CN1306084C - 改性的活性炭纤维的制备方法 - Google Patents
改性的活性炭纤维的制备方法 Download PDFInfo
- Publication number
- CN1306084C CN1306084C CNB2003101064430A CN200310106443A CN1306084C CN 1306084 C CN1306084 C CN 1306084C CN B2003101064430 A CNB2003101064430 A CN B2003101064430A CN 200310106443 A CN200310106443 A CN 200310106443A CN 1306084 C CN1306084 C CN 1306084C
- Authority
- CN
- China
- Prior art keywords
- activated carbon
- carbon fiber
- substrates
- present
- added
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及改性的活性炭纤维吸附材料的制备方法,本发明是以活性炭纤维(ACF)为基材,其上负载有纳米二氧化钛;其制备方法主要步骤是:在2~5%的硫酸钛溶液中加入0.3%~0.5%的乙二醇单甲醚,搅拌并加入活性炭纤维;加热后加入碳酸氢氨饱和溶液以调节料液的pH值至5~6;取出滤干并于烘箱保温;在氮气保护下烧结。本发明可以有效去除卷烟烟气中的焦油、苯等有害成分,还可用于毒气和有害气体防护、生活环境空气净化及水处理等领域。
Description
技术领域
本发明涉及改性的活性炭纤维吸附材料,可以用来吸附卷烟等毒气及其它有害气体、物质防护与处理
背景技术
众所周知,有害气体大量存在并且严重影响人们的身体健康。
吸烟有害于健康,是由于吸烟时产生的大量有害气体。卷烟中的有害物如焦油、尼古丁、苯并芘、甲醛、烯醛、CO、NOx等物质引起冠心病、支气管炎乃至肺癌的发病率大大增加,对健康危害很大。
降焦是目前国内外提高卷烟安全性的通用方法,主要是通过由醋酸纤维或其他材料制成的卷烟过滤嘴来达到降焦的目的。但焦油中既含有害物质,又含有许多香味物质,如果过分降低焦油含量,则会严重影响卷烟的香气和口感。此外,这类过滤嘴对极微小的气溶胶和3,4-苯并芘、甲醛、烯醛、CO、NOX等有害物质的过滤效果较差。部分卷烟厂在过滤嘴的材料中加入活性炭或沸石粉等吸附材料,以增强对有害物质的吸附过滤效果。但是这样单纯的过滤和物理吸附很难达到理想的效果。
目前,在毒气和有害气体防护、食品工业的脱色精制、生活环境空气净化、水处理等技术领域,均迫切需要吸附和处理效果好的新材料来满足市场的需求。目前对于传统活性炭纤维的吸附饱和失效问题的解决,主要是通过调节吸附操作条件(如吸附温度、pH等)来延长吸附,这种做法效果非常有限。对于再生,主要还是传统的热再生、酸碱再生、溶剂再生等,其中热再生对吸附剂的损失较大,再生设备庞大等缺点;而酸碱再生、溶剂再生是针对具体的吸附质的,不是光谱的再生方法,而且存在废液处理的问题。
发明内容
本发明的首要目的是提供一种能对去除卷烟烟气中的焦油、尼古丁、CO、苯、甲苯等物质及其它有害物质进行吸附、处理的改性的活性炭纤维的制备方法。
为实现上述目的,本发明提供的改性的活性炭纤维的制备方法,本发明是以活性炭纤维(ACF)为基材,该基材上负载有纳米二氧化钛,
本发明提供的制备方法包括以下步骤:
a、在2~5%的硫酸钛溶液中加入0.3%~0.5%的乙二醇单甲醚,搅拌均匀后加入活性炭纤维;
b、加热至75~85℃,再过1~1.5小时后加入碳酸氢氨饱和溶液以调节料液的pH值至5~6;
