CN1216311A - Emulsion paint putty - Google Patents
Emulsion paint putty Download PDFInfo
- Publication number
- CN1216311A CN1216311A CN 97109288 CN97109288A CN1216311A CN 1216311 A CN1216311 A CN 1216311A CN 97109288 CN97109288 CN 97109288 CN 97109288 A CN97109288 A CN 97109288A CN 1216311 A CN1216311 A CN 1216311A
- Authority
- CN
- China
- Prior art keywords
- emulsion paint
- proportioning
- putty
- base
- calcite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to chemical building material used for decoration of inner and outer walls. Technologically, the present invention features that the base material is produced with the material including PVA, gelatine, glycerine, glycol, CMC, sodium lauryl sulfate and water and through three-step reaction; the pigment and stuffing consists of talcum powder, wollastonite, calcite and active calcium hydroxide; and the dispersion process includes three stages of stirring, grinding in colloidal mill and filtration in filter. The product has the features of easy use, high adhesion to base and emulsion paint, high hardness and excellent water resistance, alkali resistance and watertightness. Its use makes it possible to raise working efficiency, reduce emulsion paint consumption, lower building cost and prolong the service life of emulsion paint.
Description
The invention belongs to and apply to the chemical building material product that the building inside and outside wall face is decorated.
In building, in the decoration industry, before metope brushing emulsion paint, all will be through the operation of one batch of Puttying, and up to now, the source of putty is all by the on-the-spot modulation of painter, so some places also are called putty " existing ash ".Development and progress along with building decorating industry, the emerge in multitude of medium-to-high grade emulsion paint particularly, the synthetic putty in this scene is owing to be subjected to restrictions such as material source, modulation instrument, state of the art, more and more be difficult to adapt to the requirement of decoration, peeling occurred, come off, not water-fast, many shortcomings such as the life-span is short.The present invention is by the science component design, and starting material are selected in strictness, the tight technological process and the mode of production of batch production, and the finished product putty of production has changed above-mentioned condition, has improved working efficiency, has improved base layer quality, has prolonged work-ing life.
Main points of the present invention are that base-material is made by three-step reaction by PVA, gelatin, glycerine, ethylene glycol, carboxymethyl cellulose, sodium laurylsulfate and water, color stuffing is made up of talcum powder, wollastonite, calcite and active hydrogen calcium oxide, and its dispersion process is ground through dispersed with stirring, colloidal mill successively and filter filters three phases.
Concrete prescription and technological process are as follows:
1, at first in being 1000 liters reactor, useful volume adds entry 1000kg and PVA100kg, starting agitator stirs, be blown into the water vapor heating simultaneously, temperature rise reduces the amount of steaming out, with the maintenance heat balance during to g3 ℃, make temperature remain on 93～98 ℃, add gelatin 8kg simultaneously, be incubated 1 hour, cool off stand-by.
2, getting carboxymethyl cellulose 15kg pours in the agitation vat, add 60 ℃ of hot water 400kg, stirring makes it abundant dispersion, pour tap water and ice cube 600kg altogether after being uniformly dispersed into, adjust system temperature below 10 ℃, make it fully to expand peptization, add glycerine 30kg simultaneously, the back storage and aging 48 hours that stirs is stand-by.
3, get the glue 1000kg that step 1 makes, the glue 200kg that step 2 makes adds ethylene glycol 3kg in addition, sodium laurylsulfate 10kg, and mixing and stirring promptly gets base-material.
4, getting the base-material 200kg that step 3 makes pours in the agitator, add zinc sulfide white 50kg, talcum powder 20kg, wollastonite powder 50kg, calcite in powder 250kg and active hydrogen calcium oxide powder 50kg successively, stir, pour in the colloidal mill then and grind, pour into after the grinding to filter in the centrifugal filter and get product.
The putty technical indicator that adopts above prescription and technology to make is as follows:
Condition in container: even, fine and smooth, nothing caking
Fineness is not more than: 75 μ m 1
Hardness is not less than: 5H
Solid content is not less than: 60%
Sticking power is not less than: 2 grades
Surface drying time is not more than: 6h
Do solid work the time, be not more than: 24h
Water tolerance (96h): non-foaming, do not come off
Alkali resistance (48h): non-foaming, do not come off
Watertightness (0.3MPa, 30min): do not have the infiltration phenomenon
Claims (4)
1. one kind is used for the emulsion paint putty that the building inside and outside wall face is decorated, and its functional character is the function of double its filling, back cover and reinforcing basic unit, is convenient to mechanized operation simultaneously and uses.
2. according to the described putty of claim 1, it is characterized in that base-material divided for three steps made, the first step is crossed reacting by heating by PVA, gelatin and water channel and is made, and its proportioning is followed successively by: 5～10: 0.5～0.8: 100; Second step was made up of carboxymethyl cellulose, G ﹠ W, and its proportioning is 1.5: 3: 100; The glue that the 3rd step was made respectively by first, second two step adds ethylene glycol in addition and sodium laurylsulfate forms, and its proportioning is: 100: 20: 0.3: 1.
3. according to the described putty of claim 2, it is characterized in that color stuffing is made up of zinc sulfide white, talcum material, wollastonite, calcite and active hydrogen calcium oxide, its proportioning is followed successively by: 1: 2: 1: 5: 1.
4. according to claim 2 and require 3 described putty, passed through dispersed with stirring when it is characterized in that disperseing successively, colloidal mill grinds and filter filters three process.