CN1299919C - 喷墨接受材料及使用喷墨接受材料制作的背喷灯箱片 - Google Patents
喷墨接受材料及使用喷墨接受材料制作的背喷灯箱片 Download PDFInfo
- Publication number
- CN1299919C CN1299919C CNB2004100103818A CN200410010381A CN1299919C CN 1299919 C CN1299919 C CN 1299919C CN B2004100103818 A CNB2004100103818 A CN B2004100103818A CN 200410010381 A CN200410010381 A CN 200410010381A CN 1299919 C CN1299919 C CN 1299919C
- Authority
- CN
- China
- Prior art keywords
- ink
- resin
- layer
- filler
- receiving layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种喷墨接受材料及使用喷墨接受材料制作的背喷灯箱片，喷墨接受材料包括上下两层喷墨接受体系，上层是含有填料和水溶性树脂的渗透遮盖层，下层是含有亲水性树脂和阳离子树脂的染料接受层。背喷灯箱片包含预涂黏结层的透明底基，在透明底基上涂布有含有亲水性树脂和阳离子固墨剂的染料接受层，在底基上涂布含有填料和水溶性树脂的渗透遮盖层。本发明由于采用上述喷墨接受材料和背喷灯箱片，在不同打印机上打印样张的颜色测试条，用Macbeth RD-519反射密度计测试涂层面(正面)和片基面(背面)的黄、品、青、黑四色密度，检验样张的背喷透过效果均较好。
Description
技术领域
本发明涉及一种用于广告行业制作灯箱广告、商贸展示、影楼及个人用数码照片展示以及装饰等适用于喷墨打印机的接受材料及背喷灯箱片。
背景技术
目前，喷墨打印机由于其众多的优点而越来越受到人们的欢迎，特别是它高速打印时无噪音，无需额外显影或其他程序。多喷头的使用，使它能胜任许多方面的工作。喷头上带有小细孔的喷墨打印机很受重视，喷射墨滴的方法也发明了不少，例如：静电吸引技术，压电技术，热泡技术。因此，人们需要这种能实现高速、低噪音、多色打印技术的出现。
喷墨要考虑三方面因素：打印机、墨水、接受介质。打印机控制墨滴的尺寸、数量、方位和运送转移；墨水提供形成图像的颜料；接受介质负责接受墨水。最终的喷墨打印是三者结合的产物。不过，墨水和接受介质的组成成分很大程度上影响了图像的质量好坏和稳定性。
人们都希望墨水能被快速吸收，墨滴扩散恰到好处，这样最终的图像在色彩还原、保存、贮藏等方面都具有比较大的优势。
若用聚合薄膜做记录介质会出现一个问题，那就是它的表面是疏水性或半疏水性的。必须预涂一层黏结性底层，与吸墨层结合。
喷墨打印机一般用选定样式的墨滴来形成图像，这些墨滴被涂层吸收以后形成像素点。在开始的吸收之后，颜料会继续扩散，这些扩散是必要的，以便来填充一些空白部分，获得好的图像密度。在高湿条件下，这些扩散会继续，过分的图像扩散最终导致图像锐利度和分辨率不够。
