CN1304190C - 复合材料井盖 - Google Patents

复合材料井盖 Download PDF

Info

Publication number
CN1304190C
CN1304190C CNB2005100376491A CN200510037649A CN1304190C CN 1304190 C CN1304190 C CN 1304190C CN B2005100376491 A CNB2005100376491 A CN B2005100376491A CN 200510037649 A CN200510037649 A CN 200510037649A CN 1304190 C CN1304190 C CN 1304190C
Authority
CN
China
Prior art keywords
manhole cover
composite
parts
polyamide
polystyrene
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB2005100376491A
Other languages
English (en)
Other versions
CN1640655A (zh
Inventor
郭金利
赵顶江
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CNB2005100376491A priority Critical patent/CN1304190C/zh
Publication of CN1640655A publication Critical patent/CN1640655A/zh
Application granted granted Critical
Publication of CN1304190C publication Critical patent/CN1304190C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种复合材料井盖，是配套城市市政工程中预留的检查井用的井盖，包括钢筋骨架和复合材料，所述的复合材料为10～20%不饱和聚酯树脂、2～10%聚苯乙烯、2～8%聚乙烯、0.5～2%聚酰胺、0.5～2%聚碳酸酯、0.1～0.5%过苯甲酸叔丁酯、10～25%玻璃纤维和填料。本井盖模压成型，各项性能指标符合CJ/T121-2000规定。本井盖与支座支承面接触密闭，车辆驶过时平稳、无跳动、无噪音，重量轻、寿命长、可完全取代传统的铸铁井盖。

Description

复合材料井盖
一、技术领域
本发明涉及一种市政工程建设中使用的检查井井盖，确切地说是一种复合材料井盖。
二、背景技术
在城市市政建设中涉及许多地管网工程，如给、排水、供热、供电、供气、电信、通讯等。在道路、人行道、公路或广场、停车场、绿地、草坪等都预留有通往地下设施的检查井并配套检查井盖(简称井盖)，以保证行人和交通的安全。传统的井盖多为铸铁或砼预制的，这种井盖厚重、笨拙、运输和开启都不方便，座盖配合不密合，车辆驶过时有跳动，噪音大，而且铸铁件易被偷盗，留下安全隐患。随着有机复合材料的飞速发展，国家建设部于2000年颁发了《再生树脂复合材料井盖》行业标准(CJ/T121-2000)。该标准统一了用有机复合材料加工制造井盖的标准。
三、发明内容
本发明所要解决的问题是遴选合适的有机材料及其复配比例，加工出符合CJ/T121-2000标准的井盖。
本井盖包括钢筋和复合材料，所述的复合材料有以下组份及其重量百分比：
不饱和聚酯树脂          10～20％
聚苯乙烯                2～10％
聚乙烯                  2～8％
聚酰胺                  0.5～2％
聚碳酸酯                0.5～2％
过苯甲酸叔丁酯          0.1～0.5％
玻璃纤维                10～25％
填料                    余量。
复合材料各组份优选以下重量百分比：
不饱和聚酯树脂          14～18％
聚苯乙烯               4～8％
聚乙烯                 4～6％
聚酰胺                 0.8～1.2％
聚碳酸酯               0.8～1.2％
过苯甲酸叔丁酯         0.2～0.4％
玻璃纤维               14～22％
填料                   余量。
所述的填料可以是碳酸钙、凹凸棒土、膨润土等。
在复合材料中还可以加0.1～0.5％的颜料，赋于井盖一定的色彩。
本井盖采用模压成型。将复合材料各组份按比例配料后混合均匀，然后灌模，在模具内预留有钢筋骨架，最后在一定的温度下成型，冷却脱模即得井盖。
本井盖经省质检部门检测，结果如下：
  项目   结果   标准
  抗压强度MPa   40   ≥30
  抗折强度MPa   23   ≥14
  抗冲击韧性kj/m2   98   ≥95
  抗冻融性抗压强度损失率％   9   ≤13
  热老化抗压强度相对变化率％   0.3   ≤0.4
  人工老化抗折强度相对变化率％   2   ≤3
用2％的无机酸和碱进行耐腐蚀试验，不膨胀、不变形、无龟裂，表面不变色。
井盖外观压面平整，无裂纹，无影响使用性能的局部凸凹缺陷，与支座支承面按触密闭，车辆驶过时平衡无跳动、无噪音。重量轻，使用年限长，不会丢失，可完全取代传统的铸铁井盖或砼井盖。
四、具体实施方式
(一)、现以配制100重量分复合材料为例，非限定实施例叙述如下：
1、取不饱和聚酯树脂(UP)20份，聚苯乙烯树脂(PS)10份，聚乙烯树脂(PE)8份，取聚酰胺树脂(PA)2份聚碳酸酯(PC)2份，过苯甲酸叔丁酯(TBP)0.5份，玻璃纤维25份，碳酸钙(CaCO3)32.5份，混合均匀。
2、取UP 10份，PS 2份，PE 2份，PA 0.5份，PC 0.5份，TBP 0.1份，玻璃纤维10份，凹凸棒土74.9份，混合均匀。
3、取UP 18份，PS 8份，PE 6份，PA 1.2份，PC 1.2份，TBP 0.4份，玻璃纤维22份，膨润土43.2份，混合均匀。
4、取UP 14份，PS 4份，PE 4份，PA 0.8份，PC 0.8份，TBP 0.2份，玻璃纤维14份，CaCO3 62.2份，混合均匀。
5、取UP16份，PS 6份，PE 5份，PA 1份，PC 1份，TBP 0.3份，玻璃纤维18份，CaCO3 52.7份，混合均匀。
(二)井盖的加工
将上述复合材料充分搅拌混合均匀后灌入压模机内，压模机内预留有钢筋骨架，用量约为复合材料的10％左右，于140～180℃时压制10～30分钟，成型后冷却脱模即得井盖。

Claims (3)

1、一种复合材料井盖，由钢筋和复合材料组成，其特征在于：所述的复合材料有以下组份及其重量百分比：
不饱和聚酯树脂            10～20％
聚苯乙烯                  2～10％
聚乙烯                    2～8％
聚酰胺                    0.5～2％
聚碳酸酯                  0.5～2％
过苯甲酸叔丁酯            0.1～0.5％
玻璃纤维                  10～25％
填料                      余量。
2、根据权利要求1所述的复合材料井盖，其特征在于：复合材料各组份采用以下重量百分比：
不饱和聚酯树脂            14～18％
聚苯乙烯                  4～8％
聚乙烯                    4～6％
聚酰胺                    0.8～1.2％
聚碳酸酯                  0.8～1.2％
过苯甲酸叔丁酯            0.2～0.4％
玻璃纤维                  14～22％
填料                      余量。
3、根据权利要求1或2所述的复合材料井盖，其特征在于：复合材料中加入0.1～0.5％的颜料。
CNB2005100376491A 2005-01-06 2005-01-06 复合材料井盖 Expired - Fee Related CN1304190C (zh)