(3) summary of the invention
The object of the invention is to provide the disperse dye composition that a kind of equalization is good, dyefastness is good.
Described disperse dye composition comprises suc as formula the dyestuff A shown in (I), suc as formula the dyestuff B shown in (II), suc as formula the dyestuff C shown in (III) with suc as formula the dyestuff D shown in (IV);
Wherein, R
1, R
2Independent separately is ethyl or methoxy ethyl;
R
3, R
4Independent separately is C
1~C
4Alkyl;
In the described dye composite, the weight percentage of dyestuff A is preferably 1~90%, is preferably 10~80%; The weight percentage of dyestuff B is preferably 1~50%, is preferably 1~40%; The weight percentage of dyestuff C is preferably 1~60%, is preferably 1~50%; The weight percentage of dyestuff D is preferably 1~80%, is preferably 5~70%;
Further, described dye composite also comprises one of following or its several combination arbitrarily: the dyestuff E shown in formula V, suc as formula the dyestuff F shown in (VI), suc as formula the dyestuff G shown in (VII), suc as formula the dyestuff H shown in (VIII);
R wherein
5, R
6Independent separately is ethyl or methoxy ethyl, is preferably methoxy ethyl.
The weight percentage of above-mentioned dyestuff E is preferably 0~60%, is preferably 0~50%; The weight percentage of dyestuff F is preferably 0~50%, is preferably 0~40%; The weight percentage of dyestuff G is preferably 0~45%, is preferably 0~35%; The weight percentage of dyestuff H is preferably 0~45%, is preferably 0~35%.Allocate in described proportional range with each above-mentioned component, can obtain by blue-dark blue-black tone, dye composite of the present invention is preferably the combination of following component:
1.: A+B+C+D (R
1, R
2Be ethyl, R
3, R
4Be methyl), A: B: C: D=10~80%: 1~40%: 1~50%: 5~70% (weight ratio);
2.: A+B+C+D+E+F (R
1, R
2Be ethyl, R
3, R
4Be methyl, R
5, R
6Be methoxy ethyl), A: B: C: D: E: F=1~90%: 1~50%: 1~60%: 1~80%: 1~60%: 1~50% (weight ratio);
3.: A+B+C+D+E+G (R
1, R
2Be ethyl, R
3, R
4Be methyl, R
6Be methoxy ethyl), A: B: C: D: E: G=1~90%: 1~50%: 1~60%: 1~80%: 1~50%: 1~35% (weight ratio);
4.: A+B+C+D+F+H (R
1, R
2Be ethyl, R
3, R
4Be methyl), A: B: C: D: F: H=1~90%: 1~50%: 1~60%: 1~80%: 1~40%: 1~35% (weight ratio);
5.: A+B+C+D+G+H (R
1, R
2Be ethyl, R
3, R
4Be methyl), A: B: C: D: G: H=1~90%: 1~50%: 1~60%: 1~80%: 1~45%: 1~45% (weight ratio);
6.: A+B+C+D+E+F+G (R
1, R
2Be ethyl, R
3, R
4Be methyl, R
5, R
6Be methoxy ethyl), A: B: C: D: E: F: G=1~90%: 1~50%: 1~60%: 1~80%: 1~50%: 1~40%: 1~35% (weight ratio);
7.: A+B+C+D+F+G+H (R
1, R
2Be ethyl, R
3, R
4Be methyl), A: B: C: D: E: F: G=1~90%: 1~50%: 1~60%: 1~80%: 1~50%: 1~45%: 1~45% (weight ratio);
Prepare the employed dyestuff A of disperse dye composition of the present invention, dyestuff B, dyestuff C, dyestuff D, dyestuff E, dyestuff F, dyestuff H and be respectively disclosed dyestuffs such as patent WO02068539, patent DE1644141, patent US3835154, patent US4211696, patent WO02074864, patent EP0038439 and patent EP555179 or similar these dyestuff, method or similar method with wherein record can make at an easy rate, dyestuff G is that C.I. DISPERSE YELLOW 114 can make by common known method, also can adopt the commercially available prod.