人们在努力寻找一种最佳的接受介质。人们用聚合物或它们的混合物来解决疏水性表面的问题，如美国专利4,503,111；3,889,270；4,564,560；4,555,437和4,578,285。人们也用到多涂层，如美国专利4,379,804；日本专利01041589；日本公开号86-132377；86-074879和86-41549。除此之外，还有用媒染剂与颜料混合以减少图像扩散，如美国专利4,554,181；4,578,295和4,547,405。人们还希望记录介质能有轻微的透光度和表面光泽度。这样介质的表面不能是多孔的，为了增加墨水的吸收性和亲和性，人们曾用过水溶性聚合物来形成吸墨层。如美国专利4,503,111中介绍用聚乙烯醇吡咯烷酮来做记录介质的吸墨层，它也存在缺点，如图像干燥慢，吸墨层粘性太大，纸张叠放时，发生粘连现象。美国专利5,206,071介绍了一种薄膜介质，它的基层是透明、半透明或不透明的，表面有非水溶性的吸水吸墨填充料。美国专利4,877,680中提到的一种记录介质含有基层和非疏水性吸墨层，吸墨层中含有非水溶性的聚合物。美国专利4,576,867中提到的喷墨记录纸的表面附有阳离子树脂，因此图图像耐水性和抗水性都提高了。欧洲专利0,500,021中提到的记录介质含有一个透明基层，其基层上有一个疏水的氢氧化铝层，其上还有一不透明的疏水层。
背喷介质都要有透明基层，但经常会遇到墨水透过性的问题。现在人们需要一种背喷介质，用在灯箱上，灯光透过图像射出来，从而在背面显出图像来。除此以外，介质上的图像必须明亮且生动逼真，才不影响它的户外效果。
一般的材料，因为要加白色的填料来调节介质的透过率，必然影响图像的质量，造成打印出来的图像从背面看，在灯箱中不开灯的情况下，色彩不艳丽，图像苍白。本发明的目的就是提供的透过图像效果艳丽的背喷灯箱胶片。
发明内容
本发明的目的是提供一种效果更好的喷墨接受材料及用喷墨接受材料制作的背喷灯箱片。
本发明的目的可通过以下措施来实现：
本发明包括上下两层喷墨接受体系，上层是含有填料和水溶性树脂的渗透遮盖层，下层是含有亲水性树脂和阳离子树脂的染料接受层。
本发明中的亲水性树脂为明胶、乙烯醇系聚合物、纤维素衍生物中的一种或几种。阳离子树脂是作为固墨剂来使用。作为固墨剂的阳离子树脂为至少一种选自聚乙烯吡咯烷酮、伯胺至叔胺或季胺盐的丙烯酸类单体或低聚体或聚合物、烯丙胺、二烯丙胺和氯化二烯丙基二甲基胺等胺单体的聚合物和共聚物。染料接受层中亲水性树脂和固墨剂的比例为20∶1～1∶15。透明底基为聚酯底基。渗透遮盖层含有遮盖作用的填料和作为黏结剂的树脂。遮盖填料为二氧化钛，碳酸钙，氧化铝，高岭土，硫酸钡、瓷土、煅烧瓷土等的一种或几种混合。遮盖填料选用不同尺寸的填料的组合，比例为15∶1-1∶15。当然，也可选用其他合适的材料。作为黏结剂的树脂是乙烯醇系聚合物、改性聚乙烯醇、纤维素衍生物、明胶、淀粉、阳离子淀粉、丙烯酸聚合物的一种或几种混合。渗透遮盖层中黏结性的树脂和填料的比例为15∶1～1∶15。
本发明中包含预涂黏结层的透明底基，在透明底基上涂布有含有亲水性树脂和阳离子固墨剂的染料接受层，在透明底基上涂布含有填料和水溶性树脂的渗透遮盖层。所述渗透遮盖层的涂层重量为0.2-8g/m2，染料接受层的涂层重量为2-20g/m2。或者，渗透遮盖层的涂层重量为1-5g/m2，染料接受层的涂层重量为5-18g/m2。
本发明中底基是透明的聚酯薄膜。起到黏结底基和接受层作用的黏结性底层是用气刀或刮刀涂布的方法涂在透明聚酯薄膜上的。染料接受层和渗透遮盖层是用挤压涂布的方法两层一次涂在预涂底层的聚酯薄膜上的。
本发明由于采用上述喷墨接受材料和背喷灯箱片，在不同打印机上打印样张的颜色测试条，用Macbeth RD-519反射密度计测试涂层面(正面)和片基面(背面)的黄、品、青、黑四色密度，检验样张的背喷透过效果。具体数值见表一
| 测试样 | 打印机型号 | ||||||
| Epson stylusphoto 1270 | HP deskjet3325 | Lexmark3200 | HP3500 | Novajetpro600 | |||
