CN1323679A

CN1323679A - Imitation stone furniture producing process

Info

Publication number: CN1323679A
Application number: CN 01126117
Authority: CN
Inventors: 刘宗信
Original assignee: Individual
Current assignee: Individual
Priority date: 2001-07-12
Filing date: 2001-07-12
Publication date: 2001-11-28
Anticipated expiration: 2021-07-12
Also published as: CN1132744C

Abstract

The present invention discloses manufacturing process of imitation stone furniture, its technical scheme includes the following steps: non stone material is used as source material, which is processed to shape as base plate, mixing adhesive, stone material and additive to form paint which is informly coated onto the surface of base plate, after drying for a certain time the surface of base plate forms an imitation stone layer.

Description

The processing procedure of imitation stone furniture

Technical field:

The present invention relates to a kind of manufacture method of imitation stone furniture.

Background technology:

Table now mostly is stone material, log, clamping plate or made by the close plate squeezing that wood chip compressed, wherein, the table that above-mentioned stone material is made, vision and touch sense and all have best feeling evaluation no matter, still, the made table of stone material remains in following disappearance:

1. the difficulty of drawing materials of stone material raw material, its relative price is quite expensive, and for numerous consumers, desire is bought the furniture that pure stone material (for example marble) makes and can not be achieved one's goal because of the high eighteenth of the twenty of its price, also cause existing stone furniture to represent thus, be difficult to popularize at particular place;

2. the overall weight of stone furniture is quite big, so stone furniture can only be seated in same place for a long time, in case the puzzlement of carrying will be caused in the position that needs change to put, often needing to employ numerous manpowers or facility can carry out; In addition, because weight factor is accepted the runners of Stone table top and also must be made with equal stone material, so more increase its price and weight;

3. the own extreme hardness of stone material, the furniture that can't make as other materials is with spiral shell spare or riveting parts and reach finishing, cut or assemble, therefore general stone material can only design cut rounded or square, and owing to do processing such as perforation thereon than difficulty, it is indoor that stone furniture can only be put, and limit to its field of employment.

Summary of the invention:

Technical problem to be solved by this invention is, can provide a kind of and overcomes that the stone material quality is big, processing difficulties, the new furniture material manufacture method difficult, defective such as cost an arm and a leg of drawing materials.

The technical scheme that solves the problems of the technologies described above is to adopt following making step: the material that utilizes non-stone material is as material, and this material to form is processed into the substrate of predetermined kenel; Adhesive, stone material and additive are mixed into a coating according to default ratio; Again above-mentioned coating is uniformly coated on above-mentioned substrate surface; Treat the above-mentioned substrate that is coated with coating after a dry solidification time-histories, the surface of this substrate promptly forms an imitative stone material layer.After the mat above-mentioned steps, can make the exterior substrate of a non-stone material have the seemingly imitation effect of stone material.

The present invention with above-mentioned both economical, easy method form a light weight, easily construct, draw materials easily, price is lower, and its sculpture is strong, can be designed to the outward appearance of the graceful moulding of various tool, its matter is softer, directly assemble the table pin group of accepting desktop easily, and offer the perforation that supplies the sunshading umbrella cross-under thereon, the imitation stone furniture that the present invention is made can be used for outdoor, thereby has more economic worth.

Description of drawings:

Fig. 1 is a making flow chart of the present invention.

Fig. 2 is that the present invention first implements the aspect generalized section.

Fig. 3 is that the present invention second implements the aspect generalized section.

Fig. 4 is that the present invention the 3rd implements the aspect generalized section.

Fig. 5 is another embodiment of the present invention schematic diagram.

Fig. 6 is yet another embodiment of the invention schematic diagram.

The specific embodiment:

With reference to Fig. 1,2, illustrate making flow process of the present invention, the present invention utilizes the material of non-stone material as material, this material can be clamping plate, the core plate, the wood materials that hardness such as the close plate squeezing of wood chip system are lower, plastics and fibrous plate etc., because it is easier to utilize, can lower not existing together cut according to the material hardness of substrate 10, the methods of forming such as compression and injection molding, material promptly be can be made into the substrate 10 of various kenel through processing and forming, mat one spray gun (figure does not show) on average sprays cloth coating with per 1 square metre of speed of 5 minutes on the surface of substrate 10 again, wherein coating is by adhesive, stone material and additive are formed, adhesive can be water-base resin or thermosetting resin, and stone material can be stone flour, aggregate chips, the waste material of cutting stone material such as flag or crushed stone, then can be the true effect that pigment is used increases stone material as for additive, or can be the dry solidification time that dry catalyst is used quickening coating; The mixed proportion of above-mentioned coating is 30%～70% adhesive, the stone material of 30%-70%, the additive of 0.5%-1.0%, and the mixed proportion of adhesive and stone material was the best with 1: 1; After the surface of substrate 10 attaches coating fully, through about 20～30 hours dry solidification time-histories, coating promptly hardens and makes the surface of base material 10 form an imitative stone material layer 20, after the above-mentioned step of mat, can make the outward appearance of a non-stone material substrate 10 have the effect of stone material.

