CN1405419A - Mineal wool sound-absorbing board with silent function and prepatation method thereof - Google Patents
Mineal wool sound-absorbing board with silent function and prepatation method thereof Download PDFInfo
- Publication number
- CN1405419A CN1405419A CN 01120359 CN01120359A CN1405419A CN 1405419 A CN1405419 A CN 1405419A CN 01120359 CN01120359 CN 01120359 CN 01120359 A CN01120359 A CN 01120359A CN 1405419 A CN1405419 A CN 1405419A
- Authority
- CN
- China
- Prior art keywords
- sound absorption
- mineral wool
- board
- hole
- wool board
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a mineral-wool sound-absorption board with sound-quieting function. First mix raw material for pulping, then adopt plasm-flowing method to make board, and after the base board is shaped and desiccated, cut and plane it, and then make flame plating, cotton ginning and perforation, then make re-cutting and second flame plating to obtain the finished product. The non-decorated surface of the mineral wool is stuck with separating piece-material layer. The sound-absorption holes: diameter 1-20 mm, regularly or irregularly distributed on the mineral-wool board and the good ones are through holes.
Description
Technical field
What the present invention relates to is a kind of mineral wool sound absorption board, and specifically, what the present invention relates to is a kind of mineral wool sound absorption board with mute function, and the preparation method of the mineral wool sound absorption board of described mute function.
Background technology
Mineral wool board is the new decorative material for building that integrates multiple functions such as light weight, sound-absorbing, fire prevention, heat insulation, decoration.Mineral wool board is harmless, pollution-free, be a kind ofly turn waste into wealth, the green building material of favorable environment.China began to produce from the seventies, and along with the develop rapidly of Building Trade in China, mineral wool board has been widely used in medium-to-high grade architectural decoration field.The consumption cumulative year after year, kind constantly updates.
Mineral wool board weight is lighter, is generally between the 350-450kg/m3, does not have sense of heaviness in the use, gives people's safety, relieved sensation, can alleviate the building deadweight, is a kind of safe decoration materials.Simultaneously mineral wool board also has good heat-insulating and fire-proof performance, and the average coefficient of thermal conductivity of mineral wool board is little, and easily insulation, and the primary raw material of mineral wool board is a mineral wool, and fusing point is up to 1300 ℃, and has higher fireproof performance.
At present mineral wool board has become a kind of general environmental friendly indoor ornament materials, its primary raw material mineral wool be slag through high temperature melting by supercentrifuge throw away wadding fibrous.Mineral wool in the mineral wool board is made up of numerous micropore, and when sound wave bump mineral wool board material surface, part is reflected back, and part is absorbed by sheet material, and some passes sheet material and enters the back cavity, thereby reduces reflected sound, has certain sound absorbing capabilities.
Along with the raising of people's living standard, the ornament materials performance demands is also improved constantly, improve the combination property of existing material, enlarge its purposes and become the task of top priority.
Prior art discloses multiple mineral wool board, for example, CN88213564 discloses a kind of floating clouds formula acoustical board, the described acoustical board of the document comprises string orifice plate and sound absorption material, the aperture that the aperture is respectively 5-6 and 1.5-3 millimeter is set at string on the orifice plate, aperture is evenly and is staggered, and described sound absorption material is super glass wool or mineral wool, but acoustical absorptivity only is 7.5 decibels under its 50% erection space.
CN89220712 discloses the cotton sound absorption decorative plate of a kind of mineral matter, described architectural surface of the document and substrate, and substrate is formed by the particulate minerals of spray glue is cotton, and still, its acoustically effective is still not ideal enough.
CN96228672 discloses the cotton acoustical board of a kind of rock (ore deposit), and the described acoustical board acoustically effective of the document is lower and need adopt the rigidity reinforcing rib in addition.
As seen, the sound absorbing capabilities of the mineral wool board of prior art awaits to improve.
Goal of the invention
Main purpose of the present invention is to provide a kind of mineral wool sound absorption board, and described mineral wool sound absorption board has the higher sound absorption coefficient and the sound sucting band of broad, can absorb the sound of various frequencies, plays quiet effect.
Another object of the present invention provides a kind of above-mentioned preparation method with mineral wool sound absorption board of mute function.
