CN1236755A - Cinnabarite grout and its usage - Google Patents
Cinnabarite grout and its usage Download PDFInfo
- Publication number
- CN1236755A CN1236755A CN 98111314 CN98111314A CN1236755A CN 1236755 A CN1236755 A CN 1236755A CN 98111314 CN98111314 CN 98111314 CN 98111314 A CN98111314 A CN 98111314A CN 1236755 A CN1236755 A CN 1236755A
- Authority
- CN
- China
- Prior art keywords
- parts
- boccaro
- slurry
- ground
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A red stoneware grout is mainly prepared from white prime glaze, raw red stoneware ore, clay and water through grinding. A red stoneware coated metal product is made up through coating prime glaze on surface of metal blank, calcining at 800-1000 deg.C, coating said red stoneware grout, and calcining at 800-1000 deg.c, and features the lustre and health-care function of red stoneware, light weight, high thermal conductivity and easy manufacture.
Description
The present invention relates to boccaro slurry with the making of boccaro raw ore.
The boccaro goods have unique texture and color and luster, and are harmless with the food and drink tool that boccaro is made, but pure its shortcoming of boccaro goods is that 1. boccaro raw ore consumptions are big, and the resource-constrained of boccaro raw ore; 2. relatively heavier; 3. make, the firing process complexity, yield rate is low.
The purpose of this invention is to provide a kind of boccaro slurry, can make the metal boccaro coated products that the boccaro layer is covered in the metal base primary coat with boccaro slurry of the present invention.
Technical scheme of the present invention is as follows:
A kind of boccaro slurry, it mainly comprises 100 parts of white base glazes, 52～92 parts in boccaro raw ore, 95～100 parts in 3～5 parts of clays and water fully grind pulping through ball mill, promptly get boccaro slurry of the present invention.
In above-mentioned boccaro slurry of the present invention, can add 6～7 parts of iron oxide reds, grind together, to regulate the colourity of goods.
In above-mentioned boccaro slurry of the present invention, can add 1～5 part in wheat metal plate stone, grind together, to increase trace element the human body beneficial.
In above-mentioned boccaro slurry of the present invention, can add 0.5～1.5 part of Sodium chromate or (with) 0.5～1.5 part of barium molybdate grinds together, to increase the coating adhesion of goods.
The purposes of boccaro slurry of the present invention is to apply ground-coat enamel earlier on the metal body surface, the ground-coat enamel of this ground-coat enamel and enamelware is basic identical, can mainly comprise 45～55 parts of 106 nickel enamels, 45～55 parts of 108 antimony barium ground-coat enamels, 5～10 parts of clays, 1～2 part of weisspiessglanz, 1～2 part of barium molybdate, 0.2～0.7 part of borax, 50～60 parts in 0.2～0.4 part of Sodium Nitrite and water.Drying in the air, drying below 100 ℃ after applying ground-coat enamel, burning till at 800～1000 ℃ then, after the cooling, applying boccaro slurry of the present invention again, after the oven dry of drying in the air below 100 ℃, burning till at 800～1000 ℃ again, promptly making metal boccaro coated products of the present invention.
The metal boccaro coated products that adopts boccaro slurry of the present invention to make, because the former mineral content height of boccaro in the boccaro coating, so have more the characteristics of pure boccaro goods, harmless, and it is made easily, metal body can impact briquetting, through applying, burn till and promptly get metal boccaro coated products, yield rate height, goods are light and handy, are particularly suitable for making table ware.
Further specify the present invention by the following examples.
Embodiment 1. gets 100 parts of white base glazes, adds 52 parts in boccaro raw ore, and 3 parts in Suzhou spy's soil adds 95 parts in water, puts into ball mill, grinds pulping, promptly gets boccaro slurry of the present invention.
Embodiment 2. gets 100 parts of white base glazes, adds 70 parts in boccaro raw ore, 4 parts of kaolin, and 7 parts of iron oxide reds add 100 parts in water, put into ball mill, grind pulping, promptly get boccaro slurry of the present invention.
Embodiment 3. gets 100 parts of white base glazes, adds 80 parts in boccaro raw ore, 5 parts in Suzhou spy's soil, and 6 parts of iron oxide reds, 5 parts of medical stones add 100 parts in water, put into ball mill, grind pulping, promptly get boccaro slurry of the present invention.
Embodiment 4. gets 100 parts of white base glazes, adds 92 parts in boccaro raw ore, 5 parts of kaolin, and 3 parts of medical stones add 110 parts in water, put into ball mill, grind pulping, promptly get boccaro slurry of the present invention.
