CN1312233A - 一种膨胀混凝土及其低碱高效混凝土膨胀剂 - Google Patents

一种膨胀混凝土及其低碱高效混凝土膨胀剂 Download PDF

Info

Publication number
CN1312233A
CN1312233A CN 00102864 CN00102864A CN1312233A CN 1312233 A CN1312233 A CN 1312233A CN 00102864 CN00102864 CN 00102864 CN 00102864 A CN00102864 A CN 00102864A CN 1312233 A CN1312233 A CN 1312233A
Authority
CN
China
Prior art keywords
concrete
expansion
low
cement
agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 00102864
Other languages
English (en)
Other versions
CN1101794C (zh
Inventor
李志刚
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN00102864A priority Critical patent/CN1101794C/zh
Publication of CN1312233A publication Critical patent/CN1312233A/zh
Application granted granted Critical
Publication of CN1101794C publication Critical patent/CN1101794C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明提供了一种膨胀混凝土及其低碱高效混凝土膨胀剂,膨胀混凝土是由水泥10～20%、砂子20～40%、石子30～60%,外加水泥重量6～10%的膨胀剂组成,所说膨胀混凝土为补偿收缩混凝土或大膨胀接缝混凝土其特征是由经700℃－1100℃煅烧的焦宝石20－40%、硫酸铝5－20%和硬石膏40－60%共同粉磨而成,该膨胀剂的优点是膨胀率高,掺量低,碱含量低,存放时间长,不受气候条件影响,增强高强、耐酸、耐碱、成本低,工艺简单,需水量少,有利于泵送混凝土的坍落度保持,易于生产实施。