Purpose of the present invention can be achieved in the following manner, at first prepare the required slurry of mineral wool board and carry out making sheet, then wet plate is carried out drying and modify, covering with paint and the fine finishining of carrying out secondary coating again get final product, can be in preparation process, the hole that will absorb sound is molded directly within on the mineral wool board; Also can after drying, adopt the punch press perforation.The sound absorption hole that sound absorption bore dia of the present invention is 1-20mm, sound absorption hole can be the irregular or regular distribution in a kind of sound absorption hole of aperture on mineral wool board, also can be that the irregular or regular distribution in the sound absorption hole in more than one apertures is on mineral wool board.The sound absorption hole can be through hole, also can be blind hole.Mineral wool board of the present invention can be any mineral wool board of wet production in the prior art, can contain the granulated wool of 80.46-%, 7.65% starch, 11.89% clay and other auxiliary material.
Because intensity reduces behind the pore-forming, can not satisfy actual needs, general atresia on therefore traditional mineral wool board.In order to guarantee to bore a hole the intensity of mineral wool board afterwards, the thickness of mineral wool board of the present invention is at least 14mm.The present invention adopts the hole forming method of gypsum plank, and the hole that will absorb sound in the preparation process of mineral wool board is molded directly within on the mineral wool board.
The regular distribution mode in sound absorption of the present invention hole can be described sound absorption hole with the linear pattern that center line the is parallel to each other cross linear that the hole intersects at the mineral wool board center of arranging, absorb sound is to be even or radial on the center line to arrange.When the linear pattern that is parallel to each other with center line when described sound absorption hole is arranged, form parallelogram or trapezoidal such as square, rectangle between the sound absorption hole of same apertures, the cross linear that intersects at the mineral wool board center when the sound absorption hole is when being even or radial arranging on the center line, can form circular sound absorption hole, this is that can to regard the mineral wool board center as be the center of circle, is distributed with the sound absorption hole on each radius with the circle five equilibrium.The sound absorption hole can also and be fit to other shapes of the present invention for ellipse, 8 fonts and arrange; Describedly distribute radially, be meant when the sound absorption pore size distribution from the center of circle with the radius of center of circle five equilibrium on the time, the sound absorption pore size distribution is at the bearing of trend along radius, along the bearing of trend of radius absorb sound hole center to center distance identical, increase gradually or reduce.
Preferably, sound absorption of the present invention hole is distributed on the mineral wool board brokenly for more than one sound absorption hole.Perforated percentage is at least 3%.
More preferably, sound absorption of the present invention hole is evenly or radially to arrange and be distributed on the mineral wool board in a kind of sound absorption hole of aperture, or the sound absorption hole in two kinds of different apertures evenly or radially is distributed on the mineral wool board.
Most preferably, sound absorption of the present invention hole be the sound absorption hole of 6mm or 6mm and two kinds of aperture combination of 10mm with square arrangement on mineral wool board, pitch of holes is 28mm.
The sheet layer that mineral wool sound absorption board ore deposit with mute function of the present invention isolates at further stickup one of non-decorative cover one side and Dicoration base material, described sheet material can be sheet materials such as paper, cloth, plastics.As mulberry paper, wall paper etc.
The present invention is by having the sound absorption hole of mute function in traditional mineral wool board increase, improved the absorption function of mineral wool board greatly to various frequency sound, have the higher sound absorption coefficient and the sound sucting band of broad, can absorb the sound of various frequencies, play quiet effect.
Description of drawings
Below be description of drawings of the present invention,, can be expressly understood the present invention by description of drawings and in conjunction with later detailed description, wherein:
Accompanying drawing 1 is the structural representation that mineral wool sound absorption board of the present invention adopts big aperture square arrangement;
Accompanying drawing 2 is structural representations that mineral wool sound absorption board of the present invention adopts the aperture square arrangement;
Accompanying drawing 3 is preparation flow figure of mineral wool sound absorption board of the present invention;
Accompanying drawing 4 is mounting means schematic diagrames of the bright keel of mineral wool sound absorption board of the present invention;
Accompanying drawing 5 is under the mounting means of Fig. 4, frequency-sound absorption coefficient graph of a relation of measuring when described mineral wool sound absorption board adopts the structure of big aperture square arrangement;
Accompanying drawing 6 is dark mounting means schematic diagrames of inserting keel of mineral wool sound absorption board of the present invention;
Accompanying drawing 7 is under the mounting means of Fig. 6, frequency-sound absorption coefficient graph of a relation of measuring when described mineral wool sound absorption board adopts the structure of aperture square arrangement;
Accompanying drawing 8 is that diameter is the floor map of 1mm aperture random distribution on mineral wool board; Perforated percentage 3%;
Accompanying drawing 9 is the sound absorption hole floor map that parallelogram distributes on mineral wool board in same aperture;
Accompanying drawing 10 is the sound absorption hole in same aperture floor map with equidistant circular arrangement on mineral wool board;
Accompanying drawing 11a, b are the floor map that the sound absorption hole in two kinds of different apertures has rule to arrange on mineral wool board;
Accompanying drawing 12 is sound absorption hole floor map equidistantly to arrange on mineral wool board in three kinds of different apertures;
The schematic diagram of accompanying drawing 13 another embodiment of the present invention.
