CN1390897A - Adhesive for nacreous ink of carved intaglio and its preparing process - Google Patents
Adhesive for nacreous ink of carved intaglio and its preparing process Download PDFInfo
- Publication number
- CN1390897A CN1390897A CN 02114646 CN02114646A CN1390897A CN 1390897 A CN1390897 A CN 1390897A CN 02114646 CN02114646 CN 02114646 CN 02114646 A CN02114646 A CN 02114646A CN 1390897 A CN1390897 A CN 1390897A
- Authority
- CN
- China
- Prior art keywords
- ink
- low
- engraved
- ink vehicle
- printing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
An adhesive of the nacreous ink for carved intaglio plate is prepared from high-viscosity phenolic resin, high-acidity phenolic resin, plant oil, rosin and mineral oil through filling nitrogen gas in reactor, adding resin modified phenolic resin and plant oil, heating to 170 deg.C, adding mixed solid resin, heating to 190 deg.C, cooling to 180 deg.C, and adding mineral oil. Its advantages are high transparency, low cost and energy consumption, and short preparing process.
Description
The present invention relates to a kind of engraved intaglo printing pearlite ink with low-melting ink vehicle and production technique.
Existing plate engraving ink low-melting ink vehicle mainly exists following defective or deficiency:
1. common plate engraving ink low-melting ink vehicle color depth can not fully show the optical characteristics of pearl ink;
2. common plate engraving ink low-melting ink vehicle performance is single, and multiple low-melting ink vehicle is used just can give printing ink good printability;
3. common plate engraving ink low-melting ink vehicle viscosity is little, and acid number is low, and it is many that the preparation pearl ink consumes pearly pigment, and the metalluster flicker effect is poor, and ink stability is bad, the energy consumption height;
4. common plate engraving ink low-melting ink vehicle complex manufacturing technology, man-hour is long, the cost height;
5. common plate engraving ink high viscosity low-melting ink vehicle surface is skinning easily, if employing adds the phenolic inhibitor method, not only influence is used, and also can cause waste and pollution.
The objective of the invention is to avoid above-mentioned weak point of the prior art, and provide a kind of production technique simple, fabrication cycle is short, and energy consumption is low, and cost is low, and the high engraved intaglo printing pearlite ink of transparency is with low-melting ink vehicle and production technique.
Purpose of the present invention can reach by following measure:
A kind of engraved intaglo printing pearlite ink low-melting ink vehicle, its special character is: the mass ratio that this printing ink is formed with the low-melting ink vehicle prescription is
High viscosity resol 8-15, high acid value resol 20-28, vegetables oil 30-50, rosin modified phenolic resin 5-20, Dormant oils 0-10.
The mass ratio that above-mentioned printing ink is formed with the low-melting ink vehicle prescription can be
High viscosity resol 10, high acid value resol 25, vegetables oil 45, rosin modified phenolic resin 10, Dormant oils 5.
Above-mentioned vegetables oil can be the oils of dried soon and tool conjugated double bond structures; Described solvent can be initial boiling point greater than 200 ℃ Dormant oils class; The described rosin modified phenolic resin superfine rosin that content is high so that look shallow is good.
Above-mentioned high viscosity resol, high acid value resol are good with transparent, look shallow resin all.
Above-mentioned vegetables oil can be tung oil, polymerization oleum lini, synourin oil or Chinese catalpa wet goods.
A kind of production technique that adopts above-mentioned formulation engraved intaglo printing pearlite ink with low-melting ink vehicle, its special character is: this production craft step is as follows
(1). at first, in reactor, feed nitrogen, with displaced air;
(2). then, in reactor, add rosin and vegetables oil, begin to heat up; When rising to 170 ℃, temperature adds the described solid resin of prescription;
(3). add resin, begin cooling after being warming up to 190 ℃;
(4). pour Dormant oils when being cooled to 180 ℃, range of viscosities is 25-30PaS/40 ℃, and acid number is 45-50mgKOH/g.
Above-mentionedly add rosin and vegetables oil heats up then in reactor, add solid resin when temperature rises to 170 ℃, material temperature should be not less than 150 ℃ in this reinforced process.
The present invention compared with prior art has following advantage:
1. pearl ink low-melting ink vehicle of the present invention is of light color, can satisfy the service requirements of pigment optical characteristics well;
2. production technique of the present invention is simple, and fabrication cycle is short, only needs 2-3 hour, 190 ℃ of top temperatures, and in the no preservation and controlling stage, vegetables oil mainly plays true solvent, and the production process energy consumption is low, and production cost is low;
3. lead to the nitrogen secluding air in the control process, temperature is lower than the diluting solvent boiling point, has reduced the generation of side reaction, has avoided the intensification of color, has reduced energy consumption;
4. employing modified phenolic resins is given low-melting ink vehicle high viscosity, high acid value, look shallow characteristic;
5. high viscosity, disposable the feeding intake of high acid value solid resin hybrid combination have been reduced the air that enters reaction system, have improved the transparency of low-melting ink vehicle;
6. after the low-melting ink vehicle barrelling, reinstate nitrogen seal device immediately,, prevent that reliably the low-melting ink vehicle surface is wrinkling because of the oxygen uptake skinning, reduced waste to drive away the air of sneaking in the discharging process in the finished product;
7. the optical property of finished product low-melting ink vehicle is carried out absorbancy, transmittance detection by quantitative and evaluation with ultraviolet spectrophotometer.
