CN1375477A - Ceramics with added jade powder - Google Patents
Ceramics with added jade powder Download PDFInfo
- Publication number
- CN1375477A CN1375477A CN 02109521 CN02109521A CN1375477A CN 1375477 A CN1375477 A CN 1375477A CN 02109521 CN02109521 CN 02109521 CN 02109521 A CN02109521 A CN 02109521A CN 1375477 A CN1375477 A CN 1375477A
- Authority
- CN
- China
- Prior art keywords
- jade powder
- feldspar
- base
- base material
- clay
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a kind of ceramics to which the jade powder is added, which is characterized by that it uses clay, feldspar and quartz as base material or uses talcum, feldspar, kaolin, magnesium oxide and silicon oxide as base material or uses kaolin, quartzite, feldspar and phosphate as base material and adds the jade powder to said base material, and its composition comprises (wt%) 70-90% of base material and 10-30% of jade powder. The whiteness of the product made up by said method is increased, and its Mohs' hardness, compression strength and tensile strength are greatly raised.
Description
Technical field
The present invention relates to a kind of pottery, especially a kind of pottery that adds the jade powder.
Background technology
Traditional stupalith is clay, the feldspar of solvent, the feldspathic china of quartzy three components with the feldspar, it is typical case's representative of porcelain, in addition, also having with magnesium oxide, silicon oxide such as talcum, feldspar, kaolin is the porcelain-like quality of component, is bone ash matter porcelain of component or the like with kaolin, quartzite, feldspar, phosphoric acid salt.Raw clay also claims plastic material, plastic material commonly used has: kaolin, kieselguhr, china clay, wilkinite etc., quartz is non-plastic material, feldspar is the solvent raw material, the solvent raw material is except that feldspar, also has nepheline syenite, grouan, contain lithium minerals, feldspar surrogates such as float stone, calcite, limestone, from chalk, the lime carbonate class of marble, the magnesiumcarbonate class of magnesite and magnesia, rhombspar, talcum, the magnesium silicates of serpentine, wollastonite etc., when charge calculation, according to the complete chemical analysis composition of clay, determine feldspar, the dosage of quartz etc. costs an arm and a leg owing to the jade reserves are rare, with a kind of raw material of jade, do not have in the prior art as pottery.Jade is not carved good-for-nothing, jade is often remaining waste materials when being processed into artwork, and then cost is very low for powder utilizes in these waste materials pulverizing, and the present invention is through experimental results show that, after in ceramic raw material, having added the jade powder, shortened base time of drying, throwing is easy fracture not, has reduced firing temperature, product appearance whiteness after making increases, transparency improves, and Mohs' hardness, resistance to compression, tensile strength all increase greatly, ceramic material property is improved played unexpected effect.
Summary of the invention
The purpose of this invention is to provide a kind of pottery that utilizes waste material jade powder to produce.
The object of the present invention is achieved like this:
A kind of pottery that adds the jade powder, it is characterized in that: with clay, feldspar, quartz is base-material, or be base-material with magnesium oxide, silicon oxide such as talcum, feldspar, kaolin, or be base-material with kaolin, quartzite, feldspar, phosphoric acid salt etc., in base-material, add the jade powder, its component is (weight percent): base-material accounts for 70～90%, and the jade powder accounts for 10～30%.
The pottery of above-mentioned interpolation jade powder is characterized in that: component is (weight percent): clay 30～40%, feldspar 20～25%, quartz 20～25%, jade powder 10～20%.
Benefit of the present invention is:
The prior art base after drying time is 6～10 hours, add only 6 hours jade powder after drying time, obviously shorten time of drying, and throwing is easy fracture not, burns till pate dure and reduce to 1100 ℃ by original 1300 ℃, energy efficient, product appearance after making increases ≮ 75 from degree, and transparency (1mm thickness)＞3, Mohs' hardness, resistance to compression, tensile strength all increase greatly, adding the jade powder is a kind of waste material, and cost reduces.
Embodiment
Embodiment 1:
A kind of pottery that adds the jade powder is a base-material with clay, feldspar, quartz, adds the jade powder in base-material, the granularity of jade powder is 800～1000 orders, and its component is (weight percent): clay 30%, feldspar 25%, quartz 25%, jade powder 20% adds an amount of moisture again.
Mentioned component is through mixing, and base, throwing, moulding dry 6 hours, are fired goods or test specimen under 1100 ℃ of temperature of high temperature.
After above-mentioned firing, test specimen outward appearance whiteness increases ≮ 75, and transparency (1mm thickness)＞3, Mohs' hardness, resistance to compression, tensile strength all increase greatly, is difficult for broken.
Embodiment 2:
A kind of pottery that adds the jade powder is a base-material with clay, feldspar, quartz, adds the jade powder in base-material, and the granularity of jade powder is 800～1000 orders, and its component is (weight percent): clay 40%, feldspar 20%, quartz 25%, jade powder 15%.
Claims (2)
1. pottery that adds the jade powder, it is characterized in that: with clay, feldspar, quartz is base-material, or be base-material with magnesium oxide, silicon oxide such as talcum, feldspar, kaolin, or be base-material with kaolin, quartzite, feldspar, phosphoric acid salt etc., in base-material, add the jade powder, its component is (weight percent): base-material accounts for 70～90%, and the jade powder accounts for 10～30%.
2. the pottery of interpolation jade powder according to claim 1 is characterized in that: component is (weight percent): clay 30～40%, feldspar 20～25%, quartz 20～25%, jade powder 10～20%.