CN1442510A - Non-cyanide gold imitation electro plating method of flowers and plants - Google Patents
Non-cyanide gold imitation electro plating method of flowers and plants Download PDFInfo
- Publication number
- CN1442510A CN1442510A CN 03118870 CN03118870A CN1442510A CN 1442510 A CN1442510 A CN 1442510A CN 03118870 CN03118870 CN 03118870 CN 03118870 A CN03118870 A CN 03118870A CN 1442510 A CN1442510 A CN 1442510A
- Authority
- CN
- China
- Prior art keywords
- minute
- aqueous solution
- flowers
- preparation
- copper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A non-cyanogen golden electroplating on the surface of flower, tree leaf, or beetle, includes such steps as preparing golden electroplating liquid from copper sulfate, zinc sulfate, stannous chloride, potassium pyrophosphate, potassium sodium tartrate, potassium citrate and aminotriacetic acid, washing, roughening, sensitizing, activating, reducing, chemically plating copper, polishing, electroplating golden layer, passivating and coating protective film.
Description
Technical field
The present invention relates to the technical field of the imitative gold of a kind of cyanideless electro-plating, concretely, relate to a kind of method of carrying out the imitative gold of cyanideless electro-plating on the flowers surface, also be applicable to that leaf or beetle carry out the imitative gold of cyanideless electro-plating simultaneously.
Background technology
The Chinese patent application name is called " the electrogilding methods of a kind of flowers " (notification number 1339620) and discloses a kind of prussiate that utilizes fresh flower is carried out the proof gold electric plating method, owing to use prussiate in this electroplating technology, easy first contaminate environment, second the proof gold electroplating cost is higher.
Summary of the invention
At above deficiency, the purpose of this invention is to provide a kind of non-cyanide imitating gold electroplating method that flowers are carried out, this method compliance with environmental protection requirements and cost are extremely low, can realize scale operation.
Technical scheme of the present invention is: the non-cyanide imitating gold electroplating method of a kind of flowers, and it is undertaken by following program:
Clean → roughening treatment → sensitization processing → activation treatment → reduction processing → electroless copper → bright copper plating → imitation gold plating → Passivation Treatment → be coated with protective membrane.
At first 30-40 minute clean carried out on the flowers surface 30-40 ℃ the time, take out, use the silk friction, make its surface irregularity, put into alcohol and soaked 5-10 minute with after the clear water rinsing with suds; Handle with the alligatoring aqueous solution of preparation then, in the time of 15-35 ℃, carry out roughening treatment in 1-5 minute; The sensitization aqueous solution with preparation carries out sensitization in 2-5 minute processing at 20-25 ℃; With preparing activated water solution 20-25 ℃ of activation treatment of carrying out 0.5-5 minute; Reducing solution with preparation carries out reduction processing in 1-5 minute; The electroless copper aqueous solution with preparation carries out electroless copper processing in 15-20 minute at 25-45 ℃; With the preparation the bright copper plating aqueous solution at 15-30 ℃, 2-4A/dm
2The cathode current density condition under carry out 5-10 minute acidic copper-plating of bright; With the preparation Cyanida free imitative electrogilding solution at 30-35 ℃, Ph value 8.5-8.8, cathode current density 1-1.5A/dm
2, negative electrode moves to carrying out non-cyanide imitating gold electroplating under 20-25 time/minute the condition; With the passivation aqueous solution of preparation, passivation is 30-60 minute in the time of 20-30 ℃; Protective membrane liquid with preparation is coated with protective membrane 30-45 minute under 60-80 ℃, finish flowers, and the operation of imitation gold plating is carried out on leaf or beetle surface.
Adopt present method to carry out imitation gold plating on various flowers surface, flowers through imitation gold plating are attractive in appearance, the intensity height, and has a very natural texture, adopt non-cyanide imitating gold electroplating, compliance with environmental protection requirements, and it is extremely low to adopt flowers provided by the present invention surface to carry out the cost of imitation gold plating, is suitable for scale operation.
