CN1290194A - Method for regenerating supported catalysts covered with gold particles and used for oxidising unsaturated hydrocarbons - Google Patents
Method for regenerating supported catalysts covered with gold particles and used for oxidising unsaturated hydrocarbons Download PDFInfo
- Publication number
- CN1290194A CN1290194A CN99802744A CN99802744A CN1290194A CN 1290194 A CN1290194 A CN 1290194A CN 99802744 A CN99802744 A CN 99802744A CN 99802744 A CN99802744 A CN 99802744A CN 1290194 A CN1290194 A CN 1290194A
- Authority
- CN
- China
- Prior art keywords
- catalyst
- unsaturated hydrocarbons
- propylene
- oxidation
- titanium dioxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a method for regenerating supported catalysts covered with gold particles, based on titanium dioxide or titanium dioxide hydrate and used for oxidising unsaturated hydrocarbons in a gas phase. The invention is characterised in that the catalyst is regenerated by contacting it with water, a diluted acid or a diluted hydroperoxide solution, to restore its catalytic activity. The invention also relates to the use of regenerated catalysts for oxidising ethene, propene, 1-butene or 2-butene in the gas phase.
Description
The present invention relates to a kind of method of regenerated catalyst, wherein said catalyst be used for by in the presence of molecular hydrogen in gas phase with molecular oxygen oxidation from unsaturated hydrocarbons catalytic production epoxides.The catalyst that the invention still further relates to after these regeneration is used for the application of oxidation unsaturated hydrocarbons.
Usually be lower than under 200 ℃, even there is catalyst, can not be with molecular oxygen direct oxidation unsaturated hydrocarbons in gas phase, and therefore be difficult to optionally produce easily oxidized oxidation product such as epoxides, alcohol or aldehyde, because the ensuing reaction of these oxidation products is than easier the carrying out of oxidation of employed alkene itself usually.
As unsaturated hydrocarbons, propylene oxide constitutes one of most important basic chemicals in the chemical industry.This material is used for the plastics field more than 60%, is used for the PPG of synthesis of polyurethane especially for production.In addition, the propylene oxide derivative occupies bigger market in the dihydroxylic alcohols field, in particular as lubricant and antifreeze composition.
Now, the propylene oxide in the whole world nearly 50% is synthetic by " chlorohydrin process ".All the other are 50% synthetic by " ethylene oxide process ", and this trend increases.
Chlorohydrin process (people such as F.Andreas.; Propylenchemie, Berlin 1969) in, at first,, next, obtain propylene oxide from chloropharin by isolating HCl with lime by propylene and HOCl (water and chlorine) reaction are obtained chloropharin.This method expense is big, but when snugly made full use of, this method had the selectivity (>90%) of height under high conversion.In chlorohydrin process, chlorine with unworthy calcium chloride or or the sodium-chloride water solution form lose, caused the research of today to not chloride oxidative system.
Replace inorganic oxidizer HOCl, now selected organic compound that oxygen is transferred to (ethylene oxide process) in the propylene.This indirect epoxidation is based on the following fact, and promptly organic peroxide can optionally be transferred to the oxygen in their peroxide on the alkene as hydroperoxides in liquid phase or peroxycarboxylic acid, forms epoxides.In this process, hydroperoxides are converted into alcohol and peroxycarboxylic acid is converted into acid.Hydroperoxides and peroxycarboxylic acid are produced by carrying out autoxidation with air or molecular oxygen by corresponding hydrocarbon or aldehyde respectively.An important disadvantage of indirect oxidation is the economic dependence of propylene oxide price to its coupling product market price.
Do catalyst (people such as Notari when utilizing titanium silicate (TS 1), US 4410501 (1983) and US 47 01 428) time, prove for the first time, can be under reaction condition as mild as a dove, in liquid phase with hydrogen peroxide with epoxidation of propylene, its selectivity>90% (people such as Clerici, EP-A230 949).
In liquid phase, on the titanium silicate of platinum metal, use the admixture of gas propylene oxide of molecular oxygen and molecular hydrogen, its productive rate low (JP-A 92/352771).
