CN1067664C - Sodium silicate composite cementing material used in building material field - Google Patents
Sodium silicate composite cementing material used in building material field Download PDFInfo
- Publication number
- CN1067664C CN1067664C CN98116421A CN98116421A CN1067664C CN 1067664 C CN1067664 C CN 1067664C CN 98116421 A CN98116421 A CN 98116421A CN 98116421 A CN98116421 A CN 98116421A CN 1067664 C CN1067664 C CN 1067664C
- Authority
- CN
- China
- Prior art keywords
- sodium silicate
- softening
- building material
- silicon resin
- organic silicon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a sodium silicate composite gelatinizing agent applied to building material, which is a composite gelatinizing agent made from sodium silicate used as main material, 5 of 15% softening organic silicon resin, 2 to 6% of urea, 10 to 20% additives and 10 to 20% talcum powder via a process formula, wherein the softening organic silicon resin is formed by softening and processing organic silicon resin in which 20 to 60% of macromolecular organic material glutinous rice powder, 5 to 10% soybean powder and 10 to 30% of alum inorganic auxiliary material are added via a process formula. The gelatinizing agent can develop new building material products with various characteristics and diverse purposes. The present invention has the advantages of high intensity, reliable quality, water resistance, corrosion resistance, frost resistance and durability.
Description
The invention belongs to building material technical field.The NEW TYPE OF COMPOSITE jelling agent that relates to macromolecular materials such as comprising bubble flower alkali and silicone resin.
The sodium silicate liquid body mainly was to be used for the building structure external coating in architectural application in the past, and modulation acid-proof cement and acid resisting concrete etc. are made material delivering and used.Because there are defectives such as not water-fast in it, range of application is restricted greatly.Have now based on water glass, add the inorganic polymer binding agent that auxiliary agent, stiffening agent and talcum powder etc. are formed.Do not carry out polyreaction after this inorganic polymer binding agent adds in building materials, thereby the physical and chemical performance of its building material product can not be significantly improved.
The objective of the invention is to attempt to adopt macromolecular materials such as bubble flower alkali and silicone resin to be combined into a kind of NEW TYPE OF COMPOSITE jelling agent through technology, make it not only have stronger bond and more stable physical and chemical performance, and have many good characteristics such as corrosion-resistant, water-fast, high temperature resistant and weather resistance.So will have the incomparable singularity of general inorganic coagulation material, and energy and multiple natural material and various waste material and steel gluing well, thereby develop multifrequency nature and the different building materials new product of purposes.
The present invention is to be main raw material(s) to steep colored alkali, contains a kind of NEW TYPE OF COMPOSITE jelling agent that the additive talcum powder of the urea of the softening silicone resin of its amount 5-15% and 2-6% and 10-20% is made through technical recipe, is called for short VT glue.Softening silicone resin wherein is to add the macromolecule organic material glutinous rice flour comprise its amount 20-60% and the soyflour of 5-10% and the alum inorganic auxiliary material of 10-30% to form through softening processing of technical recipe in silicone resin.
Organic substance will directly produce polyreaction after this bubble flower alkali novel composite gel material adds building material product inside, and its intensity and quality are doubled and redoubled.Make jelling agent with VT glue, with natural drift-sand (the natural sand in the desert) is that main raw material can be made into that VT glue sand is non-burning brick, hollow, the solid block of VT glue sand, and husky canal lining pipe fitting of VT glue and the husky highway of VT glue etc. are applicable to the series achievement product innovation of industry and covil construction, water conservancy project building and highway engineering building.Also can be used for ecological engineering improvement such as chemical sand-fixing.Equally, make jelling agent with VT glue and various waste materials such as coal gangue, slag, flyash well can also be utilized, develop the material series building product innovation that is applicable to different building requirements of plurality of specifications.These products not only the intensity height, quality is good but also have water-fast, corrosion-resistant, freeze proof and weather resistance.
Further describe the present invention by the following examples.All umbers and per-cent are all by weight in these embodiments.
Embodiment 1
With softening silicone resin of 8 grams and 14 gram talcum powder, add in the 78 gram sodium silicate liquids, be mixed with the bubble flower alkali NEW TYPE OF COMPOSITE jelling agent of 100 grams.
Embodiment 2
In the softening silicone resin of 12 grams and 18 gram talcum powder and 4 gram urea addings, 66 gram sodium silicate liquids, be mixed with 100 gram bubble flower alkali plural gel agent.
Embodiment 3
30 gram glutinous rice flour and 15 gram alum are added in the 40 gram silicone resins, be mixed with softening silicone resin glue by solvent.
Embodiment 4
In 40 gram glutinous rice flour and 18 gram alum and 7 gram soyflours addings, 35 gram silicone resins, be mixed with softening silicone resin glue by solvent.
Claims (1)
1, the agent of the bubble used on a kind of building materials flower alkali plural gel serves as that the softening silicone resin that is made into of the alum of the main soyflour that adds glutinous rice flour that comprises silicone resin and its amount of silicone resin 20-60% of containing its amount 5-15%, 5-10%, 10-30% and the urea of 2-6% and the talcum powder of 10-20% are made through technical recipe to steep colored alkali.