| 实施例a | 正面 | 黄 | 0.85 | 0.96 | 0.76 | 0.84 | 0.82 |
| 品 | 0.67 | 1.05 | 0.85 | 0.73 | 0.75 | ||
| 青 | 1.37 | 1.29 | 0.91 | 1.23 | 1.27 | ||
| 黑 | 1.09 | 1.98 | 1.68 | 1.02 | 1.14 | ||
| 背面 | 黄 | 2.28 | 1.92 | 1.99 | 2.03 | 2.04 | |
| 品 | 1.82 | 1.89 | 1.69 | 1.89 | 1.75 | ||
| 青 | 2.05 | 1.91 | 1.26 | 1.86 | 1.75 | ||
| 黑 | 3.18 | 0.77 | 0.68 | 2.38 | 2.35 | ||
| 实施例b | 正面 | 黄 | 0.76 | 0.88 | 0.69 | 0.74 | 0.80 |
| 品 | 0.68 | 0.95 | 0.72 | 0.71 | 0.73 | ||
| 青 | 1.25 | 1.27 | 0.91 | 1.15 | 1.21 | ||
| 黑 | 1.05 | 1.67 | 2.03 | 1.01 | 1.06 | ||
| 背面 | 黄 | 2.24 | 1.97 | 2.36 | 2.01 | 2.04 | |
| 品 | 1.83 | 1.99 | 1.75 | 1.85 | 1.81 | ||
| 青 | 1.84 | 2.04 | 1.27 | 1.86 | 1.79 | ||
| 黑 | 2.92 | 0.88 | 0.84 | 2.41 | 2.36 | ||
参照样采用Epson高光照片相纸，用Epson stylus photo 1270打印机打印颜色测试条，用Macbeth RD-519反射密度计测试黄、品、青、黑四色密度，具体数据见表二
| 打印机 | Epson高光照片相纸 | |||
| Epson stylusphoto 1270 | 黄 | 品 | 青 | 黑 |
| 1.65 | 1.66 | 1.96 | 2.34 | |
从上表的对比可看出，实施例获得的记录片材的背面密度不低于参照样的密度。
具体实施方式
本发明以下结合附图和实施例作以详细的描述：
实施例1
本发明中的喷墨接受材料，它包括上下两层喷墨接受体系，上层是含有填料和水溶性树脂的渗透遮盖层，下层是含有亲水性树脂和阳离子树脂的染料接受层。两层中各成分的重量值可根据具体需要设定。亲水性树脂为明胶、乙烯醇系聚合物、纤维素衍生物中的一种或几种。所述阳离子树脂是作为固墨剂来使用。作为固墨剂的阳离子树脂为至少一种选自聚乙烯吡咯烷酮、伯胺至叔胺或季胺盐的丙烯酸类单体或低聚体或聚合物、烯丙胺、二烯丙胺和氯化二烯丙基二甲基胺的胺单体的聚合物和共聚物。染料接受层中亲水性树脂和固墨剂的重量比例为20∶1。透明底基为聚酯底基。渗透遮盖层含有遮盖作用的填料和作为黏结剂的树脂。遮盖填料为二氧化钛，碳酸钙，氧化铝，高岭土，硫酸钡、瓷土、煅烧瓷土等的一种或几种混合。遮盖填料最好选用不同尺寸的填料的组合，重量比例为15∶1。作为黏结剂的树脂是乙烯醇系聚合物、改性聚乙烯醇、纤维素衍生物、明胶、淀粉、阳离子淀粉、丙烯酸聚合物的一种或几种混合。渗透遮盖层中黏结性的树脂和填料的重量比例为15∶1。
上述各物质的含量在所限定的范围内均可选择各个点值。
