CN1254502C - 除草地膜母粒 - Google Patents
除草地膜母粒 Download PDFInfo
- Publication number
- CN1254502C CN1254502C CN 200410024009 CN200410024009A CN1254502C CN 1254502 C CN1254502 C CN 1254502C CN 200410024009 CN200410024009 CN 200410024009 CN 200410024009 A CN200410024009 A CN 200410024009A CN 1254502 C CN1254502 C CN 1254502C
- Authority
- CN
- China
- Prior art keywords
- present
- kilograms
- polyethylene
- weed killer
- mulching film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明提供一种除草地膜母粒，它包括下述重量百分比的组份：聚乙烯20-70%、除草剂10-30%，乳化剂1-3%，将聚乙烯与除草剂混合均匀，再加入乳化剂混合搅拌均匀，用挤出机挤出造粒干燥。它可直接将本发明产品用于吹塑地膜生产工艺，从而避免了因液态配方造成的生产成本高，挤出工艺打滑地膜厚薄不均，除草剂易挥发等问题。本发明的产品呈粒状，可作为生产地膜的原料，挤出吹塑工艺中直接使用本发明产品，避免了除草剂的挥发、污染环境及除草剂的流失，由于低密度聚乙烯的用量减少，所以生产成本低，本发明经过反复试验，其组份合理，生产的地膜厚薄均匀，且除草效果好，使地膜的生产工艺简单，降低生产成本。
Description
技术领域
本发明涉及除草地膜，是一种制造除草地膜的母粒。
背景技术
由于除草地膜具有较多优点，被我国农业广泛应用。目前制造除草地膜均是自原料的配比开始直至制造出地膜产品，由于其制造工艺的特点，使进入吹塑地膜工艺中的原料一般是液态，因此它存在的不足是：生产成本高、由于除草剂的用量不合理，在挤出工艺中极易打滑，造成挤出不稳定，使膜的厚薄不均，且除草剂一直处于液态中易挥发污染环境等。
发明内容
本发明目的是，提供一种除草地膜母粒，它为除草地膜的生产提供一种粒状产品，可直接将本发明产品用于吹塑地膜生产工艺，从而避免了因液态配方造成的生产成本高，挤出工艺打滑地膜厚薄不均，除草剂易挥发等问题。
本发明为了完成发明目的，提供以下技术方案：它包括下述重量百分比的组份：聚乙烯20-70％、除草剂10-30％，乳化剂1-3％，将聚乙烯与除草剂混合均匀，再加入乳化剂混合搅拌均匀，用挤出机挤出造粒干燥。所述重量百分比的组份是：无机填料35-60％。所述重量百分比的组份是：增塑稳定剂0.1-0.4％，无料填料35-60％。其重量百分比的组份是：聚乙烯25-50％，除草剂10-25％，乳化剂1-3％。将无机填料粉碎备用，再将聚乙烯与除草剂混合均匀备用，然后将乳化剂、无机填料及增塑稳定剂置入聚乙烯与除草剂混合液中搅拌均匀后，用挤出机挤出造粒干燥。将无级填料粉碎成微米或纳米级备用，再将聚乙烯与除草剂混合均匀备用，然后将乳化剂、无机填料及增塑稳定剂置入聚乙烯与除草剂混合液中搅拌均匀后，用挤出机挤出造粒干燥。
本发明所述除草剂是乙草胺、金都尔和甲草胺。增塑稳定剂是环氧大豆油、环氧脂。所述聚乙烯是低密度聚乙烯，线性低密度聚乙烯、高密度聚乙烯。
本发明的产品呈粒状，可作为生产地膜的原料，挤出吹塑工艺中直接使用本发明产品，避免了除草剂的挥发、污染环境及除草剂的流失，由于低密度聚乙烯的用量减少，所以生产成本低，本发明经过反复试验，其组份合理，生产的地膜厚薄均匀，且除草效果好，使地膜的生产工艺简单，降低生产成本。
具体实施方式
本发明技术方案不仅限于本发明实施例，本发明所述的挤出造粒工艺为公知技术。
1、取低密度聚乙烯70公斤，乙草胺28公斤，表面活性剂2公斤备用，将乙草胺28公斤与低密度聚乙烯混合均匀，然后加入表面活性剂混合搅拌均匀，用挤出机挤出造粒干燥制成粒状产品。
2、取线性低密度聚乙烯37公斤，乙草胺20公斤，碳酸钙40公斤，环氧大豆油0.3公斤，2101乳化剂2.7公斤，将碳酸钙粉碎备用，先将乙草胺置入线性低密度聚乙烯内混合搅拌均匀，再加入粉碎后的碳酸钙、环氧大豆油及2101乳化剂混合搅拌均匀，用挤出机挤出造粒干燥制成粒状产品。
3、取高密度聚乙烯50公斤，甲草胺15公斤，滑石粉33公斤，环氧脂0.2公斤，农乳5001.8公斤备用，将滑石粉粉碎成微米级备用，先将甲草胺置入高密度聚乙烯内混合搅拌均匀，再加入微米级滑石粉、环氧脂及500农乳混合搅拌均匀，用挤出机挤出造粒干燥制成粒状产品。
4、取低密度聚乙烯30公斤，金都尔10公斤，碳酸钙59公斤，2201乳化剂1公斤，将碳酸钙粉碎成纳米级备用，将金都尔10公斤与低密度聚乙烯混合搅拌均匀，然后加入2001乳化剂混合搅拌均匀，用挤出机挤出造粒干燥制成粒状产品。
5、取低密度聚乙烯45公斤，金都尔15公斤，600乳化剂3公斤，滑石粉37公斤，将滑石粉粉碎备用，将金都尔与低密度聚乙烯混合搅拌均匀，然后加入600乳化剂、滑石粉混合搅拌均匀，用挤出机挤出造粒干燥制成粒状产品。
6、取线性低密度聚乙烯30公斤，乙草胺25公斤，碳酸钙44公斤，2101乳化剂1公斤，将碳酸钙粉碎成纳米级备用，先将乙草胺置入线性低密度聚乙烯内混合搅拌均匀，再加入纳米级碳酸钙及2101乳化剂混合搅拌均匀，用挤出机挤出造粒干燥制成粒状产品。
7、取低密度聚乙烯25公斤，金都尔13公斤，碳酸钙59公斤，2201乳化剂2.6公斤，环氧脂0.4公斤，将碳酸钙粉碎成微米级备用，将金都尔与低密度聚乙烯混合搅拌均匀，然后加入2001乳化剂、环氧脂及微米级碳酸钙混合搅拌均匀，用挤出机挤出造粒干燥制成粒状产品。
8、取低密度聚乙烯52公斤，甲草胺14.8公斤，碳酸钙30公斤，2201乳化剂3公斤，环氧脂0.2公斤，将碳酸钙粉碎成微米级备用，先将甲草胺置入低密度聚乙烯内混合搅拌均匀，再加入微米级碳酸钙、环氧脂及2201乳化剂混合搅拌均匀，用挤出机挤出造粒干燥制成粒状产品。
Claims (2)
1、除草地膜母粒，其特征在于：包括下述重量百分比的组份：聚乙烯25-50％，乙草胺或甲草胺10-25％，2101或农乳500乳化剂1-3％、增塑稳定剂0.1-0.4％和无机填料35-60％。
2、根据权利要求1所述的除草地膜母粒，其特征在于：其重量百分比的组份是：线性低密度聚乙烯37公斤、乙草胺20公斤、2101乳化剂2.7公斤、碳酸钙40公斤、环氧大豆油0.3公斤。