CN1442316A - Manufacturing method of decorative object or artificial potted landscape - Google Patents
Manufacturing method of decorative object or artificial potted landscape Download PDFInfo
- Publication number
- CN1442316A CN1442316A CN 03117686 CN03117686A CN1442316A CN 1442316 A CN1442316 A CN 1442316A CN 03117686 CN03117686 CN 03117686 CN 03117686 A CN03117686 A CN 03117686A CN 1442316 A CN1442316 A CN 1442316A
- Authority
- CN
- China
- Prior art keywords
- early
- products
- mold
- minutes
- shade
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A technology for making decoration or artificial potted landscape includes such steps as carving, preparing trunk, branches and twigs through bedding putty, painting, gilding and polishing, preparing flowers and leaves through moulding, painting, gilding and polishing, and assembling. It has high appreciative and collection value.
Description
Technical field
The present invention relates to the handicraft technical field, specifically the process for making of ornaments or artificial potted landscape.
Background technology
Existing ornaments-particularly workmanship, artificial potted landscape handicraft, the little potted landscape of jade carving that general is after the perforating grafting, goods are subjected to spatial constraints, the vestige that the perforating grafting is arranged, its preparation method generally is with husky mould, plaster mold etc., can only make goods or simple raised piece about 10 centimeters, its works can't be gilded and be inlayed, and have the frangible defective of goods.
Summary of the invention
The process for making that the purpose of this invention is to provide a kind of ornaments or artificial potted landscape, this method are better than methods such as existing husky mould, plaster mold, make goods not be subjected to spatial constraints, without design drawing, can finish according to the imagination fully.
The process for making of ornaments of the present invention or artificial potted landscape carries out according to the following steps:
1) main body is shaped:
(1) material is sawn into bulk, joggle, required branch rod-shape is processed, is engraved as to bonding then;
(2) adding saw wood ash with viscose glue adds resin and adds talcum powder and add curing agent and add catalyst=2: 3: 100: 300: 4: 4, again add an amount of atom ash and be mixed and made into putty after, above-mentioned branch bar is stamped putty, sanding and polishing is to smooth straight and even then;
(3) japanning: on whole branch bar with lacquer type organic coating or native lacquer or siccative varnish or excellent beautiful gold lacquer japanning;
(4) gild: the goods humidity after brushing lacquer reaches at 40～45% o'clock, with Jin Bo goods is gilded comprehensively, is inlayed, and will carry out repeatedly at opposite joint and joint;
(5) polishing: carry out soft polishing with hairbrush, sweep off unnecessary goldleaf, reach the degree of clean, smooth;
2) simulation, mould:
(1) model: be engraved as the required flower and the early-products of blade with materials such as timber, gypsum, rubber cement, resins, sanding and polishing brushes mould wax or floor wax to satisfied;
(2) early-products is positioned on the flat runner with viscose glue and saw wood ash;
(3) system box: according to the size of early-products, make the sylphon of different size, sylphon is enclosed within on the early-products, fix with viscose glue and saw wood ash and plate all around;
(4) system soft mode: with silicon rubber and curing agent by 25: 1～5 ratio mix mix well after, pour into and be placed with early-products sylphon interior (if not repeatedly use repeatedly, can be directly with the brushing of aforementioned proportion epoxy glue on early-products) is arranged;
(5) drying: dried in the shade 1～5 hour; Fast doing then with silicon rubber adds curing agent in 25: 5 ratio allotment, dries in the shade 1～3 hour, adds curing agent in 25: 1 ratio allotment with silicon rubber, then dries in the shade 3～5 hours;
(6) soft mode that will be surrounded by early-products is coated with mold wax, dries in the shade 15～20 minutes;
(7) make gypsum mold: transfer all to water in 3: 2 ratio with gypsum and viscose glue and mould or spread upon on half that is surrounded by the early-products soft mode, after solidifying, remove unnecessary gypsum with graduating with cutter;
(8) mould wax or floor wax brushing are not being smeared on second half soft mold of gypsum, dried in the shade 15～20 minutes;
(9) system hard mold: be layered on for two layers on second half soft mold of not smearing gypsum with thin glass fiber cloth, mix well in 100: 4: 4 ratio mixing with resin, catalyst, curing agent, brush is on glass fabric, dried in the shade 15～20 minutes, repave one deck crude fibre cloth then, brush on crude fibre cloth with the hybrid resin of aforementioned proportion again;