In EP-A 0709360 A1 people such as () Haruta, to describe the direct gaseous oxidation of propylene for the first time and formed propylene oxide, selectivity is 100%.This is in the presence of reducing agent hydrogen, with the catalytic vapor phase oxidation effect of molecular oxygen.A kind of specific usefulness nanometer-number range goldc grains coating, comprise the improved titanium dioxide of anatase as catalyst.The maximum conversion rate of propylene and productive rate are 1%.Described Au/TiO
2Catalyst only obtains to be approximately 1% propylene conversion in the very short time.For example, the typical half-life under neutral temperature (40-50 ℃) only is 100-200 minute.
So far, will be coated with goldc grains by Dilute Hydrogen Peroxide Solution and be known (people such as Thiele, J.Mol.Cat.117, pages 351-356,1997) based on the catalyst regeneration of titanium silicate.
For exploiting economy interests type propylene oxidation method, the possibility of regenerated catalyst has the importance of decision effectively.
Now be surprisingly found out that, work as water, when diluted acid or Dilute Hydrogen Peroxide Solution are handled the catalyst of inactivation, can obtain the catalytic activity of former activity maximum 80% once more.Preferably, use diluted acid (for example rare H of pH4-7.5, preferred 5.5-6
2SO
4Or HF) washs the described catalyst of inactivation.
Therefore, the present invention relates to a kind of regeneration be coated with goldc grains and based on titanium dioxide or hydrated titanium dioxide, be used for method, wherein by described catalyst is contacted its catalytic activity of regenerating with water or with diluted acid or with Dilute Hydrogen Peroxide Solution at the supported catalyst of gas phase oxidation unsaturated hydrocarbons.
Processing on the meaning of the present invention can be carried out under the temperature of room temperature or rising.In variant of the present invention, elevated pressure and/or use steam can advantageously play a role.
Can after from reactor, removing catalyst, separately handle, if perhaps catalytic oxidation propylene in the presence of hydrogen, and water or hydrogen regenerated catalyst continuously carry out then also can handling in reactor.In an embodiment of this variant of the present invention, it is favourable carrying out catalysis and regenerative operation simultaneously in the reactor that separate in a plurality of spaces connected to one another.These stages can be coupled together makes them to hocket.
It may be favourable stirring reconstituted mixt, but this is not the requirement to application of the present invention.
According to the present invention, renewable coating nanometer-number range goldc grains and based on the supported catalyst of titanium dioxide or hydrated titanium dioxide.Preferably, prepare these catalyst by " deposition-precipitation " method.
The concentration of the dilute hydrogen peroxide aqueous solution is usually at 1-10wt%, preferably in the 1-4wt% scope.
When the catalyst of the present invention regeneration is used for the oxidation unsaturated hydrocarbons, without limits to the amount of the amount of use catalyst and institute's using gases." space velocity " of the air-flow by catalyst bed per hour is typically about 0.5-20 liter/g catalyst.
Being applied under gas oxygen and the hydrogen existence of regenerated catalyst of the present invention carried out.When these gases exist under 150 ℃, except moisture, propane and CO
2Primary product outside, also form oxygenated products propylene oxide and acetone.If reaction temperature drops to<and 100 ℃, preferred 30-60 ℃, suppressed the formation of water so widely and suppressed CO fully
2Formation.Find under 30-60 ℃ temperature, except major product propylene oxide (productive rate is approximately 4-5%), to have only other component (with regard to propylene oxide, being approximately 1%) of trace.The ratio of water is 2 times (mol ratios) of propylene oxide ratio.
It is important with regard to the Space-Time yield not only that the gas phase of the inert gas that comprises propylene, oxygen, hydrogen and may exist is formed, and also is important aspect security.In theory, can use the gaseous propylene/oxygen/hydrogen/nitrogen/inert gas (for example nitrogen) of all moles composition.The preferred gas that is used for propylene oxidation is such as following: H
2/ hydrocarbon/oxygen/nitrogen: 20-80%/10-50%/1-10%/0-50%; Preferred H
2/ hydrocarbon/oxygen/nitrogen ratio is 30-75%/15-40%/3-8%/0-10%.React employed molecular oxygen and can derive from different oxygen sources, for example pure oxygen, air and other oxygen/noble gas mixtures.
