80％，粘结剂4％-8％，湿润剂0.8％-1.2％，发泡剂：1.4％-2.0％，其余为溶剂。
2.如权利要求1所述的负压实型铸造用涂料，其特征在于：按以下配方制备：骨干材料取320目锆英粉80％，粘接剂为水玻璃4％和聚乙烯醇缩甲醛3％，丙酮0.8％，烷基磺酸钠1.6％，其余为乙醇或水。
3.如权利要求1所述的负压实型铸造用涂料，其特征在于：骨干材料取320目铝矾土76％，粘接剂为磷酸钠4％和聚乙烯醇缩甲醛3％，丙酮0.8％，烷基磺酸钠1.6％，其余为水。
4.如权利要求1所述的负压实型铸造用涂料，其特征在于：骨干材料取320目石墨74％，粘接剂为水玻璃4％和聚乙烯醇缩甲醛3％，丙酮1.0％，烷基磺酸钠1.8％，其余为乙醇或水。
CN 03134231 2003-06-02 2003-06-02 负压实型铸造用涂料 Expired - Fee Related CN1209210C (zh)