(10) system gypsum hard mold: will brush second half gypsum of hybrid resin and all remove, and with the hairbrush cleaning totally, early-products be stamped mould wax, dry in the shade 10～15 minutes;
(11) system hard mold: will knock out second half of gypsum, and spread two layers of thin glass fiber cloth, and brush the hybrid resin of the ratio of stating, and repave last layer raw glass fiber cloth, and brush hybrid resin again to solidifying;
(12) open bag: hard mold is opened respectively, unnecessary glass fibre around the hard mold is cut off, and on the hard mold inwall, stamp mould wax, dried in the shade 15～20 minutes;
(13) soft mold that will be surrounded by early-products cuts a mouth, separates early-products;
(14) wax at the soft mold inwall, dried in the shade 15～20 minutes, wax again, in the hard mold of packing into after drying in the shade again 15～20 minutes;
(15) meet and close: will be hard, soft mold is integrated;
(16) inject in the soft mold with above-mentioned hybrid resin, dried in the shade 10～30 minutes;
(17) peel off: after the early-products typing, remove the soft or hard mould, early-products is taken out;
(18) cool off: early-products is put into soaked 20～30 minutes in the cold water;
(19) polishing: use the thickness sand papering, till the satisfaction;
(20) moulding: will spend, branch, leaf perforating grafting becomes required shape, and add saw wood ash with viscose glue and add resin and add talcum powder and add curing agent and add catalyst=2: 3: 25: mixing in 30: 1: 1 is mixed well, and with its location, the material carving that seam crossing is unnecessary goes, and sanding and polishing, make it smooth smooth;
(21) japanning: with lacquer type organic coating or native lacquer or siccative varnish or excellent beautiful gold lacquer japanning;
(22) gild: early-products is gilded comprehensively, polish with banister brush afterwards;
3) combination shaping
(1) flower, branch, the leaf made by above-mentioned process, is combined on the main body with methods such as perforating graftings;
(2) sanding and polishing: sanding and polishing is carried out at the position to the perforating grafting,
(3) gild, inlay: goods are leaked paste, slit and eyelet part are gilded repeatedly, are inlayed;
(4) bronzing: whole goods are handled at last, purged at last with hairbrush, hair-dryer, the press of rectifying.
(2), (3), (20) described viscose glue are 502 glue wherein: 1) (2) and 2), 2) (7) described viscose glue is 801 glue in.When coating with lacquer with soil, be 7～8 days drying time; With polyester when two-in-one, dry 2～4 hours; When three-in-one, did 40～60 minutes slow curing 1～6 day with resin soon; During with magnetic varnish, slow curing 30～50 minutes was done 10～20 minutes soon, during with excellent beautiful gold lacquer, dried in the shade 30～40 minutes.
Ornaments, the artificial potted landscape finished with process for making of the present invention, technology is meticulous, nature, lines are happy, golden pure soft and moist, relatively golden camellia (patent application formerly) has reduced cost, and having remedied golden camellia can not the quantity-produced deficiency, is to have the handicraft of viewing and admiring and collecting value.
The specific embodiment
Introduce below with process for making of the present invention and make a large stereo flower landscape golden tree peony
Embodiment:
Gold tree peony large-scale potted landscape profile: long * wide * high=2.98 meters * 2.98 meters * 2.98 meters, basic styling is that a glittering tree peony root is tied on the base based on flowerpot.
One, body profile, bar branch are made:
1, blanking: be sawn into bulk with the material of choosing (timber), circle, ellipse, elongated, square shape after the perforating, become the torch shape in the imagination by joggle, bonding grafting.
2, engraving: carve out the flame combustion shape according to the imagination.
3, adding saw wood ash with 502 glue adds resin and adds talcum powder and add ketone slurry (curing agent) and add and buy liquid (catalyst)=2: 3: 100: 300: 4: 4, again add an amount of atom ash (according to doing or rarer needs are decided) and be mixed and made into putty after, above-mentioned branch bar is stamped putty, and sanding and polishing is to smooth straight and even then.
4, japanning: with lacquer type organic coating or native lacquer or siccative varnish or excellent beautiful gold lacquer or polyester paint japanning.
5, drying: during with the soil lacquer, be 7～8 days drying time; With polyester when two-in-one, dry 2～4 hours; When three-in-one, did 40～60 minutes slow curing 1～6 day with resin soon; During with magnetic varnish, slow curing 30～50 minutes was done 10～20 minutes soon, if add the small diluted amount agent, can promptly brush promptly and gild, and dried in the shade 30～40 minutes with excellent beautiful gold lacquer.
