CN1249321A - 水性反辐射隔热涂料 - Google Patents
水性反辐射隔热涂料 Download PDFInfo
- Publication number
- CN1249321A CN1249321A CN 99114454 CN99114454A CN1249321A CN 1249321 A CN1249321 A CN 1249321A CN 99114454 CN99114454 CN 99114454 CN 99114454 A CN99114454 A CN 99114454A CN 1249321 A CN1249321 A CN 1249321A
- Authority
- CN
- China
- Prior art keywords
- water paint
- insulating water
- radioresistant
- coating
- paint according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种可涂于建筑物外墙或金属表面的水性反辐射隔热涂料,由丙烯酸合成乳液、反辐射陶瓷填料、隔热硅酸盐空心填料、颜填料、涂料助剂、稀释剂水组成,具有附着力强、涂层薄、无毒、无污染、隔热性能好的优点。
Description
本发明涉及一种可涂于建筑物外墙或金属表面的隔热涂料。
研究一种具有隔热功能的环保型外墙涂料是国内外涂料行业一直追求的目标。为此已有多项专利申请,如中国专利CN1073700A中涉及一种新颖的隔热涂料组成物,该涂料包括聚乙烯醇缩醛类树脂、颜料、隔热材料等填充料、稀释剂等,该涂料虽有一定的隔热效果,但所用稀释剂为有机溶剂,属溶剂型涂料,不符合环保要求。中国专利CN1105090A所述硅镁铝复合绝热涂料由硅镁铝氮化物与粘合剂组成,是一种涂于管道和设备上的复合绝热涂料,这种涂料的特点是导热系数低,主要用于保温,但涂膜厚度最低也需25mm才有一定的隔热保温效果。中国专利CN1106051A叙述了一种新型隔热保温涂料及其制作方法,该涂料采用成浆材料、轻质填充料、粘结剂和水等。该涂料用途主要是保温,其涂层平均厚度为3.8mm才有明显的保温效果。上述两篇专利均属于一种厚质的保温涂料。
世界专利WO86/05193讲述了一种绝热涂料,该涂料由涂料基体、二氧化硅颗粒和纤维等颗粒组成。其中二氧化硅颗粒是一种空心硅硼酸盐微球,纤维等颗粒则是蔗渣一类天然纤维等材料,其隔热效果主要源于上述二种物质具有的中空结构。因此,其隔热降温效果是有限的。
本发明的目的是克服已有技术的不足之处,提供一种涂层薄、无毒、无污染、隔热效果好的水性反辐射隔热涂料。
本发明水性反辐射隔热涂料的组成以重量配比表示如下:
成膜物丙烯酸合成乳液 30-60
反辐射陶瓷填料 5-20
隔热硅酸盐空心填料 5-20
颜填料 10-40
涂料助剂 适量
稀释剂水 足量
作为本发明涂料组分中的成膜物丙烯酸合成乳液,可以选用下列三种之一:苯乙烯—丙烯酸共聚乳液,纯丙烯酸聚合乳液,有机硅—丙烯酸共聚乳液。
本发明涂料组分中的反辐射陶瓷填料包括:含堇青石的改性红外辐射材料、含二氧化硅的陶瓷材料、硼硅玻璃陶瓷材料的一种或一种以上。
本发明涂料组分中的隔热硅酸盐空心填料为空心二氧化硅—三氧化二铝结构微球。
本发明涂料组分中的颜填料包括:二氧化钛、氧化锌、滑石粉、碳酸钙、硅灰石粉、云母粉的一种或一种以上。
本发明涂料组分中颜填料中的颜料包括:二氧化钛、氧化锌、氧化铁红、氧化铁黄的一种或一种以上。
本发明涂料组分中还可以包括具有纤维结构的绒毛粉。
本发明涂料的成膜物为水溶性丙烯酸合成乳液,稀释剂为水,所制成的涂料附着力强,耐污性佳,耐候性好,涂层薄、无毒、无污染,符合环保要求,涂料组成物中添加具有红外反辐射作用的陶瓷填料以及隔热硅酸盐空心填料,有效地提高了该涂料的隔热性能,可以做到涂层厚度150μm左右即有十分明显的隔热效果。由于绒毛粉是一种具有中空纤维结构的粉末状物质,导热系数很低,作为涂料的填料,可进一步增加涂层的隔热性能。
本发明提供如下15个实施例:例1~例5如表I所示,例6~例10如表II所示,例11~15如表III所示。
本发明水性反辐射隔热涂料的制备工艺及测试方法结合附图给予说明。
图1为本发明涂料隔热效果测试方法示意图。
图2为本发明涂料隔热效果曲线对照图。
本发明水性反辐射隔热涂料生产方法如下:先将实施例中第1至第4种组分及分散剂、消泡剂等预混合,再将颜、填料及反辐射粉、部分隔热粉料加入,在高速分散机中分散成糊状,将糊状物经研磨机研磨至一定细度,再经高速分散机,添加各种乳液、部分隔热粉、消泡剂、流平剂、增稠剂。搅拌均匀,即成为本发明水性反辐射隔热涂料。
