CN1430667A - 表面清洁 - Google Patents
表面清洁 Download PDFInfo
- Publication number
- CN1430667A CN1430667A CN01809961.0A CN01809961A CN1430667A CN 1430667 A CN1430667 A CN 1430667A CN 01809961 A CN01809961 A CN 01809961A CN 1430667 A CN1430667 A CN 1430667A
- Authority
- CN
- China
- Prior art keywords
- cleaning
- compound
- formula
- active agent
- tensio
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
通过使基材与包括下式(I)的至少一种化合物的组合物,特别是水性组合物接触而清洁基材:(R2)p-Ph-(CH2)m-COO-(AO)n-R1(I)其中,R1、AO、n、M、Ph、R2和p具有所限定的含义。式(I)化合物特别优选是苯甲酸烷基酯。这样的化合物给清洁配方提供了有用的溶解能力,同时具有相对有益的环境性能。
Description
本发明涉及表面的清洁,特别地,本发明涉及家庭、机构和工业硬表面清洁方法及清洁组合物。
在硬表面的清洁中,特别是金属、陶瓷、玻璃和塑料的表面清洁中,清洁方法通常都涉及用清洁性流体处理被清洁的基材,以帮助被清洁表面上的污垢物理或化学溶解或分散。清洁方法,特别是在家庭中,可能包括机械作用,例如摩擦或擦洗。但是,在机构清洁中,为了经济方面的原因,需要减少机械摩擦或擦洗,而在工业清洁中,如果可能通常希望避免机械摩擦或擦洗,因为机械摩擦或擦洗难以均匀地应用并且很贵。特别是在工业清洁中,可能会通过搅拌或使用超声波而供给帮助清洁的能量。
在所有这些类的清洁中,经常使用溶剂,以通过从表面和/或顶部的呈附着涂层形式的软化污垢上溶解污垢材料,特别是油、油脂或脂肪固体而改进去污效果,所述涂层形式的软化污垢是例如需要从涂漆基材上除去(剥离)的油漆或乱涂乱写的东西。碱材料可以包括例如作为缓冲剂和/或助洗剂的中等强度的碱如苏打灰(碳酸钠),或强碱如苛性苏打(氢氧化钠),后者可改善去除脂肪、蜡或油状污垢的效果,特别是通过酯类脂肪和油的水解作用。通常还包括表面活性剂材料,一般是合成表面活性剂材料,以改善从被清洁的基材表面上脱落下来的污物的润湿并帮助其保持悬浮状态。这种通用的组合物被称为清洁剂,特别是所谓的“硬表面清洁剂”。
本发明基于我们的如下发现:某些芳香酸酯是可用于清洁方法中并包括在清洁组合物中的有用的溶剂。本发明包括用于家庭、机构和工业应用领域的硬表面清洁、脱脂特别是金属脱脂、车辆清洁和包括油漆剥离和清除乱涂乱写物在内的油漆脱除的方法,并包括适合于所述方法中使用的清洁组合物。
因此,本发明提供一种清洁基材的方法,该方法包括使被清洁的基材与包括下式(I)的至少一种化合物的组合物,特别是水性组合物接触:
(R2)p-Ph-(CH2)m-COO-(AO)n-R1 (I)其中,
R1是C1~C20烷基或链烯基,优选是C1-C10烷基,更优选是C1~C6烷基,最优选是C3~C5支链烷基;
AO是亚烷基氧基,特别是亚乙氧基或亚丙氧基,并且沿(聚)亚烷基氧基链可以改变;
n是0或1~100,希望是0;
m是0,1或2,希望是0;并且
Ph是苯基,该苯基可以被(R2)p基团取代,其中每个R2独立地是C1~C4的烷基或烷氧基,并且p是0,1或2,希望是0。
