CN1385483A - 纳米内外墙改性涂料 - Google Patents

纳米内外墙改性涂料 Download PDF

Info

Publication number
CN1385483A
CN1385483A CN 02124097 CN02124097A CN1385483A CN 1385483 A CN1385483 A CN 1385483A CN 02124097 CN02124097 CN 02124097 CN 02124097 A CN02124097 A CN 02124097A CN 1385483 A CN1385483 A CN 1385483A
Authority
CN
China
Prior art keywords
wall
nano
paint used
modified paint
nano modified
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 02124097
Other languages
English (en)
Inventor
刘尚文
杨纳新
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 02124097 priority Critical patent/CN1385483A/zh
Publication of CN1385483A publication Critical patent/CN1385483A/zh
Pending legal-status Critical Current

Abstract

本发明是一种纳米内外墙改性涂料,主要结构分为成膜物质、分散介质、颜填料和助剂,原料配方的重量百分比分别为:丙烯酸树脂乳液35-55%;分散润湿剂0.1-0.3%;钛白粉4-8%;立德粉4-8%;滑石粉2-6%;纳米SiO21.5-4.5%;纳米TiO21.5-4.5%;pH调节剂0.1-0.3%;水20-30%;将所述原料水、助剂、填颜料经配置、搅拌、砂磨后再次填加助剂进行调配,最后经过滤出料。本发明成功彻底的改善了原有涂料的防水性、耐污染、耐老化、抗紫外线、抗菌性等各项技术性能,其表面硬度、光洁度达到更高标准,洗刷可达11000次以上,内外墙涂料寿命可达10年以上。

Description

纳米内外墙改性涂料
技术领域
本发明是一种纳米内外墙改性涂料。
背景技术
传统涂料目前分为有机类和无机类两种,有机涂料涂层强度低,耐热性、耐侯性差,而无机涂料存在装饰效果差、弹性弱等缺点。传统涂料涂于墙面后,使用寿命均较短,一般在3-4年左右,外墙涂料由于外部环境恶略,使用寿命更加短暂,主要原因是受到外界紫外线的侵蚀,使涂层逐渐老化、变色、脱色和起皮。
发明内容
本发明为了解决上述问题而提供一种纳米内外墙改性涂料。有效提高了涂料的耐老化性能,避免了紫外线对涂料的侵蚀,大大延长了涂料的使用寿命。
本发明是这样实现的:一种纳米内外墙改性涂料,主要结构分为成膜物质、分散介质、颜填料和助剂,原料配方的重量百分比分别为:
丙烯酸树脂乳液    35-55%;
分散润湿剂        0.1-0.3%;
钛白粉            4-8%;
立德粉            4-8%;
滑石粉            2-6%;
纳米SiO2         1.5-4.5%;
纳米TiO2         1.5-4.5%;
PH调节剂          0.1-0.3%;
水                20-30%。
本发明成功彻底的改善了原有涂料的防水性、耐污染、耐老化、抗紫外线、抗菌性等各项技术性能,装罐后不沉淀,存放时间长,不起皮层,像水一样开罐即用,且采用水为溶剂,不含苯、甲醛等有害化学物质。涂料经纳米技术改性后,其表面硬度、光洁度达到更高标准,装饰的墙面具有荷叶般的疏水性,污染物很难渗入,耐清洗,洗刷可达11000次以上。在涂刷过程中由于光洁度高,无硬块障碍,具有抗老化、不起皮、不脱落、不变色、超强耐碱性、耐洗刷、耐冻性,细菌、病菌无法渗透到细腻的墙面中,微生物无法表面存活,有适当的空气净化吸附功能,外墙涂料寿命可达10年以上,内墙15年以上。同时施工简单,干燥时间快,约1-2小时即可。
具体实施方式
以下结合实施例对本发明作详细描述:
纳米内外墙改性涂料主要结构分为成膜物质、分散介质、颜填料和助剂,原料配方的重量百分比分别为:
丙烯酸树脂乳液   45%;
分散润湿剂       0.2%;
钛白粉           6%;
立德粉           6%;
滑石粉             4%;
纳米SiO2          3%;
纳米TiO2          3%;
PH调节剂           0.2%;
水                 27.6%;
将所述原料水、助剂、填颜料经配置、搅拌、砂磨后再次填加助剂进行调配,最后经过滤出料。其中,纳米SiO2、TiO2粒径约在45-55nm,最佳约为50nm。由于紫外线是一种比可见光波长短的电磁波,其波长介于200-380nm,按波长大小又可分为短波UVC(200-280nm),中波UVB(280-320nm),长波UVA(320-380nm)。紫外线的波长越短,能量越强,对物质的危害性也越大。纳米SiO2、TiO2粒径在50nm左右,对紫外线有屏蔽散射的作用,能有效吸收紫外线,使涂料的使用寿命延长至10年以上。在自然光的作用下,纳米粒子可产生光催化氧化反应过程,产生活性氧和OH自由基,有很高的反应活性,当污染物吸附于表面时,就会与自由电子或空穴结合,发生氧化还原反应,从而达到消除污染、净化空气的目的,对氮氧化物、油脂、甲醛等物质具有明显的催化降解作用。

Claims (4)

1.一种纳米内外墙改性涂料,其特征在于:主要结构分为成膜物质、分散介质、颜填料和助剂,原料配方的重量百分比分别为:
丙烯酸树脂乳液   35-55%;
分散润湿剂       0.1-0.3%;
钛白粉           4-8%;
立德粉           4-8%;
滑石粉           2-6%;
纳米SiO2        1.5-4.5%;
纳米TiO2        1.5-4.5%;
PH调节剂         0.1-0.3%
水               20-30%。
2.如权利要求1所述的纳米内外墙改性涂料,其特征在于:所述原料配方的重量百分比分别为:
丙烯酸树脂乳液   45%;
分散润湿剂       0.2%;
钛白粉           6%;
立德粉           6%;
滑石粉           4%;
纳米SiO2        3%;
纳米TiO2        3%;
PH调节剂         0.2%;
水              27.6%。
3.如权利要求1或2所述的纳米内外墙改性涂料,其特征在于:所述纳米SiO2、TiO2粒径约在45-55nm。
4.如权利要求3所述的纳米内外墙改性涂料,其特征在于:所述纳米SiO2、TiO2粒径约在50nm。
CN 02124097 2002-06-20 2002-06-20 纳米内外墙改性涂料 Pending CN1385483A (zh)