CN1416763A - Variable-temperature cup - Google Patents
Variable-temperature cup Download PDFInfo
- Publication number
- CN1416763A CN1416763A CN 02147489 CN02147489A CN1416763A CN 1416763 A CN1416763 A CN 1416763A CN 02147489 CN02147489 CN 02147489 CN 02147489 A CN02147489 A CN 02147489A CN 1416763 A CN1416763 A CN 1416763A
- Authority
- CN
- China
- Prior art keywords
- cup
- temperature
- appearance
- variable
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The variable-temperature cup as one kind of cup with new outer decoration features the variable-temperature paint coated to the surface of the cup. The variable-temperature paint coated can be of one or several kinds on the decoration requirement. The present invention can open a completely new decoration form of cup and the variable-temperature cup can bring magic feeling.
Description
The cup that the present invention relates to use in the daily life, particularly a kind of appearance color can be with its cup Variable-temperature cup that (comprising bowl cover and cup), temperature traverse changed.
Existing cup such as common teacup, thermos cup, health-care cup etc., their appearance all has certain decoration, has plenty of the enamel of barbecue and draws, and has plenty of glazing and draws, mostly be the character pattern that coating is drawn greatly, these decorate the sales promotion of product and to bring the aesthetic feeling aspect to play a part to people certain.But so decorative form does not almost change for many years, makes to seem cup appearance decorative form outmoded, old stuff does not have vigor, and the effect aspect sales promotion is more and more littler.
Purpose of the present invention is to propose the cup that a kind of appearance is brand-new decorative form for impelling cup to sell, i.e. the color of cup appearance or the pattern Variable-temperature cup that can change with the cup temperature traverse.
Can realize purpose of the present invention by following technical proposals, a kind of cup is characterized in that, the appearance of this cup scribbles temperature and becomes coating.
The cup appearance is a metallic material, and the composition formation that its temperature becomes coating is by weight percentage:
Thermosetting acrylic resin 43--55%
Amino resin 14--20%
Epoxy resin 3--5%
Temperature variable pigments 22--30%
Wetting dispersing agent 1--2%
Levelling agent 1--2%
Butanols 3--5%
Dimethylbenzene 3--4%
Ethylene glycol monobutyl ether 2--3%
The cup appearance is a non-metallic material, and the composition formation that its temperature becomes coating is by weight percentage:
Thermoplastic acrylic resin 45--55%
Cellulose acetate 10--20%
Temperature variable pigments 25--30%
Wetting dispersing agent 1--2%
Levelling agent 1--2%
Ethylene glycol monobutyl ether 3--4%
Dimethylbenzene 3--4%
Butanone 2--3%
The warm variable pigments that temperature becomes in the coating is determined according to different decoration needs.
Effect of the present invention is, it has started a kind of cup appearance brand new decorative form, it makes full use of cup and is pouring hot water into or sealing in this characteristics that change of its cup temperature on hand, in the cup appearance, coat the temperature coating that varies with temperature and change, make the appearance color of cup, pattern changes with the cup variation of temperature, thereby give people a kind of pleasantly surprised, in surprise, the sensation of reverie, give a kind of brand new of people visual effect changeable, make people produce strong interest to this phenomenon, thereby greatly cause the desire that people buy cup, reach the purpose of cup sales promotion.If produce 1,000,000,000 cups at present by China, after becoming coating, the use temperature increases production 3%, will increase by 3,000 ten thousand cups, the output value can increase billions of units.
Below in conjunction with embodiment the present invention is further set forth:
Embodiment 1, and the appearance of cup is a metallic material, its temperature of selecting for use become paint ingredient constitute by weight percentage into:
Thermosetting acrylic resin 46%
Amino resin 15%
Epoxy resin 4%
Temperature variable pigments 24%
Wetting dispersing agent 1%
Levelling agent 1%
Butanols 4%
Dimethylbenzene 3%
Ethylene glycol monobutyl ether 2%
Wherein warm variable pigments is difference according to the difference of decorating requirement, as the discoloring temperature that requires temperature to become coating is 37 ℃, color before the variable color is green, color after the variable color is yellow, can select warm variable pigments by this requirement, prepare required temperature by the composition formation of above-mentioned temperature change coating again and become coating, the temperature for preparing is become coating, be coated in the appearance of cup according to a conventional method.According to the needs of decorating, the appearance of cup can be coated with a kind of temperature and become coating, also can be coated with two or more temperature and become coating, and coating both can show literal, also can show various patterns, mixed Chinese zodiac symbolic animal of the birth year as " happy birthday "; " I love you " mixes a red rose etc.
Embodiment two: the appearance of cup is a non-metallic material, its temperature of selecting for use become paint ingredient constitute by weight percentage into:
Thermoplastic acrylic resin 48%
Cellulose acetate 12%
Temperature variable pigments 27%
Wetting dispersing agent 1%
Levelling agent 1%
Ethylene glycol monobutyl ether 3.5%
Dimethylbenzene 3.5%
Butanone 3%
Its warm variable pigments is by the requirement different choice of decorating.As requiring the discoloring temperature of temperature change coating to be 52 ℃, variable color is preceding to be redness, is blue after the variable color, then requires the warm variable pigments of selection according to this, and becomes coating according to the required temperature of composition formation preparation of above-mentioned temperature change coating.According to a conventional method temperature is become coating and be coated in the cup appearance.The cup appearance can be coated with a kind of temperature and become coating, also can be coated with several temperature and become coating.As be coated with the temperature that 3 kinds 32 ℃, 39 ℃, 45 ℃ beginning temperature become and become coating, then 3 kinds of different variations will appear in cup appearance situation about heating up gradually at cup.Different variations will appear in different combinations, can occur several, tens kinds and even different literal, pattern and the combination appearance of hundreds of kind on a cup.This kind visual effect changeable will greatly cause people's curiosity, makes people produce strong interest to it, produces strong desire to purchase then.
Claims (3)
1, a kind of cup is characterized in that, the appearance of this cup scribbles temperature and becomes coating.
2, must ask 1 described cup by power, it is characterized in that, when the cup appearance is that its warm composition formation that becomes coating of metallic material is by weight percentage:
Thermosetting acrylic resin 43--55%
Amino resin 14--20%
Epoxy resin 3--5%
Temperature variable pigments 22--30%
Wetting dispersing agent 1--2%
Levelling agent 1--2%
Butanols 3--5%
Dimethylbenzene 3--4%
Ethylene glycol monobutyl ether 2--3%
3, by the described cup of claim 1, it is characterized in that, when the cup appearance is that its warm composition formation that becomes coating of non-metallic material is by weight percentage:
Thermoplastic acrylic resin 45--55%
Cellulose acetate 10--20%
Temperature pigment 25--30%
Wetting dispersing agent 1--2%
Levelling agent 1--2%
Ethylene glycol monobutyl ether 3--4%
Dimethylbenzene 3--4%
Butanone 2--3%