在所述方法中,所述基材一般与表面活性剂,通常是清洁性表面活性剂及式(I)化合物接触。最通常地,含表面活性剂的组合物是水性组合物,该水性组合物通常呈水包油型乳液的形式,其中油分散相中包括式(I)化合物。因此,本发明还提供一种清洁基材的方法,该方法包括使被清洁的基材与水性清洁组合物,特别是水包油型乳液形式的清洁组合物接触,该水性清洁组合物包括式(I)化合物及表面活性剂,特别是清洁性表面活性剂。
本发明还包括:
一种基材特别是金属基材的脱脂方法,其中使被脱脂的基材与包括至少一种式(I)化合物的组合物,特别是水性组合物接触;
一种硬表面清洁方法,其中使被清洁的基材与包括至少一种式(I)化合物和表面活性剂,特别是清洁性表面活性剂及助洗剂或碱的组合物,特别是水性组合物接触;
一种从表面上清除乱涂乱写的方法,其中使被清洁的表面与包括至少一种式(I)化合物和表面活性剂,特别是清洁性表面活性剂及任选的助洗剂和/或碱的组合物,特别是水性组合物接触;
一种从基材上剥离油漆的方法,其中使涂漆的基材与包括至少一种式(I)化合物和表面活性剂,特别是清洁性表面活性剂的组合物,特别是水性组合物接触;
一种钻探设备清洁方法,其中使被清洁的钻探设备表面与包括至少一种式(I)化合物和表面活性剂,特别是清洁性表面活性剂的组合物,特别是水性组合物,尤其是微乳液配方接触;和
如上所述的式(I)化合物在清洁表面,特别是在清洁硬表面中的应用。如下面所讨论的那样,希望所使用的化合物是或包括苯甲酸异丙酯。
在式(I)化合物中,R1基团是C1~C20烷基或链烯基,优选是C1~C10烷基。希望R1是C1~C6烷基,特别是支链烷基,例如是异丙基(丙-2-基)、仲丁基(丁-2-基)、异丁基(2-甲基丙-1-基)和/或叔丁基,以降低该酯被水解的可能性。在这一点上,用仲醇形成的酯特别有用,因此R1尤其是C3~C5仲烷基,非常希望是异丙基。尽管一般希望烷基R1是相对短链的基团,特别是C1~C6烷基,但是它也可以是更长链的基团,例如C6~C20烷基或链烯基,特别是C8~C18烷基或链烯基,它们可以是直链的,例如在混合酯如苯甲酸(混合C12/C13烷基)酯中的基团,或是支化的,例如2-乙基己基或异壬基,或支链C18烷基如所谓的异硬脂基(实际上是主要为支化C14~C22烷基的混合物,平均链长接近C18)。不饱和长链基团包括油基(oleyl)。当使用长链基团时,特别是长于C12的基团时,希望该基团是或包括支链和/或不饱和键,和/或希望使用这样的酯的混合物,因为这样的酯比直链饱和酯更倾向于是液态的。
尽管在酯中使用的羧酸可以是二氢肉桂酸或苯乙酸,但是非常希望是苯甲酸,即希望m是0。类似地,尽管所述酸的苯环可以被取代,但是希望该苯环是未取代的,即希望p是0。
在本发明中使用的酯可以在羧基和R1基团间包括(聚)亚烷氧基链。当存在(聚)亚烷氧基链时,希望它是(聚)亚乙氧基链、(聚)亚丙氧基链或包括亚乙氧基和亚丙氧基残基的链。一般地,希望在酯中不包括这样的链,即希望n是0。
特别有用的酯是苯甲酸异丙酯,并且本发明具体地包括一种清洁方法,其中苯甲酸异丙酯用作式(I)化合物或式(I)化合物之一。苯甲酸异丙酯具有使其特别有用的组合的特性:作为纯物质,它在宽的范围内是液体(沸点约219℃,倾点小于-60℃);它被认为是不易燃的材料(闪点约99℃),并且在通常的使用条件下它具有低的蒸气压。
式(I)的化合物可以与其它有机溶剂材料混合使用,包括已知用于清洁配方中的那些有机溶剂。这些材料包括烃类,特别是C5~C18烃,尤其是烷属烃,例如溶剂油和矿物油石蜡馏分,或萜类烃如d-苧烯;卤代烃,特别是氯代和/或氟代烃,尤其是C1~C14化合物;醇,特别是C2~C8链烷醇,例如乙醇、异丙醇和异己醇;二元醇,例如乙二醇和丙二醇;二元醇醚,例如丁氧基乙醇和二甘醇丁醚。一般地,特别是因为式(I)化合物对环境友好,所以不使用对环境不友好的已知溶剂如氯代烃和挥发性烃,但是已知对环境有较低负面影响的溶剂,例如萜烯如d-苧烯,当然可以包括在本发明使用的清洁组合物中。
