CN1314845C - Microwave shielding fiber and fabricating method - Google Patents
Microwave shielding fiber and fabricating method Download PDFInfo
- Publication number
- CN1314845C CN1314845C CNB2005100135584A CN200510013558A CN1314845C CN 1314845 C CN1314845 C CN 1314845C CN B2005100135584 A CNB2005100135584 A CN B2005100135584A CN 200510013558 A CN200510013558 A CN 200510013558A CN 1314845 C CN1314845 C CN 1314845C
- Authority
- CN
- China
- Prior art keywords
- core
- microwave shielding
- shielding fiber
- skin
- microwave
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a microwave shielding fiber and a making method thereof. The microwave shielding fiber is in a skin-core structure whose skin-core volume ratio is 2: 8 to 6: 4. Skin layer material comprises components of the percentages by weight: 49 to 89.8% of skin layer polymers, 10 to 50% of conductive powder material and 0.2 to 1% of resin acceptors. Core layer material comprises components of the percentages by weight: 13 to 79.7% of core layer polymers, 20 to 85% of microwave absorbent and 0.3 to 2% of compatibilizer. The making method comprises the procedures: 1, the material is uniformly mixed according to the formula of the skin layer material, the material is squeezed and pelletized by double screws at the temperature of 180 DEG C to 290 DEG C, and the skin layer material of the microwave shielding fiber is prepared; the material is uniformly mixed according to the formula of the core layer material, the material is squeezed and pelletized by double screws at the temperature of 180 DEG C to 280 DEG C, and the core layer material of the microwave shielding fiber is prepared; 3, the skin layer material and the core layer material obtained in the step 1 and the step 2 are spun into winding wires by a skin-core compound spinning machine according to the skin-core volume ratio, the winding wires are stretched for 2 to 4 times at the temperature of 70 DEG C to 100 DEG C, and the microwave shielding fiber is obtained.
Description
Technical field
The present invention relates to functional chemical fibre and manufacture method technology thereof, be specially a kind of microwave shielding fiber and manufacture method thereof.Its IPC Main classification number plan is Int.Cl
7D01F 10/00.
Background technology
Along with the fast development of electronics technology, use the utensil of microwave source more and more, as micro-wave oven and microwave apparatus etc.Electromagnetic waves such as relevant microwave cause people's attention day by day to the harm of human body.Studies show that bigger to human body harm, the electromagnetic wave of difficult protection mainly contains microwave radiation, x-ray radiation etc.Correspondingly, the relevant research that electromagnetic wave is effectively shielded also becomes the important subject of people's growing interest.For the many patent documentation report of electromagnetic wave shielding fiber, for example, Chinese patent CN1361315 has just reported a kind of multifunctional radiation proof fabric.It is to be main base material with natural fabric and synthetic fiber, conduction, magnetic conduction, emission far infrared and oxygen release material, is processed into nano particle, relends dispersion aids and disperses to make coating and be coated on the base material and make.This several functional materials are mixed and made into the process that coating is coated in fabric face, can make the mutual interference of multiple functional mass phase, influence the shielding electromagnetic waves effect, and coating and coated fabric feel are poor, not water-fast washing comes off easily, and shield effectiveness is not lasting yet.Chinese patent CN2416573 has reported a kind of antistatic, electromagnetic shielding multifunctional fabric.It is characterized in that the surface of its base material is coated with the conductive film layer of high conductivity equably, but it can only radio wave shield, can not absorb microwave.The spy opens the viscose that clear 61-102411 has reported a kind of X-of having alpha ray shield function.Contain the barium sulfate of 40~80% average grain diameters below 1 μ m in its prescription, make through wet spinning technology, but it only has single X-alpha ray shield function.Chinese patent CN 1089314A has then reported a kind of multi-function electromagnetic radiation shielding fibre and manufacture method thereof.It is characterized in that this fiber and (B) and its functional additive separately by fibre-forming polymer (A), X-ray material, radio and ultraviolet radiation absorber, and improve between the two that the auxiliary agent of compatibility constitutes.Though it has the function of shielding of X-ray, radio and ultraviolet radiation, do not have the microwave absorption function.The relevant document that comprises the micro-wave screening function and have multiple electro-magnetic wave absorption screening functional fibre is not simultaneously seen open report as yet.