Embodiment is a propylene oxide with propylene oxidation directly
The standard reaction condition: reactor is a fixed bed tubular reactor that is made of double-walled glass (diameter 1cm, long 20cm), and this reactor heats under 46 ℃ of control temperature by a water termostat device.Static mixing and temperature-controlled area territory are arranged in the upper reaches of reactor.In advance goldc grains-supported catalyst is placed on the frit.The catalyst loading be 1.8 liters/gram catalyst/hour.By the close phase delivery controller of solids the gas initial substance is measured from top to bottom and to be added in the reactor.The gas initial substance is than being O
2/ H
2/ C
3H
6=0.1/1.3/0.4 liter/hour.Reaction gas mixtures by gc analysis, (is removed CO with fid detector
2In addition, be applicable to all oxygen-containing organic compounds) and thermal conductivity detector (TCD) (be applicable to fixing gas CO, CO
2And H
20) detects.This instrument is by the control of CDR central data recording system.
Monitor the size of all catalyst goldc grains by TEM (transmission electron microscope).Preparation of Catalyst 1
In room temperature with under stirring, with 60 minutes time, with the 100mg H (AuCl that is dissolved in the 100ml deionized water
4) be added drop-wise to 10g hydrated titanium dioxide (BET specific surface 380m
2/ g, the water of sulphates content 0.6%, 12%) in the suspension in 0.3 liter of deionized water.Transfer to pH8 so that the precipitation gold hydroxide with 0.5 molar sodium carbonate solution.With faint yellow suspension decolouring.Suspension is at room temperature stirred 3 hours, and solid is separated, wash 4 times, use the 25ml deionized water at every turn.With solid 150 ℃ down dry 2 hours and 200 ℃ dry 1 hour down, then in air, with the contact catalyst of drying 250 ℃ of calcinings 2 hours and 400 ℃ of calcinings 5 hours down down.
Obtain containing the catalyst of 0.5wt% gold.It is characterized in that: TEM shows that the average grain diameter of contained nanometer-number range goldc grains is approximately 1-6nm.Table 1 is listed in the result who carries out catalytic reaction under the standard reaction condition (embodiment A).Preparation of Catalyst 2:
With 0.104g HAuCl
4* 4H
2The solution of O in 400ml distilled water is heated to 70 ℃ and also transfers to pH7.5 with the 0.1N sodium hydrate aqueous solution.Add 5g titanium dioxide (anatase-rutile mixed oxide in abundant stirring next time; The P25 that provides by Degussa), and with this batch mixed thing stirred again 1 hour.With this solids wash five times, use 3 liters of distilled water at every turn, vacuum drying at room temperature 12 hours, and 400 ℃ of calcinings 4 hours down.Obtain containing the gold-titanium deoxide catalyst of 1wt% gold.
Table 1 is listed in the result who carries out catalytic reaction under the standard reaction condition (Embodiment B).Embodiment 1-10
The regeneration and the catalytic activity of inactivation and the golden carried catalyst that water, diluted acid or Dilute Hydrogen Peroxide Solution are handled according to the present invention: embodiment 1
Will be owing to reaction inactivation and according to the catalyst (2g of Preparation of Catalyst 1 method preparation; The propylene oxide productive rate is 0.6%) be suspended in 100ml H
2Among the O, at room temperature stirred 1 hour, separation is also following dry 1 hour at 150 ℃.According to standard method, the contact catalyst that therefore obtains is used for propylene oxidation.
Table 1 is listed the result of catalytic reaction.Embodiment 2
Will be owing to reaction inactivation and according to the catalyst (2g of Preparation of Catalyst 1 method preparation; The propylene oxide productive rate is 0.6%) be suspended in 100ml H
2Among the O, stirred 1 hour down at 80 ℃, separate and 150 ℃ dry 1 hour down.According to standard method, the contact catalyst that therefore obtains is used for propylene oxidation.Embodiment 3
Will be owing to reaction inactivation and according to the catalyst (2g of Preparation of Catalyst 1 method preparation; The propylene oxide productive rate is 0.6%) be suspended in 100ml H
2Among the O, at room temperature stirred 3 hours, separation is also following dry 1 hour at 150 ℃.According to standard method, the contact catalyst that therefore obtains is used for propylene oxidation.
