CN1413796A - Self-drill brazing filler material of aluminium alloy and aluminium base composite and preparation method - Google Patents
Self-drill brazing filler material of aluminium alloy and aluminium base composite and preparation method Download PDFInfo
- Publication number
- CN1413796A CN1413796A CN 02133083 CN02133083A CN1413796A CN 1413796 A CN1413796 A CN 1413796A CN 02133083 CN02133083 CN 02133083 CN 02133083 A CN02133083 A CN 02133083A CN 1413796 A CN1413796 A CN 1413796A
- Authority
- CN
- China
- Prior art keywords
- gross weight
- self
- alloy
- brazing filler
- solder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A medium-temp high-strength solder without flux for Al alloy and Al-base composition contains Zn (80.6-93.71 wt.%), A (3.3-8.0), Cu (2-5), Mg (0.4-1.5), Ag (0.2-1.5), Si (0.1-1), Mn (0.2-2), Ni (0.08-0.3) and RE (0.01-0.1). It is prepared through preparing molten Al-Si alloy, adding Cu, MN and Ni to obtain intermediate alloy, and respectively adding Zn, Ag, Mg and RE under a certain condition.
Description
Technical field: the present invention relates to prescription of a kind of temperature that is used for aluminium alloy and aluminum matrix composite, high-strength, solder without soldering acid material and preparation method thereof.
Background technology: at present, the solder that is used for aluminium alloy and matrix material has following several: (1) Sn-Zn system, Sn-Pb system, Sn-Zn-Cd is (fusing point of these three kinds of solders is between 150~260 ℃), its shortcoming is that the intensity of solder is lower, solidity to corrosion is relatively poor, after its soldering, the mechanical property of joint is not good: (2) Zn-Cd system, Zn-Sn is (fusing point of these two kinds of solders is between 260~370 ℃), its shortcoming is, contain toxic Elements C d in the solder, cause environmental pollution, and the harm solder prepares personnel and solder user's health, and simultaneously the solidity to corrosion of solder is general, and is bigger to the influence of mother metal; (3) Zn-Al system, (fusing point of these two kinds of solders is between 370~450 ℃ in Zn-Al-Cu system, disclosed at present Zn-Al system and Zn-Al-Cu brazing filler metal mainly contain following several: Zn72Al28, Zn95Al5, Zn93Ag4.5Al2.5, Z65Al20Cul5, its advantage is that solder intensity is higher, corrosion resisting property is good, and it is less to the influence of mother metal, but because the Zn constituent content in these solders is higher, the equivalent coefficient of Zn is also higher, easily form compound between some friable metals in the solder, and Zn content is too high, easily cause in the brazing process corrosion phenomenon taking place at the interface, reduced the whole mechanical property of joint.Aspect solder prepares, because Zn is more crisp, be difficult to make brazing wire commonly used with the stringy method, must adopt the method for casting to cast bar-shaped solder, but palpus prefabricated mould, the casting technique more complicated, the Foundry Production rate is low, solder liquid mobile relatively poor in mould in castingprocesses, and yield rate is lower, thereby preparation cost is higher, solder surface smoothness after the casting is lower, and the solder surface is often with burr, and outward appearance is not attractive in appearance, simultaneously, because the fusing point of Si is higher, and Cu, Ni, the solubleness of alloying elements such as Mn in Zn alloy liquid is lower, thereby in the extremely difficult adding alloy of these elements liquid, existing solder technology of preparing does not address the above problem as yet fully, thereby has hindered the development and the development of solder technology.
