CN1454764A - 边密度与芯密度一致的轻质墙板 - Google Patents

边密度与芯密度一致的轻质墙板 Download PDF

Info

Publication number
CN1454764A
CN1454764A CN 03137657 CN03137657A CN1454764A CN 1454764 A CN1454764 A CN 1454764A CN 03137657 CN03137657 CN 03137657 CN 03137657 A CN03137657 A CN 03137657A CN 1454764 A CN1454764 A CN 1454764A
Authority
CN
China
Prior art keywords
density
wallboard
dumpling
reamer
core
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 03137657
Other languages
English (en)
Other versions
CN1206088C (zh
Inventor
黎欧
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 03137657 priority Critical patent/CN1206088C/zh
Publication of CN1454764A publication Critical patent/CN1454764A/zh
Application granted granted Critical
Publication of CN1206088C publication Critical patent/CN1206088C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明公开了一种混凝土隔墙板，所述轻质墙板的边密度与芯密度基本一致，其密度范围在1.25g/cm3－1.35g/cm3之间。墙板的力学性能优异，使用效果好。

Description

边密度与芯密度一致的轻质墙板
技术领域
本发明涉及一种混凝土隔墙板。
背景技术
根据目前国内生产机制轻质状况调研和反馈信息，墙板质量普遍存在左右、上下密度不均衡，出现边松和易开裂现象。这就影响了作为新型墙材取代毁地、耗能、污染环境的粘土实心砖效果，更是严重影响了新型机制轻质墙板的推广应用。
目前国内成型机传动箱的输出齿轮轴多为一种形式，即每根输出轴转速相同，每根旋向(左旋或右旋)固定。
此种传动箱形式的成型机生产的轻质墙板，两边螺旋绞刀送料量不够而导致墙板两边密实度比中间小，在挤压振动成型过程中常常出现连续微细裂缝及棱角不齐，轻微受力后板坯裂缝处马上脱落暴露的主要问题有：
(1)机制轻质墙板的质量，比起其他新型墙体材料的优势大得多，各种物理力学性能指标可以达到建设部JG3063-1999最新标准的要求。但是，墙板的质量普遍存在墙板左右、上下密度不均衡，应用中经受不起考验。
(2)以主规格90板为例：1#铰刀存在主要问题，与转速一致的2#-6#铰刀螺杆内径、旋向搭配不合理，又要造成墙板面积占70％的中间部位的密度也不够均匀，个别铰刀上方的板坯由于供料不足会出现程度不同的疏松和麻面现象。
发明内容
本发明的目的在于研制一种边密度与芯密度一致的轻质墙板，通过铰刀变速及变径的成型机，增加了成型机两边螺旋饺刀的送料量，使全部螺旋饺刀在比较均匀一致的供料、挤料状态下运行，制成边密度与芯密度一致的轻质墙板。
实现本发明做了如下试验：
A组：成型机7根饺刀，叶片外径Φ78mm，螺杆内径均为Φ52mm投料拉制墙板。结果：凸棱一侧，即1#饺刀部位，无论采用什么轻集料砼配合比，由于供料不足，呈碎料状态，一律不能成型；凸棱一侧，即7#饺刀部位，虽勉强成型，但呈严重疏松状态，密度、强度甚低。
B组：1#、7#饺刀内径由Φ52mm缩至Φ42mm时，墙板两侧均成型，象一块可用的墙板，但两侧亦显疏松，1#饺刀部位即凸棱一侧比另一侧更疏松一些。
C组：当凸棱一侧，即1#饺刀提速后拉制的墙板(7#饺刀未提速)，本侧密度明显提高：上、侧两面平整、光滑、致密、外观甚佳，密度、强度优异。
三组试验结果分析
墙板两侧疏松，说明供料不足。而A组试验，1#-7#饺刀推料量在理论上应该是基本相等的。为什么拉板实践中1#饺刀部位的板坯根本不能成型，7#饺刀部位虽能成型又特疏松？除成型机两个边模有摩擦阻力而影响1#、7#饺刀送料量稍有不足外，更要分析该代饺刀送料与中间2#-6#每根饺刀送料所承担送料量的差别。理论计算和生产实践证明，墙板两侧“边松”的主要原因，是1#、7#饺刀承担的送料量大而又没有送出足够量物料造成的。
据计算：1#饺刀承担的送料量比2#-6#中间部分每根饺刀螺杆内径增大螺旋叶片导程空腔容料多，以增加单位时间内的推料量来解决。
提速理想方案：
2#-6#饺刀转速相等时，调整螺杆内径，相邻饺刀不同旋向，合理搭配如附图3所示。
各部位密度经检测，波动在1.259g-1.377g/cm3之间。密度基本均匀，比较理想。
解决墙板边缘部位疏松、密度过小的办法为：
原1#-7#饺刀的内径为52mm，现缩小1#、7#饺刀内径具体值，使1#饺刀内径为44mm，7#饺刀内径为47mm，通过扩大螺杆叶片和导程空腔之/容料空间，提高单位时间内的物料输送量，用切割2×2×2cm标准小试件或用阿基米德法检测试件体积。经计算，墙板边缘密度从＜1.000g/cm3提高到1.266g/cm3。比中间部位均衡密度1.309g/cm3仍小0.046g/cm3，即板边供料不足，尚缺3.510％。解决的办法为：在1#、7#饺刀缩小内径的同时，提高转速。
在导程、螺杆内径、螺纹外径一定的前提下，饺刀提速是有限度的，即从较低的转速起逐步提速，推料量逐步增加。当转速增至一定值后，随着转速的提高，推料量将开始下降。用变速电机做试验，将转速从150转/分逐步提高到250转/分寻找最佳转速时发现，对一般的轻砼物料，190-200转/分比较合适。所以，在设计中确定转动箱输出轴转速为196转/分。为了提高边刀的供料量，我们把1#饺刀转速适当提高，对拉制的墙板进行检测。墙板边缘密度从未提速前的1.250g/cm3提高到1.350g/cm3，与墙板中间部位密度基本一致并略偏高，犹如“物件镶边”，使墙板的整体性有所改善，从而达到了成型机技术性能改进的实验目的。
成型机各绞刀送料量之比。以90型墙板为例：
绞刀序号 1 2 3 4 5 6 7
