CN1318526C - 红外辐射节能涂料及其制备方法 - Google Patents

红外辐射节能涂料及其制备方法 Download PDF

Info

Publication number
CN1318526C
CN1318526C CNB2004100449553A CN200410044955A CN1318526C CN 1318526 C CN1318526 C CN 1318526C CN B2004100449553 A CNB2004100449553 A CN B2004100449553A CN 200410044955 A CN200410044955 A CN 200410044955A CN 1318526 C CN1318526 C CN 1318526C
Authority
CN
China
Prior art keywords
paint
agent
phosphate
agents
film forming
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB2004100449553A
Other languages
English (en)
Other versions
CN1583905A (zh
Inventor
高延敏
陈立庄
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
EAST-CHINA SHIP INDUSTRY COLLEGE
Original Assignee
EAST-CHINA SHIP INDUSTRY COLLEGE
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by EAST-CHINA SHIP INDUSTRY COLLEGE filed Critical EAST-CHINA SHIP INDUSTRY COLLEGE
Priority to CNB2004100449553A priority Critical patent/CN1318526C/zh
Publication of CN1583905A publication Critical patent/CN1583905A/zh
Application granted granted Critical
Publication of CN1318526C publication Critical patent/CN1318526C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明为一种使用方便、价格低廉、附着力大、辐射率稳定，进行分段成膜的红外辐射节能涂料。其由有机和无机成膜物质、增黑剂、玻璃粉、助剂组成，其中成膜物质包括：聚乙烯醇、硅酸盐、磷酸盐、水性酚醛树脂的混合物；增黑物质包括：TiO2、ZrO2、Cr2O3、SiC、Al2O3；玻璃粉：pbO、Bi2O3；助剂中，采用磷酸钠、六偏磷酸钠、磷酸二氢铝为分散剂，ZnO为固化剂。制备时先将树脂混合后，然后在研磨设备上进行加工，当填料粒子平均粒径达到300目以上时，过筛，包装。本发明可有效消除涂层因热胀而产生的热应力，且在常温下成膜，可采用刷涂和滚涂以及喷涂等施工方式，可经高温固化，能在1200度下长期使用。

