CN1388081A - 一种以贝壳为骨料的混凝土 - Google Patents

一种以贝壳为骨料的混凝土 Download PDF

Info

Publication number
CN1388081A
CN1388081A CN 01114003 CN01114003A CN1388081A CN 1388081 A CN1388081 A CN 1388081A CN 01114003 CN01114003 CN 01114003 CN 01114003 A CN01114003 A CN 01114003A CN 1388081 A CN1388081 A CN 1388081A
Authority
CN
China
Prior art keywords
concrete
shell
cement
aggregate
magnesium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 01114003
Other languages
English (en)
Inventor
王金华
胡宗玢
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 01114003 priority Critical patent/CN1388081A/zh
Publication of CN1388081A publication Critical patent/CN1388081A/zh
Pending legal-status Critical Current

Abstract

本发明公开一种以贝壳为骨料的混凝土,它包含以水泥为胶凝材料,以贝壳替为骨料填加水分混合而制成的混凝土;所说的贝壳的含量为混凝土组分总量的20～90%。该混凝土可用于各种制品,例步行道砖、养植箱、建筑砌块等。该发明具有制作工艺简单、造价低廉,就地取材,变废为宝,节约天然资源,减少环境污染的重大经济和社会效益。

Description

一种以贝壳为骨料的混凝土
本发明涉及一种新材料，即用废弃贝壳替代天然砂石作为骨料制做的混凝土。
众所周知，一些海边堆积大量贝壳，沿海城市海产品加工厂和生活垃积中也抛弃数量可观的贝壳。仅就大连市为例，每年所产生的贝壳约是全年生活垃圾堆的五分之一，数量约为十八万顿。这些贝壳要运至指定垃圾填埋场填埋处理，给城市带来巨大的经济负担。另一方面，按传统方法制作混凝土，要消耗70％左右重量份的砂石。为取得这些砂石往往是崩山开采、挖掘河道，破坏自然景观，消耗大量的自然资源、坑害非浅。
本发明的目的是，提供一种利用大量的废弃贝壳全部或部分替代天然砂石而制成的混凝土，该混凝土具有成本低、废旧利用，即节约了资源，又保护了环境。
为实现本发明的目的，技术方案为：
该混凝土包含组分为：
胶凝材料；骨料；和水；
所说的胶凝材料为钙质水泥或镁质水泥，其钙质水泥为硅酸盐水泥、铝酸盐水泥、硫铝酸水泥或聚合物水泥；镁质水泥为氯氧镁水泥或硫氧镁水泥；其所说的骨料为废弃经加工处理后的贝壳；所说贝壳的含量占混凝土组分总重量的20～90％，其中以40～70％为优选。
本发明的有益效果如下：
1、该混凝土适用于各种建筑制品用，由它制成的产品，其表面具有天然石材的纹理和质感，与用普通混凝土制作的制品大大提高了产品档次，深受用户的欢迎。另外用贝壳做骨料可就地取材，免去用天然砂石的工本费和运输费每M3混凝土可节省砂石费用30元以上，仅此一项就可降低成本20％以上。
2、该混凝土，由于用废弃的贝壳可全部或部分替代天然砂石，彻底地解决了海边城市贝壳严重污染的问题，其社会效益显而易见。
本发明的实施方式
实施例1
首先将贝壳粗粉碎、清洗待用，配料时取硅酸盐水泥100重量份，取河砂40重量份，贝壳300重量份，取水50重量份然后将前述原料搅拌均匀即可。
实施例2
取氧化镁100重量份、取氯化镁水溶剂90重量份(浓度26Be)，配制成氯氧镁水泥，再取粉碎清洗后的贝壳400重量份，将所述原料混合搅拌均匀即可。
实施例3
取硫铝酸水泥120重量份，取加工粉碎贝壳400重量份，取水55重量份，取防水填加剂2重量份，将上述原料搅拌均匀即可。

Claims (4)

1、一种以贝壳为骨料的混凝土，其特征在于：该混凝土包含组分为：
胶凝材料；骨料和水；
所说的胶凝材料为钙质水泥或镁质水泥；所述的钙质水泥为硅酸盐水泥、铝酸盐水泥、硫铝酸水泥或聚合物水泥；镁质水泥为氯氧镁水泥或硫氧镁水，所说的骨料为废弃经加工处理后的贝壳；其贝壳的含量占混凝土组分总重量的20～90％
2、根据权利要求1所述的一种以贝壳为骨料的混凝土，其特征在于：所述贝壳的含量占混凝土组分总重量的40～70％
3、根据权利要求1或2所述的一种以贝壳为骨料的混凝土，其特征在于：还可包含砂石。
4、根据权利要求1或2所述的一种以贝壳为骨料的混凝土，其特征在于：还可包含填加剂。
CN 01114003 2001-05-29 2001-05-29 一种以贝壳为骨料的混凝土 Pending CN1388081A (zh)