Description

一种膨胀混凝土及其低碱高效混凝土膨胀剂
本发明属于混凝土及其外加剂技术领域。
目前现有的膨胀混凝土存在着膨胀率低、含碱量大、膨胀剂用量大，混凝土的温差较大，碱集料反应大，不能满足收缩补偿混凝土和大膨胀混凝土的工程要求。
国内外现有的混凝土膨胀剂品种较多，主要都是以硫铝酸钙水泥熟料，硅铝酸盐、水泥熟料，明矾石熟料，石灰系熟料，均有不足之处，能耗高、技术要求高，成本高、生产困难，有的不利用于饮水工程，作为主要成份，引入的碱含量高，不利于抑制混凝土碱-集料反应。更为严重的作为膨胀剂主要原料，这一商品，不能满足一定的有效时间和气候条件限制，存放变质，给工程带来了隐患。水化热高不时会出现早期裂缝和水泥的水化高峰同时出现，也是给混凝土体积稳定性，带来不利影响条件。掺量加大更会增加以上矛盾。本低碱高效膨胀剂，在10％以下掺量均可达到补偿收缩混凝土结构防水，并能有效降低混凝土的温差，抑制碱-集料反应。
本发明的目的是提供一种膨胀率较高，低碱、低掺量、原材料来源易得、其生产工艺简单、易于实施、成本较低的高效膨胀剂，以及一种补偿收缩混凝土或大膨胀接缝混凝土。
本发明的一个技术方案是提供一种膨胀混凝土，其特征在于原料重量配比为：水泥10～20份、砂子20～40份、石子30～60份，外加水泥重量6～10％的膨胀剂，所说膨胀混凝土为补偿收缩混凝土或大膨胀接缝混凝土，所说膨胀剂是由经700℃-1100℃煅烧的焦宝石、硫酸铝和硬石膏经过共同粉磨而成，且原料重量配比为煅烧的焦宝石20-40％、硫酸铝5-20％和硬石膏40-60％。
本发明的另一个技术方案是提供一种低碱高效混凝土膨胀剂，其特征在于由经700℃-1100℃煅烧的焦宝石20-40％、硫酸铝5-20％和硬石膏40-60共同粉磨而成，一般比表面积大于2500cm2/g即可，原材料易得，工艺简单，成本低。
本发明的化学反应式反应机理如下：
该膨胀剂加入混凝土中，膨胀剂中的活性Al2O3将与水泥水化产物Ca(OH)2作用，形成水化铝酸三钙，然后与石膏作用生成有早强与致密作用的膨胀组份水化硫铝三钙(钙矾石)，这种产物还对水泥石有增强作用，因为它取代了较多量的Ca(OH)2有关方程式如下：
              (1)
    (2)
该膨胀剂中的氧化硅将与水泥水化得到的Ca(OH)2作用形成水泥硅酸钙，它对混凝土的后期强度有增强作用，其反应方程式为：
           (3)
可以认定，掺该膨胀剂的混凝土，早期强度主要由水化硅酸三钙、钙矾石提供，后期强度主要由水泥中的硅酸三钙与膨胀剂中带入的SiO2水化得到的水化硅酸钙提供。
本发明由于采用了新的原料及其配比来生产膨胀剂，和膨胀混凝土，其具有显著的特点和意想不到的效果，具体如下。
表1是本发明膨胀剂所使用的原料及其制成的膨胀剂的化学成份比例。
表2是本发明的实施例1-3的原料配比。
表3是本发明实施例1-3的膨胀剂的性能。
表4是本发明的膨胀剂与现有技术比较的检测报告。
表5是本发明与现有技术的膨胀剂碱含量的比较。
表6是在不同混凝土中掺入本发明膨胀剂的性能比较。
表7是由本发明膨胀剂得到膨胀混凝土的酸碱试验。
本发明的优点是显著的。
1．本膨胀剂不用各种水泥熟料，生石灰、明矾石，改变了现有膨胀剂，在一定时间存放的限制，不因气候干湿结块变质。
该产品在结块之后性能不变，加工磨细后，可继续使用，不浪费资源，不污染环境，有利于生态环境保护。
2．原材料易得，直接用矿产品焦宝石煅烧，不加任何原料，不和水泥、石灰争原料，工艺简单，成本大大的降低，社会经济效益大。
3．由于该膨胀剂开拓新的原料、质量有保证，掺量小、低碱、有利于抑制碱-集料反应。
4．低碱高效膨胀剂，可以制造高致密，高强混凝土，保证了混凝土耐久、耐酸、耐碱，作为抗硫酸盐混凝土是较为理想的。
5．改变了现有的膨胀剂需水量大，降低水化热，推迟水泥水化高峰，有利于泵送混凝土和大流动混凝土，适用于搅拌站，改变了现有的膨胀剂水化热高的缺点。
6．按日本JISA6202-1980或中国JC476-92混凝土膨胀标准检验，产品均高于规定标准，也高于现有的产品性能，与其膨胀率、强度、抗拉、抗折强度一样，掺量就可以减少。
7．使用该膨胀剂6-8％可制备实偿收缩混凝土，8-10％可制备大膨胀剂缝混凝土，可形成0.2-0.1MPa自应力值，收到抗裂防渗之效果。填补了中国膨胀剂低碱、低掺量的空白。
对比例：一种膨胀混凝土，分别由不同所水泥：普通硅酸盐水泥、矿渣水泥、火山灰水泥、矾土水泥、粉煤灰水泥等18份、砂子28份、石子54份，外加水泥重量的8％本发明的膨胀剂，经搅拌混合而成，其性能比较见表6。
实施例1：制备一种膨胀剂，原料配比为经800℃煅烧的焦宝石40％、硫酸铝10％和硬石膏50％，将它们固体粉磨成细度为2500cm2/g即可。
实施例2：制备一种膨胀剂，原料配比为经800℃煅烧的焦宝石35％、硫酸铝5％和硬石膏60％，将它们固体粉磨成细度为2500cm2/g即可。
实施例3：制备一种膨胀剂，原料配比为经800℃煅烧的焦宝石30％、硫酸铝15％和硬石膏55％，将它们固体粉磨成细度为2500cm2/g即可。
实施例4：一种补偿收缩混凝土，是由水泥10份、砂子20份、石子30份，外加水泥重量的6％膨胀剂，经搅拌混合而成，其中膨胀剂用实施例1中的膨胀剂。
实施例5：一种大膨胀接缝混凝土，是由水泥20份、砂子30份、石子40份，外加水泥重量的10％膨胀剂，经搅拌混合而成，其中膨胀剂用实施例2中的膨胀剂。
实施例6：一种膨胀混凝土，是由水泥15份、砂子25份、石子55份，外加水泥重量的8％膨胀剂，经搅拌混合而成，其中膨胀剂用实施例3中的膨胀剂。
化学成份表    表1
项别     SiO2     Al2O3     Fe2O3  TIO2     CaO     SO3     MgO  LOSS 配比％
焦宝石     51.46     41.54     1.68   -     0.72     -     0.93     0.92     40
硬石膏     1.79     0.37     0.14   -     39.6     54.76     0.79     -     50
硫酸铝     1.2   -     8.28     0.02     10