当使用混合物时,式(I)化合物的存在量一般至少为10%,通常至少为25%,更通常为至少40%,希望至少为50%,以所使用的溶剂总重量计。当存在其它溶剂组分时,它们的使用量希望一般为1~90%,通常为1~75%,更优选为2~60%,最优选为5~50%,以所使用的载体流体的总重量计。
为了方便,在本发明清洁方法中使用的和在本发明清洁组合物中包括的式(I)化合物或包括式(I)化合物的混合物,有时被简称为清洁配方的溶剂或溶剂组分。
本发明的各种实施方案中使用的特定配方和组合物形式可以根据需要进行的特定清洁工作而变化。一般地,本发明中使用的清洁配方包括水,并且一般是水基的。式(I)化合物一般与水不混溶,这样为形成溶液,需要使式(I)化合物与存在的水相容或使式(I)化合物可溶于存在的水中的其它组分。清洁组合物的其它形式包括溶剂在水相中的乳液,水相在溶剂中的反乳液或微乳液,在微乳液中,分散相粒子非常细,一般小于约100nm,以至于微乳液不会强烈地散射可见光。
一般地,本发明中使用的配方属于如下三种一般类型之一:溶液、乳液和微乳液。溶液和微乳液配方可以配制成使用浓度,或者配制成在使用前稀释的浓缩物,而乳液一般配制成使用浓度。总的来说,这样的配方具有如下所示的组成(数值是重量百分比):
溶液配方:
组分 | 浓缩物 | 使用 | ||
典型值 | 希望值 | 典型值 | 希望值 | |
表面活性剂* | 1~30 | 2~10 | 0.5~5 | 1~5 |
助水溶剂(如果使用) | 1~15 | 1~10 | 0.3~3 | 0.5~2 |
溶剂 | 1~15 | 1~8 | 0.1~6 | 0.5~3 |
式(I)溶剂 | 1~10 | 1~5 | 0.1~5 | 0.5~2 |
其它溶剂(如果使用) | 1~10 | 1~5 | 0.1~5 | 0.5~2 |
助洗剂(几乎总是存在) | 1~30 | 5~15 | 0.5~8 | 1~5 |
水 | 至100 | 至100 |
表面活性剂通常作为洗涤剂和/或加溶剂和/或润湿剂而存在。溶液配方可以配制成可直接使用,或者配制成在水中稀释后使用,一般在水中按1∶5~1∶50的比例稀释。
乳液配方:
表面活性剂一般作为乳化剂和可能还作为洗涤剂存在,并且通常是两种或多种乳化剂,例如低HLB乳化剂和高HLB乳化剂的组合物。乳液配方可配制成可直接使用。微乳液配方:
组分 | 浓缩物 | |
典型值 | 希望值 | |
表面活性剂* | 1~15 | 5~10 |
溶剂 | 10~60 | 20~40 |
式(I)溶剂 | 10~60 | 10~40 |
其它溶剂(如果使用) | 5~50 | 5~30 |
水(至100) | 至100 | 55~75 |
组分 | 浓缩物 | |
典型值 | 希望值 | |
表面活性剂* | 10~25 | 12~20 |
共乳化剂(当使用时) | 1~10 | 2~8 |
溶剂 | 20~50 | 25~40 |
式(I)溶剂 | 20~50 | 25~40 |
其它溶剂(当使用时) | 5~30 | 10~20 |
水 | 至100 |
表面活性剂一般作为乳化剂和可能还作为洗涤剂存在,并且通常是两种或多种乳化剂,例如低HLB乳化剂和高HLB乳化剂的组合物。微乳液配方可配制成可直接使用,或在水中稀释后使用,一般在水中的稀释比例为1∶1~1∶10。在稀释时,配方的物理形态可能变化成乳液或具有不同溶剂相的类似形式。
在本发明使用的清洁配方中,非溶剂组分的一般的类型和用量描述如下。
可以存在起到很多作用的表面活性剂。这样:
可以包括洗涤剂以有助于从被清洁基材上去污。其实例包括:
