CN1318629C - 一种制备碳化钨颗粒增强钢基表层复合材料用复合剂 - Google Patents

一种制备碳化钨颗粒增强钢基表层复合材料用复合剂 Download PDF

Info

Publication number
CN1318629C
CN1318629C CNB2005100431889A CN200510043188A CN1318629C CN 1318629 C CN1318629 C CN 1318629C CN B2005100431889 A CNB2005100431889 A CN B2005100431889A CN 200510043188 A CN200510043188 A CN 200510043188A CN 1318629 C CN1318629 C CN 1318629C
Authority
CN
China
Prior art keywords
tungsten carbide
skin layer
composite material
layer composite
borax
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB2005100431889A
Other languages
English (en)
Other versions
CN1733958A (zh
Inventor
李秀兵
方亮
高义民
邢建东
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Xian Jiaotong University
Original Assignee
Xian Jiaotong University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Xian Jiaotong University filed Critical Xian Jiaotong University
Priority to CNB2005100431889A priority Critical patent/CN1318629C/zh
Publication of CN1733958A publication Critical patent/CN1733958A/zh
Application granted granted Critical
Publication of CN1318629C publication Critical patent/CN1318629C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种制备碳化钨颗粒(WCp)增强钢基表层复合材料用复合剂，该复合剂由下列重量配比材料构成：热固型水溶性酚醛树脂和硼砂15～30%，300目铝粉、270目高碳铬铁粉和270目钼铁粉的混合物1～7%，余量为水。本发明的制备WCp增强钢基表层复合材料用复合剂具有与WC颗粒润湿性好，粘结强度适度，发气量低，不良残留物少，消除金属机体与颗粒之间界面上的诸如氧化铁堆积缺陷的作用强，改善复合材料中的基体材料的组织和性能等特点，为实现通过铸渗法制备WCp增强钢基表层复合材料工件奠定了基础。