发明中使用上述喷墨接受材料制作的背喷灯箱片，它包含预涂黏结层的透明底基，在透明底基上涂布有含有亲水性树脂和阳离子固墨剂的染料接受层，在透明底基上涂布含有填料和水溶性树脂的渗透遮盖层。底基是透明的聚酯薄膜。起到黏结底基和接受层作用的黏结性底层是用气刀或刮刀涂布的方法涂在透明聚酯薄膜上的。染料接受层和渗透遮盖层是用挤压涂布的方法两层一次涂在预涂底层的聚酯薄膜上的。所述渗透遮盖层的涂层重量为0.2-8g/m2，染料接受层的涂层重量为2-20g/m2。或者，渗透遮盖层的涂层重量为1-5g/m2，染料接受层的涂层重量为5-18g/m2。本发明的喷墨接受材料是在透明的聚酯底基上预先涂布一层黏结性底层，然后在底基上涂布染料接受层和渗透遮盖层，上层(渗透遮盖层)首先接触墨水，下层(染料接受层)含有水溶性聚合物，固墨剂，固定染料。
本发明是在透明的聚酯基层上涂布黏结性底层是用于黏结表面疏水的聚酯片基和亲水层(染料接受层)，增加基层与接受层间的牢度。
染料接受层，透明，主要起固定染料的作用。打印过程中，当墨滴喷射到渗透遮盖层表面时，存在横向扩散和纵向扩散，染料接受层中的阳离子固墨剂对墨滴产生强烈的吸引力，墨滴中的染料分子来不及横向扩散便垂直穿过渗透遮盖层，到达染料接受层，形成色彩艳丽的图像。此层中的固墨组份与染料分子牢固结合，所得画面色彩饱和，边缘清晰，分辨率高。打印完成后，在高温高湿环境下长时间放置能保证画面不会发生泅渗、扩散等现象。
渗透遮盖层，白色，主要起着阻光和渗透的作用。采用不同尺寸的填料形成网状结构，以利于染料分子的渗透。打印的时候墨滴中的染料分子穿过此层中颗粒间的空隙到达染料接受层，墨滴中的大部分水则被渗透遮盖层吸收。
使用透明聚酯薄膜作为底基，采用渗透遮盖层和染料接受层这种两层的体系，可以缩短干燥时间，防止粘连，更重要的是打印时，染料分子透过白色遮盖层，到达染料接受层被固定。透过片基观看，图像明亮艳丽。开灯和开打灯时效果一样，这种背喷材料可用于制作灯箱，放在户内或户外。
在本发明的背喷灯箱片中，渗透遮盖层中含有填料和黏合剂。
在本发明的背喷灯箱片之中，渗透遮盖层中的填料包括至少一种颜料颗粒，最好是无机颜料颗粒，例如：碳酸钙、高岭土、滑石粉、二氧化钛、硫酸钡、氧化锌、氧化铝、氢氧化镁、硅藻土、石英颗粒、黏土、煅烧瓷土、白碳黑。
在本发明的背喷灯箱片之中，渗透遮盖层中优选颜料是二氧化钛颜料，还可包括其他白色颜料。其平均颗粒尺寸为20？m或更小。颜料最好占渗透遮盖层总固体量的10％-100％的重量百分比，更好是20％-80％。不同尺寸的颜料的比例为1∶15-15∶1，最好是1∶5-10∶1。
在本发明的背喷灯箱片之中，渗透遮盖层中的黏合剂包括至少一种水溶性高分子，例如：乙烯醇系聚合物、改性聚乙烯醇、纤维素衍生物、明胶、淀粉、阳离子淀粉、丙烯酸聚合物。
除了颜料和黏合剂外，还可按需要将一种或多种其它添加剂加入渗透遮盖层中，这些添加剂可包括增稠剂、润湿剂、分散剂、消泡剂、荧光增白剂、紫外吸收剂、防腐剂、表面活性剂、泡沫抑制剂、渗透剂、PH调节剂、增塑剂、流动改进剂。
在本发明的背喷灯箱片之中，渗透遮盖层的涂层重量为0.2-8g/m2，最好为1-5g/m2。
在本发明的背喷灯箱片之中，染料接受层中含有亲水性树脂和阳离子树脂。
在本发明的背喷灯箱片之中，染料接受层中的亲水性树脂包括至少一种水溶性高分子，例如：
在本发明的背喷灯箱片中，染料接受层中的亲水性树脂优选为明胶，因为明胶的吸水涨量大。亲水性树脂最好占染料接受层总固体量的10％～100％的重量百分比，更好是30％～90％。
在本发明的背喷灯箱片中，染料接受层中的阳离子树脂是用来固定墨滴中的染料分子，作为固墨剂的阳离子树脂为至少一种选自聚乙烯吡咯烷酮、伯胺至叔胺或季胺盐的丙烯酸类单体或低聚体或聚合物、烯丙胺、二烯丙胺和氯化二烯丙基二甲基胺等胺单体的聚合物和共聚物。例如PVPK90、PVPK30、丙烯酸二甲基氨基乙基酯、二甲基氨基苯乙烯、N-二甲丙烯酰胺等。与亲水性树脂的比例为1∶20-15∶1，最好是1∶10-5∶1。