阴离子洗涤剂,例如醚硫酸盐(醇烷氧化物硫酸酯)如月桂基醚硫酸钠;醚磷酸盐,例如Uniqema以Atlas G2203或Atlas G2207商品名销售的那些醚磷酸盐;烷基和烷芳基磺酸盐,例如异丙基胺十二烷基苯磺酸盐;醇硫酸盐,磺基琥珀酸单酯或二酯,醚羧酸盐;和
非离子洗涤剂,例如烷基酚乙氧化物,醇烷氧化物,特别是乙氧化物,包括Uniqema以“Synperonic”的商品名,特别是诸如A7、91/2.5、91/5、13/10、NCA850、NCE7和LF/RA30级和以商品名Brij30销售的那些,失水山梨醇脂肪酸酯,乙氧化失水山梨醇脂肪酸酯如由Uniqema以Tween20的商品名销售的失水山梨醇单油酸酯20EO,山梨醇酯如山梨醇六油酸酯,乙氧化脂肪酸酯和氧化烯嵌段共聚物。
洗涤剂的典型比例为1~30%,更通常为1~20%,希望为1~10%,以清洁配方的重量计。
溶剂的乳化剂通常是非离子表面活性剂,例如醇烷氧化物和乙氧化失水山梨醇脂肪酸酯,特别是低HLB(亲水亲脂平衡值)和高HLB乳化剂的混合物。乳化剂的典型比例为1~20%,更通常为1~15%,希望为1~10%,以清洁配方的重量计。
洗涤剂和乳化剂的功能可以重叠,这样同一材料可以提供两种功能。
可以包括润湿剂(浸润剂)以有助于润湿基材。其实例包括非离子表面活性剂,例如醇烷氧化物,特别是相对短链的醇如C8~C11醇与相对短链的聚氧化烯链如含有至多6个氧化烯残基的聚氧化烯形成的醇烷氧化物,和阴离子表面活性剂,例如磺基琥珀酸酯。润湿剂的典型比例为1~10%,更通常为2~10%,希望是2~7%,以清洁配方的重量计。
可以存在的非表面活性剂材料包括:
助水溶剂,可以包括它以使表面活性剂材料,特别是非离子表面活性剂保持溶解。阴离子表面活性剂例如磺酸盐和磷酸酯盐,阳离子表面活性剂例如季铵化合物和非离子表面活性剂例如烷基多糖。助水溶剂的典型浓度为1~25%,更通常为1~15%,希望为1~10%,以清洁配方的重量计。
助洗剂材料,包括它以提高所使用的表面活性剂的效果。实例包括磷酸盐,正磷酸盐,多磷酸盐如焦磷酸四钾,硅酸盐(silicate)和/或硅酸盐(metasilicate)如硅酸钠,和有机助洗剂,例如羟基羧酸和它们的水溶盐,特别是碱金属盐如钠或钾盐,例如诸如柠檬酸钠的柠檬酸盐和葡糖酸盐,膦酸和膦酰基烷羧酸和它们的水溶盐,特别是碱金属盐如钠或钾盐。助洗剂的典型比例为1~50%,更通常为2~30%,希望为5~20%,以清洁配方的重量计。
螯合剂,包括它特别是为了降低清洁环境中的金属离子的浓度,例如钙和镁或重金属的离子浓度。合适的螯合剂可以包括N-羧化的多胺盐,例如乙二胺四乙酸(EDTA)、次氮基三乙酸(NTA)、多羧酸、羟基羧酸如柠檬酸、聚丙烯酸、葡糖酸和庚酸的碱金属盐如钠或钾盐。螯合剂的典型浓度为1~30%,更通常为1~20%,希望为2~10%,以清洁配方的重量计。
碱,例如氢氧化钠或三乙醇胺,可以包括它们以维持碱性环境,从而有助于通过皂化脱除脂肪。典型浓度为1~20%,更通常为1~10%,希望为2~7%,以清洁配方的重量计。
酸,例如磷酸(通常为约85%重量浓度的水溶盐),可以包括它以有助于脱除例如含钙沉积物。酸的典型浓度为1~50%,更通常为2~30%,希望为5~20%,以清洁配方的重量计。
固体,例如适度的研磨剂,可以包括它以有助于从基材上机械去除污垢。这类固体的典型量为1~20%,更通常为0(1)~10%,希望为1~5%,以清洁配方的重量计。
缓蚀剂,可以包括它以降低或防止腐蚀,特别是对金属基材如铁和钢(包括不锈钢、镍和铬钢)、铜、黄铜、青铜、铝、硅铝合金和硬铝的腐蚀。其实例包括直链或支链的,特别是C8~C11的烷羧酸和它们的水溶性盐,例如诸如钠或钾的碱金属盐,或铵盐如链烷醇铵盐。缓蚀剂的典型浓度为1~10%,更通常为2~10%,希望为2~7%,以浓缩的清洁配方的重量计。