Summary of the invention
At the deficiencies in the prior art, the technical problem that quasi-solution of the present invention is determined has provided a kind of microwave shielding fiber and manufacture method technology thereof.It has the comprehensive function of shielding that absorbs such as good microwave, static, radio wave and X-ray, and good hand touch is suitable for taking simultaneously, can water-fastly wash, and has the function persistence.
The technical scheme that the present invention solves the technical problem of described microwave shielding fiber is: design a kind of microwave shielding fiber, it has skin-core structure, and the core-skin volume ratio is 2: 8-6: 4; The percentage by weight prescription of its cortex material is: cortex polymer 49-89.8%, conduction powder 10-50%, coupling agent 0.2-1%; The percentage by weight prescription of its core layer material is: core layer polymer 13-79.7%, microwave absorption 20-85%; Bulking agent 0.3-2%.
The technical scheme that the present invention solves the technical problem of described microwave shielding fiber manufacture method is: a kind of manufacture method of microwave shielding fiber, and this method is undertaken by following technology:
1. make the microwave shielding fiber cortex material: after by the prescription of described cortex material cortex polymer, conduction powder and coupling agent evenly being mixed, under 180-290 ℃ of temperature, extrude through twin-screw, granulation obtains described microwave shielding fiber cortex material;
2. make the microwave shielding fiber core layer material: after by the prescription of described core layer material core layer polymer, microwave absorption, bulking agent evenly being mixed, under 180-280 ℃ of temperature, extrude through twin-screw, granulation obtains described microwave shielding fiber core layer material;
3. make core-skin composite microwave shielding fiber: microwave shielding fiber cortex material and core layer material with above-mentioned 1,2 step gained by described core-skin volume ratio, spin out undrawn yarn with core-skin composite spinning silk machine; Again with undrawn yarn under 70-100 ℃ of temperature, stretching 2-4 doubly can obtain described core-skin composite microwave shielding fiber.
Microwave shielding fiber of the present invention is owing to adopted core-sheath composite structure, functional materials conduction powder and microwave absorption are blended in the cortex and the sandwich layer of microwave shielding fiber respectively, thereby the effect interference problem that caused of the material blend that can solve two kinds of different mechanisms of action better, thereby the actual shielding action that can improve microwave shielding fiber.Secondly, the design of the conductive materials of microwave shielding fiber of the present invention helps improving the electric conductivity of fiber at the cortex of fiber, improves its antistatic and effect radio wave shield; And microwave absorption designs the sandwich layer in microwave shielding fiber, is convenient to absorb microwave, shielding X-ray.Microwave shielding fiber manufacturing approach craft of the present invention is simple, does not need special installation, is suitable for industrial applications.After measured, the microwave reflection attenuation rate of microwave shielding fiber of the present invention is about 10db, and the X-alpha ray shield rate of fiber can be up to 90%.
The specific embodiment
A kind of microwave shielding fiber of the present invention's design, it has skin-core structure, and the volume ratio of core-skin layer is 2: 8-6: 4; The percentage by weight prescription of its cortex material is: cortex polymer 49-89.8%, conduction powder 10-50%, coupling agent 0.2-1%; The percentage by weight prescription of its core layer material is: core layer polymer 13-79.7%, microwave absorption 20-85%; Bulking agent 0.3-2%.
The manufacture method of microwave shielding fiber of the present invention is to be undertaken by following technology:
1. make the microwave shielding fiber cortex material: after by described cortex material prescription cortex polymer, conduction powder and coupling agent evenly being mixed, under 180-290 ℃ of temperature, extrude through twin-screw, granulation obtains described microwave shielding fiber cortex material;
2. make the microwave shielding fiber core layer material: after by described core layer material prescription core layer polymer, microwave absorption, bulking agent evenly being mixed, under 180-280 ℃ of temperature, extrude through twin-screw, granulation obtains described microwave shielding fiber core layer material;
3. make core-skin composite microwave shielding fiber: microwave shielding fiber cortex material and core layer material with above-mentioned 1,2 step gained by described core-skin volume ratio, spin out undrawn yarn with core-skin composite spinning silk machine; Again with undrawn yarn under 70-100 ℃ of temperature, stretching 2-4 doubly can obtain described core-skin composite microwave shielding fiber.