Description

一种制备碳化钨颗粒增强钢基表层复合材料用复合剂
技术领域
本发明属于制备复合材料过程中使用的一种材料，特别涉及一种制备碳化钨颗粒(WCp)增强钢基表层复合材料用复合剂。
背景技术
铸渗工艺制备WCp增强钢基表层复合材料，则是将作为增强相的WC颗粒预先固定在铸型型腔的特定位置，然后注入钢液，钢液浸润WC颗粒并渗透到其中的间隙中去，存在一定程度的界面交互作用，最终在铸件表面形成一层WCp增强钢基复合材料。典型工艺是普通铸渗工艺和负压铸渗工艺。特别是普通铸渗工艺在理论上具有工艺简单、耗能较少、生产周期短、设备投入少和对工件大小和形状的适应性强、生产成本低、易于大批量工业化生产等优点。
但是综合上述已有的制备技术，不难发现在铸渗工艺的运用过程中尚存在许多不足。如复合层与基体结合不良，界面上堆积氧化铁杂质；不当使用粘结剂，导致复合层厚度不均匀，表面不平整，复合层内存在气孔和夹渣等缺陷；预制压坯必须配备相应的压力成型设备和模具，延长了生产周期，使产品的制造成本显著增加；难以制备增强颗粒与基体材料润湿性较好的铸渗复合层；负压铸渗工艺需要相应的设备，成本投入高，生产周期长，难以制造较大的零部件等。之所以存在上述不足，其主要原因有两个：1)单纯粘结剂的观点，以及粘结剂选用不当；2)对铸渗过程中，颗粒与基体之间界面处发生的冶金现象认识不够深入，未采取措施消除界面上堆积氧化铁的问题。
发明内容
本发明的目的在于，提供一种制备WCp增强钢基表层复合材料用复合剂。发明的基本思路为：骨干材料采用热固型水溶性酚醛树脂硼砂。通过复合剂中加入热固型水溶性酚醛树脂，提供必要的粘结强度；通过复合剂中加入硼砂，部分消除金属机体与颗粒之间界面上的诸如氧化铁堆积的缺陷；辅助材料采用300目铝粉、270目高碳铬铁粉和270目钼铁粉，部分消除金属机体与颗粒之间界面上的诸如氧化铁堆积的缺陷，同时改善复合材料中的基体材料的组织和性能；骨干材料溶解在水中，辅助材料分散在溶液里，制成复合剂。
为了实现上述任务，本发明采取的技术解决方案是，一种制备WCp增强钢基表层复合材料用复合剂，其特征在于，该复合剂由下列重量配比材料构成：热固型水溶性酚醛树脂和硼砂15～30％，300目铝粉、270目高碳铬铁粉和270目钼铁粉的混合物1～7％，余量为水。
所述的热固型水溶性酚醛树脂和硼砂的混合物为24％，300目铝粉、270目高碳铬铁粉和270目钼铁粉的混合物为5％。
所述热固型水溶性酚醛树脂和硼砂的混合物中热固型水溶性酚醛树脂和硼砂的比例为2∶1。
本发明的制备WCp增强钢基表层复合材料用复合剂具有与WC颗粒润湿性好，粘结强度适度，发气量低，不良残留物少，消除金属机体与颗粒之间界面上的诸如氧化铁堆积缺陷的作用强，改善复合材料中的基体材料的组织和性能等特点，为实现通过铸渗法制备WCp增强钢基表层复合材料工件奠定了基础。
具体实施方式
以下是发明人给出的实施例，但并不限于这些实施例。
实施例1：
骨干材料取热固型水溶性酚醛树脂16％，硼砂8％，辅助材料取300目铝粉2％，270目高碳铬铁粉2％，270目钼铁粉1％，其余为水。骨干材料溶解在水中制成溶液，辅助材料分散在溶液里，制成复合剂。将制成的复合剂充分搅拌，使其均匀后，加入到碳化钨颗粒中，继续搅拌，使复合剂均匀包覆在碳化钨颗粒上，经加热去除水份，即可浇铸。该复合剂用于制备WCp增强钢基表层复合材料轧钢导位板，铸造出的导位板表面平整光洁，复合组织与基体组织结合良好，复合材料的综合性能十分优良。
实施例2：
本实施例与实施例1所不同的是，骨干材料取热固型水溶性酚醛树脂20％，硼砂10％，辅助材料取300目铝粉3％，270目高碳铬铁粉2％，270目钼铁粉2％，其余为水。骨干材料溶解在水中制成溶液，辅助材料分散在溶液里，制成复合剂。其余均同实施例1。
实施例3：
本实施例与实施例1所不同的是，骨干材料取热固型水溶性酚醛树脂10％，硼砂5％，辅助材料取300目铝粉3％，270目高碳铬铁粉3％，270目钼铁粉1％，其余为水。骨干材料溶解在水中制成溶液，辅助材料分散在溶液里，制成复合剂。其余均同实施例1。
实施例4：
本实施例与实施例1所不同的是，骨干材料取热固型水溶性酚醛树脂12％，硼砂6％，辅助材料取300目铝粉2.5％，270目高碳铬铁粉1.5％，270目钼铁粉1％，其余为水。骨干材料溶解在水中制成溶液，辅助材料分散在溶液里，制成复合剂。其余均同实施例1。
实施例5：
本实施例与实施例1所不同的是，骨干材料取热固型水溶性酚醛树脂14％，硼砂7％，辅助材料取300目铝粉0.5％，270目高碳铬铁粉0.3％，270目钼铁粉0.2％，其余为水。骨干材料溶解在水中制成溶液，辅助材料分散在溶液里，制成复合剂。其余均同实施例1。
当然，在上述WCp增强钢基表层复合材料工件的制备过程中，也可以选择配方范围的其他比例。总之，在本申请的配方范围内，均可以达到本发明的目的。

Claims (3)

1.一种制备碳化钨颗粒增强钢基表层复合材料用复合剂，其特征在于，该复合剂由下列重量配比材料构成：热固型水溶性酚醛树脂和硼砂的混合物15～30％，300目铝粉、270目高碳铬铁粉和270目钼铁粉的混合物1～7％，余量为水。
2.如权利要求1所述的制备碳化钨颗粒增强钢基表层复合材料用复合剂，其特征在于，所述的热固型水溶性酚醛树脂和硼砂的混合物为24％，300目铝粉、270目高碳铬铁粉和270目钼铁粉的混合物为5％。
3.如权利要求1所述的制备碳化钨颗粒增强钢基表层复合材料用复合剂，其特征在于，所述热固型水溶性酚醛树脂和硼砂的混合物中热固型水溶性酚醛树脂和硼砂的比例为2∶1。
CNB2005100431889A 2005-09-05 2005-09-05 一种制备碳化钨颗粒增强钢基表层复合材料用复合剂 Expired - Fee Related CN1318629C (zh)