CN1456535A - Process for preparing porous ceramic by water-based gel injection moulding method - Google Patents
Process for preparing porous ceramic by water-based gel injection moulding method Download PDFInfo
- Publication number
- CN1456535A CN1456535A CN 03128066 CN03128066A CN1456535A CN 1456535 A CN1456535 A CN 1456535A CN 03128066 CN03128066 CN 03128066 CN 03128066 A CN03128066 A CN 03128066A CN 1456535 A CN1456535 A CN 1456535A
- Authority
- CN
- China
- Prior art keywords
- water
- technology
- pore
- porous ceramics
- gel casting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
An injection moulding process for preparing porous ceramics from water-base gel includes such steps as preparing the stable suspension from organic monomer, cross-linking agent, trigger, disperser and ceramic powder, proportionally adding surface treated pore-forming agent while applying pressure, proportionally adding catalyst, slowly heating to 60-80 deg.C holding the temp for at least 30 min for solidifying, demoulding, drying and sintering.
Description
Technical field
The present invention relates to a kind of method for preparing porous ceramics, relate to a kind of combining specifically and prepare the method for porous bio-ceramic with water-base gel casting method and pore former method.
Background technology
Porous bio-ceramic is because of its excellent biological compatibility and help the structural performance that osseous tissue is grown into, and widely applies in clinical orthopaedics.Recently, development along with bone tissue engineer, require porous bio-ceramic not only biodegradation character will be arranged, three-dimensional communication pore as much as possible and high as far as possible void content also to be arranged, and need effectively control pore structure, specific surface area, apparent porosity and the intensity of porous ceramic film material.At present, the method for preparing porous ceramics has the pore-forming material of adding method, formed in situ method, foam impregnation method, sol-gel method etc.Wherein, add the pore-forming material method, owing to can change kind, add-on and the pore-forming material particle diameter of pore-forming material arbitrarily, thereby the porous ceramics that can make various different apertures and distribution satisfies different service requirementss, and cost is lower.Traditional forming process of ceramics technology such as dry-pressing formed, isostatic cool pressing, slip casting, extrude, though moulding processs such as curtain coating, injection moulding and injection, press filtration have obtained certain achievement by continuous improvement and raising, effect is unsatisfactory aspect the apparent porosity that improves pottery.Gel casting forming (Aquous Gelcasting) is a kind of new ceramic wet moulding technology of preparing that occurs the early 1990s in last century, this technology is compared with traditional wet therapy forming process, outstanding advantage such as simple with equipment, that the molding blank component is even, density is even, defective is few, do not need degreasing, not yielding and cracking, easy-formation complicated shape part, part near-net-shape and practicality are very strong is subjected to the very big attention of domestic and international academia and industry member.
The gel casting forming technology is the traditional grouting process and the perfect adaptation of the high polymerization theory of organic chemistry, and it has developed traditional slip-casting shaping process by introducing a kind of new typing mechanism.Its ultimate principle is that (in shearing rate is 20s in high solid loading (volume fraction is greater than 50%), low viscosity
-1The time viscosity less than 600MPa.s) ceramic size in, the organic monomer that mixes lower concentration (massfraction is less than 10%) is (as acrylamide AM, Methacrylamide MAM, vinyl pyrrole ketone NVP, methyl polyethyleneglycol methacrylic ester MPEGMA or the like) and linking agent (as methylene-bisacrylamide MBAM), when adding a spot of initiator (as ammonium persulphate) and catalyzer (as N, N, N, the N-Tetramethyl Ethylene Diamine) and the casting after, home position polymerization reaction takes place in the organic monomer in the slurry under certain temperature condition, form firm tridimensional network, thereby make the moulding of suspensoid in-situ solidifying, obtain evenly, high strength, the ceramic body of accurate dead size.Carry out the demoulding, drying, removal organism, sintering then, can make required ceramic part.Gel casting forming is compared with injection moulding or injection molding, and main difference is that organic polymer or the wax as binding agent is replaced by organic monomer in back two kinds of technologies, utilizes the organic monomer in-situ polymerization to realize then.
By a large amount of literature searches, find to use gel casting forming technology and pore-forming material method in conjunction with the report for preparing porous bio-ceramic.
Summary of the invention
The water-base gel casting legal system that the object of the present invention is to provide a kind of apparent porosity that can improve porous ceramics greatly and its pore structure of may command and have a suitable physical strength is equipped with the technology of porous ceramics.
To achieve these goals, technical scheme of the present invention is: the water-base gel casting legal system is equipped with the technology of porous ceramics, it is characterized in that realizing as follows:
(1) prepares the steady suspension that contains organic monomer, linking agent, initiator, dispersion agent and ceramic powder; (2) adding volume fraction in above-mentioned slurry is the surface treated pore-forming materials of 50～80% (with respect to above-mentioned suspension vols), and pressurization is in contact with one another pore-forming material and can be uniformly distributed in the suspension; (3) to add massfraction be the catalyzer of 0.1～0.3% (with respect to the quality of ceramic powder) and slowly be warmed up to 60～80 ℃ and keep constant temperature more than 30 minutes, promptly obtains the solidified base substrate; (4), and get final product at 850～900 ℃ of sintering with the base substrate demoulding, drying.
