CN1238654C - Process for removing oil stealing branch pipes on oil pipelines - Google Patents
Process for removing oil stealing branch pipes on oil pipelines Download PDFInfo
- Publication number
- CN1238654C CN1238654C CN 200410019229 CN200410019229A CN1238654C CN 1238654 C CN1238654 C CN 1238654C CN 200410019229 CN200410019229 CN 200410019229 CN 200410019229 A CN200410019229 A CN 200410019229A CN 1238654 C CN1238654 C CN 1238654C
- Authority
- CN
- China
- Prior art keywords
- stolen
- arm
- resin
- low temperature
- oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention discloses a technique for removing an oil stealing branch pipe on an oil transporting pipeline, which belongs to the online reparation technology of oil transporting pipelines. The technique comprises the steps that the oil stealing branch pipe is detected, fast low-temperature cured resin is prepared, and the fast low-temperature cured resin is injected into the oil stealing branch pipe; the degree of cure is detected, and the oil stealing branch pipe is eliminated. The fast low-temperature cured resin is composed of polyurethane, epoxy resin, phenolic resin, filling materials and auxiliary agents; prepared resin is detected and controlled by a computer measure and control system, the pressure of 1.0 to 1.5MPa is adopted, and the resin is injected into the oil stealing branch pipe by a high-pressure precision measuring injection pump and is solidified at the temperature of 20 to 30 DEG C in 5 to 30 minutes. The technique has the advantages of simple operation process and quick and safe implementation, and is convenient to popularize and apply.
Description
Technical field
The present invention relates to a kind of stolen branch pipe technology of removing on the petroleum pipeline, belong to the online recovery technique of petroleum pipeline.
Background technique
Crude oil long-distance transmission pipeline is often by lawless person's adapter stolen of punching, and pipeline is in case leak, and this not only causes the loss of crude oil, the generation economic loss, and very easily cause the pollution of environment, bring potential safety hazard.Remove the stolen arm operation on the petroleum pipeline, belong to mobile, field work; Have more provisional, sudden, urgent, therefore require this operation rapidly, safety, reliable.At present, the relevant both at home and abroad document of removing the stolen branch pipe technology technology on the petroleum pipeline does not appear in the newspapers.
Summary of the invention
The object of the present invention is to provide a kind of stolen branch pipe technology of removing on the petroleum pipeline, this manufacturing process is simple to operate, implements rapidly safety.
The present invention is realized by following technical proposals, adopts computer measurement and control system to detect control, and high voltage precision metered shot pump implements to remove the stolen branch pipe technology on the petroleum pipeline.It is characterized in that comprising following process:
1. the stolen arm detects
The stolen arm is detected clear and definite caliber, pipe range and stolen aperture parameters.
2. prepare quick low temperature curing resin
(1) the quick curing urethane base of low temperature resin formula: A component and mass percent thereof are: the iron powder of packing material 1: Mean particle diameter<500um, zinc powder or aluminium powder, 10-40; The WC of packing material 2: Mean particle diameter<300um, grey molybdenum ore powder, SiO
2, TiO
2, in calcium carbonate, French chalk, gesso, white clay and the silicious marl one or both, 20-60; Host 1: castor oil: 10-33; Host 2: isocyanates (TDI): 8-22; Auxiliary agent: butanone, 1-3;
B component and mass percent thereof are: modified fatty amine and di hexylidene triamine mixture: 34-68; Bisphenol-A: 32-66;
A∶B=(3-6)∶1
(2) low temperature fast curable epoxy, phenolic group resin prescription: A component and mass percent thereof are: the iron powder of packing material 1: Mean particle diameter<500um, zinc powder or aluminium powder, 15-45; The WC of packing material 2: Mean particle diameter<300um, grey molybdenum ore powder, SiO
2, TiO
2, in calcium carbonate, French chalk, gesso, white clay and the silicious marl one or both, 10-30; Host 1: epoxy resin (E-51 or E-44): 10-30; Host 2: phenolic resin: 5-25; Health alcohol: 1-8;
B component and mass percent thereof are: coumarone: 20-40; T-31:0-30; Promoter (DMP-30): 20-40; Propylene oxide propylene ether (500#): 20-45;
A∶B=(2.5-4.5)∶1
3. in the stolen arm, inject quick low temperature curing resin: with pack into the detachable cavity of high voltage precision metered shot pump of the above-mentioned quick low temperature curing resin for preparing, adopt computer control, under 1.0-1.5MPa pressure, go in the stolen arm with high pressure accurate measurement infusion, detect the position that resin arrives the stolen branched pipe with detection facility, realize at normal temperatures solidifying.
4. detection state of cure:, detect and the judgement state of cure according to the changing condition of resin hardness and tube wall temperature.
5. cut off the stolen arm: adopt the wheel disc saw, cut off the stolen arm.
This technology can be removed the stolen arm on the oil transport pipeline safely, rapidly, and is simple, convenient.
Description of drawings
Fig. 1 is the stolen manifold configuration schematic representation on the existing petroleum pipeline.1 is the stolen arm among the figure, and 2 is ball valve, and 3 is the stolen hole, and 4 is petroleum pipeline.