防沫剂,特别在喷雾清洁使用的组合物中使用。防沫剂的实例包括水溶性或水可分散的有机聚硅氧烷和非离子表面活性剂,例如醇乙氧化物-丙氧化物,如Uniqema以Synperonic LF/RA260的商品名销售的醇乙氧化物-丙氧化物。防沫剂的典型浓度为0.01~10%,更通常为0.1~5%,希望为0.5~2%,以清洁配方的重量计。
清洁组合物中可以存在的其它材料包括稳定剂、防腐剂,特别是杀生物剂如杀菌剂、香料和染料,它们的用量为常规水平。
清洁条件将根据应用领域而改变。因此,温度可以从特别适合家庭应用的环境温度到适度升高的温度,后者可以用于工业清洁,例如金属脱脂。典型的温度为15~80℃。清洁介质的pH值可以是从中等酸度到强碱性,例如4~13.5,但是更通常为9~13.5(通过包括碱如钠或钾的氢氧化物或碳酸盐而实现),并且特别是在适度升高的温度如40~80℃的温度下使用。
清洁技术可以是从手工应用和擦洗到如在工业清洁中使用的喷洁和浸洁。特别在工业清洁中,可以通过机械搅拌或例如使用超声波的声波法来提供能量。
在家庭硬表面清洁中,所述配方通常是溶液、乳液或微乳液,并且通常以直接使用浓度的产品零售,而且典型地是通过喷雾、擦洗、擦拭或刷洗而施加到被清洁的基材上。大规模清洁时一般采用机械摩擦或擦拭。
对于机构和工业清洁应用,所述配方通常是乳液或微乳液,并且一般通过喷雾、擦洗、擦拭或通过采用这样的应用作用的机器而施加到被清洁的基材上。
在与食品相关领域的工业清洁中,例如在奶品厂、酿酒厂或食品加工厂,所述配方通常通过喷雾、沉浸(特别是通过使清洁介质经过被清洁的设备,例如向下通过被清洁的线或管)、擦拭和刷洗而应用。
对于工业脱脂,所述配方通常是溶液、乳液或微乳液,并且通常通过喷雾、沉浸、擦拭和/或刷洗而应用。脱脂一般用于金属成形操作中,或用于清洁在工业制造操作过程中受到油、油脂或类似污染物污染的基材,例如电路板。
一种相关的清洁应用是钻探设备清洁,即清洁油田设备,例如钻头或生产井。对于这种应用来说,所述清洁剂通常以微乳液形式提供,该微乳液在使用前用水稀释。在海上油田操作中,减少对环境的危害是特别重要的,并且在这样的情况下,通常使用盐水(海水)作为稀释水。
在剥离油漆和清除乱涂乱写时,溶剂比例一般高于普通的清洁应用,所述溶剂包括式(I)的化合物和若使用的其它溶剂。典型地,它们可类似于用于清除牢固的油污的清洁剂。对于这些应用,溶剂的总比例通常为清洁材料总量的至少10%,并且可以高达90%。在这样的宽范围内,具有较低比例溶剂的清洁剂通常具有相对更高比例的清洁性表面活性剂,而具有较高比例溶剂的那些清洁剂可以具有较低浓度的洗涤剂。因此,以重量计,水基油漆剥离剂或乱涂清除剂可以具有15~25%的溶剂和25~30%的非离子洗涤剂,或者水基乳液配方可以含有40~65%的溶剂,分散在水相中,包括15~25%的洗涤剂。所述溶剂希望是式(I)化合物与其它溶剂例如苧烯的混合物,并且所述洗涤剂希望是醇乙氧化物和/或脂肪酸乙氧化物,且可以包括低和高HLB洗涤剂的混合物。所述配方还可以含有螯合剂,例如EDTA或NTA,含量为5~10%重量。
典型配方的实例包括(溶剂是或包括式(I)的化合物,特别是苯甲酸异丙酯,百分比是重量百分比):
重垢型硬表面清洁剂:
月桂基醚硫酸钠(27%活性) 13%
醇乙氧化物 4%
溶剂 4%
焦磷酸四钾 5%
防腐剂、香料和染料 根据需要
水 至100%
重垢型硬表面清洁剂可以原样使用或者在水中稀释后使用,用于典型的家庭基材和污垢。
金属脱脂配方-原样使用或者在水中稀释后使用(一般按1∶10比
例稀释):
1 溶剂 28%
阴离子磺酸盐洗涤剂 13%
乙氧化失水山梨醇酯 6%
