CN1389519A - Solid polymer composite facing material and its compounding process - Google Patents
Solid polymer composite facing material and its compounding process Download PDFInfo
- Publication number
- CN1389519A CN1389519A CN 02115330 CN02115330A CN1389519A CN 1389519 A CN1389519 A CN 1389519A CN 02115330 CN02115330 CN 02115330 CN 02115330 A CN02115330 A CN 02115330A CN 1389519 A CN1389519 A CN 1389519A
- Authority
- CN
- China
- Prior art keywords
- solid polymer
- polymer composite
- facing material
- pigment
- composite facing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a high-molecular complex entitative surface material and its method of preparation. The optimum weight's prepared proportion(%) of the components of the surface material is as follows: unsaturated resin 38; aluminium hydroxide 30; calcium carbonate 31.4; paint 0.6. And the method of making technique is as follows: add the quantitative filling materials aluminum hydroxide, calcium carbonate and so on into the paint and make them mix together, then high-speedily stir them; then perform mixing and stirring on the mixed and high-speedily stirred filling materials with unsaturated resin, solidifying agent and so on, and simultaneously vacuumize the mixturep finally make the above mentioned mixture model, solidify and shape, and then obtain the high-molecular complex surface material.
Description
Technical field
The present invention relates to a kind of building and ornament materials, relate in particular to a kind of interior architecture that is used for and decorate, especially for the rostone plane materiel and the compound method thereof of the various table tops of kitchen bathroom, cabinet face.
Background technology
The solid polymer composite plane materiel, it is rostone, it is the novel environmental protection interior architecture finishing material of a kind of polymer chemistry and thermofusion physical technique, texture with natural stone, be easy to processing, seamless spliced, style is followed one's bent, and nontoxic, "dead", quality even compact imporosity, greasy dirt, water stain difficult infiltration are wherein, bacterium is difficult for growing, having simultaneously the performance of heat-proof combustion-resistant, be widely used in various spatial wall body decorations such as household, office building, auditoriums, hotels, office building, be particularly useful for various table tops, cabinet face and kitchen bathroom and decorate.Solid polymer composite plane materiel on the market mainly is by inorganic filling powder and natural pigments such as unsaturated polyester, aluminium hydroxides now, add that different additive is mixed and made into, aluminium hydroxide content wherein is up to 50-70%, though flame retardant properties is better, but its water-intake rate is higher relatively, property is crisp, most importantly: because the aluminium hydroxide price is comparatively expensive, cause the production cost height, ordinary consumer is difficult to accept, and product is popularized and is restricted.
Summary of the invention
The objective of the invention is to overcome the deficiencies in the prior art part and provide a kind of cost low and better solid polymer composite facing material of over-all properties and compound method thereof.
To achieve the above object of the invention, solid polymer composite facing material of the present invention mainly stirs back reverse mould curing molding by filling powder, pigment and solidifying agent such as unsaturated polyester, aluminium hydroxide, lime carbonate by proportioning.The weight proportion of described solid polymer composite facing material (%) is: unsaturated polyester 35-40, aluminium hydroxide 28-32, lime carbonate 30-35, pigment 0.5-1.0.
Described pigment adopts natural pigment.
The process for making of solid polymer composite facing material of the present invention is as follows:
A. filling powders such as quantitative aluminium hydroxide, lime carbonate are added pigment and mix high-speed stirring;
B. will the filling powder after high-speed mixing stirs mixing stirring with unsaturated polyester, solidifying agent etc. vacuumizes simultaneously;
C. will promptly obtain solid polymer composite facing material behind the said mixture reverse mould curing molding.
Solid polymer composite facing material of the present invention, the content of aluminium hydroxide has been reduced by 50%, reduce production costs and reach 15-20%, and product is keeping having strengthened the shock resistance degree on the initial quality technological standard basis, its water-intake rate than existing plane materiel reduced by 0.01%, tensile strength increases 0.5Mpa, flexural strength increases 0.8Mpa, good toughness, and it is moderate to reach certain flame retardant properties, Barcol hardness, arbitrarily bending, splicing, alleviate product deep processing difficulty, have more superior performance than in the market solid polymer composite plane materiel.
Embodiment
The present invention is further illustrated with embodiment below:
According to unsaturated polyester: aluminium hydroxide: lime carbonate: natural pigment=38: 30: 31.4: 0.6 ratio, pour filling powders such as quantitative aluminium hydroxide, lime carbonate adding natural pigment into a mixing bowl and carry out high-speed mixing, filling powder after high-speed mixing stirs mixes stirring with unsaturated polyester, solidifying agent etc. again and vacuumizes simultaneously, last reverse mould curing molding the present invention's solid polymer composite facing material.The product that adopts production formula of the present invention to produce, its physicals such as following table:
And the physicals such as the following table of the product on the present market:
| Test item | Unit | Standard-required | Detected result |
| Proportion | g/cm 3 | ???1.7 | |
| Pasteur's intensity | ???58 | ||
| Tensile strength | Mpa | ?????≥15.5 | Qualified |
| Flexural strength | Mpa | ?????≥40.8 | Qualified |
| Water-absorbent | ?％ | ?????≤0.03 | Qualified |
| Resistance to impact shock | Height of the fall ball 2.44 | There is not influence | |
| Dry heat resistance | Do not ftracture in the table back side, bubbling | Qualified | |
| Anti-boiling water performance | The table back side does not have layering, no bubbling | Qualified | |
| Chemical resistance | Level | The A level or more than | The A level |
| The apyrous classification | Level | 1 grade or more than | 1 grade |
| Test item | Unit | Standard-required | Detected result |
| Proportion | g/cm 3 | ???1.7 | |
| Pasteur's intensity | ???58 | ||
| Tensile strength | Mpa | ?????≥15.0 | Qualified |
| Flexural strength | Mpa | ????≥40.0 | Qualified |
| Water-absorbent | ％ | ????≤0.04 | Qualified |
| Resistance to impact shock | Height of the fall ball 2.44 | There is not influence | |
| Dry heat resistance | Do not ftracture in the table back side, bubbling | Qualified | |
| Anti-boiling water performance | The table back side does not have layering, no bubbling | Qualified | |
| Chemical resistance | Level | The A level or more than | The A level |
| The apyrous classification | Level | 1 grade or more than | 1 grade |
As seen, compared with prior art, solid polymer composite facing material of the present invention not only production cost is lower, and combination property is better.
Claims (4)
1, a kind of solid polymer composite facing material, mainly formulated by unsaturated polyester, filling powder, pigment and solidifying agent, it is characterized in that: described filling powder mainly is made up of aluminium hydroxide and lime carbonate, and the weight proportion of this each component of plane materiel (%) is: unsaturated polyester 35-40, aluminium hydroxide 28-32, lime carbonate 30-35, pigment 0.5-1.0.
2, solid polymer composite facing material according to claim 1 is characterized in that: described pigment adopts natural pigment.
3, solid polymer composite facing material according to claim 1 is characterized in that: the optimum weight proportioning (%) of this each component of solid polymer composite plane materiel is: unsaturated polyester 38, aluminium hydroxide 30, lime carbonate 31.4, pigment 0.6.
4, a kind of making processing method of solid polymer composite facing material according to claim 1, it is characterized in that: this method comprises the steps:
A. filling powders such as quantitative aluminium hydroxide, lime carbonate are added pigment and mix high-speed stirring;
B. will the filling powder after high-speed mixing stirs mixing stirring with unsaturated polyester, solidifying agent etc. vacuumizes simultaneously;
C. will promptly obtain solid polymer composite facing material behind the said mixture reverse mould curing molding.