在本发明的背喷灯箱片中，染料接受层的配方中，还应加入一些助剂，以提高喷墨打印的性能，例如：防腐剂、润湿剂、荧光增白剂、表面活性剂、PH调节剂、增塑剂、吸水剂、流平剂。
在本发明的背喷灯箱片中，染料接受层的涂层重量为2-20g/m2，最好为5-18g/m2。
实施例2：
本发明中的喷墨接受材料，它包括上下两层喷墨接受体系，上层是含有填料和水溶性树脂的渗透遮盖层，下层是含有亲水性树脂和阳离子树脂的染料接受层。两层中各成分的数量可根据具体需要设定。亲水性树脂为明胶、乙烯醇系聚合物、纤维素衍生物中的一种或几种。所述阳离子树脂是作为固墨剂来使用。作为固墨剂的阳离子树脂为至少一种选自聚乙烯吡咯烷酮、伯胺至叔胺或季胺盐的丙烯酸类单体或低聚体或聚合物、烯丙胺、二烯丙胺和氯化二烯丙基二甲基胺的胺单体的聚合物和共聚物。染料接受层中亲水性树脂和固墨剂的重量比例为10∶1。透明底基为聚酯底基。渗透遮盖层含有遮盖作用的填料和作为黏结剂的树脂。遮盖填料为二氧化钛，碳酸钙，氧化铝，高岭土，硫酸钡、瓷土、煅烧瓷土等的一种或几种混合。遮盖填料最好选用不同尺寸的填料的组合，重量比例为9∶1。作为黏结剂的树脂是乙烯醇系聚合物、改性聚乙烯醇、纤维素衍生物、明胶、淀粉、阳离子淀粉、丙烯酸聚合物的一种或几种混合。渗透遮盖层中黏结性的树脂和填料的重量比例为8∶1。
所述背喷灯箱片的构成是：
渗透遮盖层：(100份质量)
R930 10
碳酸钙 5
分散助剂 0.2
明胶 5
去离子水 78.8
8811(4％) 1
将明胶浸泡在常温的水中40分钟，升温至40℃溶解，加入分散助剂(分散剂、消泡剂等)缓慢依次在搅拌下加入填料，1500转搅拌下和玻璃珠一起碾磨8小时，加入适当的助剂(增稠剂、荧光增白剂、紫外吸收剂、防腐剂、表面活性剂、泡沫抑制剂、渗透剂、PH调节剂、增塑剂、流动改进剂)，搅拌20分钟。
接受层(100份质量)
明胶 10
PVP K90 5
苯酚(50％) 0.1
8811(4％) 0.5
去离子水 79.4
将明胶浸泡在常温的水中40分钟，升温至40℃溶解，加入PVP K90溶解后继续搅拌20分钟，加入适量的助剂(防腐剂、润湿剂、荧光增白剂、表面活性剂、PH调节剂、增塑剂、流平剂等)搅拌20分钟。
将上述的渗透遮盖层和接受层用挤压涂布的方法涂在预涂底层的聚酯薄膜上，先冷冻定型，再热风干燥。接受层涂布量为干重15g/m2，渗透遮盖层为3.5g/m2。
实施例3：
本发明中的喷墨接受材料，它包括上下两层喷墨接受体系，上层是含有填料和水溶性树脂的渗透遮盖层，下层是含有亲水性树脂和阳离子树脂的染料接受层。两层中各成分的数量可根据具体需要设定。亲水性树脂为明胶、乙烯醇系聚合物、纤维素衍生物中的一种或几种。所述阳离子树脂是作为固墨剂来使用。作为固墨剂的阳离子树脂为至少一种选自聚乙烯吡咯烷酮、伯胺至叔胺或季胺盐的丙烯酸类单体或低聚体或聚合物、烯丙胺、二烯丙胺和氯化二烯丙基二甲基胺的胺单体的聚合物和共聚物。染料接受层中亲水性树脂和固墨剂的重量比例为1∶5。透明底基为聚酯底基。渗透遮盖层含有遮盖作用的填料和作为黏结剂的树脂。遮盖填料为二氧化钛，碳酸钙，氧化铝，高岭土，硫酸钡、瓷土、煅烧瓷土等的一种或几种混合。遮盖填料最好选用不同尺寸的填料的组合，重量比例为1∶5。作为黏结剂的树脂是乙烯醇系聚合物、改性聚乙烯醇、纤维素衍生物、明胶、淀粉、阳离子淀粉、丙烯酸聚合物的一种或几种混合。渗透遮盖层中黏结性的树脂和填料的重量比例为～1∶8。
所述背喷灯箱片的构成是：
渗透遮盖层：(100份质量)
A100 5
碳酸钙 10
分散助剂 0.2
1788(10％) 40
去离子水 43.8