Embodiment
Realize that the best approach of the present invention is: at first 35 minutes clean are carried out on the flowers surface 35 ℃ the time, take out, use the silk friction, make its surface irregularity, put into alcohol and soaked 8 minutes with after the clear water rinsing with suds; Handle with the alligatoring aqueous solution of preparation then and carry out roughening treatment in 3 minutes 25 ℃ the time; The sensitization aqueous solution with preparation carries out sensitization in 4 minutes processing at 23 ℃; With preparing activated water solution 23 ℃ of activation treatment of carrying out 3 minutes; Reducing solution with preparation carries out reduction processing in 3 minutes; The electroless copper aqueous solution with preparation carries out electroless copper processing in 18 minutes at 35 ℃; With the preparation the bright copper plating aqueous solution at 25 ℃, 3A/dm
2The cathode current density condition under carry out 8 minutes acidic copper-plating of bright; With the preparation Cyanida free imitative electrogilding solution at 33 ℃, Ph value 8.5-8.8, cathode current density 1.2A/dm
2, it is to carry out non-cyanide imitating gold electroplating under 23 times/minute the condition that negative electrode moves; With the passivation aqueous solution of preparation, passivation is 50 minutes in the time of 25 ℃; Protective membrane liquid with preparation is coated with protective membrane 33 minutes under 70 ℃, finish flowers, and the operation of imitation gold plating is carried out on leaf or beetle surface.
The employed aqueous formulation of above-mentioned each operation is as follows respectively:
1, the alligatoring aqueous solution is prepared by following recipe ratio:
Chromium is done (CrO
3) 100g/L
Sulfuric acid (H
2SO
4Dense) 400ml/L.
2, the sensitization aqueous solution is prepared by following recipe ratio:
Tin protochloride (SnC
122H
2O 10～25g/L
Hydrochloric acid (HCl) 40～60ml/L
Water (H
2O) some.
3, activated water solution is prepared by following recipe ratio:
Silver Nitrate (AgNO
3) 2～4g/L
Ammoniacal liquor (NH
3H
2O) add to the just dissolving again of generation precipitation.
4, reducing solution is prepared by following recipe ratio:
Formaldehyde (HCHO, 37%) 1 volume
Water (H
2O) 9 volumes.
5, the electroless copper aqueous solution is prepared by following recipe ratio:
Copper sulfate (CuSO
45H
2O) 15g/l
Seignette salt (KNaC
4H
4O
6) 40g/l
Sodium hydroxide (NaOHO 20g/l
Formaldehyde (HCHO, 37%) 15ml/l
Thiocarbamide ((NH
2)
2CS) 0.8g/l.
6, the bright copper plating aqueous solution is prepared by following recipe ratio:
Copper sulfate (CuSO
45H
2O) 225g/l
Sulfuric acid (H
2SO
4) 60g/l
Cl ion 80ml/l
2-mercaptan 18ml/l.
7, Cyanida free imitative electrogilding solution is prepared by following recipe ratio:
Copper sulfate (CuSO
45H
2O) 45g/L
Zinc sulfate (ZnSO
42H
2O) 15g/L
Tin protochloride (SnC
122H
2O) 5 (adding before electroplating) g/L
Potassium pyrophosphate (K
4P
2O
7) 320g/L
Seignette salt (KNaC
4H
4O
6) 35g/L
Tripotassium Citrate (K
3C
6H
5O
7) 20g/L
Nitrilotriacetic acid(NTA) 25g/L.
8, the passivation aqueous solution is prepared by following recipe ratio:
K
2CrO
7 40-50g/l
PH (transferring) 3-4 with acetic acid.
9, protective membrane liquid is prepared by following recipe ratio:
1 part of 115 acrylic varnish
2 parts of cyclohexanones.
Flowers imitation gold plating method of the present invention is applicable to that also to leaf, imitation gold plating is carried out on the beetle surface.