Table 1 is listed the result of catalytic reaction.Embodiment 4
Will be owing to reaction inactivation and according to the catalyst (2g of Preparation of Catalyst 1 method preparation; The propylene oxide productive rate is 0.6%) be suspended in 100ml 3%H
2O
2In the solution, at room temperature stirred 1 hour, separation is also following dry 1 hour at 150 ℃.According to standard method, the contact catalyst that therefore obtains is used for propylene oxidation.
Table 1 is listed the result of catalytic reaction.Embodiment 5
Will be owing to reaction inactivation and according to the catalyst (2g of Preparation of Catalyst 1 method preparation; The propylene oxide productive rate is 0.6%) be suspended in 100ml 6%H
2O
2In the solution, at room temperature stirred 1 hour, separation is also following dry 1 hour at 150 ℃.According to standard method, the contact catalyst that therefore obtains is used for propylene oxidation.
Table 1 is listed the result of catalytic reaction.Embodiment 6
Will be owing to reaction inactivation and according to the catalyst (2g of Preparation of Catalyst 1 method preparation; The propylene oxide productive rate is 0.6%) be suspended in 100ml 3%H
2O
2In the solution, stirred 1 hour down at 50 ℃, separate and 150 ℃ dry 1 hour down.According to standard method, the contact catalyst that therefore obtains is used for propylene oxidation.
Table 1 is listed the result of catalytic reaction.Embodiment 7
Will be owing to reaction inactivation and according to the catalyst (2g of Preparation of Catalyst 1 method preparation; The propylene oxide productive rate is 0.6%) be suspended in 100ml with 0.05 mole of H
2SO
4Transfer to the H of pH6
2Among the O, at room temperature stirred 3 hours, separate, 150 ℃ dry 1 hour and down 400 ℃ of calcinings 2 hours down.According to standard method, the contact catalyst that therefore obtains is used for propylene oxidation.Embodiment 8
Will be owing to reaction inactivation and according to the catalyst (2g of Preparation of Catalyst 1 method preparation; The propylene oxide productive rate is 0.6%) be suspended in 100ml with 0.05 mole of H
2SO
4Transfer to the H of pH6.5
2Among the O, at room temperature stirred 3 hours, separate, 150 ℃ dry 1 hour and down 400 ℃ of calcinings 2 hours down.According to standard method, the contact catalyst that therefore obtains is used for propylene oxidation.Embodiment 9
Will be owing to reaction inactivation and according to the catalyst (2g of Preparation of Catalyst 2 methods preparation; The propylene oxide productive rate is 0.2%) be suspended in the 500ml water, at room temperature to stir 1 hour, separation is also following dry 1 hour at 150 ℃.According to standard method, the contact catalyst that therefore obtains is used for propylene oxidation.
Table 1 is listed the result of catalytic reaction.Embodiment 10
Will be owing to reaction inactivation and according to the catalyst (2g of Preparation of Catalyst 2 methods preparation; The propylene oxide productive rate is 0.2%) be suspended in 100ml 3%H
2O
2In the solution, at room temperature stirred 1 hour, separation is also following dry 1 hour at 150 ℃.According to standard method, the contact catalyst that therefore obtains is used for propylene oxidation.
Table 1 is listed the result of catalytic reaction.
Claims (5)
1, a kind of coating goldc grains of regenerating and based on titanium dioxide or hydrated titanium dioxide, be used for method at the supported catalyst of gas phase oxidation unsaturated hydrocarbons, it is characterized in that, by described catalyst is contacted its catalytic activity of regeneration with water or with diluted acid or with Dilute Hydrogen Peroxide Solution.
2, the method for claim 1 is characterized in that, will be by the catalyst regeneration of " deposition-precipitation " method generation.
3, claim 1 or 2 method is characterized in that, described catalyst is randomly regenerated with steam under pressure.
4, claim 1 or 2 method is characterized in that working concentration is up to 10% aqueous hydrogen peroxide solution.
5, the supported catalyst of the arbitrary method regeneration of claim 1-4 is used in gas phase the epoxidised purposes of unsaturated hydrocarbons.