8811(4％) 1
将事先溶解好的PVA1788和去离子水加入容器内，加入分散助剂(分散剂、消泡剂等)缓慢依次在搅拌下加入填料，1500转搅拌下和玻璃珠一起碾磨8小时，加入适当的助剂(增稠剂、荧光增白剂、紫外吸收剂、防腐剂、表面活性剂、泡沫抑制剂、渗透剂、PH调节剂、增塑剂、流动改进剂)搅拌20分钟。
接受层(100份质量)
1788(10％) 70
PVPK30 10
8811(4％) 0.5
去离子水 19.5
将事先溶解好的PVA1788和去离子水加入容器内，加入PVP K30溶解后，继续搅拌20分钟，加入适量的助剂(防腐剂、润湿剂、荧光增白剂、表面活性剂、PH调节剂、增塑剂、流平剂等)搅拌20分钟。
将上述的渗透遮盖层和接受层用挤压涂布的方法涂在预涂底层的聚酯薄膜上，热风干燥。接受层涂布量为干重18g/m2，渗透遮盖层为4.3g/m2。
实施例4：
本发明包括上下两层喷墨接受体系，上层是含有填料和水溶性树脂的渗透遮盖层，下层是含有亲水性树脂和阳离子树脂的染料接受层。
本发明中的亲水性树脂为明胶、乙烯醇系聚合物、纤维素衍生物中的一种或几种。阳离子树脂是作为固墨剂来使用。作为固墨剂的阳离子树脂为至少一种选自聚乙烯吡咯烷酮、伯胺至叔胺或季胺盐的丙烯酸类单体或低聚体或聚合物、烯丙胺、二烯丙胺和氯化二烯丙基二甲基胺等胺单体的聚合物和共聚物。染料接受层中亲水性树脂和固墨剂的比例为1∶15。透明底基为聚酯底基。渗透遮盖层含有遮盖作用的填料和作为黏结剂的树脂。遮盖填料为二氧化钛，碳酸钙，氧化铝，高岭土，硫酸钡、瓷土、煅烧瓷土等的一种或几种混合。遮盖填料选用不同尺寸的填料的组合，比例为1∶15。当然，也可选用其他合适的材料。作为黏结剂的树脂是乙烯醇系聚合物、改性聚乙烯醇、纤维素衍生物、明胶、淀粉、阳离子淀粉、丙烯酸聚合物的一种或几种混合。渗透遮盖层中黏结性的树脂和填料的比例为1∶15。
所述背喷灯箱片的构成是：
渗透遮盖层：(100份质量)
SM-520 5
碳酸钙 16
分散助剂 0.3
明胶 10
去离子水 67.7
8811(4％) 1
将明胶浸泡在常温的水中40分钟，升温至40℃溶解，加入分散助剂(分散剂、消泡剂等)缓慢依次在搅拌下加入填料，1500转搅拌下和玻璃珠一起碾磨8小时，加入适当的助剂(增稠剂、荧光增白剂、紫外吸收剂、防腐剂、表面活性剂、泡沫抑制剂、渗透剂、PH调节剂、增塑剂、流动改进剂)，搅拌20分钟。
接受层(100份质量)
1788(10％) 50
羧甲基纤维素 1
LupasolFG 8
8811(4％) 0.5
去离子水 40.5
将羧甲基纤维素浸泡在常温的去离子水中溶涨，缓慢搅拌至溶解，加入10％PVA1788，搅拌20分钟，加入Lupasol FG，搅拌至完全溶解分钟，加入适量的助剂(防腐剂、润湿剂、荧光增白剂、表面活性剂、PH调节剂、增塑剂、流平剂等)搅拌20分钟。
将上述的渗透遮盖层和接受层用挤压涂布的方法涂在预涂底层的聚酯薄膜上，热风干燥。接受层涂布量为干重20g/m2，渗透遮盖层为5g/m2。
实施例5
本发明包括上下两层喷墨接受体系，上层是含有填料和水溶性树脂的渗透遮盖层，下层是含有亲水性树脂和阳离子树脂的染料接受层。
本发明中的亲水性树脂为明胶、乙烯醇系聚合物、纤维素衍生物中的一种或几种。阳离子树脂是作为固墨剂来使用。作为固墨剂的阳离子树脂为至少一种选自聚乙烯吡咯烷酮、伯胺至叔胺或季胺盐的丙烯酸类单体或低聚体或聚合物、烯丙胺、二烯丙胺和氯化二烯丙基二甲基胺等胺单体的聚合物和共聚物。染料接受层中亲水性树脂和固墨剂的比例为1∶10。透明底基为聚酯底基。渗透遮盖层含有遮盖作用的填料和作为黏结剂的树脂。遮盖填料为二氧化钛，碳酸钙，氧化铝，高岭土，硫酸钡、瓷土、煅烧瓷土等的一种或几种混合。遮盖填料选用不同尺寸的填料的组合，比例为1∶12。当然，也可选用其他合适的材料。作为黏结剂的树脂是乙烯醇系聚合物、改性聚乙烯醇、纤维素衍生物、明胶、淀粉、阳离子淀粉、丙烯酸聚合物的一种或几种混合。渗透遮盖层中黏结性的树脂和填料的比例为1∶11。
