CN1231608C - 饰品合金 - Google Patents
饰品合金 Download PDFInfo
- Publication number
- CN1231608C CN1231608C CN 02138019 CN02138019A CN1231608C CN 1231608 C CN1231608 C CN 1231608C CN 02138019 CN02138019 CN 02138019 CN 02138019 A CN02138019 A CN 02138019A CN 1231608 C CN1231608 C CN 1231608C
- Authority
- CN
- China
- Prior art keywords
- alloy
- platinum
- content
- accounts
- ornaments
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种贵金属基合金,特别涉及一种制作装饰品用的饰品合金,它包含有银和铂,其中,银的含量占合金总重量的50%以上,该饰品合金的成本极低,合金的色泽好,可塑性强,便于加工成各种各样的装饰品,强度和硬度较好。
Description
技术领域
本发明涉及一种贵金属基合金,特别涉及一种制作装饰品用的饰品合金。
背景技术
现有技术中常用含铂90%以上的合金作为制作装饰品的材料,因为铂金比较稀少且价格昂贵,因而饰品制作成本很高。
发明内容
本发明的目的在于克服现有技术中的不足之处,而提供一种价格便宜、色泽好的饰品合金。
本发明的目的是通过如下方式来实现的。
饰品合金,其组成要点为:它的组成为银,铂和铑,其中,银的含量占合金总重量的80%~97%,铂的含量占合金总重量的2%~15%,铑的含量占合金总重量的1~5%。
银为白色而有光泽的贵金属,质软,其延展性是除金以外其他金属中最好的,其在地壳中的含量要比铂高几十上百倍,提炼也很方便,同时价格也较为便宜;而铂为银白色金属,质同样很柔软。
这样,本发明用银取代了大部分的铂,成本大大降低了,而成品的色泽并未受到丝毫的影响(铂和银同样是银白色的金属),并且这种组合还令本发明具有出乎意料的有益效果:铂合金的延展性得到了很好的改善,因而采用这种饰品合金制作装饰品时,制作性能加强了。
铂的含量占合金总重量的2%~15%,从技术要求方面而言,该饰品合金的制作性能可以得到很好的改善,且合金本身的强度和硬度能够得到较好的保留;而就成本而言,银的含量达到这样的比例,成本的下降幅度显而易见。
综合考虑各项指数,最佳的银及铂的含量比例应为:银的含量占合金总重量的90%,铂的含量占合金总重量的6%。
铑为银白色金属,表面光亮,质极硬,耐磨,在热的状态下十分柔韧,易于加工成细丝或薄片。这样,在合金中加入微量铑,可以进一步改善合金的制作性能(便于加工成各种细小且精美的饰品),并且铑的质极硬,比铂硬,从而可以确保在加入足够的银以后合金的强度和硬度仍然非常好。
钯也为银白色金属,质较柔软,具有良好的延展性和可塑性,能锻造、压延和拉丝,并且光泽度好,钯比铑在自然界中的含量高且价格便宜,因此也可以在合金中加入钯而不是铑以在保证合金硬度的同时进一步降低成本。
在合金中或加入铑或加入钯,使得合金的可塑性能改善了很多,据大百科全书及试验表明:铂与铂系元素熔成合金后,强度和硬度明显比铂增大,铑、钯为铂系元素,因而铂铑合金、铂钯合金的强度和硬度比铂大。
综上所述,本发明相比现有技术具有如下优点:成本极低,合金的色泽好,可塑性强,便于加工成各种各样的装饰品,强度和硬度较好。
具体实施方式
下面结合实施例对本发明进行理详细的描述。
实施例1:饰品合金,含有银和铂,其中,银的含量占合金总重量的80%,铂的含量占合金总重量的15%,铑的含量占合金总重量的5%。
实施例2:饰品合金,含有银和铂,其中,银的含量占合金总重量的85%,铂的含量占合金总重量的2%,钯的含量占合金总重量的13%。
实施例3:饰品合金,含有银和铂,其中,银的含量占合金总重量的97%,铂的含量占合金总重量的2%,钯的含量占合金总重量的1%。
最佳实施例:饰品合金,含有银和铂,其中,银的含量占合金总重量的90%,铂的含量占合金总重量的6%,铑的含量占合金总重量的4%。
Claims (3)
1、饰品合金,其特征在于,它的组成为银,铂和铑,其中,银的含量占合金总重量的80%~97%,铂的含量占合金总重量的2%~15%,铑的含量占合金总重量的1~5%。
2、根据权利要求1所述的饰品合金,其特征在于,银的含量占合金总重量的90%。
3、根据权利要求1所述的饰品合金,其特征在于,铂的含量占合金总重量的6%。