Disperse dye composition of the present invention generally needs to add auxiliary agent and disperses.After for example dyestuff A, dyestuff B, dyestuff C, dyestuff D and/or dyestuff E and/or dyestuff F and/or dyestuff G and/or dyestuff H being mixed by above-mentioned proportioning, in the presence of auxiliary agent, water or other wetting agent, carry out corpusculed with pulverizers such as sand mill or shredders; Also dyestuff A, dyestuff B, dyestuff C, dyestuff D and/or dyestuff E and/or dyestuff F and/or dyestuff G and/or dyestuff H can be carried out corpusculed with pulverizers such as sand mill or shredders respectively in the presence of auxiliary agent, water or other wetting agent in addition handles the back and mixes with above-mentioned ratio.Usually, auxiliary agent is 0.8~5: 1 with the ratio of former dyestuff weight.
Described auxiliary agent is dyestuff dispersion agent commonly used, diffusant etc. when composite, comprise one of following or its several mixture arbitrarily: anionic dispersing agents such as the formaldehyde condensation products of the formaldehyde condensation products of naphthene sulfonic acid and alkyl benzene sulphonate (ABS), the formaldehyde condensation products of alkyl naphthalene sulfonic acid, cresol sulfonic acid, sulfonated lignin, the perhaps non-ionic dispersing agents such as ethylene oxide adduct of the ethylene oxide adduct of the segmented copolymer of oxyethane, propylene oxide, alkylphenol, polystyrene phenol.Particularly, naphthalene sulfonic acidformaldehyde condensation product such as dispersing agent NNO, alkyl naphthalene sulfonic acid formaldehyde condensation products such as Dispersant MF (condensation compound of methyl naphthalene sulfonic acid and formaldehyde), dispersing agent CNF (benzyl naphthalenesulfonate formaldehyde condensation compound) etc., sulfonated lignin such as sodium lignosulfonate (as commercial dispersants Reax 83A, Reax 85A) etc.
Disperse dye composition of the present invention, the liquid state after can corpusculed, emulsifiable paste attitude or with spray-drying process etc. carry out dried powdery, graininess is supplied with dyeing.Disperse dye composition of the present invention the hyperfine polyester fiber material is dyeed have the dye uptake height, characteristics such as fastness of dyeing excellence, favorable reproducibility, good level-dyeing property.
(4) embodiment
The invention will be further described below in conjunction with embodiment, but protection scope of the present invention is not limited to this.
Embodiment 1
With 30 gram dyestuff A (R
1, R
2Formula (I) compound for ethyl), 4 gram dyestuff B (R
3, R
4Formula (II) compound for methyl), 6 gram dyestuff C, 10 gram dyestuff D, 68 gram dispersion agent Reax85A and 140 gram pure water one are reinstated sand mill and are carried out corpusculed (making dispersion treatment), spraying drying can obtain blue color during gained disperse dye composition printed fabrics again.
Embodiment 2~14
According to the preparation method of embodiment 1, press the continuous data shown in the table 1 with dyestuff A (R
1, R
2Formula (I) compound for ethyl), dyestuff B (R
3, R
4Formula (II) compound for methyl), dyestuff C, dyestuff D, dyestuff E (R
5, R
6Formula V compound for methoxy ethyl), dyestuff F, dyestuff G and dyestuff H, piece together to mix with 68 gram Reax 83A, 140 gram pure water and be disperse dye composition of the present invention, the result is as follows:
Table 1
The embodiment title | Dyestuff A (gram) | Dyestuff B (gram) | Dyestuff C (gram) | Dyestuff D (gram) | Dyestuff E (gram) | Dyestuff F (gram) | Dyestuff G (gram) | Dyestuff H (gram) |
Embodiment 2 | 40 | 2 | 3 | 5 | 0 | 0 | 0 | 0 |
Embodiment 3 | 28 | 2 | 5 | 8 | 5 | 2 | 0 | 0 |
Embodiment 4 | 24 | 1 | 6 | 11 | 5 | 0 | 3 | 0 |
Embodiment 5 | 22 | 4 | 6 | 11 | 0 | 5 | 0 | 2 |
Embodiment 6 | 18 | 5 | 8 | 12 | 0 | 0 | 5 | 2 |
Embodiment 7 | 20 | 2 | 6 | 15 | 2 | 3 | 2 | 0 |
Embodiment 8 | 20 | 3 | 5 | 16 | 0 | 1 | 3 | 2 |
Embodiment 9 | 18 | 10 | 1 | 5 | 8 | 8 | 0 | 0 |
Embodiment 10 | 18 | 5 | 10 | 2 | 7 | 0 | 8 | 0 |
Embodiment 11 | 15 | 6 | 3 | 11 | 0 | 8 | 0 | 7 |
Embodiment 12 | 12 | 5 | 8 | 10 | 0 | 0 | 7 | 8 |
Embodiment 13 | 10 | 8 | 2 | 15 | 6 | 5 | 4 | 0 |
Embodiment 14 | 10 | 4 | 6 | 12 | 0 | 7 | 6 | 5 |
Embodiment 15
With 25 gram dyestuff A (R
1, R
2Formula (I) compound for methoxy ethyl), 5 gram dyestuff B (R
3, R
4Formula (II) compound for ethyl), 8 gram dyestuff C, 12 gram dyestuff D, 68 gram dispersion agent Reax 85A and 140 gram pure water one are reinstated sand mill and are carried out corpusculed (making dispersion treatment), spraying drying can obtain blue color during gained disperse dye composition printed fabrics again.