Summary of the invention: the present invention is directed to the problems referred to above a kind of whole mechanics and the aluminium alloy of mechanical property and the self-drill brazing filler and preparation method of aluminum matrix composite that can improve alloy is provided, its objective is such realization: the self-drill brazing filler of aluminium alloy and aluminum matrix composite, it is by Zn, Al, Cu, Mg, Ag, Si, Mn, Ni and rare earth are formed, each component is respectively by weight ratio: Zn:80.6~93.71%, Al:3.3~8.0%, Cu:2.0~5.0%, Mg:0.4~1.5%, Ag:0.2~1.5%, Si:0.1~1.0%, Mn:0.2~2.0%, Ni:0.08~0.3%, rare earth 0.01~0.1%, the preparation method of the self-drill brazing filler of aluminium alloy and aluminum matrix composite is: a, the Al piece that accounts for solder gross weight 3.3~8.0% is put into crucible, then crucible being placed Heating temperature is in 650~800 ℃ the process furnace, treat to put into after Al melts fully the crystallization Si piece that accounts for solder gross weight 0.1~1.0%, be incubated 10~20 minutes, get Al-Si master alloy liquid; B, the Cu that will account for solder gross weight 2.0~5.0%, 0.2~2.0% Mn, 0.08~0.3% Ni join in the Al-Si master alloy liquid, the temperature of process furnace is increased to 700~900 ℃, treat that each alloy fully melts the back pouring and becomes block, get the Al-Si-Cu-Mn-Ni master alloy; C, the Zn piece that will account for solder gross weight 80.6~93.71% are put into crucible, then crucible is placed in the process furnace, furnace temp is 650~800 ℃, after treating that the Zn piece melts fully, the Al-Si-Cu-Mn-Ni master alloy is joined in the Zn liquid, and furnace temp is increased to 650~900 ℃, after treating that the Al-Si-Cu-Mn-Ni master alloy melts fully, add the Ag that accounts for solder gross weight 0.2~1.5%, after treating that Ag melts fully, adding accounts for the Mg of solder gross weight 0.4~1.5% and 0.01~0.1% rare earth; D, the gained solution-cast is become ingot casting, be the self-drill brazing filler of aluminium alloy and aluminum matrix composite.The invention has the advantages that: the fusing point of this solder is lower: aluminium commonly used is 520~590 ℃ with the fusing point of solder-al-si filler metal, and the fusing point of solder of the present invention is 381~390 ℃, and the fusing point of solder reduces greatly; Do not need to use brazing flux in the brazing process, and aluminium commonly used must be with brazing flux to remove the oxide film on aluminium surface before welding with solder-al-si filler metal; Wettability to aluminium alloy and matrix material thereof is good, and this solder is 19 ° in the wetting angle of surface of aluminum plate; Can obtain high-intensity joint, adopt the aluminium sheet of this solder welding, its strength of joint can reach 160MPa, and the intensity of joint is about 120MPa behind the employing al-si filler metal soldering aluminium sheet; After the soldering, the corrosion resistance of joint is preferable; The applicable surface of this solder is wider, can be used for the soldering of fine aluminium, heat-treatable aluminum alloy, cast aluminium, wrought aluminium, corrosion-resisting aluminium, duralumin, ultralumin, high strength alumin ium alloy, aluminium-lithium alloy, aluminum matrix composite, fine copper, copper alloy and Solder for Al-Cu Joint Welding foreign material; The solder manufacturing process is simple, cost is lower, is convenient to extensive, production in enormous quantities; This preparation method has solved high-melting-point, the adding difficult problem of high melting point alloy in Zn alloy liquid, and joint form is butt joint, overlap joint, T-joint, pipe-tube stub, pipe-plate joint, plate-plate joint etc.