Fig. 2 is a manufacturing process block diagram of the present invention.
Embodiment
Embodiment 1
Stolen arm parameter: caliber: 50mm, pipe range: 360mm, ball valve: DN50, stolen aperture: 4mm.
Low temperature fast curable epoxy, phenolic group resin prescription:
A component and mass percent: iron powder (Mean particle diameter 50um): 30; CaCO
3Powder (Mean particle diameter 40um): 48; Bad epoxy resins E-51:12; Phenolic resin: 8; Health alcohol: 2;
B component and mass percent: coumarone: 30; Promoter (DMP-30): 30; Propylene oxide propylene ether (500#): 40;
A∶B=4∶1
Low temperature fast-curing resin method for implanting: injection pressure: 1.2MPa; Unit time injection amount: 190g/min; Per unit volume consumption: 2.31g/cm
3Under curing time: 20-25 ℃, 23-28min;
Adopt the wheel disc sawing to cut;
Existing stolen arm parameter: caliber: 50mm, length: 300mm, ball valve: DN50, stolen aperture: 2mm.
The quick curing urethane base of low temperature resin formula:
A component and mass percent: iron powder (Mean particle diameter 50um): 23; WC, grey molybdenum ore powder (Mean particle diameter 30um): 47; Castor oil: 18; Isocyanates (TDI): 10; Butanone: 2;
B component and mass percent: polyamine (modified fatty amine, di hexylidene triamine) mixture: 60; Bisphenol-A: 40;
A∶B=5∶1
New type low temperature fast-curing resin method for implanting: injection pressure: 1.3MPa; Unit time injection amount: 130g/min; Per unit volume consumption: 2.25g/cm
3Under curing time: 20-25 ℃, 25-28min.Adopt the wheel disc sawing to cut;
Claims (2)
1. stolen branch pipe technology of removing on the petroleum pipeline, this technology implements to remove stolen arm on the petroleum pipeline by adopting computer measurement and control system and high voltage precision metered shot pump, it is characterized in that comprising following process:
1) the stolen arm detects:
The stolen arm is detected clear and definite caliber, pipe range and stolen aperture parameters;
2) prepare quick low temperature curing resin:
The quick curing urethane base of low temperature resin formula: A component and mass percent thereof are: the iron powder of packing material 1: Mean particle diameter<500um, zinc powder or aluminium powder, 10-40; The WC of packing material 2: Mean particle diameter<300um, grey molybdenum ore powder, SiO
2, TiO
2, in calcium carbonate, French chalk, gesso, white clay and the silicious marl one or both, 20-60; Host 1: castor oil: 10-33; Host 2: isocyanates: 8-22; Auxiliary agent: butanone, 1-3;
B component and mass percent thereof are: modified fatty amine and di hexylidene triamine mixture: 34-68; Bisphenol-A: 32-66;
A∶B=(3-6)∶1;
3) in the stolen arm, inject quick low temperature curing resin: with pack into the detachable cavity of high voltage precision metered shot pump of the above-mentioned quick low temperature curing resin for preparing, adopt computer control, under 1.0-1.5MPa pressure, go in the stolen arm with high pressure accurate measurement infusion, detect the position that resin arrives the stolen branched pipe with detection facility, realize at normal temperatures solidifying;
4) detect state of cure:, detect and the judgement state of cure according to the changing condition of resin hardness and tube wall temperature;
5) cut off the stolen arm: adopt the wheel disc saw, cut off the stolen arm.
2. stolen branch pipe technology of removing on the petroleum pipeline, this technology implements to remove stolen arm on the petroleum pipeline by adopting computer measurement and control system and high voltage precision metered shot pump, it is characterized in that comprising following process:
1) the stolen arm detects:
The stolen arm is detected clear and definite caliber, pipe range and stolen aperture parameters;
2) prepare quick low temperature curing resin:
Low temperature fast curable epoxy, phenolic group resin prescription: A component and mass percent thereof are: the iron powder of packing material 1: Mean particle diameter<500um, zinc powder or aluminium powder, 15-45; The WC of packing material 2: Mean particle diameter<300um, grey molybdenum ore powder, SiO
2, TiO
2, in calcium carbonate, French chalk, gesso, white clay and the silicious marl one or both, 10-30; Host 1: epoxy resin E-51 or E-44:10-30; Host 2: phenolic resin: 5-25; Health alcohol: 1-8;
B component and mass percent thereof are: coumarone: 20-40; T-31:0-30; Altax P-30:20-40; Propylene oxide propylene ether 500#:20-45;
A∶B=(2.5-4.5)∶1;
3) in the stolen arm, inject quick low temperature curing resin: with pack into the detachable cavity of high voltage precision metered shot pump of the above-mentioned quick low temperature curing resin for preparing, adopt computer control, under 1.0-1.5MPa pressure, go in the stolen arm with high pressure accurate measurement infusion, detect the position that resin arrives the stolen branched pipe with detection facility, realize at normal temperatures solidifying;
4) detect state of cure:, detect and the judgement state of cure according to the changing condition of resin hardness and tube wall temperature;
5) cut off the stolen arm: adopt the wheel disc saw, cut off the stolen arm.