6, gild: humidity reaches at 40～45% o'clock, with 24K standard goldleaf above-mentioned early-products is gilded comprehensively, inlays, and polishes with banister brush afterwards, purges unnecessary Jin Bo, reaches meticulous bright and clean degree.
Two, simulation, mould:
1, model: be engraved as the required flower and the early-products of blade with materials such as timber, gypsum, rubber cement, resins, sanding and polishing brushes mould wax or floor wax to satisfied:
2, early-products is positioned on the flat runner with 502 glue and saw wood ash;
3, system box: according to the size of early-products, make the sylphon of different size, sylphon is enclosed within on the early-products, fix with 502 glue and saw wood ash and plate all around;
4, system soft mode: after mixing well in 25: 1 ratio mixing with silicon rubber and curing agent, pour into and be placed with early-products and have in the sylphon;
5, drying: dried in the shade 1～5 hour;
6, the soft mode that will be surrounded by early-products is coated with mold wax, dries in the shade 15 minutes;
7, make gypsum mold: transfer all to water in 3: 2 ratio with gypsum and viscose glue and mould or spread upon on half that is surrounded by the early-products soft mode, after solidifying, remove unnecessary gypsum with graduating with cutter;
8, mould wax or floor wax brushing are not being smeared on second half soft mold of gypsum, dried in the shade 15 minutes;
9, system hard mold: be layered on for two layers on second half soft mold of not smearing gypsum with thin glass fiber cloth, with resin, buy liquid (catalyst), ketone slurry (curing agent) and mix well by 100: 4: 4 ratio mixing, brush is on glass fabric, dried in the shade 15 minutes, repave one deck crude fibre cloth then, brush on crude fibre cloth with the hybrid resin of aforementioned proportion again;
10, system gypsum hard mold: will brush second half gypsum of hybrid resin and all remove, and with the hairbrush cleaning totally, early-products be stamped mould wax, dry in the shade 10～15 minutes;
11, system hard mold: will knock out second half of gypsum, and spread two layers of thin glass fiber cloth, and brush the hybrid resin of the ratio of stating, and repave last layer raw glass fiber cloth, and brush hybrid resin again to solidifying;
12, Kai Bao: hard mold is opened respectively, unnecessary glass fibre around the hard mold is cut off, and on the hard mold inwall, stamp mould wax, dried in the shade 15 minutes;
13, the soft mold that will be surrounded by early-products cuts a mouth, separates early-products;
14, wax at the soft mold inwall, dried in the shade 15 minutes, wax again, in the hard mold of packing into after drying in the shade again 15 minutes;
15, meet and close: will be hard, soft mold is integrated;
16, inject in the soft mold with above-mentioned hybrid resin, dry in the shade the time: 10～30 minutes;
17, peel off: after the early-products typing, remove the soft or hard mould, early-products is taken out;
18, cool off: early-products is put into soaked 20～30 minutes in the cold water:
19, polishing: use the thickness sand papering, till the satisfaction;
20, moulding: will spend, branch, leaf perforating grafting becomes required shape, and add saw wood ash with 502 glue and add resin and add talcum powder and add ketone slurry (curing agent) and add and buy liquid (catalyst)=2: 3: 25: after 30: 1: 1 ratio mixing is mixed well, locate with it;
Three, combination shaping
1, flower, branch, the leaf made by above-mentioned process, is combined on the torch main body with methods such as perforating graftings.
2, sanding and polishing: sanding and polishing is carried out at the position to the perforating grafting.
3, gild, inlay: goods are leaked paste, slit and eyelet part are gilded repeatedly, are inlayed.
4, bronzing: whole goods are handled at last, purged at last with hairbrush, hair-dryer, the press of rectifying.