Embodiment one: the self-drill brazing filler of aluminium alloy and aluminum matrix composite is by Zn in the present embodiment, Al, Cu, Mg, Ag, Si, Mn, Ni and rare earth are formed, each component is respectively by weight ratio: Zn:80.6~93.71%, Al:3.3~8.0%, Cu:2.0~5.0%, Mg:0.4~1.5%, Ag:0.2~1.5%, Si:0.1~1.0%, Mn:0.2~2.0%, Ni:0.08~0.3%, rare earth 0.01~0.1%, the preparation method of the self-drill brazing filler of aluminium alloy and aluminum matrix composite is: a, the Al piece that accounts for solder gross weight 3.3~8.0% is put into crucible, then crucible being placed Heating temperature is in 650~800 ℃ the process furnace, treat to put into after Al melts fully the crystallization Si piece that accounts for solder gross weight 0.1~1.0%, be incubated 10~20 minutes, get Al-Si master alloy liquid; B, the Cu that will account for solder gross weight 2.0~5.0%, 0.2~2.0% Mn, 0.08~0.3% Ni join in the Al-Si master alloy liquid, the temperature of process furnace is increased to 700~900 ℃, treat that each alloy fully melts the back pouring and becomes block, get the Al-Si-Cu-Mn-Ni master alloy; C, the Zn piece that will account for solder gross weight 80.6~93.71% are put into crucible, then crucible is placed in the process furnace, furnace temp is 650~800 ℃, after treating that the Zn piece melts fully, the Al-Si-Cu-Mn-Ni master alloy is joined in the Zn liquid, and furnace temp is increased to 650~900 ℃, after treating that the Al-Si-Cu-Mn-Ni master alloy melts fully, add the Ag that accounts for solder gross weight 02~1.5%, after treating that Ag melts fully, adding accounts for the Mg of solder gross weight 0.4~1.5% and 0.01~0.1% rare earth; D, the gained solution-cast is become ingot casting, be the self-drill brazing filler of aluminium alloy and aluminum matrix composite.
Embodiment two: what present embodiment and embodiment one were different is, the preparation method of the self-drill brazing filler of aluminium alloy and aluminum matrix composite is: a, the Al piece that will account for solder gross weight 3.3~8.0% are put into crucible, then crucible being placed Heating temperature is in 750 ℃ the process furnace, treat to put into after Al melts fully the crystallization Si piece that accounts for solder gross weight 0.1~1.0%, be incubated 15 minutes, get Al-Si master alloy liquid; B, the Cu that will account for solder gross weight 2.0~5.0%, 0.2~2.0% Mn, 0.08~0.3% Ni join in the Al-Si master alloy liquid, the temperature of process furnace is increased to 800 ℃, treat that each alloy fully melts the back pouring and becomes block, get the Al-Si-Cu-Mn-Ni master alloy; C, the Zn piece that will account for solder gross weight 80.6~93.71% are put into crucible, then crucible is placed in the process furnace, furnace temp is 710 ℃, after treating that the Zn piece melts fully, the Al-Si-Cu-Mn-Ni master alloy is joined in the Zn liquid, and furnace temp is increased to 770 ℃, after treating that the Al-Si-Cu-Mn-Ni master alloy melts fully, add the Ag that accounts for solder gross weight 0.2~1.5%, after treating that Ag melts fully, adding accounts for the Mg of solder gross weight 0.4~1.5% and 0.01~0.1% rare earth; D, the gained solution-cast is become ingot casting, be the self-drill brazing filler of aluminium alloy and aluminum matrix composite.
Embodiment three: what present embodiment and embodiment one, two were different is, after ingot casting is processed into diameter and is 40~60mm, long 40~60mm bar-shaped, preheating under 100~220 ℃ of conditions, under 195~225 ℃ of conditions, carry out hot extrusion then, according to the difference of extruding number of times, can produce diameter is the thread aluminium alloy of 1.0~5.0mm and the self-drill brazing filler of aluminum matrix composite.
Embodiment four: what present embodiment and embodiment three were different is, ingot casting is processed into bar-shaped back preheating under 150 ℃ of conditions that diameter is 50mm, long 50mm, under 200~220 ℃ of conditions, carry out hot extrusion then, the extrusion temperature control accuracy is ± 5 ℃, according to the difference of extruding number of times, can produce diameter is the thread aluminium alloy of 1.0~5.0mm and the self-drill brazing filler of aluminum matrix composite.
Claims (5)
1, the self-drill brazing filler of a kind of aluminium alloy and aluminum matrix composite, it is characterized in that it is made up of Zn, Al, Cu, Mg, Ag, Si, Mn, Ni and rare earth, each component is respectively by weight ratio: Zn:80.6~93.71%, Al:3.3~8.0%, Cu:2.0~5.0%, Mg:0.4~1.5%, Ag:0.2~1.5%, Si:0.1~1.0%, Mn:0.2~2.0%, Ni:0.08~0.3%, rare earth 0.01~0.1%.