Described dispersion agent is anion surfactants such as ammonium polyacrylate, ammonium polymethacrylate, Xylo-Mucine.
Described surface-treated pore-forming material is for adding organic solvent, as dehydrated alcohol; Pore-forming material is polystyrene foam microballoon, polyethylene microballoon, polyaminoester microball etc.
The described pressure that is pressurised into about 0.4MPa.
Described organic monomer is acrylamide AM, Methacrylamide MAM, vinyl pyrrole ketone NVP, methyl polyethyleneglycol methacrylic ester MPEGMA or the like; Described linking agent is methylene-bisacrylamide MBAM; Described initiator is an ammonium persulphate; Described catalyzer is N, N, N, N-Tetramethyl Ethylene Diamine.
Innovative point of the present invention is with a kind of new method---water-base gel casting technology and pore-forming material method combine and prepare porous bio-ceramic, on this basis by selecting for use suitable dispersion agent (as ammonium polymethacrylate PMAA-NH
4) solved stability, the flowability problem of biological ceramics powder in water of high volume content, and make organic pore-forming agents can in water base suspension, disperse fully and evenly suspend by surface-active-treatment.Utilize the loss of viscous liquid to pressure transmission, cause the inhomogeneous pressurized between pressure drop on the direction of exerting pressure and foam ball, control the three-dimensional structure of porous ceramics with the pressure about 0.4MPa, and can change the size of the communication aperture between the spherical hole by regulating the pressure size, formed a kind of more complete porous bio-ceramic new preparation process.
The present invention combines gel casting forming technology and pore-forming material method, improves the apparent porosity of porous ceramics greatly, and its pore structure of may command and have suitable physical strength.
Description of drawings
Fig. 1 is the view of organic foam small-sphere of the present invention in mould
Wherein 1-organic foam small-sphere, 2-ceramic size, 3-mould, 4-add 0.4Mpa pressure.
Embodiment
The water-base gel casting legal system is equipped with the technology of porous ceramics, at first according to the performance requriements for the treatment of producing porous ceramic, select the ceramic powder of preparation appropriate particle size, select suitable organic monomer system and dispersion medium, in conjunction with its suspension characteristic in the aqueous solution, prepare high solid loading, low viscous ceramic size.The organic monomer system that can be used for the hydrogel injection molding and forming technology should meet the following conditions: (1) monomer and linking agent must be water miscible (the former can molten massfraction be 20% at least, and the latter is 2% at least).If their solubleness in water is low excessively, organic monomer just is not solution polymerization but the solution precipitation polymerization so just can not mold the uniform base substrate of density, and can influence the intensity of base substrate.(2) gel of the dilute solution of monomer and linking agent formation should have certain intensity (ultimate compression strength is not less than 100Pa), so just can play the effect of custom-molded in place, and can guarantee enough demoulding strengths.(3) do not influence the flowability of slurry, if monomer and linking agent can reduce the flowability of slurry, so high solid phase, low viscous ceramic size just are difficult to preparation.
Secondly, by process for treating surface (as adding organic solvent, as dehydrated alcohol etc.) change the hydrophilicity and the density of pore-forming material (organic foam small-sphere) and make it be evenly distributed in the above-mentioned ceramic size and do not produce floating and layering, again prepared slurry is injected satisfactory mould, and it is applied pressure about 0.4MPa, gang mould tool integral body is heated to 60～80 ℃ and keep constant temperature more than 30 minutes then, make the organic monomer generation home position polymerization reaction in the ceramic size, thereby make ceramic powder and organic pore-forming agents original position curing molding in mould.Through the demoulding, drying, under certain temperature increasing schedule, burn organism (pore-forming material, polymkeric substance) and the sintering that loses in the base substrate again, thereby obtain the porous ceramics of high apparent porosity.
Key problem in technology of the present invention:
At first, preparation high solid loading, low viscous ceramic size, this is the key that can the present invention successful.Under the desired viscosity of gel injection molding and forming technology, the principal element that influences solid load is the colloid property of powder in medium.Polymolecularity, the high stability of particle in medium is the precondition of preparation high solid loading, low viscosity suspensoid, and its key is to select suitable dispersion agent.
Next is the surface treatment of pore-forming material.Because the pore former material of selecting for use generally is an organic foam small-sphere, the general oleophylic of this material and not hydrophilic, and ceramic size is the water base suspension of high solid loading, so must carry out certain surface modification to organic foam small-sphere, makes ceramic size can inject space between the filling ball smoothly.In addition, biological tissue grows into because biologic bracket material requires prepared solid support material must possess the hole connectivity structure, therefore, be necessary to make spherical pore-forming material to become surface contact state from a contact condition, make between ball and the ball and form communicating aperture, so must make the pore-forming material in the mould bear pressure and closely contact by certain external force.The state of organic foam small-sphere in mould as shown in Figure 1.Example:
Adopt water-base gel casting in conjunction with the preparation of pore-forming material method success β-TCP porous ceramics, the apparent porosity of pottery reaches more than 80%, intensity can reach 3～5MPa.Concrete technology is as follows:
1. the preparation of powder:
(1) β-TCP ceramic powder adopts solid reaction process synthetic, and this powder ball milling 24 hours, it is stand-by that 40 mesh sieves are crossed in dry back.
