CN1278876C

CN1278876C - Artificial wood grain product and its making method

Info

Publication number: CN1278876C
Application number: CN 03140490
Authority: CN
Inventors: 潘桂兴
Original assignee: Individual
Current assignee: Individual
Priority date: 2003-09-12
Filing date: 2003-09-12
Publication date: 2006-10-11
Anticipated expiration: 2023-09-12
Also published as: CN1491812A

Abstract

The present invention relates to a simulated wood grain product and a processing method thereof, which is characterized in that an oil paint colorant is added in a primary water basin, the oil paint colorant and water flow in a secondary water basin through a retainer device in the mode of conjunction when the oil paint colorant and the water float on a water surface because of different gravity magnitudes, a basal body which needs lacquering is put in the bottom of the secondary water basin from the side part, and the basal body is moved, and is lifted upward at slow speed; when the basal body leaves the water surface, the oil paint colorant is automatically pasted on the basal body, and the simulated wood grain product is formed by heating, drying, polishing and paintsweeping. The paint coat of simulated wood grains has the advantages of natural color distribution, clear grain, high compactness of the combination of the paint coat and the surface of the basal body, low manufacture cost and good use effect; the grains are close to the grains of natural wood grains, the paint coat can not be disengaged or peeled off because of external factors, and the present invention is suitable for various materials. Simultaneously, the paint coat can be coated on products of various shapes, for example, the paint coat is coated on the products in the shape of plane, stereo, an anomaly shape, etc.

Description

A kind of processing method of Wood-grain-imitating goods

Technical field

The present invention relates to a kind of processing method of Wood-grain-imitating goods.

Background technology

At present, prefer the goods that have wood grain on the market, and wood grain goods range of application is bigger, as be applied to furniture, on the product decoration or the like, but to form the wood grain sample at product surface, now dual modes that adopt more, a kind of mode is to paste woodgrained paper with super glue at product surface, wood grain skin etc., the material of this product is to contain the glue of volatile organic solvent and the woodgrained paper made from timber, the wood grain skin, neither environmental protection, waste the forest reserves again, and, the product of making as run into malaria or touch acidity or alkalescence material the time, the effect of its super glue will be lost efficacy, make the woodgrained paper of stickup, the wood grain skin produces the phenomenon that breaks away from or peel off, thereby has influence on the outward appearance of whole product; Another kind of mode is with manually drawing wood grain on product, but because of its effect of drawing is very coarse, the not enough natural beauty of lines, and operating efficiency is lower, the more high shortcoming of cost and can't promoting.

Summary of the invention

The processing method that the purpose of this invention is to provide a kind of natural beauty, wood grain difficult drop-off, Wood-grain-imitating goods that processing cost is low.

The present invention is achieved in that a kind of processing method for preparing the Wood-grain-imitating goods, adopts following steps:

A) will paint colorant and put into water-filled one-level pond;

B) when the paint colorant flies on the water surface because of proportion is different, flow in the secondary pond by barrier apparatus with water;

C) matrix is put into the secondary basin bottom, and upwards mentioned at a slow speed, break away from the water surface;

D) to put into temperature be 30-80 ° baker heating 2-8 minute to the matrix that the surface is stained with the Wood-grain-imitating enamelled coating;

E) glazing, sweep lacquer;

F) typing.

Above-mentioned described barrier apparatus is broach shape barrier, netted barrier.

Matrix of the present invention after above-mentioned steps, its surface-coated or be stained with the enamelled coating of one or more layers Wood-grain-imitating.

Above-mentioned described matrix is plasthetics, bakelite goods, tempering goods, glassware, metallic article, ceramic.

Above-mentioned described matrix be shaped as circle, flat shape, three-dimensional shape or irregular concaveconvex shape.

The Wood-grain-imitating goods that the present invention adopts above-mentioned described processing method to make, because the physics thing characteristic of paint colorant and water, proportion is different, the paint colorant can only fly on the water surface, the present invention has promptly adopted this characteristic, matrix is put into water, when water breaks away from the water surface, the paint colorant promptly adheres to matrix surface naturally, thereby be coated with the enamelled coating of Wood-grain-imitating at matrix surface, formed approaching natural, the wood grain lines of clear and smooth, give the sensation of back to nature, and the compactness height that combines between matrix surface and the enamelled coating, can not break away from or peel off because of extraneous factor;

Manufacturing cost of the present invention is lower, result of use is good, decorate properties is stronger, the scope of application is wider, applicable to various materials, is on the product of matrix as plastic cement, bakelite, metal, safety glass, pottery, wood powder die material, middle particle board material etc., can be machined on the product of Any shape simultaneously, as be machined on the products such as flat shape, three-dimensional shape, irregular concaveconvex shape, thereby promote value of the product and sense organ greatly, meet the present people's consumer psychology and the consumption consciousness.