c、取出后滤干,放入烘箱于120±5℃保温1~2小时;
d、在氮气保护的情况下置于马弗炉中于400±10℃~500±10℃烧结1~1.5小时,冷却至室温后即得新型吸附剂。
由上述方案可知,本发明旨在针对现有技术的缺陷,以近年来发展起来的一种新型吸附材料—活性炭纤维(ACF)作为基材,负载纳米二氧化钛从而制造出一种性能优异的新型吸附材料。
作为香烟滤材使用时,一方面它不仅可以有效去除卷烟烟气中的焦油、尼古丁、CO、苯、甲苯、NOX、甲醛、烯醛类物质,另一方面不改变卷烟香味,保持卷烟良好的口感。
此外,新型吸附材料还可广泛应用于毒气和有害气体防护、食品工业的脱色精制、生活环境空气净化、水处理等领域,能够解决吸附饱和失效、再生困难等问题。采用本发明制造的新型活性炭纤维既具有良好的吸附性能,又具有良好的光催化活性。这使得在进行吸附时,可同时辅以光照,能够提高吸附效率,推迟吸附剂的失效时间,减少再生次数;待吸附失效后,可通过光照对更换下来的吸附剂进行彻底再生。这就较好地解决了活性炭纤维地吸附饱和失效,再生困难问题。
具体实施方式
在2~5%的硫酸钛溶液中加入0.3%~0.5%的乙二醇单甲醚,搅拌均匀后加入活性炭纤维,加热至75~85℃,1~1.5小时后加入碳酸氢氨饱和溶液以调节料液的pH值至5~6。取出后滤干,放入烘箱于120±5℃1~2小时恒温1小时,在氮气(常压)保护的情况下置于马弗炉中于400~500℃烧结1~1.5小时,冷却至室温后即得新型吸附剂。
采用本发明制造的新型活性炭纤维,应用在卷烟降害方面,焦油可降低60~70%左右,烟碱可降低50~60%左右,CO、苯、甲苯、Nox及醛类物质可降低60~70%左右。
采用本发明制造的新型活性炭纤维,应用于水处理、环境空气净化方面,能够提高吸附效率和吸附容量,延长吸附时间4倍以上;再生时可采用光再生,具有能耗低、无污染等优点。其原理如下:
(1)吸附与光催化氧化同步进行,既发挥了吸附剂的吸附性能,又发挥了纳米二氧化钛的光催化氧化作用,一些大分子被降解成小分子甚至矿化,这更有利于吸附剂吸附,并能够推迟吸附剂的失效时间,减少再生次数,相当于能够显著提高吸附容量。
(2)由于第一步的催化降解作用,被吸附的有机物部分已经被降解成小分子甚至矿化,到再生阶段时,更容易彻底再生,提高了再生效率。
由于光源可以是人工光源,也可以是太阳光,能耗低且无二次污染。
实施例 | 组成 | 对卷烟的降害效果 | 催化吸附效果 | 光再生效率 | ||||
硫酸钛质量浓度 | 乙二醇单甲醚 | 烧结温度(℃) | 焦油去除率 | 烟碱去除率 | 苯、甲苯及醛类去除率 | 延长吸附时间 | ||
I | 2% | 0.3% | 400 | 70% | 60% | 70% | 3倍 | 75% |
II | 3% | 0.3% | 450 | 65% | 57% | 64% | 4倍 | 80% |
III | 4% | 0.5% | 500 | 63% | 55% | 60% | 5倍 | 85% |
IV | 5% | 0.5% | 500 | 60% | 50% | 60% | 5倍 | 88% |
Claims (1)
1、一种改性的活性炭纤维的制备方法,本发明以活性炭纤维(ACF)为基材,该基材上负载有纳米二氧化钛,包括以下步骤:
a、在2~5%的硫酸钛溶液中加入0.3%~0.5%的乙二醇单甲醚,搅拌均匀后加入活性炭纤维;
b、加热至75~85℃,再过1~1.5小时后加入碳酸氢氨饱和溶液以调节料液的pH值至5~6;
c、取出后滤干,放入烘箱于120±5℃保温1~2小时;
d、在常压氮气保护的情况下置于马弗炉中于400±10℃~500±10℃烧结1~1.5小时,冷却至室温后即得新型吸附剂。