Because coating of the present invention is to be coated on to solidify to form imitative stone material layer 20 on the substrate 10, so imitative stone material layer 20 be according to originally be cut into kenel diversified than the graceful lines sense of tool substrate 10 shapes and decide, except that the desktop of table shown in Figure 2 tool is cut edge 11 the simple and easy vertical bar design, Fig. 3, among 4 the embodiment, more can find out the various different kenels that substrate 10 of the present invention is made moulding, it is circular-arc that its desktop side cut 11 can be made into single or multiple lift, also can be made into the oblique shape of leading of tool step therein, or can make stepped in the bottom surface of substrate 10, form when allowing imitative stone material layer 20 curing molding and the substrate 10 existing desktops 10 same kenels of cutting edge, allow manufactured goods outward appearance of the present invention have splendid aesthetic feeling.

With reference to Fig. 5,6; because imitative stone material layer 20 hardness of substrate 10 and last moulding thereof are lower; thereby various material can be made in order to accept the table pin group 30 of desktop; and the mat locking part directly locks in substrate 10 inboards; and constitute a table tool attractive in appearance, in addition, can on the substrate 10 of table tool, offer a perforation 12; be inserted in a protective sleeve 60 and plug a sunshading umbrella 70 in perforation 12, making it form one can be at the occasional table tool of outdoor application.

In sum, the present invention utilizes hardness lower, weight is lighter, the non-stone material material that price is lower is processed to form the furniture substrate 10 of many types of attitude, coating with the approximate true stone material of hybrid density evenly is coated with curing molding one imitative stone material layer 20 again, not only can significantly reduce price, weight, hardness, and the sculpture of its material is high and its outward appearance can be done the design of multiple variation, its vision is all identical with stone material with touch feeling, adding that plurality of raw materials draws materials all can be directly from cutting waste material, allow essence economic benefit of the present invention improve greatly, the present invention eliminated the disappearance of stone material table already fully.

Claims

1. the processing procedure of an imitation stone furniture is characterized in that comprising following making step:

A. the material that utilizes non-stone material is as material, and this material to form is processed into the substrate of predetermined kenel;

B. adhesive, stone material and additive are mixed into a coating according to default ratio;

C. above-mentioned coating is uniformly coated on above-mentioned substrate surface;

D. treat the above-mentioned substrate that is coated with coating after a dry solidification time-histories, the surface of this substrate promptly forms an imitative stone material layer.

2. it is made that the processing procedure of imitation stone furniture according to claim 1, the material that it is characterized in that substrate can be the close plate squeezing of clamping plate, core plate, wood chip system.

3. the processing procedure of imitation stone furniture according to claim 1 is characterized in that the material of substrate can be plastics and fibrous plate.

4. the processing procedure of imitation stone furniture according to claim 1, the method for processing forming that it is characterized in that substrate be according to substrate material difference can be cut, the method for forming such as compression and injection molding.

5. the processing procedure of imitation stone furniture according to claim 1, the mixed proportion that it is characterized in that coating is the adhesive of 30%-70%, the stone material of 30%-70%, the additive of 0.5%-1.0%, wherein the mixed proportion of adhesive and stone material was the best with 1: 1.

6. the processing procedure of imitation stone furniture according to claim 1 is characterized in that adhesive can be water-base resin or thermosetting resin.

7. the processing procedure of imitation stone furniture according to claim 1 is characterized in that stone material can be stone flour, aggregate chips, flag and crushed stone.

8. the processing procedure of imitation stone furniture according to claim 1 is characterized in that the pigment that additive can be increases the stone material true effect.

9. the processing procedure of imitation stone furniture according to claim 1 is characterized in that additive can be the dry catalyst of accelerating the coating dry solidification time.

10. the processing procedure of imitation stone furniture according to claim 1 is characterized in that coating dry solidification time-histories is 20～30 hours.