如图1所示,采用自制的隔热涂料性能测试仪对实施例涂料的隔热性能进行测试。图中1为反辐射隔热涂料,2为样板,3为密封箱,4为250W白炽灯,5为稳压电源,6为温度传感器,7为温度显示器,8为密封膏
涂料样板2底材分为水泥石棉板或普通金属材料样板。涂敷方法为用水性弹性底涂打底,再将例1、6、11中的隔热涂料分别在三个样板上涂两遍,保证干膜厚度≥150μm。制好的样板放入隔热涂料性能测试仪中密封好,采用两种方法进行测试。第一种方法如图1所示,将样板置于250W白炽灯下进行室内测试;第二种方法是将样板及测试系统置于户外盛夏阳光下进行测试,测试结果如表IV、表V和图2所示。图2中A为未涂本发明涂料的水泥板,B1为涂实施例1涂料的水泥板,B2为涂实施例6涂料的水泥板,B3为涂实施例11涂料的水泥板。
由表IV、表V测试结果表明,将本发明涂料涂敷于水泥石棉板表面,干膜厚度只需150μm左右,涂有本发明涂料的水泥板下面的温度较之于未涂的低10~15℃,证明本发明涂料具有优良的隔热性能。实验证明本发明涂料在金属、橡胶类防水卷材表面涂敷也具有良好的隔热效果。
实施例 表I
实施例含量(%重量)成分 | 1 | 2 | 3 | 4 | 5 |
苯—丙乳液296DS | 400 | 300 | 350 | 380 | 380 |
苯—丙乳液AD36 | 80 | 100 | 100 | 100 | 100 |
水 | 60 | 80 | 55 | 70 | 60 |
HEC(2%) | 54 | 80 | 50 | 40 | 50 |
分散剂(DP-518) | 4 | 4 | 4 | 4 | 4 |
消泡剂(德谦082) | 2 | 2 | 4 | 4 | 4 |
防雾剂(MB-11) | 1 | 2 | 1 | 2 | 2 |
成膜助剂(醇酯-12) | 8 | 10 | 8 | 8 | 10 |
增韧剂(邻苯二甲酸二丁酯) | 20 | 20 | 20 | 15 | 20 |
丙二醇 | 20 | 30 | 20 | 20 | 30 |
二氧化钛 | 75 | 100 | 100 | 75 | 75 |
碳酸钙 | 50 | 25 | 50 | 50 | 25 |
滑石粉 | 50 | 50 | 50 | 50 | 50 |
硅灰石粉 | 50 | 50 | 50 | 50 | 50 |
氧化锌 | 15 | 15 | 20 | 15 | 20 |
堇青石粉 | 45 | 60 | 50 | 45 | 40 |
空心二氧化硅——三氧化二铝结构微球 | 50 | 50 | 50 | 55 | 60 |
氨水〔28%〕 | 4 | 5 | 4 | 4 | 4 |
增稠剂〔WT-102〕 | 10 | 15 | 12 | 11 | 14 |
消泡剂〔德谦082〕 | 2 | 2 | 2 | 2 | 2 |
表II
实施例含量(%重量)成分 | 6 | 7 | 8 | 9 | 10 |
纯丙烯酸乳液(Nacrylic2550) | 250 | 280 | 300 | 300 | 280 |
苯丙弹性乳液〔AD36〕 | 100 | 80 | 80 | 80 | 80 |
水 | 65 | 70 | 71 | 50 | 70 |
HEC〔1%〕 | 50 | 80 | 80 | 80 | 80 |
分散剂〔DP-518〕 | 5 | 5 | 5 | 5 | 5 |
消泡剂(德谦082) | 4 | 4 | 4 | 4 | 4 |
防雾剂(MB-11) | 2 | 2 | 2 | 2 | 2 |
成膜助剂〔醇酯-12〕 | 10 | 10 | 10 | 10 | 10 |
增韧剂(邻苯二甲酸二丁酯) | 8 | 10 | 10 | 10 | 10 |
丙二醇 | 20 | 20 | 20 | 20 | 20 |
二氧化钛 | 125 | 100 | 125 | 100 | 125 |
碳酸钙 | 75 | 50 | 50 | 50 | 50 |
滑石粉 | 75 | 75 | 50 | 75 | 50 |
硅灰石粉 | 100 | 100 | 75 | 100 | 75 |
氧化锌 | 10 | 15 | 10 | 15 | 15 |
堇青石粉 | 35 | 35 | 40 | 35 | 35 |
空心二氧化硅——三氧化二铝结构微球 | 50 | 50 | 50 | 50 | 70 |
氨水〔28%〕 | 4 | 4 | 4 | 4 | 4 |
增稠剂〔WT-102〕 | 10 | 8 | 12 | 8 | 13 |
消泡剂〔德谦082〕 | 2 | 2 | 2 | 2 | 2 |
表III
实施例含量(%重量)成分 | 11 | 12 | 13 | 14 | 15 |
硅丙乳液(KD6) | 220 | 220 | 300 | 300 | 250 |
苯丙弹性乳液〔AD36〕 | 200 | 200 | 160 | 160 | 150 |