(2) high-temperature agglomerant is through fusion-quenching, grind into powder again.
2. the preparation of the β of low viscosity, high solid loading-TCP slurry:
Select for use distilled water as dispersion medium, dispersion agent adopts ammonium polyacrylate (PMAA-NH
4), 's 10: 1: 50 mixed dissolving with organic monomer (AM), linking agent (MBAM) and distilled water by mass ratio, again β-TCP ceramic powder (β-TCP powder with high-temperature agglomerant by 4: 1 blended mixtures of mass ratio) is mixed with above-mentioned solution, add back in the line with rubber ball grinder, the mixing of an amount of dispersion agent and initiator solution (wt% is 10%) again and make slurry, adopt HCl and NH
4OH solution is regulated pH value of slurry, finally prepares satisfactory high solid loading, low viscous suspension, and β-TCP powder volume fraction can reach about 60%.Monomer is acrylamide (AM) in body series, and linking agent is bisacrylamide (MBAM), and ammonium persulphate is as initiator, and Tetramethyl Ethylene Diamine is as catalyzer.
3. the surface modification of pore-forming material and adding:
The pore former material of selecting for use is the polystyrene foam microballoon, this polymkeric substance polymer oleophylic and not hydrophilic, so must carry out surface modification to it, make ceramic size can with foam microballoon uniform mixing.The present invention adopts the soaked in absolute ethyl alcohol polystyrene, and ethanol is entered in the granules of polystyrene, makes it hydrophilic purpose thereby reach surface modification, and has improved the density of foam microballoon.The polystyrene microsphere of modification is joined in the above suspension for preparing again, fully stir and make it uniform mixing, the external force of then slurry being poured into mould and applying about 0.4MPa is out of shape the foam microballoon a little.
4, handle:
After above-mentioned steps was finished, gang mould tool integral body was heated to 60～80 ℃ and keep constant temperature more than 30 minutes, makes the organic monomer generation home position polymerization reaction in the ceramic size, thereby makes ceramic powder and organic pore-forming agents original position curing molding in mould.Be dried to water ratio with the base substrate demoulding and about 50 ℃ less than 5% (quality percentage composition), then the exsiccant base substrate at 850～900 ℃ of sintering, be incubated 0.5～1 hour, heat-up rate＜3 ℃/min, cooling rate＜2 ℃/min.
The result:
The performance test that the porous ceramics that makes is correlated with is found, the apparent porosity of pottery reaches more than 80%, and aperture overall dimension reaches the mm level, and intensity can reach 3～5MPa, be that the communicating aperture of 10～100 μ m connects with the aperture between the Kong Yukong, pore structure is three-dimensional communicating structure.
Claims (6)
1, the water-base gel casting legal system is equipped with the technology of porous ceramics, it is characterized in that realizing as follows: (1) prepares the more stable suspension that contains organic monomer, linking agent, initiator, dispersion agent and ceramic powder; (2) adding with respect to above-mentioned suspension vol mark in above-mentioned slurry is 50～80% surface treated pore-forming materials, and pressurization is in contact with one another pore-forming material and can be uniformly distributed in the suspension; (3) add with respect to the catalyzer of the massfraction 0.1～0.3% of ceramic powder and slowly be warmed up to 60～80 ℃ and keep constant temperature more than 30 minutes, promptly obtain the solidified base substrate; (4) with the base substrate demoulding, drying, and sintering gets final product.
2, water-base gel casting legal system according to claim 1 is equipped with the technology of porous ceramics, it is characterized in that described dispersion agent is ammonium polyacrylate or anion surfactants such as ammonium polymethacrylate or Xylo-Mucine.
3, water-base gel casting legal system according to claim 1 is equipped with the technology of porous ceramics, it is characterized in that described surface-treated pore-forming material is for adding organic solvent, as dehydrated alcohol; Pore-forming material is polystyrene foam microballoon, polyethylene microballoon, polyaminoester microball etc.
4, water-base gel casting legal system according to claim 1 is equipped with the technology of porous ceramics, it is characterized in that the pressure about the described 0.4MPa of being pressurised into.
5, water-base gel casting legal system according to claim 1 is equipped with the technology of porous ceramics, it is characterized in that described organic monomer is acrylamide AM or Methacrylamide MAM or vinyl pyrrole ketone NVP or methyl polyethyleneglycol methacrylic ester MPEGMA; Described linking agent is methylene-bisacrylamide MBAM; Described initiator is an ammonium persulphate; Described catalyzer is N, N, N, N-Tetramethyl Ethylene Diamine.
6, the water-base gel casting legal system is equipped with the technology of porous ceramics according to claim 1 or 5, it is characterized in that described organic monomer and linking agent must be water miscible, organic monomer can molten massfraction be 20% at least, and linking agent can molten massfraction be 2% at least.