异己醇 4%
水 至100%
2 溶剂 15%
低HLB醇乙氧化物 14%
高HLB醇乙氧化物 6%
季铵助水溶剂 2.5%
乙醇 4%
焦磷酸四钾 2%
EDTA Na4 1%
水 至100%
3 溶剂 33%
表面活性剂混合物* 17%
水 至100%
*-市售阴离子、非离子和阳离子表面活性剂的混合物
重垢型乳液清洁剂:
溶剂 60%
乙氧化脂肪酸 14%
醇乙氧化物 6%
水 至100%
铁路货车外部清洁剂
醇乙氧化物 10%
磷酸(85%) 40%
烷基磷酸酯 15%
溶剂 5%
水 至100%
胶印印刷板清洁剂
溶剂 15~20%
低HLB醇乙氧化物 12~14%
高HLB醇乙氧化物 14~16%
NTA(38%) 5~7%
二甘醇丁醚 2~3%
水 至100%
卡车清洗配方
氢氧化钠 2%
硅酸钠 1%
葡糖酸钠 2%
EDTANa4 1%
低泡润湿剂* 5%
溶剂 3%
Atsurf H1500 3%
水 至100%
*-醇乙氧化物-丙氧化物
该卡车清洗配方一般根据污垢等的性质,以1∶10~1∶50的水稀释液使用。基材一般为涂漆的金属。该配方可以在室温~60℃的温度下,通过喷雾而应用。
屏幕清洗配方
1 醇乙氧化物 1%
三乙醇胺 0.2~0.5%
溶剂 至100%
2 醇乙氧化物 2%
三乙醇胺 0.2%
焦磷酸四钾 2%
甘油 2.5%
异丙醇 42%
溶剂 42%
水 至100%
这些是浓缩物,一般在水中按1∶20~1∶100稀释后使用,用于清洗汽车挡风玻璃。
手清洁剂
溶剂 40%
非离子/阴离子表面活性剂混合物 12%
阴离子表面活性剂 0.5%
甘油 1%
矿物油 2%
水 至100%
该配方一般原样使用,以从手上除去油和油脂。
下列实施例举例说明本发明。所有份和百分比均基于重量,除非另有说明。
材料
Sol 1 苯甲酸异丙酯
Sol 2 苯甲酸(2-乙基己)酯
CSol 1 D-苧烯
CSol 2 N-甲基吡咯烷酮
Csol 3 苄醇
H1C 市售家庭硬表面清洁剂(Mr Muscle),从SC Johnson Wax得到
H1 加入1%重量Sol 1的H1C
H2C 市售家庭硬表面清洁剂,从Mc Brides得到
H2 加入1%重量Sol 1的H2C
D3 水基Sol 1(基本的)金属脱脂剂配方
D3C 水基Sol 2(基本的)金属脱脂剂配方
Surfl Synperonic91/2.5和Synperonic91/6的1∶1混合物,二者均得自Uniqema
Surf2 Monamulse DEB-一种非离子和阴离子表面活性剂的混合物,得自Uniqema
试验方法
擦洗试验
将用丙酮清洁过并用实验室绵纸干燥过的白色瓷砖表面,涂布试验用的厨房污垢,该污垢通过混合下列组分制备:碳黑7克,肉汤颗粒95克,猪油90克,明胶12克和水796克,总计1000克,并加热直至均匀。将该污垢涂布到瓷砖的顶边成为温热污垢的平坦的线,然后用加热丝缠绕的棒(6号棒)铺展过瓷砖表面,在预热过的70℃烘箱中焙烤该瓷砖1小时,并使其冷却到室温。使用Gardner分光光度计在标注的测量点(以使后面的测量可以在同一点进行),采用库仑分析法测量所述污垢(δE值);将有污垢的板夹住在擦洗试验平台上,并将三滴试验清洁剂加到该瓷砖表面。擦洗试验机是一个机械臂,在其末端带有海绵,该海绵可以重复擦洗测试表面以模拟擦洗清洁,在海绵上施加160N·m2的负荷,一次擦洗长度为12cm。该瓷砖按5擦(1擦=来回一次)一组进行擦洗,并测量试验部位的颜色。所评估的清洁效果是擦洗的瓷砖的δE值比初始瓷砖的δE值减少的差值。可以进行多次试验并采用平均结果。
金属脱脂