Description of drawings

Fig. 1 is a flow chart of the present invention;

Fig. 2 is the generalized section that the present invention makes product;

Fig. 3 is another structural representation that the present invention makes product;

Fig. 4 is the structural representation again that the present invention makes product.

The specific embodiment

As shown in Figure 1, the processing method of Wood-grain-imitating goods of the present invention, its step is as follows: at first be divided into high and low two-stage pond, first order pond height is about 1 meter, pond, second level height is about 0.5 meter, pond size, the degree of depth are doubly built by the 2-3 of matrix, if when matrix is big, it is 1.5-2M that area can be built in the pond ², the degree of depth is a 1-1.2 rice.Between one-level pond and the secondary pond barrier apparatus is arranged, water can flow into the secondary pond from the one-level pond by barrier apparatus, and this barrier apparatus can be controlled water (flow) direction and speed, can also adopt the electrical shunt Steering gear.After the water in one-level pond is expired, adding quantity is the paint colorant of 0.05-0.8Kg, the depth of its color can be decided according to the color of required wood grain, different with the proportion of paint colorant in the pond owing to water, the paint colorant flies on the water surface, the water in one-level pond completely back overflows to the secondary pond, paint colorant simultaneously and under the drive of current, flow into the secondary pond by barrier apparatus, the paint colorant that enters the secondary pond is divided into linear during through barrier apparatus, and fly at the water surface, at this moment the matrix of required coating Wood-grain-imitating can be put into the secondary basin bottom, mobile matrix floats to the water surface the position of linear paint; With 0.3-1 rice/minute at a slow speed matrix is upwards mentioned, break away from the water surface, when matrix leaves the water surface, contact with the paint colorant, paint colorant and promptly adsorb automatically or be pasted on matrix surface, thus the enamelled coating of formation Wood-grain-imitating; Again this matrix is put in the baker, carried out heating, drying 2-8 minute with 30-80 ° temperature; Moisture content and paint on the matrix parch, and make the adhesive force of paint colorant and matrix stronger, and the surface is more level and smooth; Again with the matrix glazing, sweep lacquer, typing, can obtain color and luster, lines, brightness etc. as wood grain, the present invention is ornamental stronger, technological process is simple

As shown in Figure 2, matrix 1 of the present invention, its raw material can be various materials, as plastic cement, bakelite, metal, safety glass, ceramic material etc.Adopt the method for the invention matrix 1 surface can apply or be stained with the enamelled coating 2 of one or more layers Wood-grain-imitating, matrix 1 can be multiple body, as plane body, solid, irregular concave-convex etc.

As shown in Figure 3, the handle that the bakelite material is made is a matrix 1, and its matrix 1 surface is crooked shape, adopts the method for the invention in its surface-coated the enamelled coating 2 of one deck Wood-grain-imitating to be arranged, and makes handle surfaces cover wood grain lines and color clearly.

As shown in Figure 4, be matrix 1 with timber after the processing or the chair made of plastic material, be the plane at the seat place of matrix 1, adopt the method for the invention and, make its chair more attractive in appearance, ornamental stronger at the enamelled coating 2 of its surface-coated one deck Wood-grain-imitating.

Claims

1, a kind of processing method for preparing the Wood-grain-imitating goods is characterized in that:

Adopt following steps:

A) will paint colorant and put into water-filled low-level culture pool;

C) matrix (1) is put into the secondary basin bottom, and upwards mention at a slow speed, break away from the water surface;

D) to put into temperature be 30-80 ° baker heating 2-8 minute to the matrix (1) that the surface is stained with Wood-grain-imitating enamelled coating (2);

E) glazing, sweep lacquer;

F) typing.

2, the processing method of preparation Wood-grain-imitating goods according to claim 1 is characterized in that: described barrier apparatus is broach shape barrier, netted barrier.

3, the processing method of preparation Wood-grain-imitating goods according to claim 1 is characterized in that: described matrix (1) after described step, its surface-coated or be stained with the enamelled coating (2) of one or more layers Wood-grain-imitating.

4, the processing method of preparation Wood-grain-imitating goods according to claim 1 is characterized in that: described matrix (1) is plasthetics, bakelite goods, tempering goods, glassware, metallic article, ceramic.

5, the processing method of preparation Wood-grain-imitating goods according to claim 1 is characterized in that: described matrix (1) be shaped as circle, flat shape, three-dimensional shape or irregular concaveconvex shape.