The invention will be further described below in conjunction with specific embodiment:
The present invention fills a prescription and forms the embodiment mass ratio:
High viscosity resol 8-15, high acid value resol 20-28, vegetables oil 30-50,
Rosin modified phenolic resin 5-20, Dormant oils 0-10.
The present invention fills a prescription and forms embodiment better quality ratio:
High viscosity resol 10, high acid value resol 25, vegetables oil 45,
Rosin modified phenolic resin 10, Dormant oils 5.Dispensing information of the present invention:
In the present invention's prescription, vegetables oil can adopt the oils of dried soon and tool conjugated double bond structures, as tung oil, polymerization oleum lini, synourin oil, Chinese catalpa wet goods.The rosin superfine rosin that content is high so that look shallow is that rosin modified phenolic resin is good.Solvent can adopt initial boiling point greater than 200 ℃ Dormant oils class.Its appearance requirement of the used resin of the present invention is transparent, look shallow.
The acid value of plate engraving ink low-melting ink vehicle usefulness synthetic resins, viscosity ratio are in the present invention's usefulness synthetic resins and the prior art:
| Title | Acid value | Viscosity |
| High acid value resol | 110-125mgKOH /g | ????1.0-2.0Pa·S/35 ????℃ |
| Rosin modified phenolic resin | 115-140mgKOH /g | ????0.45-0.55Pa·S/ ????35℃ |
| High viscosity resol | 20-25mgKOH/g | ????4.0-5.0Pa·S/35 ????℃ |
| Oil soluble phenol resol | 100-115mgKOH /g | ????0.35-0.40 ????Pa·S/35℃ |
Production technique of the present invention is as follows:
1. in reactor, feed the nitrogen replacement air;
2. in reactor, add rosin and vegetables oil, begin to heat up; Add the described solid resin of prescription when temperature rises to 170 ℃, notice that temperature of charge should be not less than 150 ℃ in the reinforced process;
3. add resin, begin cooling after being warming up to 190 ℃;
4. pour Dormant oils when being cooled to 180 ℃, to regulate viscosity.Range of viscosities is 25-30PaS/40 ℃, and acid number is 45-50mgKOH/g.
Claims (7)
1. engraved intaglo printing pearlite ink low-melting ink vehicle is characterized in that: the mass ratio that this printing ink is formed with the low-melting ink vehicle prescription is
High viscosity resol 8-15, high acid value resol 20-28, vegetables oil 30-50, rosin modified phenolic resin 5-20, Dormant oils 0-10.
2. engraved intaglo printing pearlite ink low-melting ink vehicle as claimed in claim 1 is characterized in that: the mass ratio that this printing ink is formed with the low-melting ink vehicle prescription is
High viscosity resol 10, high acid value resol 25, vegetables oil 45, rosin modified phenolic resin 10, Dormant oils 5.
3. engraved intaglo printing pearlite ink low-melting ink vehicle as claimed in claim 1 or 2 is characterized in that: described vegetables oil is the oils of dried soon and tool conjugated double bond structures; Described solvent is an initial boiling point greater than 200 ℃ Dormant oils class; Described rosin modified phenolic resin is that look shallow and superfine rosin that content is high.
4. engraved intaglo printing pearlite ink low-melting ink vehicle as claimed in claim 3 is characterized in that: described high viscosity resol, high acid value resol are transparent, look shallow resin.
5. engraved intaglo printing pearlite ink low-melting ink vehicle as claimed in claim 4 is characterized in that: described vegetables oil is tung oil, polymerization oleum lini, synourin oil or Chinese catalpa oil.
6. production technique that adopts the described formulation engraved intaglo printing pearlite ink of claim 1 with low-melting ink vehicle, it is characterized in that: production craft step of the present invention is as follows
(1). at first, in reactor, feed nitrogen, with displaced air;
(2). then, in reactor, add rosin modified phenolic resin and vegetables oil, begin to heat up; When rising to 170 ℃, temperature adds solid resin;
(3). add resin, begin cooling after being warming up to 190 ℃;
(4). pour Dormant oils when being cooled to 180 ℃, range of viscosities is 25-30PaS/40 ℃, and acid number is 45-50mgKOH/g.
7. the engraved intaglo printing pearlite ink as claimed in claim 6 production technique of low-melting ink vehicle, it is characterized in that: describedly in reactor, add rosin modified phenolic resin and vegetables oil heats up then, add solid resin when temperature rises to 170 ℃, material temperature should be not less than 150 ℃ in this reinforced process.