CN1428385A - Liquified porcelain and its preparation method - Google Patents
Liquified porcelain and its preparation method Download PDFInfo
- Publication number
- CN1428385A CN1428385A CN 01136980 CN01136980A CN1428385A CN 1428385 A CN1428385 A CN 1428385A CN 01136980 CN01136980 CN 01136980 CN 01136980 A CN01136980 A CN 01136980A CN 1428385 A CN1428385 A CN 1428385A
- Authority
- CN
- China
- Prior art keywords
- major ingredient
- preparation
- resin
- epoxy
- resins
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a liquefied porcelain and its preparation method. Its composition includes main material: epoxy resin, linear epoxy resin, polyurethane resin, precipitate barium sulfate, rutile powder, xylene, cyclohexanone, amino resin, talcum powder, and solidifying agent T31. Its preparation method includes the following steps: adding epoxy resin and xylene into reaction still, adding cyclodexanone solvent, filtering liquid resin, feeding liquid resin into grinding machine, at the same time adding polyurethane resin, rutile powder, titanium pigment, precipitate barium sulfate, amino resin and talcum powder, mixing, grinding, filtering, mixing with pigment in rotary-drum machine so as to obtain main material, then said main material is mixed with solidifying agent according to a certain ratio, it can be used.
Description
One, technical field
The present invention relates to a kind of coating and preparation method thereof.
Two, background technology
At present, the coating that uses on cement, timber, plastics, gypsum, glass reinforced plastic and metal mainly is paint, uses back and base material avidity poor,, thereby intensity is not high, and mill property is poor, smooth finish is also bad.
Three, technical scheme
Of the present invention reporting provides a kind of liquefied ceramic prescription and preparation method thereof, and for realizing described purpose, the formulation weight per-cent of liquefied ceramic of the present invention is:
Major ingredient: Resins, epoxy 601E-20 10～30%
Resins, epoxy 604E-12 10-20%
Linear loop epoxy resins 621 4-12%
Urethane resin 2-7%
Process white 2-7
Rutile Cornstarch 25-40%
Dimethylbenzene 10-30%
Pimelinketone 10-25%
Aminoresin 2-7%
Talcum powder 2-9% solidifying agent: the preparation process of T31 35-70% major ingredient major ingredient is as follows: a) add Resins, epoxy and dimethylbenzene in reactor, add cyclohexanone solvent again, warming while stirring to 110 ℃-125 ℃, constant temperature 2-3 hour to all dissolvings, take out from reactor after being cooled to 35-40 ℃ then and put into container; B) with in the container liquid resin filter; C) liquid resin after will filtering is introduced shredder, with after advancing to add urethane resin, rutile Cornstarch, process white, aminoresin, talcum powder and mixing, grinds at normal temperatures 2-4 hour; D) ground material is used 180-240 purpose strainer filtering; E) material after filtering adds in the jar rolling machine simultaneously with the pigment of the 1-5% of material and mixes, and grinds at normal temperatures 2～4 hours, can finish paintedly, just makes the finished product major ingredient.
Solidifying agent is to adopt commercially available prod T31 or T32 epoxy curing agent.This solidifying agent be contain the fatty amine of phenyl ring must the property compound.During use, can use after major ingredient and solidifying agent be mixed in proportion, and according to the different purposes consumption of each composition at a high speed.
The present invention compared with prior art has following advantage: nontoxic, unleaded, and existing good snappiness, two have suitable hardness; Waterproof, fire-retardant, wear and shock-resistant, antiacid alkali, and have the good smooth finish of committee, and with cement, metal, timber, plastics, gypsum, glass reinforced plastic, solid fiberboard, wax fabulous avidity being arranged all, coverage and conjugation are fabulous.
Four, specific embodiment
1, preparation major ingredient
(1) in reactor, add 4000 gram Resins, epoxy 601E-20 and dimethylbenzene,
6000 gram Resins, epoxy 604E-12, the linear loop epoxy resins of 3000 grams and
The dimethylbenzene of 5000 grams adds 6800 cyclohexanone solvents that restrain again, and the limit is stirred
Mix the limit and be warmed up to 115 ℃, constant temperature was lowered the temperature to all dissolvings in 3 hours then
From reactor, take out after 40 ℃ and put into container;
(2) with in the container liquid resin filter;
(3) liquid resin after the filtration is introduced shredder, with the poly-ammonia that advance to add 2800 grams
The rutile Cornstarch R930 of ester resin 7110J4,9000 grams, 1800 grams
Process white, 1500 the gram aminoresin 590-3,1800 the gram talcums
Powder ground 3 hours after mixing at normal temperatures;
(4) with ground material with 190 purpose strainer filterings;
(5) the middle network yellow ultramarines of 800 of material after the filtration and material grams add simultaneously
Mix in the jar rolling machine, ground at normal temperatures 2 hours, can finish painted,
Just make the finished product major ingredient.
2, preparation liquid porcelain
The major ingredient of getting 1 kilogram mixes with 0.3 kilogram T31 material, stir in network yellow liquefied ceramic.
Claims (2)
1, a kind of liquefied ceramic prescription is characterized by: the preparation component is: major ingredient: Resins, epoxy 601E-20 10～30%
Resins, epoxy 604E-12 10-20%
Linear loop epoxy resins 621 4-12%
Urethane resin 2-7%
Process white 2-7
Rutile Cornstarch 25-40%
Dimethylbenzene 10-30%
Pimelinketone 10-25%
Aminoresin 2-7%
Talcum powder 2-9% solidifying agent: T31 35-70% major ingredient
2, a kind of preparation method of liquefied ceramic as claimed in claim 1, it is characterized in that: the preparation process of major ingredient is as follows: add Resins, epoxy and dimethylbenzene in (1) reactor, add cyclohexanone solvent again, warming while stirring to 110 ℃-125 ℃, constant temperature 2-3 hour to all dissolvings, are cooled to then to take out from reactor behind 40 ℃ of the 35-to put into container; (2) in the container liquid resin filter; (3) liquid resin after will filtering is introduced shredder, with after advancing to add urethane resin, rutile Cornstarch, process white, aminoresin, talcum powder and mixing, grinds at normal temperatures 2-4 hour; (4) ground material is used 180-240 purpose strainer filtering; (5) material after filtering adds in the jar rolling machine simultaneously with the pigment of the 1-5% of material and mixes, and grinds at normal temperatures 2～4 hours, can finish paintedly, just makes the finished product major ingredient.
During use, can use after major ingredient and solidifying agent be mixed in proportion, and according to the different purposes consumption of each composition at a high speed.