CN1458367A - Decorative board and its producing method - Google Patents
Decorative board and its producing method Download PDFInfo
- Publication number
- CN1458367A CN1458367A CN 02117767 CN02117767A CN1458367A CN 1458367 A CN1458367 A CN 1458367A CN 02117767 CN02117767 CN 02117767 CN 02117767 A CN02117767 A CN 02117767A CN 1458367 A CN1458367 A CN 1458367A
- Authority
- CN
- China
- Prior art keywords
- decorative panel
- particle
- panel according
- coating
- sheet material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The decorative board includes base board, surface paint layer and granular layer. During its production, the paint layer is first painted to the base board, the grains are thrown onto the paint layer, paint is then painted to cover the granular layer and the other layer of grains are thrown, and the decorative board is finally dried. The decorative board thus produced is beautiful, low in cost and moistureproof, and has the function of adsorbing harmful gas.
Description
Technical field:
The present invention relates to a kind of decorative panel and manufacture method thereof.
Background technology:
Sheet material is as a kind of widely used building and ornament materials, generally adopt gypsum plank, mineral wool board, shaving board etc. in the prior art, these decorative panel moisture resistances are poor, the formaldehyde that dalle discharged in the time of can not being adsorbed on room decorating, pernicious gas such as stupid, these gases have a strong impact on health, even carcinogenic.
Summary of the invention:
The object of the present invention is to provide a kind of decorative panel and manufacture method thereof.
This decorative panel comprises the sheet material base material and covers dope layer and the stratum granulosum that is coated with at the sheet material substrate surface.
Described sheet material base material for dull and stereotyped, fall step or hidden insert type ceiling, the hidden insert type ceiling has two plate faces up and down, at least be provided with asymmetric dark insert edge in the relative pair of end portions of ceiling, a side wherein is provided with the last scrap (bridge) step that cooperates with T type keel, opposite side is provided with the dark insert edge of asymmetric grooved, the dark insert edge of described asymmetric grooved comprises a last scrap (bridge) step that cooperates with T type keel and is used to hide the following scrap (bridge) step of T type keel that formation one can embed the notch of T type keel one flank between last scrap (bridge) step and following scrap (bridge) step.
During manufacturing, coating covered be coated on the sheet material base material, again particle is shed on dope layer, coating is covered be applied on the stratum granulosum then, again particle is shed on dope layer dry then the processing.
Described sheet material base material is a kind of in sheet asbestos, mineral wool board, shaving board, the fiberboard.
Coating is covered when being applied on the sheet material base material, cover the mode of being coated with and be a kind of during roller coat, spraying and bullet are coated with.
Described coating is a kind of in acrylic coating, polyethylene coating, polyurethane coating, the epoxy type coating.
Described particle is a kind of in attapulgite clay, kieselguhr, swell soil, zeolite, perlite, the marble powder.The surface of attapulgite clay, kieselguhr, bentonite clay particle is a loose structure, have adsorptivity, can be good at adsorbing the pernicious gas that produces in building, the decoration process, and loose structure helps to strengthen the adhesion stress with dope layer, make stratum granulosum firm, difficult drop-off.Zeolite, perlite, the smooth surface of marble powder particle, quality are hard, its smooth surface has good reflex, can make the decorative panel surface produce the visual effect of flicker, excellent decoration is arranged, hard particle makes decorative panel have coarse feel simultaneously, and is different with common sheet material sense of touch.
Described particle be 10 orders to 50 purpose fine powders, this particle should use through calcining back.The calcining heat of particle is between 800-1300 ℃, and calcination time 2 to 5 hours is so that the volatilization of the volatile material in the particle makes pellet hardness increase simultaneously.
The produced decorative panel good decorative property of this method, intensity height have the effect of adsorbing pernicious gas, and manufacture method is simple, with low cost simultaneously.
Description of drawings:
Fig. 1 is the structural representation of decorative panel cross section, the 1st, and stratum granulosum, the 2nd, dope layer, the 3rd, sheet material base material.
Fig. 2 is that the sheet material base material is the schematic perspective view of dark plate.
The specific embodiment:
The present invention will be further described below in conjunction with accompanying drawing.
Described decorative panel comprises sheet material base material 3, dope layer 2, stratum granulosum 1.
