CN1416979A - Double-layered alkali grain covering agent for middle ladle - Google Patents
Double-layered alkali grain covering agent for middle ladle Download PDFInfo
- Publication number
- CN1416979A CN1416979A CN 01132125 CN01132125A CN1416979A CN 1416979 A CN1416979 A CN 1416979A CN 01132125 CN01132125 CN 01132125 CN 01132125 A CN01132125 A CN 01132125A CN 1416979 A CN1416979 A CN 1416979A
- Authority
- CN
- China
- Prior art keywords
- slag
- molten steel
- covering agent
- double
- cao
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a double-layered alkali grain heat-insulting covering agent for middle ladle. The heat-insulting covering agent consists of top slag in 10-50 wt% and bottom slag in 50-90 wt%. The bottom slag consists of SiO2 8-15 wt%, CaO 50-60 wt%, MgO 10-20 wt%, Al2O3 1-5 wt%, Fe2O3 1-3 wt%, and fixed carbon 0.01-1 wt%. The top slag consists of SiO2 85-93 wt%, CaO 0.001-3 wt%, MgO 0.001-3 wt%, Al2O3 0.001-3 wt%, Fe2O3 0.003-0.5 wt%, and fixed carbon 0.01-1 wt%. The heat-insulting covering agent forms two layers of slag, the bottom layer covers molten steel to prevent secondary oxidation, reduce carbon content in molten steel and adsorb alumina floating to the surface of molten steel, and the top layer in porous and loose structure covers molten steel to prevent incrusting and carburization.
Description
Technical field
The present invention relates to a kind of alkali grain tundish thermal-insulating covering agent, particularly a kind of double-layered alkali grain tundish thermal-insulating covering agent.
Background technology
The alkaline molten steel tundish thermal-insulating covering agent that at home and abroad generally adopts must add charring rice husk thermal insulation at present, but because the charring rice husk carbon content up to becoming 30-50%, causes molten steel recarburization easily, also causes environmental pollution.
Summary of the invention
The objective of the invention is to overcome the alkaline molten steel tundish insulation of generally adopting in the prior art and cover, must add charring rice husk thermal insulation, cause molten steel recarburization easily, also cause environmental pollution problems.Technical solution of the present invention design double-layered alkali grain tundish thermal-insulating covering agent, it is characterized in that: thermal-insulating covering agent is made of end slag and top slag, the percentage by weight of end slag and top slag is: top slag 10%-50%, end slag 50-90%, (1) end slag is made of following composition and percentage by weight: SiO
28-15%, CaO 50-60%, MgO 10-20%, Al
2O
31-5%, Fe
2O
31-3%, fixed carbon 0.01-1%, (2) top slag is made of following composition and percentage by weight: SiO
285-93%, CaO 0.001-3%, MgO 0.001-3%, Al
2O
30.001-3%, Fe
2O
30.003-0.5%, fixed carbon 0.01-1%.Advantage of the present invention is to make the heat preserving agent of adding form two-layer slag up and down, the bottom slag covers the molten steel face, prevent the secondary oxidation of molten steel, reduce the content of carbon in the molten steel, the effect that can adsorb the aluminium oxide that floats in the molten steel is arranged, the upper strata slag can be loose porous spongy covering molten steel, prevents the molten steel crust, avoids carburetting.
The specific embodiment
Below in conjunction with embodiment the present invention is described in further detail,
Respectively the end slag and the top slag of thermal-insulating covering agent are prepared (1) end slag: get SiO
215 kilograms, 60 kilograms of CaO, 19 kilograms of MgO, Al
2O
35 kilograms, Fe
2O
30.5 kilogram, 0.5 kilogram in fixed carbon stirs into the mixture of double centner, and (2) top slag is got SiO
292.5 kilogram, 3 kilograms of CaO, MgO1.5 kilogram, Al
2O
32 kilograms, Fe
2O
30.5 kilogram, 0.5 kilogram in fixed carbon stirs into the mixture of double centner.Get 80 kilograms of end slags, 20 kilograms of top slags then, ladle in the middle of the disposable input, double-layered alkali grain molten steel tundish thermal-insulating covering agent forms double-deck slag at once, end slag melting point is low, form molten slag layer rapidly and cover the molten steel face, because lower oxyde content is low, can prevent secondary oxidation of steel, because fixedly phosphorus content is low, can be to molten steel recarburization, because covering MgO saturation value is low in the middle of the alkalescence, is lined with compatibility preferably with alkaline tundish, top slag melting point height, be spongy loose attitude heat-insulation layer, can improve the crust drawback, again because of fixed carbon content is low, the sorrow of no carburetting.
Claims (1)
- Double-layered alkali grain tundish thermal-insulating covering agent is characterized in that: thermal-insulating covering agent is made of end slag and top slag, and the percentage by weight of end slag and top slag is:Top slag 10%-50%, end slag 50-90%,(1) end slag is made of following composition and percentage by weight:SiO 2 8-15%,CaO 50-60%MgO 10-20%Al 2O 3 1-5%Fe 2O 3 1-3%Fixed carbon 0.01-1%,(2) the top slag is made of following composition and percentage by weight:SiO 2 85-93%,CaO 0.001-3%MgO 0.001-3%Al 2O 3 0.001-3%Fe 2O 3 0.003-0.5%Fixed carbon 0.01-1%.