Claims (7)
1, the non-cyanide imitating gold electroplating method of a kind of flowers is characterized in that it is undertaken by following program:
Clean → roughening treatment → sensitization processing → activation treatment → reduction processing → electroless copper → bright copper plating → imitation gold plating → Passivation Treatment → be coated with protective membrane; Its concrete steps are:
At first 30-40 minute clean carried out on the flowers surface 30-40 ℃ the time, take out, use the silk friction, make its surface irregularity, put into alcohol and soaked 5-10 minute with after the clear water rinsing with suds; Handle with the alligatoring aqueous solution of preparation then, in the time of 15-35 ℃, carry out roughening treatment in 1-5 minute; The sensitization aqueous solution with preparation carries out sensitization in 2-5 minute processing at 20-25 ℃; With preparing activated water solution 20-25 ℃ of activation treatment of carrying out 0.5-5 minute; Reducing solution with preparation carries out reduction processing in 1-5 minute; The electroless copper aqueous solution with preparation carries out electroless copper processing in 15-20 minute at 25-45 ℃; With the preparation the bright copper plating aqueous solution at 15-30 ℃, 2-4A/dm
2The cathode current density condition under carry out 5-10 minute acidic copper-plating of bright; With the preparation Cyanida free imitative electrogilding solution at 30-35 ℃, Ph value 8.5-8.8, cathode current density 1-1.5A/dm
2, negative electrode moves to carrying out non-cyanide imitating gold electroplating under 20-25 time/minute the condition; With the passivation aqueous solution of preparation, passivation is 30-60 minute in the time of 20-30 ℃; Protective membrane liquid with preparation is coated with protective membrane 30-45 minute under 60-80 ℃, finish flowers, and the operation of imitation gold plating is carried out on leaf or beetle surface.
2, the non-cyanide imitating gold electroplating method of a kind of flowers according to claim 1 is characterized in that the described alligatoring aqueous solution prepares by following recipe ratio:
Chromium is done (CrO
3) 100g/L
Sulfuric acid (H
2SO
4Dense) 400ml/L.
3, the non-cyanide imitating gold electroplating method of a kind of flowers according to claim 1 is characterized in that described reducing solution prepares by following recipe ratio:
Formaldehyde (HCHO, 37%) 1 volume
Water (H
2O) 9 volumes.
4, the non-cyanide imitating gold electroplating method of a kind of flowers according to claim 1 is characterized in that the described electroless copper aqueous solution prepares by following recipe ratio:
Copper sulfate (CuSO
45H
2O) 15g/l
Seignette salt (KNaC
4H
4O
6) 40g/l
Sodium hydroxide (NaOHO 20g/l
Formaldehyde (HCHO, 37%) 15ml/l
Thiocarbamide ((NH
2)
2CS) 0.8g/l.
5, the non-cyanide imitating gold electroplating method of a kind of flowers according to claim 1 is characterized in that described Cyanida free imitative electrogilding solution prepares by following recipe ratio:
Copper sulfate (CuSO
45H
2O) 45g/L
Zinc sulfate (ZnSO
42H
2O) 15g/L
Tin protochloride (SnC
122H
2O) 5g/L
Potassium pyrophosphate (K
4P
2O
7) 320g/L
Seignette salt (KNaC
4H
4O
6) 35g/L
Tripotassium Citrate (K
3C
6H
5O
7) 20g/L
Nitrilotriacetic acid(NTA) 25g/L.
6, the non-cyanide imitating gold electroplating method of a kind of flowers according to claim 1 is characterized in that the described passivation aqueous solution prepares by following recipe ratio:
K
2CrO
7 40-50g/l
Transfer PH 3-4 with acetic acid.
7, the non-cyanide imitating gold electroplating method of a kind of flowers according to claim 1 is characterized in that described protective membrane liquid prepares by following recipe ratio:
1 part of 115 acrylic varnish
2 parts of pimelinketone.