Specific embodiments
Below be detailed description of the present invention, by following description also in conjunction with the embodiments, can be expressly understood the present invention more, specific as follows:
At first prepare the required slurry of mineral wool board with mute function of the present invention, wherein, described slurry comprises:the granulated wool of 80.46-%, 7.65% starch, 11.89% clay and other auxiliary material in mixing machinery, add mixing with above-mentioned material, adopt slurry flowing process making sheet then, after the molding substrate drying, it is cut planing, carry out paint spay-coating again, embossing after the coating drying on the substrate, substrate is bored a hole, again through essence cut, secondary spraying can obtain finished product.If desired, can carry on the back and cover processing after substrate be bored a hole, just at the sheet layer of the non-decorative cover stickup one of described mineral wool board with the Dicoration base material isolation, described sheet material can be sheet materials such as paper, cloth, plastics.As mulberry paper, wall paper etc.; Described coating is made up of emulsion, titanium dioxide, calcium carbonate etc.After the coating drying on the substrate, substrate is carried out fine finishining, and then advance secondary and cover with paint, lacquer, colour wash, etc., with reference to the preparation method of gypsum plank. exists
Embodiment 1
At first prepare the required slurry of mineral wool board with mute function of the present invention, wherein, described slurry comprises: 80.46% A, 7.65% B, 11.89% C adds above-mentioned material in the mixing machinery, adopt slurry flowing process making sheet then, the thickness 14mm of substrate.
Behind drying substrates, it is cut planing, carry out the sprayed coating first time again.Described coating is made up of emulsion, titanium dioxide, calcium carbonate etc.After the coating drying on the substrate, adopt punch press punching on mineral wool board, according to the distribution of pin on the mould, can obtain the mineral wool board of various sound absorption pore size distributions.
After substrate is bored a hole, at the mulberry paper of the non-decorative cover stickup one of described mineral wool board with the Dicoration base material isolation.
Substrate is carried out embossing and fine finishining, and then carry out the covering with paint of secondary coating, dry getting final product.
The machined parameters of described mineral wool board is same as the prior art.
Other are consistent with embodiment 1, just the specification of substrate and on the distribution mode in sound absorption hole as follows:
The specification of prepared material is 15 * 595 * 595mm, and thickness is 15mm; The sound absorption hole is a through hole, big aperture square arrangement, and big bore dia is 10mm, hole diameter is 6mm; Hole center distance 28mm, perforated percentage is 13.6%.Structure as shown in Figure 1.
Measure its material sound absorption coefficient in the following way, wherein:
Specifications of surveys adopts GBJ47-83, and 4.2 * 2.4m is total to 10.08m
2Material be installed in the reverberation room, periphery has the 40mm armored concrete slab to go along with sb. to guard him, and adopts bright keel (seeing accompanying drawing 4) to install, measuring apparatus is the RTA-840 system.Installation constitution as shown in Figure 4, empty 385mm air layer behind the material.Measurement result is as shown in table 1.Table 1
Wherein: a is the 100-5000HZ average sound absorption coefficient, and NRC (noise reduction coefficient) is a 250HZ-2000HZ octave average sound absorption coefficient.
Frequency-sound absorption coefficient graph of a relation that Fig. 5 measures when adopting the structure of big aperture square arrangement for described mineral wool sound absorption board;
In the prior art, specification is (12--8) * 596 * 596mm or (12--15) * 496 * 496mm, unit weight 45-60kg/m
3, flexural strength is greater than 10kg/cm
2The sound-absorption coefficient of mineral wool board of wet production be about 0.3-0.4.As seen mineral wool board of the present invention can absorb the sound wave of various frequencies preferably.