Embodiment 16
With 20 gram dyestuff A (R
1, R
2Formula (I) compound for methoxy ethyl), 3 gram dyestuff B (R
3, R
4Formula (II) compound for ethyl), 7 gram dyestuff C, 10 gram dyestuff D, 5 gram dyestuff E (R
5, R
6Formula V compound for ethyl), 5 gram dyestuff F, 68 gram dispersion agent Reax 85A and 140 gram pure water one reinstate sand mill and carry out corpusculed (making dispersion treatment), spraying drying can obtain the mazarine tone during gained disperse dye composition printed fabrics again.
Embodiment 17
With 20 gram dyestuff A (R
1, R
2Formula (I) compound for methoxy ethyl), 3 gram dyestuff B (R
3, R
4Formula (II) compound for ethyl), 4 gram dyestuff C, 7 gram dyestuff D, 5 gram dyestuff F, 5 gram dyestuff G, 6 gram dyestuff H, 68 gram dispersion agent Reax 85A and 140 gram pure water one are reinstated sand mill and are carried out corpusculed (making dispersion treatment), spraying drying can obtain black tone during gained disperse dye composition printed fabrics again.
Embodiment 18
Respectively getting 0.5 dispersed dye that make of gram embodiment 1~17 is dispersed in 500 ml waters, mix with 60 milliliters water after drawing 20 milliliters, transferring dye bath PH with acetic acid is 4.5~5, be warming up to 70 ℃ put into simultaneously 2 the gram hyperfine polyester fibers dye, in 30 minutes, be warmed up to 130 ℃ by 70 ℃, be incubated after 45 minutes, begin sampling when being cooled to below 90 ℃.Adopt GB GB/T3921-1997, GB/T3920-1997, GB/T5718-1997 to survey its fastness of dyeing.Test result sees Table 2.
Table 2
The embodiment title | Washing fastness (60 ℃) | Crock fastness | Sublimation fastness (180 ℃) | Tone |
Embodiment 1 | 4~5 grades | 4~5 grades | 4~5 grades | Blue |
Embodiment 2 | 4~5 grades | 4~5 grades | 4~5 grades | Dark blue |
Embodiment 3 | 4~5 grades | 4~5 grades | 4~5 grades | Dark blue |
Embodiment 4 | 4~5 grades | 4~5 grades | 4~5 grades | Dark blue |
Embodiment 5 | 4~5 grades | 4~5 grades | 4~5 grades | Dark blue |
Embodiment 6 | 4~5 grades | 4~5 grades | 4~5 grades | Dark blue |
Embodiment 7 | 4~5 grades | 4~5 grades | 4~5 grades | Dark blue |
Embodiment 8 | 4~5 grades | 4~5 grades | 4~5 grades | Dark blue |
Embodiment 9 | 4~5 grades | 4~5 grades | 4~5 grades | Black |
Embodiment 10 | 4~5 grades | 4~5 grades | 4~5 grades | Black |
Embodiment 11 | 4~5 grades | 4~5 grades | 4~5 grades | Black |
Embodiment 12 | 4~5 grades | 4~5 grades | 4~5 grades | Black |
Embodiment 13 | 4~5 grades | 4~5 grades | 4~5 grades | Black |
Embodiment 14 | 4~5 grades | 4~5 grades | 4~5 grades | Black |
Embodiment 15 | 4~5 grades | 4~5 grades | 4~5 grades | Blue |
Embodiment 16 | 4~5 grades | 4~5 grades | 4~5 grades | Dark blue |
Embodiment 17 | 4~5 grades | 4~5 grades | 4~5 grades | Black |