CN1404173A - 铝酸蓄电池正极铅膏配方 - Google Patents
铝酸蓄电池正极铅膏配方 Download PDFInfo
- Publication number
- CN1404173A CN1404173A CN02112897A CN02112897A CN1404173A CN 1404173 A CN1404173 A CN 1404173A CN 02112897 A CN02112897 A CN 02112897A CN 02112897 A CN02112897 A CN 02112897A CN 1404173 A CN1404173 A CN 1404173A
- Authority
- CN
- China
- Prior art keywords
- lead
- percent
- short fiber
- acid accumulator
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种铅酸蓄电池正极铅膏配方，除含有铅粉、硫酸、水外，在配方中添加了二氧化铅及干质短纤维。各成分重量百分比为：铅粉60％～80％，二氧化铅5％～20％，干质短纤维0.1％～0.15％，水10％～15％，硫酸4％～10％。本发明由于添加了二氧化铅，使正极在化成前已建立了骨架，降低了电池化成的槽压，有效的提高了化成电流效率，缩短了化成时间，节约了成本；使用回收二氧化铅做添加剂，还可以有效的对旧电池进行回收利用，保护了环境。加入干质短纤维，有效的增加了活性物质间的结合力，保证正极有足够的强度。
Description
技术领域
本发明涉及一种铅酸蓄电池正极铅膏配方，属铅酸蓄电池技术领域。
背景技术
铅酸蓄电池性能的好坏大多取决于正极的性能，长期以来铅酸蓄电池正极存在着化成困难、活性物质转化率低等问题(尤其是在采用电池化成时)，这就使得铅酸蓄电池的性能受到了严重的影响，尤其是在重量比能量方面。针对这种情况一般所采用的应对措施是增加化成时间，这样做的结果是使电池的制造周期增长，并消耗了过多的电能，造成了资源的浪费。人们曾试图通过添加正极添加剂来改善这一现状，但由于铅酸电池正极的电极电位很高，添加剂容易分解，因而这项工作进行的并不顺利。后来有人提出在正极中添加红丹(Pb3O4)，较好的解决了这一问题，但由于红丹有一定的毒害性，因而寻找一种更加适用的配方也就成为当务之急。
发明内容
本发明的目的是克服现有技术中的不足之处，提供一种能够提高活性物质转化率、缩短电池化成时间、节约制造成本、提高活性物质结合力、有利于环保的铅酸蓄电池正极铅膏配方。
本发明的技术方案是：由铅粉、二氧化铅、干质短纤维、水、硫酸所组成的正极铅膏配方中，其各成分所占重量百分比为：铅粉60％～80％，二氧化铅5％～20％，干质短纤维0.1％～0.15％，水10％～15％，硫酸4％～10％。
上述二氧化铅为废铅酸电池回收物，粒径≤106μm，所述干质纤维为腈纶，长度≤5mm，含水量≤0.1％。
采用以上技术方案，二氧化铅的添加，使正极在化成前已建立了骨架，降低了电池化成的槽压，有效的提高了化成电流效率，缩短了化成时间，节约了成本，使用回收二氧化铅做添加剂，还可以有效的对旧电池进行回收利用，保护了环境。干质短纤维的添加，有效的增加了活性物质间的结合力，保证正极有足够的强度。
具体实施方式
废旧电池中二氧化铅可用如下方法制备：从废旧电池中选取容量合格的正极板，将其用纯水洗净，烘干，然后进行研磨，过150目～250目筛，即可在和膏时作为添加剂使用。举实例如下：按如下重量百分比称取各成分：铅粉68.9％，二氧化铅13％，短纤维0.1％，水13％，硫酸5％，制作2V5Ah电池一只，采用电池内化成，化成结果显示，正极板中的二氧化铅含量达到了91％，而普通配方的电池经化成反应后二氧化铅含量只有82％，电池的容量得到了较大的提高。
Claims (3)
1、一种铅酸蓄电池正极铅膏配方，含有铅粉、硫酸、水，其特征在于还含有二氧化铅、干质短纤维，各配方成分在铅膏配方中的重量百分比为：铅粉60％～80％，二氧化铅5％～20％，干质短纤维0.1％～0.15％，水10％～15％，硫酸4％～10％。
2、据权利要求1所述的铅酸蓄电池正极铅膏配方，其特征在于配方中所用的二氧化铅为废铅酸电池回收物，粒径≤106μm。
3、据权利要求1所述的铅酸蓄电池正极铅膏配方，其特征在于配方中所用的干质短纤维为腈纶，长度≤5mm，含水量≤0.1％。