所述背喷灯箱片的构成是：
渗透遮盖层：(100份质量)
A100 10
R930 10
分散助剂 0.3
明胶 16
去离子水 62.7
8811(4％) 1
将明胶浸泡在常温的水中40分钟，升温至40℃溶解，加入分散助剂(分散剂、消泡剂等)缓慢依次在搅拌下加入填料，1500转搅拌下和玻璃珠一起碾磨8小时，加入适当的助剂(增稠剂、荧光增白剂、紫外吸收剂、防腐剂、表面活性剂、泡沫抑制剂、渗透剂、PH调节剂、增塑剂、流动改进剂)搅拌20分钟。
接受层(100份质量)
1799(10％) 65
PVP K90 6
8811(4％) 0.5
去离子水 24.5
将事先溶解好的PVA 1799和去离子水加入容器内，搅拌20分钟，加入PVP K90溶解后搅拌20分钟，加入适量的助剂(防腐剂、润湿剂、荧光增白剂、表面活性剂、PH调节剂、增塑剂、流平剂等)搅拌20分钟。
将上述的渗透遮盖层和接受层用挤压涂布的方法涂在预涂底层的聚酯薄膜上，热风干燥。接受层涂布量为干重18g/m2，渗透遮盖层为3.2g/m2。
在不同打印机上打印样张的颜色测试条，用Macbeth RD-519反射密度计测试涂层面(正面)和片基面(背面)的黄、品、青、黑四色密度，检验样张的背喷透过效果。具体数值见表一
| 测试样 | 打印机型号 | ||||||
| Epson stylusphoto 1270 | HP deskjet3325 | Lexmark3200 | HP3500 | Novajetpro600 | |||
| 黄 | 0.85 | 0.96 | 0.76 | 0.84 | 0.82 | ||
| 实施例A | 黄 | 0.85 | 0.96 | 0.76 | 0.84 | 0.82 | |
| 青 | 0.57 | 1.09 | 0.85 | 0.23 | 0.25 | ||
| 黑 | 1.09 | 1.98 | 1.68 | 1.02 | 1.14 | ||
| 背面 | 黄 | 2.28 | 1.92 | 1.99 | 2.03 | 2.04 | |
| 品 | 1.82 | 1.89 | 1.69 | 1.89 | 1.75 | ||
| 青 | 2.05 | 1.91 | 1.26 | 1.86 | 1.75 | ||
| 黑 | 3.18 | 0.77 | 0.68 | 2.38 | 2.35 | ||
| 实施例B | 正面 | 黄 | 0.76 | 0.88 | 0.69 | 0.74 | 0.80 |
| 品 | 0.68 | 0.95 | 0.72 | 0.71 | 0.73 | ||
| 青 | 1.25 | 1.27 | 0.91 | 1.15 | 1.21 | ||
| 黑 | 1.05 | 1.67 | 2.03 | 1.01 | 1.06 | ||
| 黄 | 2.24 | 1.97 | 2.36 | 2.01 | 2.04 | ||
| 品 | 1.83 | 1.99 | 1.75 | 1.85 | 1.81 | ||
| 青 | 1.84 | 2.04 | 1.27 | 1.86 | 1.79 | ||
| 黑 | 2.92 | 0.88 | 0.84 | 2.41 | 2.36 |
参照样采用Epson高光照片相纸，用Epson stylus photo 1270打印机打印颜色测试条，用Macbeth RD-519反射密度计测试黄、品、青、黑四色密度，具体数据见表二