Claims (4)
1, the process for making of a kind of ornaments or artificial potted landscape is characterized in that carrying out according to the following steps:
1) main body is shaped:
(1) material is sawn into bulk, joggle, required branch rod-shape is processed, is engraved as to bonding then;
(2) adding saw wood ash with viscose glue adds resin and adds talcum powder and add curing agent and add catalyst=2: 3: 100: 300: 4: 4, again add an amount of atom ash and be mixed and made into putty after, above-mentioned branch bar is stamped putty, sanding and polishing is to smooth straight and even then;
(3) japanning: on whole branch bar with lacquer type organic coating or native lacquer or siccative varnish or excellent beautiful gold lacquer japanning;
(4) gild: the goods humidity after brushing lacquer reaches at 40～45% o'clock, with Jin Bo early-products is gilded comprehensively, is inlayed;
(5) polishing: carry out soft polishing with hairbrush, sweep off unnecessary goldleaf, reach the degree of clean, smooth;
2) simulation, mould:
(1) model: be engraved as the required flower and the early-products of blade with materials such as timber, gypsum, rubber cement, resins, sanding and polishing brushes mould wax or floor wax to satisfied;
(2) early-products is positioned on the flat runner with viscose glue and saw wood ash, the ratio of viscose glue and saw wood ash is 2: 3;
(3) system box: according to the size of early-products, make the sylphon of different size, sylphon is enclosed within on the early-products, fix with the viscose glue of aforementioned proportion and saw wood ash and plate all around;
(4) make soft mode: after mixing well in 25: 1～5 ratio mixing with silicon rubber and curing agent, pour in the sylphon that is placed with early-products;
(5) drying: dried in the shade 1～5 hour;
(6) soft mode that will be surrounded by early-products is coated with mold wax, dries in the shade 15～20 minutes;
(7) system gypsum mold: with gypsum and viscose glue in 3: 2 ratio accent all water mould or brush be surrounded by the early-products soft mode half on, after solidifying, remove unnecessary gypsum with graduating with cutter;
(8) mould wax or floor wax brushing are not being smeared on second half soft mold of gypsum, dried in the shade 15～20 minutes;
(9) system hard mold; Be layered on for two layers on second half soft mold of not smearing gypsum with thin glass fiber cloth, mix well in 100: 4: 4 ratio mixing with resin, catalyst, curing agent, brush is on glass fabric, dried in the shade 15～20 minutes, repave one deck crude fibre cloth then, brush on crude fibre cloth with the hybrid resin of aforementioned proportion again;
(10) system gypsum hard mold: will brush second half gypsum of hybrid resin and all remove, and with the hairbrush cleaning totally, early-products be stamped mould wax, dry in the shade 10～15 minutes;
(11) system hard mold: will knock out second half of gypsum, and spread two layers of thin glass fiber cloth, and brush the hybrid resin of the ratio of stating, and repave last layer raw glass fiber cloth, and brush hybrid resin again to solidifying;
(12) open bag: hard mold is opened respectively, unnecessary glass fibre around the hard mold is cut off, and on the hard mold inwall, stamp mould wax, dried in the shade 15～20 minutes;
(13) soft mold that will be surrounded by early-products cuts a mouth, separates early-products;
(14) wax at the soft mold inwall, dried in the shade 15～20 minutes, wax again, in the hard mold of packing into after drying in the shade again 15～20 minutes;
(15) meet and close: will be hard, soft mold is integrated;
(16) inject in the soft mold with above-mentioned hybrid resin, dry in the shade the time: 10～30 minutes;
(17) peel off: after the early-products typing, remove the soft or hard mould, early-products is taken out:
(18) cool off: early-products is put into soaked 20～30 minutes in the cold water;
(19) polishing: use the thickness sand papering, till the satisfaction;
(20) moulding: will spend, branch, leaf perforating grafting becomes required shape, and add saw wood ash with viscose glue and add resin and add talcum powder and add curing agent and add catalyst=2: 3: 25: mixing in 30: 1: 1 is mixed well, and locatees with it;
(21) japanning: with lacquer type organic coating or native lacquer or siccative varnish or excellent beautiful gold lacquer japanning;
(22) gild: early-products is gilded comprehensively, polish with banister brush afterwards;
3) combination shaping
(1) flower, branch, the leaf made by above-mentioned process are combined on the main body with methods such as perforating graftings;
(2) sanding and polishing: sanding and polishing is carried out at the position to the perforating grafting,
(3) gild, inlay: goods are leaked paste, slit and eyelet part are gilded repeatedly, are inlayed;
(4) bronzing: whole goods are handled at last, purged at last with hairbrush, hair-dryer, the press of rectifying.
2, the process for making of ornaments according to claim 1 or artificial potted landscape is characterized in that 1) in (2) and 2) in (2), (3), (20) described viscose glue be 502 glue, 2) in (7) described viscose glue be 801 glue.
3, the process for making of ornaments according to claim 1 or artificial potted landscape is characterized in that described curing agent is import ketone slurry.
4, the process for making of ornaments according to claim 1 or artificial potted landscape is characterized in that described catalyst is for buying liquid.