CN1778493A - Cap agent with light alkaline particle steel coating - Google Patents
Cap agent with light alkaline particle steel coating Download PDFInfo
- Publication number
- CN1778493A CN1778493A CNA2004100843367A CN200410084336A CN1778493A CN 1778493 A CN1778493 A CN 1778493A CN A2004100843367 A CNA2004100843367 A CN A2004100843367A CN 200410084336 A CN200410084336 A CN 200410084336A CN 1778493 A CN1778493 A CN 1778493A
- Authority
- CN
- China
- Prior art keywords
- steel coating
- cap agent
- alkaline particle
- particle steel
- ladle
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A light-weight alkaline particle used as the covering agent of steel ladle contains siO2 (18-26 Wt%), CaO (26-34), MgO (6-12), Al2O3 (5-8), Fe2O3 (0.5-2.0), and stabilized C (18-26). Its advantages are low specific bulk weight, high insulating performance, and high effect to prevent oxidization of molten steel and decrease the corrosion to refractory of ladle.
Description
Technical field
The present invention relates to a kind of ladle covering agent, particularly a kind of cap agent with light alkaline particle steel coating.
Background technology
The basic steel covering agent bulk density that adopts both at home and abroad is bigger at present, though have the performance of certain dross inclusion adsorption, heat insulation effect is not good.Though have a heat-insulating property preferably and acid chrome black covering agent bulk density is less, cause secondary oxidation of steel easily, and acid coverture can cause erosion to the anti-material of alkaline ladle.
Summary of the invention
The purpose of this invention is to provide a kind of alkaline granule steel ladle covering agent that reducible oxide-based composition content is low, bulk density is little that has.The present invention designs a kind of cap agent with light alkaline particle steel coating, it is characterized in that having following constituent and percentage by weight to constitute: SiO
218%~26%; CaO26%~34%; MgO6%~12%; Al
2O
35%~8%; Fe
2O
30.5%~2%; Fixed carbon 18%~26%.Bulk density is 0.4~0.7g/cm
3Advantage of the present invention is: the bulk density of coverture is little, has good heat-insulating property; And containing higher fixed carbon, the heat that can utilize its chemical reaction to produce further remedies the heat loss of molten steel, improves heat insulation effect; Fusing point is suitable, can form three layers of melting structure rapidly, and reducible oxide-based composition content is low, can prevent secondary oxidation of steel; Basicity CaO/SiO
21.1~1.8, have field trash ability in certain absorption molten steel, can not corrode the ladle basic refractory, help prolonging the bag age of ladle.
Concrete mode
Below in conjunction with embodiment the present invention is elaborated:
Embodiment 1: get SiO
225 kilograms, CaO31 kilogram, MgO10 kilogram, Al
2O
37.5 kilogram, Fe
2O
31.5 kilogram, 25 kilograms in fixed carbon.Be mixed into 100 kilograms of mixtures, add suitable quantity of water and mix thoroughly and be baked to moisture less than 1% after making the particle of Φ 8~10mm * 8~25mm by extruder grain, packing again after the screening.
Embodiment 2: get SiO
222 kilograms, CaO33 kilogram, MgO11 kilogram, Al
2O
37 kilograms, Fe
2O
31 kilogram, 26 kilograms in fixed carbon.Be mixed into 100 kilograms of mixtures, add suitable quantity of water and mix thoroughly and be baked to moisture less than 1% after making the particle of Φ 8~10mm * 8~25mm by extruder grain, packing again after the screening.This coverture forms three-decker rapidly after adding ladle during use.Because the bulk density of coverture is little, has good heat-insulating property; And contain higher fixed carbon, and utilize the heat of its chemical reaction generation, can further remedy the heat loss of molten steel, improve heat insulation effect; Because reducible oxide-based composition content is low, can prevent secondary oxidation of steel; Because coverture is an alkalescence, can not corrode the ladle basic refractory, helps prolonging the bag age of ladle.
Claims (2)
1, a kind of cap agent with light alkaline particle steel coating is characterized in that having following constituent and percentage by weight to constitute:
SiO
2?18%~26%,
CaO?26%~34%,
MgO?6%~12%,
Al
2O
3?5%~8%,
Fe
2O
3?0.5%~2%,
Fixed carbon 18%~26%.
2, by the described a kind of cap agent with light alkaline particle steel coating of claim 1, it is characterized in that: the bulk density of cap agent with light alkaline particle steel coating is 0.4~0.7g/cm
3