CN1258653A - 复合硅酸盐水泥 - Google Patents

复合硅酸盐水泥 Download PDF

Info

Publication number
CN1258653A
CN1258653A CN00100108A CN00100108A CN1258653A CN 1258653 A CN1258653 A CN 1258653A CN 00100108 A CN00100108 A CN 00100108A CN 00100108 A CN00100108 A CN 00100108A CN 1258653 A CN1258653 A CN 1258653A
Authority
CN
China
Prior art keywords
portland cement
slag
gypsum
nickel slag
composite portland
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN00100108A
Other languages
English (en)
Inventor
谢尧生
刘艳军
王绍华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN00100108A priority Critical patent/CN1258653A/zh
Publication of CN1258653A publication Critical patent/CN1258653A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种复合硅酸盐水泥,其特征在于它由15—50份镍渣,40—70份硅酸盐水泥熟料,8—10份石膏,10—20份粒化高炉矿渣混合后研磨至比表面积为4000—5000cm2/g超细粉体,可制成325＃、425＃、525＃水泥,该复合硅酸盐水泥具有早期强度好,其它各项常规指标均符合复合硅酸盐水泥标准的优点,可用于矿井回填混凝土的胶凝材料及一般民用建筑用胶凝材料,同时也充分利镍渣废物,变废为宝,为人类造福,改善了环境。

Description

复合硅酸盐水泥
本发明涉及一种复合硅酸盐水泥，具体地说它是以镍渣，硅酸盐水泥熟料，石膏和粒化高炉矿渣为组份的复合硅酸盐水泥。
镍渣是镍冶炼的一种尾弃物，虽然它还含有多种成份，但回收利用价值小，因此常年堆放不能再用，据不完全统计，仅金川镍矿每年就有20万吨的镍渣，从建厂至今已有几百万吨，即占有大量的土地，也污染环境。
本发明的目的正是为了充分利用被尾弃的镍渣合理开发而提供一种用镍渣制造复合硅酸盐水泥，用于矿井回填混凝土的胶凝材料及一般民用建筑用胶凝材料，从而即可变废为宝，又可改善环境，也为国家节省大量的资金。
本发明的目的是这样实现的：
一种复合硅酸盐水泥，其特征在于它由下述重量配比的原料和方法制成的325#、425#、525#水泥：
镍渣               15-50份
硅酸盐水泥熟料     40-70份
石膏               8-10份
粒化高炉矿渣       10-20份
将上述配比的镍渣、硅酸盐水泥熟料、石膏、粒化高炉矿渣，混合后用研磨机磨细至比表面积为4000-5000cm2/g超细粉体。
本发明所用的镍渣经过统计分析，主要含有Ni-0.21％、Cu-0.24％、Fe-40.24％、Co-0.108％、CaO-1.29％、MgO-9.1％、SIO2-35.08％、S-0.6％，这些组份具有较好的活性，它利化高炉矿渣均属于活性组合材料，用于混凝土中可预防碱集料反应，同时早强性能好。
由于采取上述技术方案，使本发明技术具有下列优点及效果。
a)充分利用现有的镍渣废料，既解决污染问题，也可变废为宝，用于矿井回填混凝土的胶凝材料及一般民用建筑用胶凝材料，为国家节省大量资金；
b)该复合硅酸盐水泥性能好，成本低，效益好。
实施例1
取镍渣50kg，硅酸盐水泥熟料40kg，石膏10kg，粒化高炉矿渣10kg，混合后研磨至比表面积为4000cm2/g的超细粉体，即为325#水泥，经中国建筑材料科学院检测，该复合硅酸盐水泥7天的抗压强度为20Mpa，抗折强度为5.59Mpa，28天的抗压强度为34Mpa，抗折强度为6.0Mpa，符合国家标准。
实施例2
取镍渣40kg，硅酸盐水泥熟料50kg，石膏9kg，粒化高炉矿渣15kg，混合后研磨至比表面积为4500cm2/g的超细粉体，即为425#水泥，经检测，该复合硅酸盐水泥7天的抗压强度为25.7Mpa，抗折强度为5.51Mpa，28天的抗压强度为45Mpa，抗折强度为6.1Mpa，符合国家标准。
实施例3
取镍渣15kg，硅酸盐水泥熟料70kg，石膏8kg，粒化高炉矿渣20kg，混合后研磨至比表面积为5000cm2/g的超细粉体，即为525#水泥，经检测：该复合硅酸盐水泥3天的抗压强度为30.08Mpa，抗折强度为5.75Mpa；28天的抗压强度为56.2Mpa，抗折强度为7.30Mpa。

Claims (1)

1.一种复合硅酸盐水泥，其特征在于它由下述重量配比的原料和方法制成的325#、425#、525#水泥：
镍渣              15-50份
硅酸盐水泥熟料    40-70份
石膏              8-10份
粒化高炉矿渣      10-20份
将上述配比的镍渣、硅酸盐水泥熟料、石膏、粒化高炉矿渣，混合后用研磨机磨细至比表面积为4000-5000cm2/g超细粉体。
CN00100108A 2000-01-10 2000-01-10 复合硅酸盐水泥 Pending CN1258653A (zh)