2, the preparation method of the self-drill brazing filler of a kind of aluminium alloy and aluminum matrix composite, the Al piece that it is characterized in that a, will account for solder gross weight 3.3~8.0% is put into crucible, then crucible being placed Heating temperature is in 650~800 ℃ the process furnace, treat to put into after Al melts fully the crystallization Si piece that accounts for solder gross weight 0.1~1.0%, be incubated 10~20 minutes, get Al-Si master alloy liquid; B, the Cu that will account for solder gross weight 2.0~5.0%, 0.2~2.0% Mn, 0.08~0.3% Ni join in the Al-Si master alloy liquid, the temperature of process furnace is increased to 700~900 ℃, treat that each alloy fully melts the back pouring and becomes block, get the Al-Si-Cu-Mn-Ni master alloy; C, the Zn piece that will account for solder gross weight 80.6~93.71% are put into crucible, then crucible is placed in the process furnace, furnace temp is 650~800 ℃, after treating that the Zn piece melts fully, the Al-Si-Cu-Mn-Ni master alloy is joined in the Zn liquid, and furnace temp is increased to 650~900 ℃, after treating that the Al-Si-Cu-Mn-Ni master alloy melts fully, add the Ag that accounts for solder gross weight 0.2~1.5%, after treating that Ag melts fully, adding accounts for the Mg of solder gross weight 0.4~1.5% and 0.01~0.1% rare earth; D, the gained solution-cast is become ingot casting, be the self-drill brazing filler of aluminium alloy and aluminum matrix composite.
3, the preparation method of the self-drill brazing filler of aluminium alloy according to claim 2 and aluminum matrix composite, the Al piece that it is characterized in that a, will account for solder gross weight 3.3~8.0% is put into crucible, then crucible being placed Heating temperature is in 750 ℃ the process furnace, treat to put into after Al melts fully the crystallization Si piece that accounts for solder gross weight 0.1~1.0%, be incubated 15 minutes, get Al-Si master alloy liquid; B, the Cu that will account for solder gross weight 2.0~5.0%, 0.2~2.0% Mn, 0.08~0.3% Ni join in the Al-Si master alloy liquid, the temperature of process furnace is increased to 800 ℃, treat that each alloy fully melts the back pouring and becomes block, get the Al-Si-Cu-Mn-Ni master alloy; C, the Zn piece that will account for solder gross weight 80.6~93.71% are put into crucible, then crucible is placed in the process furnace, furnace temp is 710 ℃, after treating that the Zn piece melts fully, the Al-Si-Cu-Mn-Ni master alloy is joined in the Zn liquid, and furnace temp is increased to 770 ℃, after treating that the Al-Si-Cu-Mn-Ni master alloy melts fully, add the Ag that accounts for solder gross weight 0.2~1.5%, after treating that Ag melts fully, adding accounts for the Mg of solder gross weight 0.4~1.5% and 0.01~0.1% rare earth; D, the gained solution-cast is become ingot casting, be the self-drill brazing filler of aluminium alloy and aluminum matrix composite.
4, according to the preparation method of the self-drill brazing filler of claim 2 or 3 described aluminium alloys and aluminum matrix composite, after it is characterized in that ingot casting is processed into diameter and is 40~60mm, long 40~60mm bar-shaped, preheating under 100~220 ℃ of conditions, under 195~225 ℃ of conditions, carry out hot extrusion then, promptly get the self-drill brazing filler of thread aluminium alloy and aluminum matrix composite.
5, the preparation method of the self-drill brazing filler of aluminium alloy according to claim 4 and aluminum matrix composite, it is characterized in that ingot casting is processed into bar-shaped back preheating under 150 ℃ of conditions that diameter is 50mm, long 50mm, under 200~220 ℃ of conditions, carry out hot extrusion then, promptly get the self-drill brazing filler of thread aluminium alloy and aluminum matrix composite.