Embodiment 3
Other are consistent with embodiment 1, just the specification of substrate and on the distribution mode in sound absorption hole as follows:
The specification of the material of prepared mineral wool board is 15 * 600 * 600, thickness 15mm; The sound absorption hole is a through hole, the aperture square arrangement, and hole diameter is 6mm; Hole center distance 18mm, perforated percentage is 8.7%.As shown in Figure 2, do not paste sheet layer on the mineral wool board.
Measure its material sound absorption coefficient in the following way, wherein:
Specifications of surveys adopts GBJ47-83, and 4.2 * 2.4m is total to 10.08m
2Material be installed in the reverberation room, periphery has the 40mm armored concrete slab to go along with sb. to guard him, and adopts the dark keel (seeing accompanying drawing 6) of inserting to install, measuring apparatus is the RTA-840 system.Empty 385mm air layer behind the material, installation constitution is as above shown in Figure 6.The results are shown in Table 2.
Sound absorption coefficient:
Wherein: a is the 100-5000HZ average sound absorption coefficient, and NRC (noise reduction coefficient) is that the 250HZ-2000HZ octave is average
Sound absorption coefficient.
Accompanying drawing 7 is under the mounting means of Fig. 6, frequency-sound absorption coefficient graph of a relation of measuring when described mineral wool sound absorption board adopts the structure of aperture square arrangement.
Embodiment 4
Other are consistent with embodiment 1, just the specification of substrate and on the distribution mode in sound absorption hole as follows:
The specification of prepared material is 14 * 595 * 595mm, and thickness is 14mm; The sound absorption hole is a surface holes, and bore dia is a 1mm aperture random distribution; Perforated percentage 3%, structure are as shown in Figure 8.
Measure its material sound absorption coefficient in the following way, wherein:
Specifications of surveys adopts GBJ47-83, and 4.2 * 2.4m is total to 10.08m
2Material be installed in the reverberation room, periphery has the 40mm armored concrete slab to go along with sb. to guard him, and adopts bright keel (seeing accompanying drawing 4) to install, measuring apparatus is the RTA-840 system.Installation constitution as shown in Figure 4, empty 385mm air layer behind the material.The result is 0.55 for the 100-5000HZ average sound absorption coefficient after measured, and 250HZ-2000HZ octave average sound absorption coefficient NRC is 0.62.
Embodiment 5-12
Among the embodiment 5-12, the preparation method of mineral wool board is with embodiment 1, and the mensuration of sound absorbing capabilities is seen embodiment 2, and difference is aperture and distribution thereof.
| Aperture mm | Mesopore mm | Macropore mm | Attract pore size distribution | Hole center distance (or Equal round) | Plate thickness mm | ??a | ?? | |
| Embodiment | ||||||||
| 5 embodiment 6 embodiment 7 embodiment 8 embodiment 9 embodiment 10 embodiment 11* embodiment 12** | ??1 ??2 ??3 ??4 ??3 | ??8 ??8 ??6 ??10 | ??10 ??12 ??16 ??20 | The random circular quadrangle of the random circle of parallelogram is circular | | ??14 ??14 ??15 ??20 ??15 ??16 ??15 ??15 | ??0.65 ??0.61 ??0.71 ??0.73 ??0.72 ??0.75 ??0.68 ??0.73 | ??0.71 ??0.65 ??0.76 ??0.78 ??0.76 ??0.79 ??0.70 ??0.77 |
* among the embodiment 11, the distance between the center line from the mineral wool board center along radius of a circle direction hole is 10+n, and wherein n is from the mineral wool board center, the garden week number in sound absorption hole
Among the * embodiment 12, the distance between the center line from the mineral wool board center along radius of circle direction sound absorption hole is 10+2n, and wherein n is from the mineral wool board center, the garden week number in sound absorption hole
Among the embodiment 7,9,11,12 360 degree/18,360 degree/10,360 degree/6,360 degree/12, for the central point with mineral wool board is the center of circle, with the five equilibrium angle of circle five equilibrium, the sound absorption pore size distribution is on the radius of five equilibrium central angle.