Described sheet material base material for dull and stereotyped, fall step or hidden insert type ceiling, the hidden insert type ceiling has two plate faces 4 up and down, at least be provided with asymmetric dark insert edge 5 in the relative pair of end portions of ceiling, a side wherein is provided with the last scrap (bridge) step 6 that cooperates with T type keel, opposite side is provided with the dark insert edge 7 of asymmetric grooved, the dark insert edge 7 of described asymmetric grooved comprises a last scrap (bridge) step that cooperates with T type keel 6 and is used to hide the following scrap (bridge) step 8 of T type keel that formation one can embed the notch 9 of T type keel one flank between last scrap (bridge) step 6 and following scrap (bridge) step 8.
Embodiment 1:
Attapulgite clay is ground into 25 purpose particles, calcined 3 hours down at 1000 ℃; With sheet asbestos as the sheet material base material, the acrylic coating roller coat on the sheet material base material, is evenly shed one deck attapulgite clay particle on dope layer, again acrylic coating is sprayed on the stratum granulosum, on dope layer, evenly shed one deck attapulgite clay particle again, dry then the processing.
Embodiment 2:
Diatomite in powder is broken into 20 purpose particles, calcined 2 hours down at 1100 ℃; With sheet asbestos as the sheet material base material, the acrylic coating roller coat on the sheet material base material, is evenly shed one deck diatomite particle on dope layer, acrylic coating is sprayed on the diatomite particle layer again, on dope layer, evenly shed one deck diatomite particle again, dry then the processing.
Embodiment 3:
Bentonite in powder is broken into 25 purpose particles, calcined 4 hours down at 950 ℃; With shaving board as the sheet material base material, the acrylic coating roller coat on the sheet material base material, is evenly shed one deck bentonite clay particle on dope layer, again the acrylic coating bullet is coated on the bentonite clay particle layer, on dope layer, evenly shed one deck bentonite clay particle again, dry then the processing.
Embodiment 4:
Zeolite powder is broken into 50 purpose fine powders, calcined 2 hours down at 1300 ℃; With fiberboard as the sheet material base material, the acrylic coating roller coat on the sheet material base material, is evenly shed one deck zeolite granular fine powder on dope layer, acrylic coating is sprayed on the zeolite granular layer again, on dope layer, evenly shed one deck zeolite granular fine powder again, dry then the processing.
Embodiment 5:
Perlite particle is ground into 25 purpose fine powders, calcined 4.5 hours down at 1200 ℃; With mineral wool board as the sheet material base material, the acrylic coating roller coat on the sheet material base material, is evenly shed one deck perlite particle fine powder on dope layer, acrylic coating is sprayed on the perlite particle layer again, on dope layer, evenly shed one deck perlite particle fine powder again, dry then the processing.
Claims (9)
1. decorative panel is characterized in that: this decorative panel comprises the sheet material base material and covers dope layer and the stratum granulosum that is coated with at the sheet material substrate surface.
2. decorative panel according to claim 1, it is characterized in that: described sheet material base material is for dull and stereotyped, fall step or hidden insert type ceiling, the hidden insert type ceiling has two plate faces up and down, at least be provided with asymmetric dark insert edge in the relative pair of end portions of ceiling, a side wherein is provided with the last scrap (bridge) step that cooperates with T type keel, opposite side is provided with the dark insert edge of asymmetric grooved, the dark insert edge of described asymmetric grooved comprises a last scrap (bridge) step that cooperates with T type keel and is used to hide the following scrap (bridge) step of T type keel that formation one can embed the notch of T type keel one flank between last scrap (bridge) step and following scrap (bridge) step.
3. decorative panel according to claim 1 is characterized in that: described sheet material base material is a kind of in sheet asbestos, mineral wool board, shaving board, the fiberboard.
4. decorative panel according to claim 1 is characterized in that: described coating is a kind of in acrylic coating, polyethylene coating, polyurethane coating, the epoxy type coating.
5. decorative panel according to claim 1 is characterized in that: described particle is a kind of in attapulgite clay, kieselguhr, swell soil, zeolite, perlite, the marble powder.
6. the particle of decorative panel according to claim 5, it is characterized in that: the surface of attapulgite clay, kieselguhr, bentonite clay particle is a loose structure, has adsorptivity, and loose structure helps to strengthen the adhesion stress with dope layer.
7. the particle of decorative panel according to claim 5 is characterized in that: zeolite, perlite, the smooth surface of marble powder particle, quality are hard.
8. the manufacture method of decorative panel according to claim 1 is characterized in that: during manufacturing, coating covered be coated on the sheet material base material, again particle is shed on dope layer, then coating is covered and be applied on the stratum granulosum, again particle is shed on dope layer, dry then the processing.
9. the manufacture method of decorative panel according to claim 8 is characterized in that: described particle at 10 orders between 50 orders.