水 | 150 | 150 | 80 | 80 | 120 |
丙二醇 | 20 | 20 | 20 | 20 | 20 |
分散剂〔DP-518〕 | 5 | 5 | 5 | 5 | 5 |
消泡剂(德谦082) | 4 | 4 | 4 | 4 | 4 |
防腐剂〔MB-11〕 | 2 | 2 | 2 | 2 | 2 |
钛白粉 | 100 | 100 | 125 | 125 | 125 |
重钙 | 40 | 40 | 15 | 15 | 15 |
滑石粉 | 75 | 75 | 75 | 50 | 75 |
堇青石粉 | 45 | 60 | 90 | 90 | 60 |
空心二氧化硅——三氧化二铝结构微球 | 60 | 60 | 60 | 90 | 90 |
云母粉 | 10 | 10 | 10 | 10 | 10 |
氧化铁红 | 1 | 1 | 1 | 1 | 1 |
氧化铁黄 | 4 | 4 | 4 | 4 | 4 |
绒毛粉 | 20 | 20 | 20 | 20 | 20 |
消泡剂(汉高NXZ) | 2 | 2 | 2 | 2 | 2 |
成膜助剂(Texanol) | 12 | 12 | 12 | 12 | 12 |
增稠剂〔汉高2000〕 | 4 | 3 | 2 | 2 | 4 |
水 | 26 | 12 | 13 | 8 | 31 |
表IV 灯光下隔热涂料性能测试结果(水泥石棉板)
实例温度℃时间 | 0 | 1 | 2 | 3 |
未涂水泥板 | 实施例1 | 实施例6 | 实施例11 | |
9:00 | 24 | 24 | 24 | 24 |
9:30 | 29 | 27 | 26 | 25 |
10:00 | 35 | 32.5 | 32 | 31 |
10:30 | 36 | 33 | 32.5 | 31 |
11:00 | 38 | 33.5 | 33 | 31.5 |
11:30 | 41 | 35 | 34 | 33 |
12:00 | 44.5 | 37.5 | 36 | 35 |
12:30 | 44.5 | 37.5 | 36 | 35 |
表V 1999年6月21日 大气温度32℃
实例温度℃时间 | 0 | 1 | 2 | 3 |
未涂水泥板 | 实施例1 | 实施例6 | 实施例11 | |
9:00 | 25 | 24.5 | 24.5 | 24.5 |
9:30 | 30.5 | 28 | 28 | 26 |
10:00 | 34 | 31 | 30 | 29 |
10:30 | 41 | 36 | 34 | 30 |
11:00 | 47 | 38.5 | 36 | 32 |
11:30 | 48.5 | 40 | 37 | 33 |
12:00 | 50.5 | 41 | 37.5 | 34 |
12:30 | 52 | 42 | 38.5 | 35 |
13:00 | 52.5 | 42.5 | 39 | 35 |
13:30 | 52.5 | 41.5 | 39.5 | 35.5 |
14:00 | 51.5 | 41 | 38.5 | 35 |
14:30 | 50 | 41 | 38.5 | 35 |
15:00 | 48 | 40 | 37 | 34.5 |
15:30 | 47.5 | 38 | 36 | 34 |
16:00 | 43 | 35 | 34 | 32 |
16:30 | 42 | 35 | 33 | 32 |
17:00 | 41.5 | 34 | 33 | 31.5 |
Claims (7)
1.一种可涂于建筑物外墙或金属表面的水性反辐射隔热涂料,其特征是涂料的组成以重量配比表示如下:
成膜物丙烯酸合成乳液 30-60
反辐射陶瓷填料 5-20
隔热硅酸盐空心填料 5-20
颜填料 10-40
涂料助剂 适量
稀释剂水 足量
2.根据权利要求1所述的水性反辐射隔热涂料,其特征是其中所述的丙烯酸合成乳液为下列三种之一:苯乙烯—丙烯酸共聚乳液,纯丙烯酸聚合乳液,有机硅—丙烯酸共聚乳液。
3.根据权利要求1所述的水性反辐射隔热涂料,其特征是其中所述的反辐射陶瓷填料包括:含堇青石的改性红外辐射材料、含二氧化硅的陶瓷材料、硼硅玻璃陶瓷材料的一种或一种以上。
4.根据权利要求1所述的水性反辐射隔热涂料,其特征是其中所述的隔热硅酸盐空心填料为空心二氧化硅—三氧化二铝结构微球。
5.根据权利要求1所述的水性反辐射隔热涂料,其特征是其中所述的颜填料包括:二氧化钛、氧化锌、滑石粉、碳酸钙、硅灰石粉、云母粉的一种或一种以上。
6.根据权利要求1或5所述的水性反辐射隔热涂料,其特征是其中所述的颜填料中颜料包括:二氧化钛、氧化锌、氧化铁红、氧化铁黄的一种或一种以上。
7.根据权利要求1所述的水性反辐射隔热涂料,其特征是组分中包括重量配比为2-5的具有纤维结构的绒毛粉。