绞刀对应墙板截面积之比 1.402 1 1 1 1 1 1.243
(板宽595MM，厚90MM，孔径59MM)
要保证成型机制出的墙材各部位(尤其是两边槽部位)均匀一致、密度一样，必须对成型机的核心部件绞刀进行周密设计。使其能够保证墙板成形过程中各部位的物料供应一致。使1号7号绞刀缩径、提速、搭配合理旋向，采用双头螺纹等工艺。墙材成型机使用此型绞刀后，制出的轻质墙材，经检验，其各部位的密度均保证在墙材国家标准范围以内，实现了墙板各部位密度均匀一致，墙板的力学性能优异，使用效果好。下表即为本发明所述墙材成型机所用绞刀的主要参数：
  绞刀序号     1     2    3    4    5    6    7
绞刀送料螺旋外径(mm) 75 75 75 75 75 75 75
绞刀送料螺旋底径(mm) 45 52 52 52 52 52 50
绞刀抽空管直径(mm)     59     59   59    59    59    59    59
绞刀转速r/min 235 196 196 196 196 196 235
绞刀旋向    顺    逆   顺    逆    逆    顺    逆
本发明所述轻质墙板的边密度与芯密度基本一致，其密度范围在1.25g/cm3-1.35g/cm3之间。
附图说明
附图1为本发明所述轻质墙板的剖面示意图
附图2为生产本发明所述轻质墙板的成型机转动箱及绞刀示意图
附图3为附图2的A向铰刀旋向示意图
具体实施
生产所述墙板的配方：
材料名称 材料规格        配方代号(0217) 每平方米消耗量
  配比值   实际用量
   水泥(kg)     PO32.5     100     23
  粉煤灰(kg)     III级灰     80    18.4
  煤渣(kg)    电厂尾灰     60    13.8
  珍珠岩(L)   75-100kg/m3     160    36.8
    砂(kg)     4-8mm     60    13.8
  废料(kg)     中砂     60    13.8
   外加剂   过10mm筛     30     6.9
   水灰比     0.38
  搅拌时间         150～200min
备注 1.陶粒必须先充分预湿，应浸泡1小时左右。2.保证搅拌时间、控制好水灰比。3.该配比所用原材料必须符合工艺参数中要求。4.该配方从2003年5月17日实施。5.必须严格按配比执行准确计量
制成板材的性能指标如下：
                           干体积密度检测表
  样品名称     SDY混凝土空心墙板       配方代号     0217
  检测时间     2003年3月15日      受检板批号     0082
检测截面序号                        干体积密度检测结果(g/cm3)
  板凸槽上部   板凸槽下部  板面上部 板面下部   板凹槽上部   板凹槽下部
    1    1.26     1.24     1.26     1.24     1.26     1.24
    2    1.27     1.25     1.27     1.25     1.27     1.24
    3    1.26     1.26     1.25     1.23     1.25     1.24
    4    1.27     1.25     1.27     1.24     1.27     1.23
    5    1.24     1.24     1.28     1.24     1.24     1.24
    6    1.25     1.24     1.24     1.23     1.24     1.23
    7    1.25     1.25     1.26     1.22     1.26     1.22
    8    1.26     1.26     1.25     1.24     1.25     1.24
    9    1.27     1.23     1.27     1.25     1.27     1.24
    10     1.28     1.26     1.28     1.24     1.28     1.24
    11     1.25     1.24     1.25     1.25     1.25     1.25
    12     1.26     1.25     1.24     1.24     1.26     1.24
    13     1.24     1.23     1.25     1.23     1.23     1.23
    14     1.26     1.25     1.26     1.26     1.26     1.26
    15     1.27     1.26     1.27     1.23     1.28     1.26
    16     1.24     1.24     1.26     1.24     1.25     1.24
    17     1.28     1.26     1.28     1.26     1.28     1.25
    18     1.25     1.25     1.25     1.25     1.24     1.24
    19     1.26     1.25     1.25     1.24     1.28     1.23
    20     1.25     1.24     1.25     1.23     1.24     1.23
  平均值                                  1.25
  最大偏差                                  0.07
    结论              墙板的各个点的干体积密度在允许范围以内。

Claims (1)

1.一种边密度与芯密度一致的轻质墙板，其特征在于：所述轻质墙板的边密度与芯密度基本一致，其密度范围在1.25g/cm3-1.35g/cm3之间。
CN 03137657 2003-06-19 2003-06-19 边密度与芯密度一致的轻质墙板 Expired - Fee Related CN1206088C (zh)