将同一大小和材料的钢试样在丙酮中清洁并在空气中干燥。清洁试样称重(以克计,精确至0.1毫克)并涂布污垢。试验污垢是下列组分的混合物:硬脂酸15克,油酸15克,固体植物油脂30克,润滑油(例如机油)25克,和十八烷醇(硬脂醇)8克,总计93克。将各试样浸渍到已知温度的熔化试验污垢中,浸没至在试样上预先做好的标记处,浸渍约2秒,将试样在大气中冷却,直到污垢固化,然后将试样再称重以确定在试样上的污垢重量(约0.2克)。
将试验清洁溶液,即含有3%重量试验溶剂的溶液和3%重量的Surf1的水性清洁混合物,放置在Zeltex Vista Color试验机装置中,并使其达到试验温度,通常为40或60℃。将各试样浸入到试验溶液中,以垂直运动方式上下运动预定时间(足以实际比较各试验溶液),从试验溶液中取出,使其在大气中干燥,并再次称重以确定去掉的污垢量。所评估的清洁效果是通过洗涤除掉的初始存在的污垢的重量百分比。进行多次试验,取平均结果。
油漆剥离
金属板的表面喷上丙酮,以清洁金属板并在室温下于空气中干燥。使用1英寸(约25mm)刷子在金属板上涂布一平层试验油漆,并在室温下干燥7天。
使用吸液管将2毫升试验溶剂加到涂漆的表面成连续的线,对于每种试验溶剂线的长度相等。然后在30、60和90分钟(测试纯溶剂)或在10、20和30分钟(测试溶剂混合物)观察效果。采用从1=差(无剥离)到5=好(完全除掉油漆)的油漆剥离性能分级标准记录观察结果和效果’。
注:丙烯酸漆要求在试验时间后用工业用薄纸擦去溶剂(一种沿溶剂线从上到下的擦拭动作,对每个试验施加类似的手的压力),以评估油漆脱除效果。
实施例1
采用擦洗清洁试验测试式(I)化合物(苯甲酸异丙酯)促进市售的表面清洁洗涤剂效果的能力。单独使用市售材料进行比较试验。结果列于下表1中,从这些结果可以清楚地看到,包括了苯甲酸异丙酯可以显著地提高清洁剂的效果。
表1
实施例2
实施例号 | 清洁剂 | 清洁效率(%) | |||
摩擦次数 | |||||
0 | 5 | 10 | 15 | ||
C1.1 | HlC | 0 | 34 | 68 | 72 |
1.1 | H1 | 0 | 52 | 79 | 88 |
C1.2 | H2C | 0 | 52 | 62 | 72 |
1.2 | H2 | 0 | 59 | 86 | 91 |
比较苯甲酸异丙酯和苧烯(作为对环境具有低的影响的清洁溶剂而受到重视)作为水基清洁体系的组分的性能。比较的擦洗清洁试验的结果列于表2,从中可以看到,包括苯甲酸异丙酯的配方比苧烯配方的结果更好。
表2
实施例3
实施例号 | 清洁剂 | 清洁效率(%) | |||
摩擦次数 | |||||
0 | 5 | 10 | 15 | ||
C1.2 | D3C | 0 | 23 | 37 | 49 |
1.2 | D3 | 0 | 59 | 70 | 88 |
使用苯甲酸异丙酯作为在水中的清洁溶剂的水基金属脱脂配方被测试用于金属脱脂,试验时间为5或10分钟。使用d-苧烯作为溶剂制备类似的制剂,并进行测试以作为比较。试验结果(多次试验的平均值)列于下表3。结果又一次表明,苯甲酸异丙酯配方比苧烯配方性能更好,特别是在较短的试验中。
表3
实施例4
实施例号 | 配方 | 时间(分钟) | 效率(%) |
3.1 | D3 | 5 | 44 |
3.2 | D3 | 10 | 57 |
C3.1 | DC3 | 5 | 24 |
C3.2 | DC3 | 10 | 54 |
研究了Sol1和Sol2用作脱除醇酸漆、丙烯酸漆和氨基甲酸乙酯漆的油漆脱除剂的能力。采用上述方法,使用纯溶剂Sol1和Sol2、用作比较的CSol1和CSol2及Sol1和Sol2与Csol3和Csol4的混合物进行试验。结果列于下表4。
表4
实施例5
实施例号 | 溶剂 | 共溶剂 | 油漆种类 | ||||