Embodiment 5. gets 100 parts of white base glazes, adds 90 parts in boccaro raw ore, 4 parts in Suzhou spy's soil, and 5 parts of medical stones, 1.0 parts of Sodium chromates, 1.0 parts of barium molybdates add 100 parts in water, put into ball mill, grind pulping, promptly get boccaro slurry of the present invention.
Embodiment 6. gets 50 parts of 106 nickel enamels, 50 parts of 108 antimony barium ground-coat enamels, and 5 parts of clays, 1 part of weisspiessglanz, 1 part of barium molybdate, 0.2 part of borax, 0.2 part of Sodium Nitrite, 50 parts in water is put into ball mill, grinds pulping, promptly gets the ground-coat enamel material.
Embodiment 7. gets 50 parts of 106 nickel enamels, 50 parts of 108 antimony barium ground-coat enamels, and 10 parts of clays, 2 parts of weisspiessglanzs, 2 parts of barium molybdates, 0.7 part of borax, 0.4 part of Sodium Nitrite, 60 parts in water is put into ball mill, grinds pulping, promptly gets the ground-coat enamel material.
Embodiment 8. usefulness 0.5mm steel plates strike out the electric cooker inner container shape, the surface is after clean, be coated with thick embodiment 6 ground-coat enamel material with 0.1～0.2mm, after 80 ℃ of oven dry, 880 ℃ of roastings 180 seconds, after the cooling, be coated with boccaro slurry with the thick embodiment 1 of 0.3～0.4mm, 880 ℃ of roastings 180 seconds, promptly get metal boccaro coating electric cooker inner container of the present invention after 80 ℃ of oven dry.
Embodiment 9. usefulness 0.8mm steel plates strike out the electric cooker inner container shape, the surface is after clean, be coated with thick embodiment 7 ground-coat enamel material with 0.1～0.2mm, after 85 ℃ of oven dry, 950 ℃ of roastings 150 seconds, after the cooling, be coated with boccaro slurry with the thick embodiment 2 of 0.3～0.4mm, 980 ℃ of roastings 150 seconds, promptly get metal boccaro coating electric cooker inner container of the present invention after 80 ℃ of oven dry.
This electric cooker inner container has bright-coloured boccaro look, and boccaro texture is strong.
Embodiment 10. usefulness 0.8mm steel plates strike out the electric cooker inner container shape, the surface is after clean, be coated with thick embodiment 6 ground-coat enamel material with 0.1～0.2mm, after 90 ℃ of oven dry, 880 ℃ of roastings 180 seconds, after the cooling, be coated with boccaro slurry with the thick embodiment 3 of 0.3～0.4mm, after 80 ℃ of oven dry,, promptly get metal boccaro coating electric cooker inner container of the present invention 900 ℃ of roastings 180 seconds.This inner bag not only has good boccaro texture, and health-care effect is arranged.
Embodiment 11. usefulness 0.5mm steel plates strike out the electric cooker inner container shape, the surface is after clean, be coated with thick embodiment 7 ground-coat enamel material with 0.1～0.2mm, after 80 ℃ of oven dry, 980 ℃ of roastings 150 seconds, after the cooling, be coated with boccaro slurry with the thick embodiment 5 of 0.3～0.4mm, after 75 ℃ of oven dry,, promptly get metal boccaro coating electric cooker inner container of the present invention 900 ℃ of roastings 180 seconds.This inner bag not only has good boccaro texture and health-care effect, and the bonding force of coating and metal is good especially.
Claims (5)
1. a boccaro slurry is characterized in that mainly comprising 100 parts of white base glazes, 52～92 parts in boccaro raw ore, and 3～5 parts of clays and water grind pulping for 95～110 parts.
2. boccaro slurry according to claim 1 is characterized in that being added with 3～7 parts of iron oxide reds.
3. boccaro slurry according to claim 1 and 2 is characterized in that being added with 1～5 part of medical stone.
4. the purposes of boccaro slurry, it is characterized in that at metal body surface-coated ground-coat enamel, after drying in the air below 100 ℃, drying, burn till, apply the boccaro slurry then at 800～1000 ℃, after the oven dry of drying in the air below 100 ℃, burn till at 800～1000 ℃ and to make metal boccaro coated products.
5. report the purposes of the boccaro slurry of stating according to claim 4, it is characterized in that ground-coat enamel mainly comprises 45～55 parts of 106 nickel enamels, 45～55 parts of 108 antimony barium ground-coat enamels, 5～10 parts of clays, 1～2 part of weisspiessglanz, 1～2 part of barium molybdate, 0.2～0.7 part of borax, 50～60 parts in 0.2～0.4 part of Sodium Nitrite and water.