The polymer that uses in the described skin of microwave shielding fiber of the present invention and manufacture method thereof, the core layer material is conventional fibre-forming polymer: as polytrimethylene terephthalate (PTT), polybutylene terephthalate (PBT) (PBT), polycaprolactam (PA-6), polyethylene terephthalate (PET), melt index is a kind of in polypropylene (PP) of 30-50 etc.
Conduction powder in the described fiber sheath layered material of microwave shielding fiber of the present invention and manufacture method thereof is one or more in carbon black, nickel powder, copper powder, cobalt powder, the aluminium powder etc.The average grain diameter of conduction powder is 0.01-5.0 μ m.The good carbon black of the conduction preferred electric conductivity of powder, it is 0.01-0.08 μ m that commercial carbon black requires average grain diameter, and surface of carbon black is through handling.
The described coupling agent in the fiber sheath layered material of microwave shielding fiber of the present invention and manufacture method thereof is γ-glycidoxypropyltrimewasxysilane, γ-methacryloxy trimethoxy silane, N-β-(amino-ethyl)-γ TSL 8330, a kind of in the γ-An Jibingjisanyiyangjiguiwan.
Microwave absorption in the described fibre core layered material of microwave shielding fiber of the present invention and manufacture method thereof is a tri-iron tetroxide, one or more in strontium ferrite, barium ferrite, neodymium iron boron, the ferronickel boron.The average grain diameter of microwave absorption is 0.05-1.5 μ m.Selected microwave absorption is mainly used in shield microwaves, but simultaneously with shielding X-ray function.
Bulking agent in the described fibre core layered material of microwave shielding fiber of the present invention and manufacture method thereof is an isopropyl triisostearoyltitanate; three (dodecyl benzenesulfonyl) isopropyl titanate; three (two hot phosphorus acyloxy) isopropyl titanate, one or both in isopropyl tri(dioctylpyrophosphato)titanate, stearic acid, zinc stearate, the Tissuemat E.
The described core-skin volume ratio of microwave shielding fiber of the present invention and manufacture method thereof is 2: 8-6: 4; But the core-skin ratio is 3: 7-5: 5 is even more ideal.Cortex ratio as fruit fiber is excessive, and the sandwich layer ratio is too little, and the microwave absorbing property of fiber sandwich layer just reduces; Otherwise too small as the cortex ratio of fruit fiber, the sandwich layer ratio is too big, though this helps the increase of fiber microwave absorbing property, can influence the spinning properties of fiber, and practical art is bad, therefore requires core-skin layer volume ratio to be controlled in the described scope.
Microwave shielding fiber manufacture method of the present invention is used conventional equipment, and technology is simple, and processing ease is with low cost, is convenient to industrialization promotion and uses.
Below provide several specific embodiment of the present invention:
Embodiment 1:
Get 89.8 parts of (weight of dried polyethylene terephthalate, down together), average grain diameter is 10 parts of 0.01 μ m and surface treated carbon black powders, 0.2 part of γ-glycidoxypropyltrimewasxysilane, after fully mixing, extrude through twin-screw under 290 ℃, granulation produces the fiber sheath layered material; Get 13 parts of polyethylene terephthalate, average grain diameter is that the strontium ferrite magnetic powder of 0.6 μ m accounts for 85 parts, 0.5 part of Tissuemat E, 1.5 parts of isopropyl triisostearoyltitanates after fully mixing, are extruded through twin-screw under 280 ℃, granulation produces the fibre core layered material; After gained core-skin material fully dried, spin out undrawn yarn than with core-skin composite spinning silk machine by 2: 8 fiber sheath core volume; Again undrawn yarn is stretched 3 times under 100 ℃ of temperature, obtain core-skin composite microwave shielding fiber finished silk.After measured, the microwave reflection attenuation rate of gained fiber is 10db, and X-alpha ray shield rate is 91%.