Description

红外辐射节能涂料及其制备方法
所属技术领域
本发明属于化工涂料领域，特指一种红外辐射节能涂料及其制备方法。
背景技术
目前所使用的红外辐射涂料，附着力低，施工不便，需要高温固化，使用温度低，且液体涂料开灌后存在保存困难的缺点。例如：专利89105088和专利95103141仍存在附着力较差，辐射率不稳定的问题。
发明内容
本发明的目的是提供一种使用方便、价格低廉、附着力大、辐射率稳定，进行分段成膜的红外辐射节能涂料及其制备方法。
本发明是由有机和无机成膜物质、增黑剂、玻璃粉和助剂组成的红外辐射涂料，其中成膜物质包括：聚乙烯醇、硅酸盐、磷酸盐和水性酚醛树脂的混合物；增黑剂包括：ZrO2和Cr2O3和Al2O3或SiC或TiO2；玻璃粉：pbO和Bi2O3；助剂中，采用磷酸钠、六偏磷酸钠或磷酸二氢铝为分散剂，ZnO为固化剂；配方的质量百分比组成范围为：
聚乙烯醇1-15％，硅酸钠10-30％，磷酸钠0-5％，磷酸二氢铝0-10％和水性酚醛树脂5-8％；TiO2 0-30％，ZrO2 4-5％，Cr2O3 2-3％，SiC 0-30％和Al2O3 20-30％；pbO 3-10％和Bi2O3 0.3-1％；ZnO 10-12％和六偏磷酸钠0-5％。
该涂料生产工艺如下：
先将成膜物质与增黑剂以及玻璃粉混合后，再加入水作为溶剂，同时加入助剂，然后在研磨设备上进行加工，当填料粒子平均粒径达到300目以上时，过筛，包装。
本发明采用分段固化方法，即在常温下采用硅酸钠和聚乙烯醇以及磷酸盐固化，在250～300℃采用玻璃粉固化，在高温下硅酸盐和陶瓷材料进一步反应而固化。
本发明的优点：
(1)采用有机树脂和无机成膜物质进行成膜，采用多种增黑物质、陶瓷材料，充分考虑了底材与涂料的热胀系数，从而最大程度消除了涂层因热胀而产生的热应力。
(2)由于采用水溶性较好的高分子材料作为低温成膜物质，则可以根据使用量，用水调节成所需要的粘度进行施工，在常温下成膜，采用刷涂和滚涂以及喷涂等施工方式，克服了目前液体开灌后保存困难的缺点。
(3)由于采用不同的高温成膜物质，经高温固化，本发明能在1200度下长期使用。
(4)其具有使用方便、施工容易、价格低廉、附着力大、辐射率稳定的特点。
具体实施方式
实施例1：
本涂料按如下组分配比制备而成(质量百分比)：
聚乙烯醇5％、硅酸钠20％、水性酚醛树脂5％、TiO2 15％、Al2O3 20％、ZrO2 4％、Cr2O33％、ZnO 12％、SiC 4％、PbO 10％、Bi2O3 1％、六偏磷酸钠1％
制备过程为：分别将成膜物质，增黑剂、玻璃粉、助剂按比例混合均匀后，先在成膜物质中加入水作为溶剂，加入助剂，水的加入量为成膜物质和陶瓷填料总和的1/4，在100℃加热溶解，然后加入陶瓷填料混合分散均匀，研磨到平均径达到300目以上时，调节一定的粘度，过筛，包装。
实施例2：
本涂料按如下组分配比制备而成(质量百分比)：
聚乙烯醇10％、硅酸钾25.7％、磷酸二氢铝6％、水性酚醛树脂8％、α-Al2O3 30％、ZnO 10％、PbO 3％、Bi2O3 0.3％、ZrO2 5％、Cr2O3 2％
制备过程为：分别将成膜物质，增黑剂、玻璃粉、助剂按上述物质质量比，在预定混合槽内混合均匀后，先在成膜物质中加入水，助剂，水的加入量为成膜物质和陶瓷填料总和的1/4，然后加在分散机上混合分散，分散均匀后，在球磨机器内研磨到平均粒径达到300目以上时，加入水调和到所需要的粘度，过筛，包装。
所述实施例仅用于说明本发明技术方案，并不用于限制本发明。

Claims (2)

1.红外辐射节能涂料，其特征是由有机和无机成膜物质、增黑剂、玻璃粉和助剂组成的红外辐射涂料，其中成膜物质包括：聚乙烯醇、硅酸盐、磷酸盐和水性酚醛树脂的混合物；增黑剂包括：ZrO2和Cr2O3和Al2O3或SiC或TiO2；玻璃粉：pbO和Bi2O3；助剂中，采用磷酸钠、六偏磷酸钠或磷酸二氢铝为分散剂，ZnO为固化剂；配方的质量百分比组成范围为：
聚乙烯醇1-15％，硅酸钠10-30％，磷酸钠0-5％，磷酸二氢铝0-10％和水性酚醛树脂5-8％；TiO2 0-30％，ZrO2 4-5％，Cr2O3 2-3％，SiC 0-30％和Al2O3 20-30％；pbO 3-10％和Bi2O3 0.3-1％；ZnO 10-12％和六偏磷酸钠0-5％。
2.制备权利要求1所述的红外辐射节能涂料的方法，其特征是先将成膜物质与增黑剂以及玻璃粉混合后，再加入水作为溶剂，同时加入助剂，然后在研磨设备上进行加工，当填料粒子平均粒径达到300目以上，过筛，包装。
CNB2004100449553A 2004-06-07 2004-06-07 红外辐射节能涂料及其制备方法 Expired - Fee Related CN1318526C (zh)