类型 | % | 类型 | % | 醇酸光漆 | 丙烯酸漆 | 氨基甲酸乙酯漆 | |
4.1 | Sol1 | 100 | - | - | 0 | 5 | 5 |
C4.1 | CSol1 | 100 | - | - | 0 | 0 | 5 |
4.2 | Sol2 | 100 | - | - | 5 | 5 | 5 |
C4.2 | CSol2 | 100 | - | - | 5 | 5 | 5 |
4.3 | Sol2 | 90 | CSol2 | 10 | 3 | 5 | 5 |
C4.3 | CSol1 | 90 | CSol2 | 10 | 0 | 0 | 4 |
4.4 | Sol1 | 90 | CSol2 | 10 | 5 | 5 | 5 |
4.5 | Sol2 | 90 | CSol3 | 10 | 4 | 5 | 5 |
C4.4 | CSol1 | 90 | CSol3 | 10 | 0 | 4 | 1 |
4.6 | Sol2 | 80 | CSol2 | 20 | 4 | 5 | 5 |
4.7 | Sol1 | 80 | CSol2 | 20 | 5 | 5 | 5 |
4.8 | Sol2 | 80 | CSol3 | 20 | 5 | 5 | 5 |
C4.5 | CSol1 | 80 | CSol3 | 20 | 0 | 3 | 1 |
使用机油作为污垢(代替在上述标准方法中使用的合成污垢),研究式1表示的化合物去除污垢的能力。结果列于下表5。表5
实施例6
实施例号 | 溶剂 | 温度(℃) | 效率(%) |
5.1 | Sol2 | 20 | 89.4 |
5.2 | Sol2 | 40 | 88.5 |
制备一种微乳液洗涤剂配方,具有如下组成:
材料 %重量
Surf 2 28.3
Sol 1 44
水 至100
测试该配方的9∶1水稀释物脱除上述试样上的合成污垢,处理温度为40℃,处理时间10分钟。测得的脱脂效率为97%。
Claims (9)
1.一种清洁基材的方法,该方法包括使被清洁的基材与包括下式(I)的至少一种化合物的组合物,特别是水性组合物接触:
(R2)p-Ph-(CH2)m-COO-(AO)n-R1 (I)
其中,
R1是C1~C20的烷基或链烯基;
AO是亚烷氧基,并且沿(聚)亚烷氧基链可以改变;
n是0或1~100;
m是0,1或2;并且
Ph是苯基,该苯基可以被(R2)p基团取代,其中每个R2独立地是C1~C4的烷基或烷氧基,并且p是0,1或2。
2.如权利要求1的方法,其中m、n和p都为0。
3.如权利要求1或2的方法,其中R1是C1~C10烷基,优选是C3~C5支链烷基。
4.如权利要求1-3中任意一项的方法,其中式(I)化合物是或包括苯甲酸异丙酯。
5.如权利要求1-4中任意一项的方法,该方法用于通过使基材与包括至少一种式(I)化合物的组合物,特别是水性组合物接触而脱除基材,特别是金属基材上的油脂。
6.如权利要求1-4中任意一项的方法,该方法用于通过使需要清洁的硬表面与包括至少一种式(I)化合物和表面活性剂,特别是清洁性表面活性剂及助洗剂或碱的组合物,特别是水性组合物接触而清洁硬表面。
7.如权利要求1-4中任意一项的方法,该方法用于从表面上清除乱涂乱写,其中使被清洁的表面与包括至少一种式(I)化合物和表面活性剂的组合物,特别是水性组合物接触。
8.如权利要求1-4中任意一项的方法,该方法用于从基材上剥离油漆,其中使涂漆的基材与包括至少一种式(I)化合物和表面活性剂,特别是清洁性表面活性剂的组合物,特别是水性组合物接触。
9.如权利要求1-4中任意一项的方法,该方法用于钻探设备清洁,其中使被清洁的钻探设备表面与包括至少一种式(I)化合物和表面活性剂,特别是清洁性表面活性剂的水性微乳液组合物接触。