Embodiment 2:
Get 49 parts of the polypropylene of melt index 50, average grain diameter is 50 parts in the copper powder material of 5 μ m, and 1 part of γ-methacryloxy trimethoxy silane after fully mixing, extrudes through twin-screw under 190 ℃, and granulation produces the fiber sheath layered material; Get 59.4 parts of the polypropylene of melt index 50, average grain diameter is that the barium ferrite magnetic powder of 1 μ m accounts for 40 parts, and 0.6 part of three (dodecyl benzenesulfonyl) isopropyl titanate after fully mixing, is extruded through twin-screw under 195 ℃, and granulation produces the fibre core layered material; After the core-skin material fully dried, be at core-skin composite spinning silk machine to spin out undrawn yarn at 5: 5 by skin, the core volume ratio of fiber; Again undrawn yarn is stretched 4 times under 70 ℃ of temperature, obtain core-skin composite microwave shielding finished silk.After measured, the microwave reflection attenuation rate of gained fiber is 8db, X-alpha ray shield rate 81%.
Embodiment 3:
Get 59.2 parts of the polypropylene of melt index 30, average grain diameter is 40 parts of the nickel powders of 1 μ m, and 0.8 part of N-β-(amino-ethyl)-γ TSL 8330 after fully mixing, extrudes through twin-screw under 180 ℃, and granulation produces the fiber sheath layered material; Get 49 parts of the polypropylene of melt index 30, barium ferrite magnetic powder accounts for 20 parts, and average grain diameter is that the NdFeB magnetic powder of 0.8 μ m accounts for 30 parts, 1 part of three (dodecyl benzenesulfonyl) isopropyl titanate after fully mixing, is extruded through twin-screw under 190 ℃, granulation produces the fibre core layered material; Be to carry out spinning at 3: 7 by skin, the core volume ratio of fiber then, again undrawn yarn stretched 3 times under 75 ℃ of temperature, can obtain described microwave shielding fiber.After measured, the microwave reflection attenuation rate of gained fiber is 7db, X-alpha ray shield rate 86%.
Embodiment 4:
Get 69.4 parts of dried polycaprolactams, average grain diameter is 30 parts in the aluminium powder material of 3 μ m, and 0.6 part of γ-An Jibingjisanyiyangjiguiwan after fully mixing, is extruded through twin-screw under 250 ℃, and granulation produces the fiber sheath layered material; Get 38.5 parts of polycaprolactams, average grain diameter is that the strontium ferrite magnetic powder of 1.3 μ m accounts for 30 parts, and ferroferric oxide magnetic powder accounts for 30 parts, 1.5 parts of isopropyl tri(dioctylpyrophosphato)titanates after fully mixing, are extruded through twin-screw under 250 ℃, granulation produces the fibre core layered material; After the core-skin material fully dried, be at core-skin composite spinning silk machine to spin out undrawn yarn at 4: 6, again undrawn yarn stretched 2 times under 95 ℃ of temperature, obtain core-skin composite finished product silk by fiber sheath, core volume ratio; After measured, the microwave reflection attenuation rate of gained fiber is 9db, X-alpha ray shield rate 89%.
Embodiment 5:
Get 79.6 parts of dried polybutylene terephthalate (PBT)s, average grain diameter is 20 parts in the cobalt powder material of 2 μ m, and 0.4 part of γ-methacryloxy trimethoxy silane after fully mixing, extrudes granulation through twin-screw under 265 ℃.Produce the fiber sheath layered material; Get 28.6 parts of polybutylene terephthalate (PBT)s, average grain diameter is that the ferronickel boron magnetic powder of 1.2 μ m accounts for 70 parts, 1.0 parts of isopropyl triisostearoyltitanates, and 0.4 part of zinc stearate after fully mixing, is extruded granulation through twin-screw under 255 ℃.Produce the fibre core layered material; Be to carry out spinning at 6: 4 by skin, the core volume ratio of fiber then, the 3 times of post processings that again undrawn yarn stretched under 90 ℃ of temperature can obtain described microwave shielding fiber.After measured, the microwave reflection attenuation rate of gained fiber is 8db, X-alpha ray shield rate 85%.
