CN1358789A - Art and craft sculpture clay - Google Patents
Art and craft sculpture clay Download PDFInfo
- Publication number
- CN1358789A CN1358789A CN 00128291 CN00128291A CN1358789A CN 1358789 A CN1358789 A CN 1358789A CN 00128291 CN00128291 CN 00128291 CN 00128291 A CN00128291 A CN 00128291A CN 1358789 A CN1358789 A CN 1358789A
- Authority
- CN
- China
- Prior art keywords
- clay
- kapok
- mentioned
- sorbic acid
- talcum powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a modeling substance which is non-toxic, harmless and pollutionless, and whose product does not crack and deform and can be made into large product by using wood or metal as supporting material and its preparation method. Said invention modeling substance is made upby using carboxymethyl cellulose CMC, carboxy methylcellulose sodium CMS, dibutyl phthalate, propanetriol, polyethylene glycol, sodium benzoate, sorbic acid, light calcium sodium carbonate, talcum powder, magnesium carbonate and pure water through mixing process.
Description
The present invention relates to a kind of sculpture mud and preparation method thereof.A kind of art and craft sculpture clay and preparation method thereof particularly.
Present sculpture has multiple with mud, the natural clay of the use that wherein has auxiliary material is in addition made sculpture clay, and this sculpture clay exists following defective; Because its intensity is low and to timber, the adhesion of rigid materials such as reinforcing bar is low, so goods can not make large-scale goods by reinforcement, can only make the goods of smallclothes.In case and after the goods drying, the crack makes the goods of moulding produce flaw, even damages easily.The sculpture clay that also has is to be mixed and made into paper pulp, potter's clay and tamanori, and this sculpture clay rheological is big, and its goods are yielding, and the surface is not really smooth, and summer is easily mouldy, and is not easy to store.
The present invention aims to provide a kind of nontoxic, and is harmless, pollution-free, and goods do not split, indeformable, can be with timber, and things such as metal are upholder art and craft sculpture clay of making massive article and preparation method thereof.
Composition of raw materials of the present invention is: (by weight)
Carboxyl methyl cellulose (9-12) %
Carboxymethyl cellulose CMS (9.00-12.00) %
Dibutyl phthalate (0.30-0.80) %
Glycerol (3.50-4.50) %
Polyoxyethylene glycol (polymerization degree 6000) is % (0.40-0.70)
Sodium Benzoate (0.02-0.50) %
Sorbic Acid (0.04-0.06) %
Light body yellow soda ash calcium (8.04-8.50) %
Magnesiumcarbonate (5.00-7.00) %
Talcum powder (24.46-25.46) %
Kapok (no seed, clean kapok) is % (0.15-0.25)
Pure water (34.00-36.00) %
The production compound method is:
1, earlier with polyoxyethylene glycol, Sodium Benzoate, Sorbic Acid dissolved in purified water, and then with O-phthalic
Dibutyl phthalate, glycerol are put into, and stir.
2, kapok is put into proportioning machine, break and loose, it is even to put into carboxyl methyl cellulose, carboxymethyl cellulose CMS, light body yellow soda ash calcium, magnesiumcarbonate, talcum powder, fusion again.
3, the mixture that above-mentioned (2) make is put into stirrer, with stirring,, stir to no meal until all adding with adding the aqueous solution that above-mentioned (1) makes.
4, the mixture that above-mentioned (3) are made is put into and is rolled the material machine and carry out backing, to being the clay shape, is art and craft sculpture clay of the present invention.
5, the art and craft sculpture clay that above-mentioned (4) make is put into forcing machine, through extruding, stripping and slicing, heat sealing is carried out in the packing bag of packing into.
The art and craft sculpture clay that adopts prescription of the present invention and production compound method to make has following technical indicator:
Color and luster white or broken white, color and luster is even
Smell is little fragrance, does not have bad smell
Form is flexible glue mud substantially, and is opaque, no bubble
The impurity component cleaning, feel exquisiteness, no particulate material
Upright sticking together got clay and be twisted into taper, and be upright 2 hours, not askew not oblique
Under the extensibility normal temperature＜32MM
PH value 6-7
46 ℃ of resistance toheats 2 hours (wait to move to behind the normal temperature 2 hours, promptly restore to the original state)
Cold tolerance-18 ℃ 2 hours (wait to move to behind the normal temperature 2 hours, promptly restore to the original state)
Adhesion is got the 20g clay, and is coated in the timber bar, and post shrinkage in 24 hours hours packs tightly, no
Split, indeformable
Drying regime can stand slight impact after 48 hours, can stand after seven days normally to collide with ten
It back substantially dry can painted and long-term storage
Because product of the present invention has above performance, therefore, it is a kind of nontoxic, harmless, pollution-free, and goods do not split, indeformable, can be with timber, and reinforcing bar is upholder art and craft sculpture clay of making large-scale goods and preparation method thereof.
It can be with metal, timber, and plastics, paper product etc. are core body, make large-scale sculpture, this sculpture not only can be placed on indoor, can also place outdoorly, stands wind and weather.
It is fit to teaching uses, and can give full play to student's imagination, carries out sculpture creation.Simultaneously, can also inspire and cultivate children's sculpture talent as toy.
Embodiment:
Adopt following proportioning get the raw materials ready (weight ratio);
Carboxyl methyl cellulose 21.00Kg
Carboxymethyl cellulose CMS 21.00Kg
Dibutyl phthalate 1.00Kg
Glycerol 8.00Kg
Polyoxyethylene glycol (polymerization degree 6000) 1.00Kg
Sodium Benzoate 0.10Kg
Sorbic Acid 0.10Kg
Light body yellow soda ash calcium 15.00Kg
Magnesiumcarbonate 12.00Kg
Talcum powder 49.00Kg
Kapok (no seed, clean kapok) 0.50Kg
Pure water 71.30Kg
Amount to 200.00Kg
According to production compound method of the present invention, above-mentioned each component is progressively added and mixes, stirring becomes art and craft sculpture clay, and carry out sculpture and become the fawn on the meadow in the large-scale park, tint after the drying, vivid true to nature, and can stand round-the-clock variation, the crack is not indeformable.
Claims (1)
1, a kind of art and craft sculpture clay and preparation method thereof is characterized in that its composition of raw materials is: (by weight)
Carboxyl methyl cellulose (9-12) %
Carboxymethyl cellulose CMS (9.00-12.00) %
Dibutyl phthalate (0.30-0.80) %
Glycerol (3.50-4.50) %
Polyoxyethylene glycol (polymerization degree 6000) is % (0.40-0.70)
Sodium Benzoate (0.02-0.50) %
Sorbic Acid (0.04-0.06) %
Light body yellow soda ash calcium (8.04-8.50) %
Magnesiumcarbonate (5.00-7.00) %
Talcum powder (24.46-25.46) %
Kapok (no seed, clean kapok) is % (0.15-0.25)
Pure water (34.00-36.00) %
The production compound method is:
(1) puts into earlier with polyoxyethylene glycol, Sodium Benzoate, Sorbic Acid dissolved in purified water, and then with dibutyl phthalate, glycerol, stir;
(2) kapok is put into proportioning machine, break and loose, it is even to put into carboxyl methyl cellulose, carboxymethyl cellulose CMS, light body yellow soda ash calcium, magnesiumcarbonate, talcum powder, fusion again;
(3) mixture that above-mentioned (2) are made is put into stirrer, with stirring with adding the aqueous solution that above-mentioned (1) makes, until all adding, stirs to no meal;
(4) mixture that above-mentioned (3) are made is put into and is rolled the material machine and carry out backing, to being the clay shape.