CN1288922A - Preparation of aqueous anticorrosive all-purpose glue - Google Patents
Preparation of aqueous anticorrosive all-purpose glue Download PDFInfo
- Publication number
- CN1288922A CN1288922A CN 99120505 CN99120505A CN1288922A CN 1288922 A CN1288922 A CN 1288922A CN 99120505 CN99120505 CN 99120505 CN 99120505 A CN99120505 A CN 99120505A CN 1288922 A CN1288922 A CN 1288922A
- Authority
- CN
- China
- Prior art keywords
- polyvinyl alcohol
- controlled
- polyacrylate
- alcohol solution
- reaction
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present method of all-purpose adhesive is characterized by that firstly the epoxy resin, butylcellosolve, op-10, polyvinyl alcohol solution and sodium silicate are mixed in turn, reaction temp. can be controlled at 38-40 deg.C, then polyacrylate is added, and the reaction temp. can be controlled at 50 deg.C, after the above-mentioned formation product is cooled to 20-25 deg.C, the polyamide is added. The weight ratio of epoxy resin, butylcellosolve, op-10, polyvinyl alcohol so lution, sodium silicate, polyacrylate and polyamide is (25-50):(2.5-10):(5-15):(75-150):(1.5-3):(50-100):(25-50).
Description
The invention belongs to tackiness agent preparation technology field, particularly a kind of preparation technology of multilayered structure LIPN emulsion interpenetrating polymer networks glue.
Original like product is mainly used in coating (not comprising Corrosion resisting paint without need of cleaning rust) and caking agent as EVA and the polyacrylic acid lipid LIPN that develops in recent years, and its scope of application is subjected to certain limitation.
The object of the present invention is to provide a kind of have water-fast, anticorrosion, nontoxic, pollution-free, the preparation technology of the aqueous anticorrosive all-purpose glue that the excellent property and the scope of application are extensive.
Technical solution of the present invention can realize according to following mode:
A kind of preparation technology of aqueous anticorrosive all-purpose glue is characterized in that: earlier Resins, epoxy, ethylene glycol butyl ether, OP-10, polyvinyl alcohol solution, water glass are mixed successively, temperature of reaction is controlled at 38-40 ℃; Add polyacrylate again, temperature of reaction is controlled at 50 ℃; Treat to add polymeric amide after above-mentioned resultant is cooled to 20-25 ℃; The weight ratio of above-mentioned raw materials thing Resins, epoxy, ethylene glycol butyl ether, OP-10, polyvinyl alcohol solution, water glass, polyacrylate, polymeric amide is followed successively by: (25-50): (2.5-10): (5-15): (75-150): (1.5-3): (50-100): (25-50).
The present invention has multiple function, excellent property.The single-component ambient cure, easy to use; Nontoxic, pollution-free, non-stimulated, water-fast, anticorrosion, bonding force is strong, can reach more than 10 years work-ing life.
Optimum implementation of the present invention is described in detail in detail below;
Embodiment 1:
A kind of preparation technology of aqueous anticorrosive all-purpose glue is characterized in: earlier Resins, epoxy, ethylene glycol butyl ether, OP-10, polyvinyl alcohol solution, water glass are mixed successively, temperature of reaction is controlled at 39 ℃; Add polyacrylate again, temperature of reaction is controlled at 50 ℃; Treat to add polymeric amide after above-mentioned resultant is cooled to 21 ℃; The weight ratio of above-mentioned raw materials thing Resins, epoxy, ethylene glycol butyl ether, OP-10, polyvinyl alcohol solution, water glass, polyacrylate, polymeric amide is followed successively by: 30: 5: 10: 80: 2: 60: 30.
Embodiment 2:
A kind of preparation technology of aqueous anticorrosive all-purpose glue is characterized in: earlier Resins, epoxy, ethylene glycol butyl ether, OP-10, polyvinyl alcohol solution, water glass are mixed successively, temperature of reaction is controlled at 40 ℃; Add polyacrylate again, temperature of reaction is controlled at 50 ℃; Treat to add polymeric amide after above-mentioned resultant is cooled to 23 ℃; The weight ratio of above-mentioned raw materials thing Resins, epoxy, ethylene glycol butyl ether, OP-10, polyvinyl alcohol solution, water glass, polyacrylate, polymeric amide is followed successively by: 45: 6: 11: 90: 2.6: 65: 45.
Product of the present invention can be used for: (1) interior exterior wall and Corrosion resisting paint without need of cleaning rust base-material; (2) caking agent; (3) polymer cement and preparation 80-100mpa high-strength concrete; (4) cement waterproof agent and early strength water-reducing agent; When this glue mixes cement 1-2%, but diminishing 20-30% can reach 28 days intensity of normal concrete in 7 days, and later stage ultimate compression strength can improve 20-30%, and tensile strength improves 1-2 doubly.(5) easily and other resin commissure in order to modification.
Claims (1)
1, a kind of preparation technology of aqueous anticorrosive all-purpose glue is characterized in that: earlier Resins, epoxy, ethylene glycol butyl ether, OP-10, polyvinyl alcohol solution, water glass are mixed successively, temperature of reaction is controlled at 38-40 ℃; Add polyacrylate again, temperature of reaction is controlled at 50 ℃; Treat to add polymeric amide after above-mentioned resultant is cooled to 20-25 ℃; The weight ratio of above-mentioned raw materials thing Resins, epoxy, ethylene glycol butyl ether, OP-10, polyvinyl alcohol solution, water glass, polyacrylate, polymeric amide is followed successively by: (25-50): (2.5-10): (5-15): (75-150): (1.5-3): (50-100): (25-50).