Embodiment 6:
Get dried polytrimethylene terephthalate 59.2, average grain diameter is 20 parts in the aluminium powder material of 2 μ m, and average grain diameter is 20 parts in the nickel powder material of 1 μ m, 0.8 part of γ-An Jibingjisanyiyangjiguiwan after fully mixing, is extruded through twin-screw under 250 ℃, granulation produces the fiber sheath layered material; Get 79.4 parts of dried polytrimethylene terephthalates, average grain diameter is that the strontium ferrite magnetic powder of 1.5 μ m accounts for 20 parts, and 0.6 part of stearic acid after fully mixing, is extruded through twin-screw under 250 ℃, and granulation produces the fibre core layered material; Carry out spinning and post processing by embodiment 4 methods then, can obtain described microwave shielding fiber.After measured, the microwave reflection attenuation rate of gained fiber is 6db, X-alpha ray shield rate 79%.
Embodiment 7:
Get 69.1 parts of dried polycaprolactams, average grain diameter is 10 parts of the treated carbon black powders in 0.08 μ m and surface, 20 parts in cobalt powder material, 0.9 part of N-β-(amino-ethyl)-γ TSL 8330, after fully mixing, extrude through twin-screw under 250 ℃, granulation produces the fiber sheath layered material; Get 69.2 parts of dried polycaprolactams, average grain diameter is that the NdFeB magnetic powder of 1.4 μ m accounts for 30 parts, and 0.8 part of three (dodecyl benzenesulfonyl) isopropyl titanate after fully mixing, is extruded through twin-screw under 250 ℃, and granulation produces the fibre core layered material; Carry out spinning and post processing by embodiment 4 methods then, can obtain described microwave shielding fiber.After measured, the microwave reflection attenuation rate of gained fiber is 7db, X-alpha ray shield rate 76%.
Claims (5)
1. microwave shielding fiber, it has skin-core structure, and the core-skin volume ratio is 2: 8-6: 4; The percentage by weight prescription of its cortex material is: cortex polymer 49-89.8%, conduction powder 10-50%, coupling agent 0.2-1%; The percentage by weight prescription of its core layer material is: core layer polymer 13-79.7%, microwave absorption 20-85%; Bulking agent 0.3-2%.
2. the manufacture method of the described microwave shielding fiber of claim 1, this manufacture method comprises:
(1) make the microwave shielding fiber cortex material: after by the described cortex material prescription of claim 1 cortex polymer, conduction powder and coupling agent evenly being mixed, under 180-290 ℃ of temperature, extrude through twin-screw, granulation obtains described microwave shielding fiber cortex material;
(2) make the microwave shielding fiber core layer material: after by the described core layer material prescription of claim 1 core layer polymer, microwave absorption, bulking agent evenly being mixed, under 180-280 ℃ of temperature, extrude through twin-screw, granulation obtains described microwave shielding fiber core layer material;
(3) make core-skin composite microwave shielding fiber: microwave shielding fiber cortex material and core layer material with above-mentioned (1), (2) step gained by the described core-skin volume ratio of claim 1, spin out undrawn yarn with core-skin composite spinning silk machine; Again with undrawn yarn under 70-100 ℃ of temperature, stretching 2-4 doubly obtains core-skin composite microwave shielding fiber.
3. microwave shielding fiber according to claim 1 is characterized in that described core-skin volume ratio is 3: 7-5: 5.
4. microwave shielding fiber according to claim 1 is characterized in that described conduction powder is a carbon black, and its average grain diameter is 0.01-0.08 μ m, and surface of carbon black is through handling.
5. the manufacture method of microwave shielding fiber according to claim 2 is characterized in that described conduction powder is a carbon black, and its average grain diameter is 0.01-0.08 μ m, and surface of carbon black is through handling.