Among the embodiment 7, be 15 along the distance between the center line in the radial direction of five equilibrium central angle sound absorption hole;
Among the embodiment 9, diameter is that 3 and 12 sound absorption hole is staggered on each circumference, is 35 along the distance between the center line in the radial direction sound absorption hole of five equilibrium central angle.
Embodiment 13
Central point with mineral wool board is the center of circle, and the center of circle is divided into 8 parts, every part of miter angle, along the diametric(al) of each miter angle, in order successively evenly distribution diameter be 1,2,3,4 ... to 20 sound absorption hole, the hole center distance increases gradually, as shown in figure 13.
The schematic diagram of embodiment 5 is seen accompanying drawing 9, and the schematic diagram of embodiment 7 is seen accompanying drawing 10, and the schematic diagram of embodiment 9,11 is seen accompanying drawing 11a, b, and the schematic diagram of embodiment 10 is seen accompanying drawing 12.
In the accompanying drawing, 1 is former wall, and 2 is bright keel, and 3 are the sound absorption mineral wool board, and 4 is the dark keel of inserting, and 5 is sheet layer, and 6 is the hole.
Claims (11)
1. mineral wool sound absorption board with mute function, to it is characterized in that being distributed with diameter on the described mineral wool board be 1-20mm, have the sound absorption hole of sound absorption function, described sound absorption hole is through hole or blind hole.
2. a kind of mineral wool sound absorption board according to claim 1 with mute function, it is characterized in that described sound absorption hole for sound absorption holes, one or more apertures irregular or regular distribution on mineral wool board, the hole center to center distance in two adjacent sound absorption holes is at least 3% for the 3-50mm. perforated percentage, the thickness of mineral wool board is at least 14mm, and described sound absorption hole is preferably through hole.
3. according to the described a kind of mineral wool sound absorption board of claim 2 with mute function, it is characterized in that described sound absorption hole arranges with the linear pattern that the center line in hole is parallel to each other on mineral wool board, form square, rectangle or parallelogram between the sound absorption hole of same apertures.
4. a kind of mineral wool sound absorption board according to claim 2 with mute function, on the straight line of cross linear for the sound absorption centerline hole that the sound absorption pore size distribution that it is characterized in that described one or more radiuses is intersected at the mineral wool board center, the sound absorption hole is even or radial and arranges.
5. a kind of mineral wool sound absorption board with mute function according to claim 2 is characterized in that described sound absorption hole even or radial arranging on the radius of the central angle five equilibrium at mineral wool board center; The arrangement mode in described radial sound absorption hole of arranging is the center from mineral wool board, the edge along radial direction to mineral wool board, and the center to center distance in sound absorption hole increases gradually or reduces.
6. a kind of mineral wool sound absorption board according to claim 5 with mute function, the arrangement mode that it is characterized in that described radial sound absorption hole of arranging is the center from mineral wool board, edge along radial direction to mineral wool board, the radius in sound absorption hole increases gradually or reduces.
7. a kind of mineral wool sound absorption board with mute function according to claim 1 is characterized in that the diameter in described sound absorption hole is preferably 6mm, and pitch of holes is 28mm, perforated percentage 8.7%.
8. a kind of mineral wool sound absorption board according to claim 1 with mute function, the sound absorption hole that the diameter that it is characterized in that described sound absorption hole is preferably 6mm and two kinds of aperture combination of 10mm with square arrangement on mineral wool board, pitch of holes is 28mm, perforated percentage 13.6%.
9。According to each described a kind of mineral wool sound absorption board of claim 1-8, it is characterized in that described sheet material can be sheet materials such as paper, cloth, plastics at the sheet layer of the non-decorative cover stickup one of described mineral wool board with the Dicoration base material isolation with mute function.Preferred mulberry paper or cloth.
10. each described a kind of preparation method of claim 1-4,6-9 with mineral wool sound absorption board of mute function, at first with raw material mixed pulp in mixing machinery, adopt slurry flowing process making sheet then, after the molding substrate drying, it is cut planing, carry out paint spay-coating, embossing again, it is characterized in that on the mineral wool board that obtains, boring a hole, again through essence cut, secondary spraying can obtain finished product.
11. a kind of preparation method according to claim 10 with mineral wool sound absorption board of mute function, it is characterized in that described sheet material can be sheet materials such as paper, cloth at the sheet layer of the further stickup one of non-decorative cover one side of described mineral wool board with the Dicoration base material isolation; Preferred mulberry paper.