膨胀剂     53.25     43.11     1.82   -     40.32     63.04     1.72     0.94     100
组份配比    表2
实施例编号     组分配比％
    焦宝石     硬石膏     硫酸铝
    实施例1     40     50     10
    实施例2     35     60     5
    实施例3     30     55     15
本发明膨胀剂的性能    表3
实施例号 替代水泥率％     项别     3d     7d  14d  28d  42d  180d  360d     备注
01 8 限制膨胀率％抗折强度MP抗压强度MPa   0.034  0.0625.939.2  0.0496.849.5  0.0778.053.8  0.0888.0561.5  0.1078.164.7  0.7098.566.2     水养
02 8 限制膨胀率％抗折强度Mpa抗压强度MPa   0.0273.919.8  0.0535.132.3  0.0796.541.2  0.0928.149.7  0.1009.063.0  0.1059.868.4  0.1308.468.7     水养
03 8 限制膨胀率％抗折强度MPa抗压强度MPa  0.0346.637.5  0.0447.045.0  0.0607.350.6  0.1208.562.5  0.1309.669.7  0.1359.769.8     水养
本发明膨胀剂与现有技术相比的检测报告    表4
名    称 JC476-92标准规定值 AEA UEA CEA 本发明膨胀剂
    含水率％     5.0     2.1     1.8     2.1     2
    氧化镁％     5.0     1.25     2.1     1.1     1.8
细度 水筛法％≤     10.0     8.6     8.3     8.8     82
凝结时间 初凝(min)≥     45     1.50     1.6     16.5     108
    终凝(h)≤     10.0     3.50     2.41     3.40     2.50
限制膨胀率％ 水中14d等品≥     0.04     0.056     0.051     0.051     0.057
    合格品≥     0.02
空气中28≥     -0.02     0.008     0.007     0.007     0.008
抗压强度MPa     7d     30.0     44.8     41.0     43.2     44.5
    28d≥     47.0     56.2     63.2     54.8     64.5
抗折强度MPa     7d≥     5.0     6.7     6.2     6.8     7.5
    28d     6.8     8.8     9.2     8.6     9.8
    掺量(为水泥重量的百分比)     12     12     12     8
碱含量对比表    表5
序号 膨胀剂名称     主要组成 碱含量％ 生产国
No.1 CSA膨胀剂 硫铝酸熟料 1.9～2.1 日本
No.2 UEA膨胀剂 硫铝酸钙熟料、硬石膏、明矾石 1.0～1.5 中国
No.3 U-Ⅱ膨胀剂 天然明矾石、煅烧明矾石、硬石膏 1.7～2.0 中国
No.4 硫铝酸盐膨胀 硫铝酸钙熟料硬石膏、明矾石 1.0～1.5 中国
No.5 硫铝剂酸钙膨胀剂 粉煤灰、氟石膏 1.2～1.4 中国
No.6 铝酸钙膨胀剂 铝酸钙熟料、硬石膏、明矾石 0.71～1.0 中国
No.7 明矾石膨胀剂 明矾石、石膏 2.5～3.0 中国
No.8 U-Ⅲ膨胀剂 硅铝酸盐熟料、明矾石、硬石膏 0.9～1.2 中国
No.9 石灰系膨胀剂 石灰系熟料 1.2～1.4 中国
No.10 本发明高效膨胀剂 焦宝石，硬石膏，硫酸铝 0.4～0.6 中国
在不同混凝土中掺入本发明膨胀剂的性能比较    表6
混凝土中所用水泥品种 掺入本发明膨胀剂％ 强度增长率 抗收缩开裂性 放热速度     耐化学侵蚀性
硫酸盐 弱酸 海水
普通硅酸盐水    泥     0 中等 中等 中等 低 低 低
    8 高 很高 较低 高 高 高
矿渣水泥     0 中等 中等 中等 中 低 低
8 高 很高 较低 高 高 高
火山灰水泥     0 低 低 低 高 高 中
    8 高 很高 较低 高 高 高
矾土水泥     0 很高 低 很高 很 高 高
    8 高 很高 较低 高 高 高
粉煤灰水泥     0 低 低 低 高 高 中
    8 高 很高 较低 高 高 高
本发明的膨胀混凝土的酸碱试验    表7
序号 水泥用量(kg/m3) 水灰比 膨胀剂掺量％ 侵蚀介质     抗压强度(MPa)
28d  90d  180d  14  27
 1  380  0.50     8     水中 54.8  61.3  64.3  75.0  76.2
 2  380  0.50     8  0.02N硫酸 54.8  57.9  66.2  66.4  68.5
 3  380  0.50     8     0.05碱 54.8  63.0  66.7  74.5  75.5

Claims (2)

1．一种膨胀混凝土，其特征在于原料重量配比为：水泥10～20份、砂子20～40份、石子30～60份，外加水泥重量6～10％的膨胀剂，所说膨胀混凝土为补偿收缩混凝土或大膨胀接缝混凝土，所说膨胀剂是由经700℃-1100℃煅烧的焦宝石、硫酸铝和硬石膏经过共同粉磨而成，且原料重量配比为煅烧的焦宝石20-40％、硫酸铝5-20％和硬石膏40-60％。
2．一种低碱高效混凝土膨胀剂，是由经700℃-1100℃煅烧的焦宝石、硫酸铝和硬石膏经过共同粉磨而成，其特征在于原料重量配比为煅烧的焦宝石20-40％、硫酸铝5-20％和硬石膏40-60％。
CN00102864A 2000-03-06 2000-03-06 一种膨胀混凝土及其低碱混凝土膨胀剂 Expired - Fee Related CN1101794C (zh)