| 打印机 | Epson高光照片相纸 | |||
| 黄 | 品 | 青 | 黑 | |
| 1.65 | 1.66 | 1.96 | 2.34 | |
从上表的对比可看出，实施例获得的记录片材的背面密度不低于参照样的密度。
用于实施例所用材料；
明胶---照相用明胶，焦作明胶厂生产
R-930---二氧化钛，日本ISK公司生产
A-100---二氧化钛，日本ISK公司生产
SD520---二氧化硅，北京航天赛德公司生产
PVP K90---分子量为100万左右的聚乙烯吡咯烷酮。BASF公司生产
PVP K30---分子量为5万左右的聚乙烯吡咯烷酮。BASF公司生产
Lupasol FG---聚胺类化合物，BASF公司生产
1788---聚乙烯醇，山西三维集团生产
1799---聚乙烯醇，山西三维集团生产
8811---琥珀酸二异辛酯磺酸钠，乐凯集团第二胶片厂生产
Claims (16)
1、一种喷墨接受材料，其特征在于：它包括上下两层喷墨接受体系，上层是含有填料和水溶性树脂的渗透遮盖层，下层是含有亲水性树脂和阳离子树脂的染料接受层。
2、根据权利要求1所述的喷墨接受材料，其特征在于：所述亲水性树脂为明胶、乙烯醇系聚合物、纤维素衍生物中的一种或几种。
3、根据权利要求1所述的喷墨接受材料，其特征在于：所述阳离子树脂是作为固墨剂来使用。
4、根据权利要求1或3所述的喷墨接受材料，其特征在于：所述作为固墨剂的阳离子树脂为至少一种选自聚乙烯吡咯烷酮、伯胺至叔胺或季胺盐的丙烯酸类单体或低聚体或聚合物、烯丙胺、二烯丙胺和氯化二烯丙基二甲基胺的胺单体的聚合物和共聚物。
5、根据权利要求1或2或3所述的喷墨接受材料，其特征在于：所述染料接受层中亲水性树脂和作为固墨剂的阳离子树脂的重量比例为20∶1～1∶15。
6：根据权利要求1或2或3所述的喷墨接受材料，其特征是渗透遮盖层含有遮盖作用的填料和作为黏结剂的水溶性树脂。
7：根据权利要求1或2或3所述的喷墨接受材料，其特征在于：所述填料为二氧化钛，碳酸钙，氧化铝，高岭土，硫酸钡、瓷土、煅烧瓷土中的一种或几种混合。
8：根据权利要求1或2或3所述的喷墨接受材料，其特征在于：遮盖填料选用不同尺寸的填料的组合，重量比例为15∶1-1∶15。
9：根据权利要求1或2或3所述的喷墨接受材料，其特征在于：所述作为黏结剂的水溶性树脂是乙烯醇系聚合物、改性聚乙烯醇、纤维素衍生物、明胶、淀粉、阳离子淀粉、丙烯酸聚合物中的一种或几种混合。
10：根据权利要求1或2或3所述的喷墨接受材料，其特征在于：渗透遮盖层中水溶性树脂和填料的重量比例为15∶1～1∶15。
11：一种使用如权利要求1所述的喷墨接受材料制作的背喷灯箱片，其特征在于：它包含预涂黏结层的透明底基，在透明底基上涂布有含有亲水性树脂和阳离子固墨剂的染料接受层，在透明底基上涂布含有填料和水溶性树脂的渗透遮盖层。
12：根据权利要求11所述的背喷灯箱片，其特征在于：所述底基是透明的聚酯薄膜。
13：根据权利要求11所述的背喷灯箱片，其特征在于：所述起到黏结底基和接受层作用的黏结性底层是用气刀或刮刀涂布的方法涂在透明底基上的。
14、根据权利要求11所述的背喷灯箱片，其特征在于：所述染料接受层和渗透遮盖层是用挤压涂布的方法两层一次涂在预涂底层的透明底基上的。
15、根据权利要求11所述的背喷灯箱片，其特征在于：所述渗透遮盖层的涂层重量为0.2-8g/m2，染料接受层的涂层重量为2-20g/m2。
16、根据权利要求11所述的背喷灯箱片，其特征在于：所述渗透遮盖层的涂层重量为1-5g/m2，染料接受层的涂层重量为5-18g/m2。